CN107687048A - A kind of wool imitates the production technology of straight-bar machines tmaterial - Google Patents
A kind of wool imitates the production technology of straight-bar machines tmaterial Download PDFInfo
- Publication number
- CN107687048A CN107687048A CN201710691755.4A CN201710691755A CN107687048A CN 107687048 A CN107687048 A CN 107687048A CN 201710691755 A CN201710691755 A CN 201710691755A CN 107687048 A CN107687048 A CN 107687048A
- Authority
- CN
- China
- Prior art keywords
- lopping
- wool
- tmaterial
- drying
- straight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the production technology that a kind of wool imitates straight-bar machines tmaterial, selects, patterning design, looming weaving, bleachinges and dyeing, drying and stentering forming process by raw material, completes the production technology that wool imitates straight-bar machines tmaterial;The advantage of the invention is that：The weaving method that the knitting fabric of the present invention passes through uniqueness, cloth cover is set to produce the effect that V-type eyed structure and plain plane coexist, mesh portion third dimension is strong, plain part is flat vertical bar, there is the effect of flat knitting by using the woven fabric of circular knitting machine, woven woollen shirt fabric can be commonly used to, weaving is convenient and simple.
Description
Technical field
The invention belongs to be knitted fabric technical field, and in particular to a kind of wool imitates the production technology of straight-bar machines tmaterial.
Background technology
Current consumer proposes higher and higher requirement to the comfortableness and feature of textile, and knitting fabric is to utilize
Various raw materials and the yarn of kind are formed coil, connect into the technical process of knitted fabric through string set again by knitting needle.It is knitted fabric matter
Ground is soft, there is good wrinkle resistance and gas permeability, and has larger extensibility and elasticity.Come with New textile material, new technology
Development and enterprise innovation consciousness enhancing, greatly driven the exploitation dynamics of weaving face fabric and horizontal improved.
Wool fiber is mainly made up of protein, and P, N element are contained in fiber, is had preferably naturally from anti-flammability, the limit
Oxygen index (OI) LOI=24.5~25.0, the advantages that flexible good, hygroscopicity of fiber is strong, fiber hollow heat insulation is warming.
Weft-knitted fabric mainly has three kinds of construction units, i.e., lopping, tuck and does not weave.Lopping is represented to eat full pin, knitted
Pin completes whole braiding process, forms coil.Half pin is eaten in tuck expression, and knitting needle simply eats yarn without knocking over, lopping, in old line
Circle arc is formed on circle.Represent not eat pin without weaving, knitting needle does not eat pin, and flotation line is formed in fabric backing.One group of coil is completed to compile
The structure knitted is referred to as road.
Weft-knitted fabric is mainly two kinds of facecloth and double-sided cloth at present, both cloth it is relatively simple for structure, lack flower
The change of type, using being subject to certain restrictions.
Circular knitting machine fabric is more fine and smooth, and flat knitting is more rough, how using circular knitting machine fabric knitting to go out knitting for flat knitting
Thing effect, it is the technological break-through sought by each enterprise.
The content of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to a kind of profile effect with flat knitting is now provided,
The succinct wool of weaving process imitates the production technology of straight-bar machines tmaterial.
In order to solve the above technical problems, the technical solution adopted by the present invention is：A kind of wool imitates the production of straight-bar machines tmaterial
Technique, its innovative point are：Select, patterning design, looming weaving, bleaching and dyeing, drying and stentering forming process by raw material, complete
Wool imitates the production technology of straight-bar machines tmaterial；Comprise the following steps that：
（1）Raw material selects：From 34Nm 100% wool, the twist factor of the wool is 270；
（2）Patterning design：The tmaterial is combined by V-type mesh knitting zone and plain weave knitting zone, the plain weave area
The both ends of V-type mesh knitting zone are compounded in, the V-type mesh woven extent plain weave area is integral structure；
（3）Looming weaving：Weaved using 30 pin 24G single-side computer jacquard weave, the V-type mesh knitting zone is by 8 road yarns
One circulation of composition carries out braiding and formed, and wool yarns are that 163mm/50 mesh yarn is grown；
（4）Bleaching and dyeing：Carry out floating bottom oil removing under the conditions of 85 DEG C, auxiliary agent is DA degreasers, soda ash, hydrogen peroxide, hydrogen peroxide stabilizer
And bleeding agent, pH values 9.5-10.5, processing time are 42-48 minutes, are then dyed using conventional dyeing process, use is dense
The HKY color fixing agent for 3% is spent, makees fixation treatment, color fixing temperature is 42-46 DEG C, time 20min, 10min is washed, in 104-
106 DEG C of drying 2min, pad ULTRA softening agents, it is normal temperature to pad bath temperature degree；
（5）Drying：Fabric after bleachinging and dyeing carries out drying, and the drying temperature is 110-120 DEG C, and the criteria thus the drying time is 30-
60s；
（6）Stentering forming：Carry out stentering forming after drying on forming machine again, the breadth is 1.5-1.7m, the forming machine
Speed is 25-30m/min, and the setting temperature is 75-85 DEG C.
