CN107668810A - A kind of high temperature resistance wig and preparation method thereof - Google Patents
A kind of high temperature resistance wig and preparation method thereof Download PDFInfo
- Publication number
- CN107668810A CN107668810A CN201711103134.6A CN201711103134A CN107668810A CN 107668810 A CN107668810 A CN 107668810A CN 201711103134 A CN201711103134 A CN 201711103134A CN 107668810 A CN107668810 A CN 107668810A
- Authority
- CN
- China
- Prior art keywords
- parts
- wig
- high temperature
- temperature resistance
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high temperature resistance wig and preparation method thereof, the high temperature resistance wig is made up of following weight composition:0.3 1.2 parts of 15 80 parts of Flame-retardant PET polyester, 13 parts of organic silicone oil emulsion, 0.2 1.3 parts of dimethyl silicone polymer, 2 3.5 parts of tencel binding agent, 8 13 parts of dispersant, 12 parts of amido silicon oil and polyvinyl alcohol.High temperature resistance wig of the present invention uses Flame-retardant PET polyester when preparing, and can effectively improve the heat-resisting quantity of wig, make feel more comfortable, while also improve toughness；The polyvinyl alcohol of addition, it can effectively extend the service life of wig；Organic silicone oil emulsion, dimethyl silicone polymer and amido silicon oil are with the addition of in preparation process simultaneously, in wig surface filming, enhances and prevents melting drop.
Description
Technical field
The present invention relates to a kind of high temperature resistance wig and preparation method thereof.
Background technology
Existing wig is all manufactured using in general PVC, polyamide fibre or terylene mostly, finished product often can not high temperature, no
Stranding can be turned round, it is impossible to be exposed to the sun, such product can bring puzzlement to many women that like to be beautiful, because cannot in temperature too high summer
Wearing is gone out, and because strandings can not be turned round, can not high temperature, think that the wig of another hair style can only be changed when change hair style,
So also add consumption to user.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of high temperature resistant, anti-to melt drop, comfortable feel, the good anti-height of toughness
Warm wig.
To solve the above problems, the present invention is achieved through the following technical solutions：A kind of high temperature resistance wig, the anti-height
Warm wig is made up of following weight composition:Flame-retardant PET polyester 15-80 parts, organic silicone oil emulsion 1-3 parts, poly- diformazan
Radical siloxane 0.2-1.3 parts, tencel binding agent 2-3.5 parts, dispersant 8-13 parts, amido silicon oil 1-2 parts and polyvinyl alcohol 0.3-
1.2 part.
Another technical problem to be solved by this invention is to provide a kind of preparation method of high temperature resistance wig,
The present invention is achieved through the following technical solutions：The preparation process of the high temperature resistance wig is as follows：
1) extract by weight ratio Flame-retardant PET polyester 15-80 parts, tencel binding agent 2-3.5 parts, dispersant 8-13 parts and
Polyvinyl alcohol 0.3-1.2 part mixed fiber polymer dopes；
2) first product wig fiber is made by Rong Yiren spinning process in the mixing stoste of step 1；
3) organic silicone oil emulsion 1-3 parts, dimethyl silicone polymer 0.2-1.3 parts and amido silicon oil are extracted by weight ratio
1-2 parts are mixed into immersion emulsion；
4) the first product wig fiber of step 2 is placed in immersion emulsion made of step 3 and impregnated, make emulsion false in first product
Film forming is reacted on hair fiber；
5) it is finished product to carry out the fiber wig of step 4 film forming after whole hair, component, machine roll up moulding, steam shaping, drying
High temperature resistance wig.
Further, the viscosity of the amido silicon oil is 10Pa.s, and ammonia value is 0.4mmol/g.
The beneficial effect of high temperature resistance wig of the present invention is：The high temperature resistance wig uses Flame-retardant PET polyester when preparing, and can have
The heat-resisting quantity of the raising wig of effect, makes feel more comfortable, while also improve toughness；The polyvinyl alcohol of addition, can be effective
Extend the service life of wig；Organic silicone oil emulsion, dimethyl silicone polymer and amino silicone are with the addition of in preparation process simultaneously
Oil, in wig surface filming, enhance and prevent melting drop.
Embodiment
Following examples are used to illustrate the present invention, but are not limited to the scope of the present invention.
Embodiment 1
A kind of high temperature resistance wig of the present invention, the high temperature resistance wig are made up of following weight composition:Flame-retardant PET
15 parts of polyester, 1 part of organic silicone oil emulsion, 0.2 part of dimethyl silicone polymer, 2 parts of tencel binding agent, 8 parts of dispersant, amido silicon oil
1 part and 0.3 part of polyvinyl alcohol.
The preparation process of the high temperature resistance wig is as follows：
1) 15 parts of Flame-retardant PET polyester, 2 parts of tencel binding agent, 8 parts of dispersant and polyvinyl alcohol are extracted by weight ratio
0.3 part of mixed fiber polymer dope；
2) first product wig fiber is made by Rong Yiren spinning process in the mixing stoste of step 1；
3) it is mixed that 1 part of 1 part of organic silicone oil emulsion, 0.2 part of dimethyl silicone polymer and amido silicon oil are extracted by weight ratio
Synthesis immersion emulsion；
4) the first product wig fiber of step 2 is placed in immersion emulsion made of step 3 and impregnated, make emulsion false in first product
Film forming is reacted on hair fiber；
5) it is finished product to carry out the fiber wig of step 4 film forming after whole hair, component, machine roll up moulding, steam shaping, drying
High temperature resistance wig.
