CN107675582A - A kind of method of waste old producer row facility water permeable pavement material - Google Patents
A kind of method of waste old producer row facility water permeable pavement material Download PDFInfo
- Publication number
- CN107675582A CN107675582A CN201710907513.4A CN201710907513A CN107675582A CN 107675582 A CN107675582 A CN 107675582A CN 201710907513 A CN201710907513 A CN 201710907513A CN 107675582 A CN107675582 A CN 107675582A
- Authority
- CN
- China
- Prior art keywords
- finished product
- waste old
- water permeable
- permeable pavement
- facility water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of method of waste old producer row facility water permeable pavement material, belong to road surface seepy material field.Comprise the following steps:(1)Cleaning;(2)Section;(3)Slitting;(4)Semi-finished product make;(5)Finished product makes.It has good permeability rate, and permeability rate size can be precisely controlled by Auto-regulating System of Density of Heavy Medium;By to raw material size and Auto-regulating System of Density of Heavy Medium, can precisely adjust void size, meet different application requirements;Internal network structure, there are higher physics and mechanical performance than the pavement of common waste old manufacture.
Description
Technical field
The present invention relates to a kind of method of waste old producer row facility water permeable pavement material, belong to road surface seepy material
Field.
Background technology
Sponge city, it is new generation of city storm water man- agement concept, refers to that city is adapting to environmental change and reply rainwater band
Natural calamity come etc. has good " elasticity ", also referred to as " water elasticity city ".International term is " low shadow
Ring exploitation storm-water system structure ".Water suction when raining, water storage, infiltration, water purification, it is necessary to when by the water stored " release " and be subject to profit
With.And current people's row facility road surface, when there is rainstorm weather, it may appear that serious seeping phenomenon.Need badly a kind of permeable
People's row facility paving material, power-assisted is provided to build sponge city.
China every year caused junked tire with 8-10% speed increase.2010, Chinese junked tire yield was about
2.5 hundred million, recovery utilization rate is only 50% or so, less than the half of western developed country, causes the huge wasting of resources.Useless wheel
Tire belongs to waste old, and the processing of scrap rubber is one of serious problems that current people face.In order to meet the material improved constantly
Expect performance requirement, rubber develops towards high intensity, wear-resisting, stable and ageing-resistant direction, but cause and discard simultaneously after
The problem of rubber long-term is unable to natural degradation, it is dirty that substantial amounts of waste old causes black more intractable than plastic pollution
Dye, and waste the rubber sources of preciousness.There is a kind of waste old recycling mode at present, be to be ground into waste old
Graininess is powdered, then remakes into material impervious to water, is not suitable for road pavement, rainy day easy ponding.
A kind of method of waste old producer row facility water permeable pavement material is designed, waste old is processed into permeable
Paving material, the problem of waste old pollutes environment is on the one hand can solve the problem that, on the other hand can utilize this permeable paving
Material builds sponge city.
The content of the invention
The technical problems to be solved by the invention are:A kind of waste old producer row facility water permeable pavement material is provided
Method, it solve by waste old make adult row facility water permeable pavement material, reduce waste old pollution, improve road surface
The problem of permeability rate.
The technical problems to be solved by the invention take following technical scheme to realize:
A kind of method of waste old producer row facility water permeable pavement material, comprises the following steps:
(1)Cleaning:The impurity such as stone, valve inside in removing waste old;
(2)Section:The sheet material of clean waste old thickness needed for slicer is split into, while remove the steel wire of rubber for tire
Layer;
(3)Slitting:Sheet material is cut into the rubber strip of required length and width;
(4)Semi-finished product make:According to(10-30):1 ratio of weight and number weighs rubber strip and binding agent, puts into together in agitator
After stirring, taking-up is put into moulding box, is pressed into process stipulation density, then moulding box is put into drying room in 80-140 DEG C of condition
Lower curing 1-3 hours, curing terminate to take out semi-finished product out of moulding box after standing 12-24 hours again;
(5)Finished product makes:Semi-finished product are cut into required thickness with peeler or pingqie machine, then is cut with hydraulic pressure and is machined to institute
Length and width is needed, the internal cuboid finished product for having network-like space is made.