Further, the step（3）In the specific braiding structure of V-type mesh knitting zone be：The first via and the second tunnel
For lopping, lopping, lopping, lopping；3rd road and the 4th tunnel are tuck, lopping, tuck, lopping；5th road and the 6th tunnel be into
Circle, lopping, lopping, lopping；7th road and the 8th tunnel are lopping, tuck, lopping, tuck.
Further, the step（4）In auxiliary agent in DA degreasers addition be 2g/l, soda ash addition is 1.4g/
L, hydrogen peroxide addition are 14g/l, and hydrogen peroxide stabilizer addition is 4g/l, and bleeding agent FFA additions are 0.4g/l.
Beneficial effects of the present invention are as follows：The knitting fabric of the present invention makes cloth cover produce V-type by the weaving method of uniqueness
The effect that eyed structure and plain plane coexist, mesh portion third dimension is strong, and plain part is flat vertical bar, by using circle
The woven fabric of machine has the effect of flat knitting, can be commonly used to woven woollen shirt fabric, and weaving is convenient and simple.
Brief description of the drawings
Fig. 1 is the structural representation of the V-type eyed structure of the present invention.
Embodiment
Embodiments of the present invention are illustrated by particular specific embodiment below, those skilled in the art can be by this explanation
Content disclosed by book understands other advantages and effect of the present invention easily.
It is as shown in Figure 1 the structural representation of V-type eyed structure of the invention.
Embodiment 1
A kind of wool imitates the production technology of straight-bar machines tmaterial, selected by raw material, patterning design, looming weaving, bleaching and dyeing, drying and
Stentering forming process, complete the production technology that wool imitates straight-bar machines tmaterial；Comprise the following steps that：
（1）Raw material selects：From 34Nm 100% wool, the twist factor of wool is 270；
（2）Patterning design：Tmaterial is combined by V-type mesh knitting zone and plain weave knitting zone, and plain weave area is compounded in V-type
The both ends of mesh knitting zone, V-type mesh woven extent plain weave area are integral structure；
（3）Looming weaving：Weaved using 30 pin 24G single-side computer jacquard weave, V-type mesh knitting zone is made up of 8 road yarns
One circulation carries out braiding and formed, and wool yarns are grown for 163mm/50 mesh yarn；
（4）Bleaching and dyeing：Carry out floating bottom oil removing under the conditions of 85 DEG C, auxiliary agent is DA degreasers, soda ash, hydrogen peroxide, hydrogen peroxide stabilizer
And bleeding agent, pH value 9.5, processing time are 42 minutes, are then dyed using conventional dyeing process, concentration is 3% HKY
Color fixing agent, make fixation treatment, color fixing temperature is 42 DEG C, time 20min, washes 10min, dries 2min at 104 DEG C, pads
ULTRA softening agents, it is normal temperature to pad bath temperature degree；
（5）Drying：Fabric after bleachinging and dyeing carries out drying, and drying temperature is 110 DEG C, criteria thus the drying time 30s；
（6）Stentering forming：Stentering forming, breadth 1.5m are carried out on forming machine again after drying, forming machine speed is 25m/
Min, setting temperature are 75 DEG C.
The specific braiding structure of V-type mesh knitting zone is：The first via and the second tunnel are lopping, lopping, lopping, lopping；The
Three roads and the 4th tunnel are tuck, lopping, tuck, lopping；5th road and the 6th tunnel are lopping, lopping, lopping, lopping；7th tunnel
It is lopping, tuck, lopping, tuck with the 8th tunnel.