The viscosity of the amido silicon oil is 10Pa.s, and ammonia value is 0.4mmol/g.
Embodiment 2
Its difference from Example 1 is that the high temperature resistance wig is made up of following weight composition:It is fire-retardant
80 parts of PET polyester, 3 parts of organic silicone oil emulsion, 1.3 parts of dimethyl silicone polymer, 3.5 parts of tencel binding agent, 13 parts of dispersant, ammonia
1.2 parts of 2 parts of base silicone oil and polyvinyl alcohol.
Embodiment 3
Its difference from Example 1 is that the high temperature resistance wig is made up of following weight composition:It is fire-retardant
50 parts of PET polyester, 2 parts of organic silicone oil emulsion, 0.6 part of dimethyl silicone polymer, 3 parts of tencel binding agent, 10 parts of dispersant, amino
0.6 part of 1.5 parts of silicone oil and polyvinyl alcohol.
Embodiment 4
Its difference from Example 1 is that the high temperature resistance wig is made up of following weight composition:It is fire-retardant
19 parts of PET polyester, 1.4 parts of organic silicone oil emulsion, 0.4 part of dimethyl silicone polymer, 2.2 parts of tencel binding agent, 9 parts of dispersant,
0.4 part of 1.1 parts of amido silicon oil and polyvinyl alcohol.
Embodiment 5
Its difference from Example 1 is that the high temperature resistance wig is made up of following weight composition:It is fire-retardant
71 parts of PET polyester, 2.6 parts of organic silicone oil emulsion, 1.1 parts of dimethyl silicone polymer, 3.3 parts of tencel binding agent, 12 parts of dispersant,
1 part of 1.9 parts of amido silicon oil and polyvinyl alcohol.
Embodiment 6
Its difference from Example 1 is that the high temperature resistance wig is made up of following weight composition:It is fire-retardant
33 parts of PET polyester, 2.1 parts of organic silicone oil emulsion, 0.7 part of dimethyl silicone polymer, 2.5 parts of tencel binding agent, dispersant 9.3
0.8 part of part, 1.4 parts of amido silicon oil and polyvinyl alcohol.
Embodiment 7
Its difference from Example 1 is that the high temperature resistance wig is made up of following weight composition:It is fire-retardant
47 parts of PET polyester, 1.6 parts of organic silicone oil emulsion, 0.3 part of dimethyl silicone polymer, 2.9 parts of tencel binding agent, dispersant 8.8
0.65 part of part, 1.7 parts of amido silicon oil and polyvinyl alcohol.
Embodiment 8
Its difference from Example 1 is that the high temperature resistance wig is made up of following weight composition:It is fire-retardant
60 parts of PET polyester, 2 parts of organic silicone oil emulsion, 0.5 part of dimethyl silicone polymer, 3 parts of tencel binding agent, 10 parts of dispersant, amino
0.5 part of 1.5 parts of silicone oil and polyvinyl alcohol.
The present invention is not limited to above-mentioned preferred forms, anyone the present invention enlightenment under draw other it is any with
Product as the present invention is same or like, is within the scope of the present invention.
Claims (3)
- A kind of 1. high temperature resistance wig, it is characterised in that：The high temperature resistance wig is made up of following weight composition:It is fire-retardant PET polyester 15-80 parts, organic silicone oil emulsion 1-3 parts, dimethyl silicone polymer 0.2-1.3 parts, tencel binding agent 2-3.5 parts, point Powder 8-13 parts, amido silicon oil 1-2 parts and polyvinyl alcohol 0.3-1.2 parts.
- A kind of 2. preparation method of the high temperature resistance wig prepared described in claim 1, it is characterised in that：This method includes following step Suddenly：1) Flame-retardant PET polyester 15-80 parts, tencel binding agent 2-3.5 parts, dispersant 8-13 parts and poly- second are extracted by weight ratio Enol 0.3-1.2 part mixed fiber polymer dopes；2) first product wig fiber is made by Rong Yiren spinning process in the mixing stoste of step 1；3) organic silicone oil emulsion 1-3 parts, dimethyl silicone polymer 0.2-1.3 parts and amido silicon oil 1-2 are extracted by weight ratio Part is mixed into immersion emulsion；4) the first product wig fiber of step 2 is placed in immersion emulsion made of step 3 and impregnated, make emulsion fine in first product wig Film forming is reacted in dimension；5) it is the anti-height of finished product to carry out the fiber wig of step 4 film forming after whole hair, component, machine roll up moulding, steam shaping, drying Warm wig.
- A kind of 3. high temperature resistance wig according to claim 1, it is characterised in that：The viscosity of the amido silicon oil is 10Pa.s, ammonia value are 0.4mmol/g.