As preferred embodiment, the step(3)The size of middle rubber strip is length 20-200mm, width 1-10mm, thickness
1-10mm。
As preferred embodiment, the step(4)Middle bonding agent uses polyurethane one-component glue.
As preferred embodiment, the step(5)The size of middle cuboid finished product is thickness 5-100mm, Chang Du≤100m, wide
Du≤2000mm, density 400-1500kg/m3。
Waste old is first fabricated to rubber strip, then after rubber strip is stirred, by suppressing, curing, cutting, be made
Cuboid finished product, finished product is laid on people's row facility road surface.Finished product is by crisscross rambling rubber strip superposition pressure
System forms, so gap between rubber strip and rubber strip be present so that rectangle finished product is internally formed irregular network-like sky
Gap, but unit volume internal pore rate is uniform, and it is permeable that network-like space can be used in fast uniform.
The beneficial effects of the invention are as follows:It has good permeability rate, and can be precisely controlled by Auto-regulating System of Density of Heavy Medium permeable
Rate size;By to raw material size and Auto-regulating System of Density of Heavy Medium, can precisely adjust void size, meet different application requirements;In-house network
Shape structure, there are higher physics and mechanical performance than the pavement of common waste old manufacture, for example, elongation, stretching are by force
Degree, tearing strength, bending, rebound degree, service life are more preferable;Because technique is simple, without crushing, manufacturing cost is only common
The 30%-70% of the pavement of waste old manufacture, is allowed to basis and the prospect for more having popularization and application;It can be set by simply special
It is standby that road surface after the completion of laying is cleaned, ensure that permeability rate is steady in a long-term, it is short to solve other current all porous pavements
The problem of life-span.
Embodiment
In order to be easy to understand to technological means, creation characteristic, reached purpose and effect of the present invention, further below
Illustrate the present invention.
A kind of method of waste old producer row facility water permeable pavement material, comprises the following steps:
(1)Cleaning:The impurity such as stone, valve inside in removing waste old;
(2)Section:The sheet material of clean waste old thickness needed for slicer is split into, while remove the steel wire of rubber for tire
Layer;
(3)Slitting:Sheet material is cut into the rubber strip of required length and width;
(4)Semi-finished product make:According to(10-30):1 ratio of weight and number weighs rubber strip and binding agent, puts into together in agitator
After stirring, taking-up is put into moulding box, is pressed into process stipulation density, then moulding box is put into drying room in 80-140 DEG C of condition
Lower curing 1-3 hours, curing terminate to take out semi-finished product out of moulding box after standing 12-24 hours again;
(5)Finished product makes:Semi-finished product are cut into required thickness with peeler or pingqie machine, then is cut with hydraulic pressure and is machined to institute
Length and width is needed, the internal cuboid finished product for having network-like space is made.
Step(3)The size of middle rubber strip is length 20-200mm, width 1-10mm, thickness 1-10mm.
Step(4)Middle bonding agent uses polyurethane one-component glue.
Step(5)The size of middle cuboid finished product is thickness 5-100mm, Chang Du≤100m, Kuan Du≤2000mm, density
400-1500kg/m3。
Waste old is first fabricated to rubber strip, then after rubber strip is stirred, by suppressing, curing, cutting, be made
Cuboid finished product, finished product is laid on people's row facility road surface.Finished product is by crisscross rambling rubber strip superposition pressure
System forms, so gap between rubber strip and rubber strip be present so that rectangle finished product is internally formed irregular network-like sky
Gap, but unit volume internal pore rate is uniform, and it is permeable that network-like space can be used in fast uniform.
