CN107663470A - A kind of lubrication wiredrawing soap - Google Patents

A kind of lubrication wiredrawing soap Download PDF

Info

Publication number
CN107663470A
CN107663470A CN201710878960.1A CN201710878960A CN107663470A CN 107663470 A CN107663470 A CN 107663470A CN 201710878960 A CN201710878960 A CN 201710878960A CN 107663470 A CN107663470 A CN 107663470A
Authority
CN
China
Prior art keywords
container
minutes
emulsion
mixed
mixing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710878960.1A
Other languages
Chinese (zh)
Inventor
李国英
杨士娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Hong Ya Powdered Lubricant Manufacturing Co Ltd
Original Assignee
Tianjin Hong Ya Powdered Lubricant Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Hong Ya Powdered Lubricant Manufacturing Co Ltd filed Critical Tianjin Hong Ya Powdered Lubricant Manufacturing Co Ltd
Priority to CN201710878960.1A priority Critical patent/CN107663470A/en
Publication of CN107663470A publication Critical patent/CN107663470A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of lubrication wiredrawing soap, it is made up of the composition of following parts by weight：Vegetable oil, three second oleate soaps, APES, T 80, A 20, polyethylene glycol, calcium hydroxide；Three second oleate soaps are mixed in the first container with vegetable oil, calcium hydroxide, polyethylene glycol and A 20 are mixed in second container, APES is mixed in the 3rd container with T 80, mix emulsion fluid in second container is gradually poured into the first container, and carry out under stirring, and upon mixing, mixing is stirred for 5 minutes to uniform；Mix emulsion fluid in 3rd container is gradually poured into the first container, and carried out under stirring, and upon mixing, be stirred for 10 minutes to uniform；The above-mentioned complete emulsion of mixing heats under the conditions of 80 DEG C, after heating, naturally cools to room temperature and gets product.Reduce loss and discharge improves drawing speed again, be really achieved the wire-drawing lubrication product of environmentally friendly pickling-free, the feature of environmental protection is good.

