CN107651938A - A kind of pottery and preparation method thereof - Google Patents
A kind of pottery and preparation method thereof Download PDFInfo
- Publication number
- CN107651938A CN107651938A CN201710988970.0A CN201710988970A CN107651938A CN 107651938 A CN107651938 A CN 107651938A CN 201710988970 A CN201710988970 A CN 201710988970A CN 107651938 A CN107651938 A CN 107651938A
- Authority
- CN
- China
- Prior art keywords
- parts
- idiosome
- pottery
- raw material
- mass percentage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of pottery and preparation method thereof.The ceramic idiosome includes according to mass percentage:25 ~ 30 parts of clay, 24 ~ 27 parts of potassium feldspar, 15 ~ 18 parts of quartz, 12 ~ 16 parts of marble, 12 ~ 16 parts of kaolin, 16 ~ 20 parts of spodumene, 10 ~ 12 parts of bauxite, eluriate 13 ~ 15 parts of mud, 7 ~ 9 parts of gangue;Glaze layer includes according to mass percentage:20 ~ 23 parts of dolomite, 10 ~ 13 parts of perovskite, 10 ~ 12 parts of potassium feldspar, 7 ~ 9 parts of aluminium borate, 7 ~ 9 parts of aluminium metaphosphate, 9 ~ 12 parts of smithsonite.Ceramics of the invention have the advantages of lightweight, be readily cleaned;This method, which has, saves the characteristics of easily operated.
Description
Technical field
The invention belongs to bathroom field, and in particular to a kind of pottery and preparation method thereof.
Background technology
Due to being provided with a dumb light glaze layer on the surface of sanitary equipment body, make the surface lubrication of china sanitary ware, one can be given people
The valuable abundant sensation of kind, it will not make one to feel dazzling under light fixture irradiation indoors, will not also give people the frivolous sensation of quality.
However, traditional ceramic sanitary appliance has inconvenience more producing due to heavier mass with handling process.And the glaze layer pair on sanitary equipment surface
In using when the difficulty or ease rinsed play decisive role.
The content of the invention
The present invention provides a kind of pottery and preparation method thereof, and the pottery has the advantages of lightweight, be readily cleaned.
Technical solution of the present invention is as follows.
A kind of pottery, idiosome include according to mass percentage:25 ~ 30 parts of clay, 24 ~ 27 parts of potassium feldspar, quartz
15 ~ 18 parts, 12 ~ 16 parts of marble, 12 ~ 16 parts of kaolin, 16 ~ 20 parts of spodumene, 10 ~ 12 parts of bauxite, eluriate mud 13 ~ 15
Part, 7 ~ 9 parts of gangue;
Glaze layer includes according to mass percentage:20 ~ 23 parts of dolomite, 10 ~ 13 parts of perovskite, 10 ~ 12 parts of potassium feldspar, aluminium borate
7 ~ 9 parts, 7 ~ 9 parts of aluminium metaphosphate, 9 ~ 12 parts of smithsonite.
Preferably, idiosome includes according to mass percentage:27 parts of clay, 25 parts of potassium feldspar, 16 parts of quartz, marble 14
Part, 14 parts of kaolin, 17 parts of spodumene, 11 parts of bauxite, eluriate 12 parts of mud, 8 parts of gangue;
Glaze layer includes according to mass percentage:21 parts of dolomite, 12 parts of perovskite, 11 parts of potassium feldspar, 8 parts of aluminium borate, inclined phosphorus
Sour 8 parts of aluminium, 10 parts of smithsonite.
A kind of preparation method of pottery, comprises the following steps:
(1)It is 1 according to idiosome raw material and mill ball mass ratio after idiosome raw material is mixed according to proportioning:3 ~ 4 carry out ball milling, obtain
To porcelain mud;
(2)By step(1)After obtained porcelain mud mixes with water, after carrying out injection forming, drying, idiosome is obtained;
(3)It is 1 according to glaze layer raw material and mill ball mass ratio after glaze layer raw material is mixed according to proportioning:3 ~ 4 carry out ball milling, obtain
Glazing material layer after to ball milling;
(4)Glazing material layer after ball milling is sprayed on closestool idiosome, 1 ~ 2h is fired at 400 ~ 500 DEG C, then proceedes to heat up,
2 ~ 3h, then 1250 ~ 1350 DEG C of the cause that heats up are stopped at 700 ~ 900 DEG C, 1 ~ 2h is fired, obtains pottery.
Compared with prior art, advantage of the invention is that:
Ceramics of the invention have the advantages of lightweight, be readily cleaned;This method, which has, saves the characteristics of easily operated.
Embodiment
Make further specific detailed description, but embodiments of the present invention are not to the present invention with reference to specific embodiment
It is limited to this, for especially not dated technological parameter, can refer to routine techniques progress.
Embodiment 1
Idiosome includes according to mass percentage:27 parts of clay, 25 parts of potassium feldspar, 16 parts of quartz, 14 parts of marble, kaolin 14
Part, 17 parts of spodumene, 11 parts of bauxite, eluriate 12 parts of mud, 8 parts of gangue;
Glaze layer includes according to mass percentage:21 parts of dolomite, 12 parts of perovskite, 11 parts of potassium feldspar, 8 parts of aluminium borate, inclined phosphorus
Sour 8 parts of aluminium, 10 parts of smithsonite.
(1)It is 1 according to idiosome raw material and mill ball mass ratio after idiosome raw material is mixed according to proportioning:3 carry out ball milling,
Obtain porcelain mud;
(2)By step(1)After obtained porcelain mud mixes with water, after carrying out injection forming, drying, idiosome is obtained;
(3)It is 1 according to glaze layer raw material and mill ball mass ratio after glaze layer raw material is mixed according to proportioning:4 carry out ball milling, obtain
Glazing material layer after to ball milling;
(4)Glazing material layer after ball milling is sprayed on closestool idiosome, 2h is fired at 400 DEG C, then proceedes to heat up, in 7900
2h is stopped at DEG C, then 1350 DEG C of the cause that heats up, 1h is fired, obtains pottery.