Embodiment 1
A kind of method of waste old producer row facility water permeable pavement material, comprises the following steps:
(1)Cleaning:The impurity such as stone, valve inside in removing waste old;
(2)Section:The sheet material of clean waste old thickness needed for slicer is split into, while remove the steel wire of rubber for tire
Layer;
(3)Slitting:Sheet material is cut into the rubber strip of required length and width;
(4)Semi-finished product make:According to(10-30):1 ratio of weight and number weighs rubber strip and binding agent, puts into together in agitator
After stirring, taking-up is put into moulding box, is pressed into process stipulation density, then moulding box is put into drying room ripe under the conditions of 90 DEG C
Change 2 hours, curing terminates to take out semi-finished product out of moulding box after standing 24 hours again;
(5)Finished product makes:Semi-finished product are cut into required thickness with peeler or pingqie machine, then is cut with hydraulic pressure and is machined to institute
Length and width is needed, the internal cuboid finished product for having network-like space is made.
Step(3)The size of middle rubber strip is length 60mm, width 3mm, thickness 3mm.
Step(4)Middle bonding agent uses polyurethane one-component glue.
Step(5)The size of middle cuboid finished product is thickness 50mm, length 20m, width 1m, density 700kg/m3。
Embodiment 2
A kind of method of waste old producer row facility water permeable pavement material, comprises the following steps:
(1)Cleaning:The impurity such as stone, valve inside in removing waste old;
(2)Section:The sheet material of clean waste old thickness needed for slicer is split into, while remove the steel wire of rubber for tire
Layer;
(3)Slitting:Sheet material is cut into the rubber strip of required length and width;
(4)Semi-finished product make:According to(10-30):1 ratio of weight and number weighs rubber strip and binding agent, puts into together in agitator
After stirring, taking-up is put into moulding box, is pressed into process stipulation density, then moulding box is put into drying room ripe under the conditions of 80 DEG C
Change 3 hours, curing terminates to take out semi-finished product out of moulding box after standing 24 hours again;
(5)Finished product makes:Semi-finished product are cut into required thickness with peeler or pingqie machine, then is cut with hydraulic pressure and is machined to institute
Length and width is needed, the internal cuboid finished product for having network-like space is made.
Step(3)The size of middle rubber strip is length 20mm, width 1mm, thickness 1mm.
Step(4)Middle bonding agent uses polyurethane one-component glue.
Step(5)The size of middle cuboid finished product is thickness 5mm, length 1m, width 0.5m, density 800kg/m3。
Embodiment 3
A kind of method of waste old producer row facility water permeable pavement material, comprises the following steps:
(1)Cleaning:The impurity such as stone, valve inside in removing waste old;
(2)Section:The sheet material of clean waste old thickness needed for slicer is split into, while remove the steel wire of rubber for tire
Layer;
(3)Slitting:Sheet material is cut into the rubber strip of required length and width;
(4)Semi-finished product make:According to(10-30):1 ratio of weight and number weighs rubber strip and binding agent, puts into together in agitator
After stirring, taking-up is put into moulding box, is pressed into process stipulation density, then moulding box is put into drying room under the conditions of 100 DEG C
Curing 1 hour, curing terminate to take out semi-finished product out of moulding box after standing 12 hours again;
(5)Finished product makes:Semi-finished product are cut into required thickness with peeler or pingqie machine, then is cut with hydraulic pressure and is machined to institute
Length and width is needed, the internal cuboid finished product for having network-like space is made.
Step(3)The size of middle rubber strip is length 200mm, width 10mm, thickness 10mm.
Step(4)Middle bonding agent uses polyurethane one-component glue.
Step(5)The size of middle cuboid finished product is thickness 100mm, length 2m, width 1m, density 600kg/m3。
Mounting means:
Dispensing is installed:This installation form is to use glue special(Polyurethane mono component wet solidifying glue
), it is distributed, material is stained with the basis of being connected on the basis of with point-like;
Mechanical erection:Material is connected with basis with Special embolus or card, cleaned with the dismounting of convenient material;
Spliced installation:Edge of materials is made into lock form, on the basis of material connection is positioned over using lock.