DA degreasers addition is 2g/l in auxiliary agent, and soda ash addition is 1.4g/l, and hydrogen peroxide addition is 14g/l, double
Oxygen water stabilizer addition is 4g/l, and bleeding agent FFA additions are 0.4g/l.
Embodiment 2
A kind of wool imitates the production technology of straight-bar machines tmaterial, selected by raw material, patterning design, looming weaving, bleaching and dyeing, drying and
Stentering forming process, complete the production technology that wool imitates straight-bar machines tmaterial；Comprise the following steps that：
（1）Raw material selects：From 34Nm 100% wool, the twist factor of wool is 270；
（2）Patterning design：Tmaterial is combined by V-type mesh knitting zone and plain weave knitting zone, and plain weave area is compounded in V-type
The both ends of mesh knitting zone, V-type mesh woven extent plain weave area are integral structure；
（3）Looming weaving：Weaved using 30 pin 24G single-side computer jacquard weave, V-type mesh knitting zone is made up of 8 road yarns
One circulation carries out braiding and formed, and wool yarns are grown for 163mm/50 mesh yarn；
（4）Bleaching and dyeing：Carry out floating bottom oil removing under the conditions of 85 DEG C, auxiliary agent is DA degreasers, soda ash, hydrogen peroxide, hydrogen peroxide stabilizer
And bleeding agent, pH values 10.5, processing time are 48 minutes, are then dyed using conventional dyeing process, concentration is 3%
HKY color fixing agent, make fixation treatment, color fixing temperature is 46 DEG C, time 20min, washes 10min, and 2min, leaching are dried at 106 DEG C
ULTRA softening agents are rolled, it is normal temperature to pad bath temperature degree；
（5）Drying：Fabric after bleachinging and dyeing carries out drying, and drying temperature is 120 DEG C, criteria thus the drying time 60s；
（6）Stentering forming：Stentering forming, breadth 1.7m are carried out on forming machine again after drying, forming machine speed is 30m/
Min, setting temperature are 85 DEG C.
The specific braiding structure of V-type mesh knitting zone is：The first via and the second tunnel are lopping, lopping, lopping, lopping；The
Three roads and the 4th tunnel are tuck, lopping, tuck, lopping；5th road and the 6th tunnel are lopping, lopping, lopping, lopping；7th tunnel
It is lopping, tuck, lopping, tuck with the 8th tunnel.
DA degreasers addition is 2g/l in auxiliary agent, and soda ash addition is 1.4g/l, and hydrogen peroxide addition is 14g/l, double
Oxygen water stabilizer addition is 4g/l, and bleeding agent FFA additions are 0.4g/l.
Embodiment 3
A kind of wool imitates the production technology of straight-bar machines tmaterial, selected by raw material, patterning design, looming weaving, bleaching and dyeing, drying and
Stentering forming process, complete the production technology that wool imitates straight-bar machines tmaterial；Comprise the following steps that：
（1）Raw material selects：From 34Nm 100% wool, the twist factor of wool is 270；
（2）Patterning design：Tmaterial is combined by V-type mesh knitting zone and plain weave knitting zone, and plain weave area is compounded in V-type
The both ends of mesh knitting zone, V-type mesh woven extent plain weave area are integral structure；
（3）Looming weaving：Weaved using 30 pin 24G single-side computer jacquard weave, V-type mesh knitting zone is made up of 8 road yarns
One circulation carries out braiding and formed, and wool yarns are grown for 163mm/50 mesh yarn；
（4）Bleaching and dyeing：Carry out floating bottom oil removing under the conditions of 85 DEG C, auxiliary agent is DA degreasers, soda ash, hydrogen peroxide, hydrogen peroxide stabilizer
And bleeding agent, pH values 10, processing time are 45 minutes, are then dyed using conventional dyeing process, concentration is 3% HKY
Color fixing agent, make fixation treatment, color fixing temperature is 44 DEG C, time 20min, washes 10min, dries 2min at 105 DEG C, pads
ULTRA softening agents, it is normal temperature to pad bath temperature degree；
（5）Drying：Fabric after bleachinging and dyeing carries out drying, and drying temperature is 115 DEG C, criteria thus the drying time 45s；
（6）Stentering forming：Stentering forming, breadth 1.6m are carried out on forming machine again after drying, forming machine speed is 27m/
Min, setting temperature are 80 DEG C.