Embodiment 2
Idiosome includes according to mass percentage:25 parts of clay, 24 parts of potassium feldspar, 15 parts of quartz, 12 parts of marble, kaolin 12
Part, 16 parts of spodumene, 10 parts of bauxite, eluriate 13 parts of mud, 7 parts of gangue;
Glaze layer includes according to mass percentage:23 parts of dolomite, 13 parts of perovskite, 12 parts of potassium feldspar, 9 parts of aluminium borate, inclined phosphorus
Sour 9 parts of aluminium, 12 parts of smithsonite.
(1)It is 1 according to idiosome raw material and mill ball mass ratio after idiosome raw material is mixed according to proportioning:4 carry out ball
Mill, obtains porcelain mud;
(2)By step(1)After obtained porcelain mud mixes with water, after carrying out injection forming, drying, idiosome is obtained;
(3)It is 1 according to glaze layer raw material and mill ball mass ratio after glaze layer raw material is mixed according to proportioning:4 carry out ball milling, obtain
Glazing material layer after to ball milling;
(4)Glazing material layer after ball milling is sprayed on closestool idiosome, 1h is fired at 500 DEG C, then proceedes to heat up, in 900
2h is stopped at DEG C, then 1250 DEG C of the cause that heats up, 2h is fired, obtains pottery.
Embodiment 3
Idiosome includes according to mass percentage:30 parts of clay, 27 parts of potassium feldspar, 18 parts of quartz, 16 parts of marble, kaolin 16
Part, 20 parts of spodumene, 12 parts of bauxite, eluriate 15 parts of mud, 9 parts of gangue;
Glaze layer includes according to mass percentage:20 parts of dolomite, 10 parts of perovskite, 10 parts of potassium feldspar, 7 parts of aluminium borate, inclined phosphorus
Sour 7 parts of aluminium, 9 parts of smithsonite.
(1)It is 1 according to idiosome raw material and mill ball mass ratio after idiosome raw material is mixed according to proportioning:3 ~ 4 carry out ball
Mill, obtains porcelain mud;
(2)By step(1)After obtained porcelain mud mixes with water, after carrying out injection forming, drying, idiosome is obtained;
(3)It is 1 according to glaze layer raw material and mill ball mass ratio after glaze layer raw material is mixed according to proportioning:3 ~ 4 carry out ball milling, obtain
Glazing material layer after to ball milling;
(4)Glazing material layer after ball milling is sprayed on closestool idiosome, 2h is fired at 450 DEG C, then proceedes to heat up, in 800
3h is stopped at DEG C, then 1300 DEG C of the cause that heats up, 2h is fired, obtains pottery.
It should be appreciated that the detailed description carried out above by optimal enforcement example to technical scheme is schematical
It is and nonrestrictive, it is impossible to assert that the embodiment of the present invention is only limitted to this, for the general of the technical field of the invention
For logical technical staff, without departing from the inventive concept of the premise, the technical scheme described in each embodiment is modified,
Or equivalent substitution is carried out to which part technical characteristic, it should all be considered as belonging to what claims that the present invention submits determined
Scope of patent protection.
Claims (3)
1. a kind of pottery, it is characterised in that idiosome includes according to mass percentage:25 ~ 30 parts of clay, potassium feldspar 24 ~
27 parts, 15 ~ 18 parts of quartz, 12 ~ 16 parts of marble, 12 ~ 16 parts of kaolin, 16 ~ 20 parts of spodumene, 10 ~ 12 parts of bauxite, eluriate
13 ~ 15 parts of mud, 7 ~ 9 parts of gangue;
Glaze layer includes according to mass percentage:20 ~ 23 parts of dolomite, 10 ~ 13 parts of perovskite, 10 ~ 12 parts of potassium feldspar, aluminium borate
7 ~ 9 parts, 7 ~ 9 parts of aluminium metaphosphate, 9 ~ 12 parts of smithsonite.
2. pottery according to claim 1, it is characterised in that idiosome includes according to mass percentage:27 parts of clay,
25 parts of potassium feldspar, 16 parts of quartz, 14 parts of marble, 14 parts of kaolin, 17 parts of spodumene, 11 parts of bauxite, eluriate 12 parts of mud, coal
8 parts of spoil;
Glaze layer includes according to mass percentage:21 parts of dolomite, 12 parts of perovskite, 11 parts of potassium feldspar, 8 parts of aluminium borate, inclined phosphorus
Sour 8 parts of aluminium, 10 parts of smithsonite.
3. the preparation method of pottery described in claim 1, it is characterised in that comprise the following steps:
(1)It is 1 according to idiosome raw material and mill ball mass ratio after idiosome raw material is mixed according to proportioning:3 ~ 4 carry out ball milling, obtain
To porcelain mud;
(2)By step(1)After obtained porcelain mud mixes with water, after carrying out injection forming, drying, idiosome is obtained;
(3)It is 1 according to glaze layer raw material and mill ball mass ratio after glaze layer raw material is mixed according to proportioning:3 ~ 4 carry out ball milling, obtain
Glazing material layer after to ball milling;
(4)Glazing material layer after ball milling is sprayed on closestool idiosome, 1 ~ 2h is fired at 400 ~ 500 DEG C, then proceedes to heat up,
2 ~ 3h, then 1250 ~ 1350 DEG C of the cause that heats up are stopped at 700 ~ 900 DEG C, 1 ~ 2h is fired, obtains pottery.