Description

A kind of lubrication wiredrawing soap
Technical field
The invention belongs to metallic article wiredrawing wire rod deep process technology field, more particularly to a kind of lubrication wiredrawing soap.
Background technology
Metal wire-drawing equipment and product are widely applied, such as：Compressor wire, prestressed steel bar, prestress steel twist Silk, drum steel wire, medicine core steel wire, steel bead wire, high-pressure rubber tube steel wire, cutting steel wire, sheath steel wire, alloy-steel wire, spring steel Silk, stainless steel wire, rope making wire and various non-ferrous metal wire rods product in.And the said goods are main in process of production Using pickling drawing process.
The country is all use wire drawing powder drawing after first pickling on the basis of wire drawing industry now, not only processing technology complexity, Processing cost is added, and the acid solution used easily causes environmental pollution, the feature of environmental protection is poor.
Therefore, above-mentioned technological deficiency in the prior art be present, be that those skilled in the art's technology urgently to be resolved hurrily is asked Topic.
The content of the invention
It is an object of the invention to provide a kind of lubrication wiredrawing soap, it is intended to solve technical problem present in prior art, And after this lubrication wiredrawing soap, it is directly placed into wire-drawing soap can without pickling and pulls out qualified steel wire, environmental protection Effect is good.
What the present invention was realized in：
A kind of lubrication wiredrawing soap, is made up of the composition of following parts by weight：
And its preparation method is：Three second oleate soaps are put into the first container for fill vegetable oil and mixed, 800 turns/ Minute stirring 25 minutes it is standby into emulsion；Calcium hydroxide, polyethylene glycol and A-20 are mixed in second container, 1000 Rev/min stirring 15 minutes it is standby into emulsion；APES is mixed in the 3rd container with T-80,800 Rev/min stirring 10 minutes it is standby into emulsion；Mix emulsion fluid in second container is gradually poured into the first container, And carried out under 300 revs/min of stirring actions, and after the mix emulsion fluid in second container pours into the first container completely, Mixing is stirred for 5 minutes to uniform；Mix emulsion fluid in 3rd container is gradually poured into the first container, and 400 Carried out under rev/min stirring action, and after the mix emulsion fluid in the 3rd container pours into the first container completely, be stirred for 10 Minute to uniform；
The above-mentioned complete emulsion of mixing heats under the conditions of 80 DEG C, and with 200 revs/min of stirrings in heating process Effect is lower to be carried out, and is heated and is stopped after stirring 25 minutes, naturally cools to room temperature and get product.
Preferably, the vegetable oil uses the mixture of one or both of soybean oil or rapeseed oil.
A kind of preferable embodiment, is made up of the composition of following parts by weight：
The beneficial effects of the present invention are：
Not only reduce loss and discharge improves drawing speed again, drawing road number, be really achieved the wire drawing of environmentally friendly pickling-free Lubrication product, the feature of environmental protection are good.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to this hair It is bright to be further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not For limiting the present invention.
A kind of lubrication wiredrawing soap, is made up of the composition of following parts by weight：
And its preparation method is：Three second oleate soaps are put into the first container for fill vegetable oil and mixed, 800 turns/ Minute stirring 25 minutes it is standby into emulsion；Calcium hydroxide, polyethylene glycol and A-20 are mixed in second container, 1000 Rev/min stirring 15 minutes it is standby into emulsion；APES is mixed in the 3rd container with T-80,800 Rev/min stirring 10 minutes it is standby into emulsion；Mix emulsion fluid in second container is gradually poured into the first container, And carried out under 300 revs/min of stirring actions, and after the mix emulsion fluid in second container pours into the first container completely, Mixing is stirred for 5 minutes to uniform；Mix emulsion fluid in 3rd container is gradually poured into the first container, and 400 Carried out under rev/min stirring action, and after the mix emulsion fluid in the 3rd container pours into the first container completely, be stirred for 10 Minute to uniform；
The above-mentioned complete emulsion of mixing heats under the conditions of 80 DEG C, and with 200 revs/min of stirrings in heating process Effect is lower to be carried out, and is heated and is stopped after stirring 25 minutes, naturally cools to room temperature and get product.
In above-mentioned formula, the vegetable oil uses the mixture of one or both of soybean oil or rapeseed oil.
One of which preferred embodiment what processing mode is as follows：
A kind of lubrication wiredrawing soap, is made up of the composition of following parts by weight：
And its preparation method is：Three second oleate soaps are put into the first container for fill soybean oil and mixed, 800 turns/ Minute stirring 25 minutes it is standby into emulsion；Calcium hydroxide, polyethylene glycol and A-20 are mixed in second container, 1000 Rev/min stirring 15 minutes it is standby into emulsion；APES is mixed in the 3rd container with T-80,800 Rev/min stirring 10 minutes it is standby into emulsion；Mix emulsion fluid in second container is gradually poured into the first container, And carried out under 300 revs/min of stirring actions, and after the mix emulsion fluid in second container pours into the first container completely, Mixing is stirred for 5 minutes to uniform；Mix emulsion fluid in 3rd container is gradually poured into the first container, and 400 Carried out under rev/min stirring action, and after the mix emulsion fluid in the 3rd container pours into the first container completely, be stirred for 10 Minute to uniform；
The above-mentioned complete emulsion of mixing heats under the conditions of 80 DEG C, and with 200 revs/min of stirrings in heating process Effect is lower to be carried out, and is heated and is stopped after stirring 25 minutes, naturally cools to room temperature and get product.
The beneficial effects of the present invention are：
Not only reduce loss and discharge improves drawing speed again, drawing road number, be really achieved the wire drawing of environmentally friendly pickling-free Lubrication product, the feature of environmental protection are good.
Although the above-mentioned embodiment to the present invention is described, not to the limit of the scope of the present invention System, one of ordinary skill in the art should be understood that on the basis of technical scheme those skilled in the art need not Various modifications or deformation that performing creative labour can make are paid still within protection scope of the present invention.

Claims (3)

  1. A kind of 1. lubrication wiredrawing soap, it is characterised in that：It is made up of the composition of following parts by weight：
    And its preparation method is：Three second oleate soaps are put into the first container for fill vegetable oil and mixed, at 800 revs/min Stirring 25 minutes it is standby into emulsion；Calcium hydroxide, polyethylene glycol and A-20 are mixed in second container, at 1000 revs/min Clock stir 15 minutes it is standby into emulsion；APES is mixed in the 3rd container with T-80, at 800 revs/min Clock stir 10 minutes it is standby into emulsion；Mix emulsion fluid in second container is gradually poured into the first container, and 300 Carried out under rev/min stirring action, and after the mix emulsion fluid in second container pours into the first container completely, be stirred for mixing 5 minutes to uniform；Mix emulsion fluid in 3rd container is gradually poured into the first container, and made in 400 revs/min of stirrings Carried out under, and after the mix emulsion fluid in the 3rd container pours into the first container completely, be stirred for 10 minutes to uniform；
    The above-mentioned complete emulsion of mixing heats under the conditions of 80 DEG C, and with 200 revs/min of stirring actions in heating process Carry out, heat and stop after stirring 25 minutes, naturally cool to room temperature and get product.
  2. 2. lubrication wiredrawing soap as claimed in claim 1, it is characterised in that：The vegetable oil is using in soybean oil or rapeseed oil The mixture of one or both.
  3. 3. lubrication wiredrawing soap as claimed in claim 2, it is characterised in that：It is made up of the composition of following parts by weight：
CN201710878960.1A 2017-09-26 2017-09-26 A kind of lubrication wiredrawing soap Pending CN107663470A (en)