The specific braiding structure of V-type mesh knitting zone is：The first via and the second tunnel are lopping, lopping, lopping, lopping；The
Three roads and the 4th tunnel are tuck, lopping, tuck, lopping；5th road and the 6th tunnel are lopping, lopping, lopping, lopping；7th tunnel
It is lopping, tuck, lopping, tuck with the 8th tunnel.
DA degreasers addition is 2g/l in auxiliary agent, and soda ash addition is 1.4g/l, and hydrogen peroxide addition is 14g/l, double
Oxygen water stabilizer addition is 4g/l, and bleeding agent FFA additions are 0.4g/l.
The knitting fabric of the present invention is total to cloth cover generation V-type eyed structure and plain plane by the weaving method of uniqueness
The effect deposited, mesh portion third dimension is strong, and plain part is flat vertical bar, has straight-bar machines by using the woven fabric of circular knitting machine
The effect of fabric, can be commonly used to woven woollen shirt fabric, and weaving is convenient and simple.
Above-described embodiment is presently preferred embodiments of the present invention, is not the limitation to technical solution of the present invention, as long as
The technical scheme that can be realized on the basis of above-described embodiment without creative work, it is regarded as falling into patent of the present invention
Rights protection scope in.
Claims (3)
1. a kind of wool imitates the production technology of straight-bar machines tmaterial, it is characterised in that：Selected by raw material, be patterning design, upper woven
Make, bleaching and dyeing, drying and stentering forming process, completion wool imitate the production technology of straight-bar machines tmaterial；Comprise the following steps that：
Raw material selects：From 34Nm 100% wool, the twist factor of the wool is 270；
Patterning design：The tmaterial is combined by V-type mesh knitting zone and plain weave knitting zone, and the plain weave area is compound
At the both ends of V-type mesh knitting zone, the V-type mesh woven extent plain weave area is integral structure；
Looming weaving：Weaved using 30 pin 24G single-side computer jacquard weave, the V-type mesh knitting zone is made up of 8 road yarns
One circulation carries out braiding and formed, and wool yarns are grown for 163mm/50 mesh yarn；
（4）Bleaching and dyeing：Carry out floating bottom oil removing under the conditions of 85 DEG C, auxiliary agent is DA degreasers, soda ash, hydrogen peroxide, hydrogen peroxide stabilizer
And bleeding agent, pH values 9.5-10.5, processing time are 42-48 minutes, are then dyed using conventional dyeing process, use is dense
The HKY color fixing agent for 3% is spent, makees fixation treatment, color fixing temperature is 42-46 DEG C, time 20min, 10min is washed, in 104-
106 DEG C of drying 2min, pad ULTRA softening agents, it is normal temperature to pad bath temperature degree；
（5）Drying：Fabric after bleachinging and dyeing carries out drying, and the drying temperature is 110-120 DEG C, and the criteria thus the drying time is 30-
60s；
（6）Stentering forming：Carry out stentering forming after drying on forming machine again, the breadth is 1.5-1.7m, the forming machine
Speed is 25-30m/min, and the setting temperature is 75-85 DEG C.
2. a kind of wool according to claim 1 imitates the production technology of straight-bar machines tmaterial, it is characterised in that：The step
（3）In the specific braiding structure of V-type mesh knitting zone be：The first via and the second tunnel are lopping, lopping, lopping, lopping；3rd
Road and the 4th tunnel are tuck, lopping, tuck, lopping；5th road and the 6th tunnel are lopping, lopping, lopping, lopping；7th road and
8th tunnel is lopping, tuck, lopping, tuck.
3. a kind of wool according to claim 1 imitates the production technology of straight-bar machines tmaterial, it is characterised in that：The step
（4）In auxiliary agent in DA degreasers addition be 2g/l, soda ash addition is 1.4g/l, and hydrogen peroxide addition is 14g/l, dioxygen
Water stabilizer addition is 4g/l, and bleeding agent FFA additions are 0.4g/l.