CN107675497A - A kind of pure-cotton fabric increases soft method - Google Patents
A kind of pure-cotton fabric increases soft method Download PDFInfo
- Publication number
- CN107675497A CN107675497A CN201711119574.0A CN201711119574A CN107675497A CN 107675497 A CN107675497 A CN 107675497A CN 201711119574 A CN201711119574 A CN 201711119574A CN 107675497 A CN107675497 A CN 107675497A
- Authority
- CN
- China
- Prior art keywords
- parts
- pure
- cotton fabric
- ether ammonium
- ammonium ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of pure-cotton fabric to increase soft method, by pure-cotton fabric at 40 DEG C~60 DEG C, using bath raio 30:1 mode, it is immersed in and increases in soft liquid 30 minutes, after centrifugal dehydration, is dried at 100 DEG C~120 DEG C；It is described to increase in soft liquid comprising the season ether ammonium ester softening agent that mass percent is 3%~5%.Present invention may apply to pure-cotton fabric, can effectively improve the pliability of pure-cotton fabric, and fabric will not be caused to damage.
Description
Technical field
The present invention relates to a kind of pure-cotton fabric to increase soft method, belongs to weaving processing technology field.
Background technology
Fabric, due to eliminating natural oil wax, often reduces it after pre-treatment and a series of dyeing and finishings add formula
Original smooth sense, makes feel become coarse.In addition, some fabrics need to pass through high-temperature process, such as resin finishing, the heat for closing fibre is determined
Type, the decatize of acrylic fibers be expanded and pigment printing etc., also fabric feeling can be made to become thick and stiff.Most of fine fabric and pure of closing
Hair, after nap silk fabric is scrubbed or soap washes, be hardened, feel it is coarse, the problems such as uncomfortable is worn, in order to overcome this to lack
Point, it is necessary to improved using softening agent.With fine fabric hair development is closed, soft finish requirement of the people to fabric is increasingly
Urgently, the importance of softening agent is also just particularly important.
The content of the invention
It is an object of the present invention to provide a kind of pure-cotton fabric to increase soft method.It goes for pure-cotton fabric, can be effective
The pliability of pure-cotton fabric is improved, and fabric will not be caused to damage.
Technical scheme：A kind of pure-cotton fabric increases soft method, is characterized in, by pure-cotton fabric at 40 DEG C~60 DEG C
Under, using bath raio 30:1 (volume：Quality) mode, be immersed in and increase in soft liquid 30 minutes, after centrifugal dehydration, 100 DEG C~120
Dried at DEG C；It is described to increase in soft liquid comprising the season ether ammonium ester softening agent that mass percent is 3%~5%.
Above-mentioned pure-cotton fabric increases in soft method, the season ether ammonium ester softening agent, in parts by mass, includes amido silicon oil 25
~35 parts, 45~50 parts of season ether ammonium ester, 2~6 parts of methylparoban, 1~3 part of Butyl Chemosept, 1~5 part of spices and
150~200 parts of deionized water.
Foregoing pure-cotton fabric increases in soft method, preferably, the season ether ammonium ester softening agent, in parts by mass, comprising
28~32 parts of amido silicon oil, 47~48 parts of season ether ammonium ester, 3~4 parts of methylparoban, 2~3 parts of Butyl Chemosept, perfume
170~180 parts of 3~4 parts of material and deionized water.
Foregoing pure-cotton fabric increases in soft method, and the preparation method of the season ether ammonium ester softening agent is：By deionized water plus
Heat is slowly added to ether ammonium ester, methylparoban and Butyl Chemosept, using agitator, in 300rpm speed to 60 DEG C
Lower mixing 10~15 minutes, it is cooled to 25 DEG C with 1 DEG C per minute of speed, adds amido silicon oil and spices, using agitator,
Mixed 25~30 minutes under 250rpm speed.
Compared with prior art, the present invention is handled pure-cotton fabric using season ether ammonium ester softening agent, can be effectively pure
Adhere to hydrophilic radical on cotton face fabric, so as to effectively reduce pure-cotton fabric skin-friction force, improve the flexibility of pure-cotton fabric
Energy.It is more green and the natural degradation ability of the softening agent of the present invention is strong.
Embodiment
With reference to embodiment, the present invention is further illustrated, but is not intended as the foundation limited the present invention.
Embodiment.A kind of pure-cotton fabric increases soft method, by pure-cotton fabric at 40 DEG C~60 DEG C, using bath raio 30:1 side
Formula, it is immersed in and increases in soft liquid 30 minutes, after centrifugal dehydration, is dried at 100 DEG C~120 DEG C；Described increase in soft liquid includes quality
Percentage is 3%~5% season ether ammonium ester softening agent.The season ether ammonium ester softening agent, in parts by mass, includes amido silicon oil 25
~35 parts, 45~50 parts of season ether ammonium ester, 2~6 parts of methylparoban, 1~3 part of Butyl Chemosept, 1~5 part of spices and
150~200 parts of deionized water.Preferably, the season ether ammonium ester softening agent, in parts by mass, includes amido silicon oil 28~32
Part, 47~48 parts of season ether ammonium ester, 3~4 parts of methylparoban, 2~3 parts of Butyl Chemosept, 3~4 parts of spices and go from
Sub- 170~180 parts of water.The preparation method of the season ether ammonium ester softening agent is：Deionized water is heated to 60 DEG C, is slowly added to ether
Ammonium ester, methylparoban and Butyl Chemosept, using agitator, mixed 10~15 minutes under 300rpm speed, with
1 DEG C per minute of speed is cooled to 25 DEG C, adds amido silicon oil and spices, using agitator, 25 are mixed under 250rpm speed
~30 minutes, season ether ammonium ester softening agent decentralization prepared by this method was high, viscosity can as little as 30cps, prepare and disperse when increasing soft liquid
Faster.
Claims (4)
1. a kind of pure-cotton fabric increases soft method, it is characterised in that：By pure-cotton fabric at 40 DEG C~60 DEG C, using bath raio 30:1
Mode, it is immersed in and increases in soft liquid 30 minutes, after centrifugal dehydration, is dried at 100 DEG C~120 DEG C；Described increase in soft liquid includes matter
Measure the season ether ammonium ester softening agent that percentage is 3%~5%.
2. pure-cotton fabric according to claim 1 increases soft method, it is characterised in that：The season ether ammonium ester softening agent, by matter
Part meter is measured, includes 25~35 parts of amido silicon oil, 45~50 parts of season ether ammonium ester, 2~6 parts of methylparoban, p-hydroxybenzoic acid fourth
150~200 parts of 1~3 part of ester, 1~5 part of spices and deionized water.
3. pure-cotton fabric according to claim 2 increases soft method, it is characterised in that：The season ether ammonium ester softening agent, by matter
Part meter is measured, includes 28~32 parts of amido silicon oil, 47~48 parts of season ether ammonium ester, 3~4 parts of methylparoban, p-hydroxybenzoic acid fourth
170~180 parts of 2~3 parts of ester, 3~4 parts of spices and deionized water.
4. the pure-cotton fabric according to Claims 2 or 3 increases soft method, it is characterised in that the season ether ammonium ester softening agent
Preparation method is：Deionized water is heated to 60 DEG C, is slowly added to ether ammonium ester, methylparoban and Butyl Chemosept,
Using agitator, mixed 10~15 minutes under 300rpm speed, be cooled to 25 DEG C with 1 DEG C per minute of speed, add amino
Silicone oil and spices, using agitator, mixed 25~30 minutes under 250rpm speed.