Application places:
(1)Pavement:With good water permeability, clanability energy, shock-absorbing capacity, coordinate with pervious foundation layer, can be formed
Good permeable system, and the service life of pervious foundation layer can be greatly improved, the blocking probability of pervious foundation layer is reduced, makes sea
The walkway system in continuous city is more efficient, the long-life;
(2)Bicycle lane/bicycle capacity:Surface gathered water probability can be effectively reduced, and has good antiskid, shock-absorbing function,
Improve the driving safety of sleet sky non-motor vehicle, comfortableness;
(3)Body-building square/kindergarten playground:With good security performance, service life length;
(4)Body-building pavement/runway:Assign material excellent shock-absorbing function with controllable space, athletic injury is greatly decreased;
(5)Floating floor sound insulation pad layer:With good load, voidage is can control, greatly improves the anti-acoustic capability of floor;
(6)Sound panel;
(7)Plant pit cover plate:With high permeability rate, the long-life, it is quick for installation, be hardly damaged, better than current existing several cave cover plates
Material;
(8)Carpet/doormat;
(9)Carpet bed course.
It has good permeability rate, and permeability rate size can be precisely controlled by Auto-regulating System of Density of Heavy Medium;By to raw material
Size and Auto-regulating System of Density of Heavy Medium, void size can be precisely adjusted, meet different application requirements;Internal network structure, than common waste and old rubber
Glue manufacture pavement have higher physics and mechanical performance, for example, elongation, tensile strength, tearing strength, bending,
Rebound degree, service life are more preferable;Raw material need not remove the nylon mesh in the following junked tires of diameter 850mm, be waste and old small
The application of tire provides new channel and direction;Because technique is simple, without crushing, manufacturing cost is only common waste old
The 30%-70% of the pavement of manufacture, it is allowed to basis and the prospect for more there are popularization and application;Can be by simple special equipment to laying
After the completion of road surface cleaned, ensure that permeability rate is steady in a long-term, solve at present other all porous pavements are short-life asks
Topic.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, without departing from the spirit and scope of the present invention, this hair
Bright also to have various changes and modifications, these changes and improvements are both fallen within the scope of protection of present invention.Application claims
Protection domain is by appended claims and its equivalent thereof.
Claims (4)
- A kind of 1. method of waste old producer row facility water permeable pavement material, it is characterised in that comprise the following steps:(1)Cleaning:The impurity such as stone, valve inside in removing waste old;(2)Section:The sheet material of clean waste old thickness needed for slicer is split into, while remove the steel wire of rubber for tire Layer;(3)Slitting:Sheet material is cut into the rubber strip of required length and width;(4)Semi-finished product make:According to(10-30):1 ratio of weight and number weighs rubber strip and binding agent, puts into together in agitator After stirring, taking-up is put into moulding box, is pressed into process stipulation density, then moulding box is put into drying room in 80-140 DEG C of condition Lower curing 1-3 hours, curing terminate to take out semi-finished product out of moulding box after standing 12-24 hours again;(5)Finished product makes:Semi-finished product are cut into required thickness with peeler or pingqie machine, then is cut with hydraulic pressure and is machined to institute Length and width is needed, the internal cuboid finished product for having network-like space is made.
- A kind of 2. method of waste old producer row facility water permeable pavement material according to claim 1, it is characterised in that: The step(3)The size of middle rubber strip is length 20-200mm, width 1-10mm, thickness 1-10mm.
- A kind of 3. method of waste old producer row facility water permeable pavement material according to claim 1, it is characterised in that: The step(4)Middle bonding agent uses polyurethane one-component glue.
- A kind of 4. method of waste old producer row facility water permeable pavement material according to claim 1, it is characterised in that: The step(5)The size of middle cuboid finished product is thickness 5-100mm, Chang Du≤100m, Kuan Du≤2000mm, density 400- 1500kg/m3。