CN107649840A - 一种千斤顶调整螺纹杆的生产工艺 - Google Patents
一种千斤顶调整螺纹杆的生产工艺 Download PDFInfo
- Publication number
- CN107649840A CN107649840A CN201711054539.5A CN201711054539A CN107649840A CN 107649840 A CN107649840 A CN 107649840A CN 201711054539 A CN201711054539 A CN 201711054539A CN 107649840 A CN107649840 A CN 107649840A
- Authority
- CN
- China
- Prior art keywords
- threaded rod
- finished product
- semi
- processing
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种千斤顶调整螺纹杆的生产工艺,包括以下步骤:准备材料、断料处理、冷镦处理、搓丝处理、热处理、高温发黑处理。本发明一种千斤顶调整螺纹杆的生产工艺,采用45K盘圆钢材依次通过断料处理、冷镦处理、搓丝处理、热处理和高温发黑处理,得到千斤顶调整螺纹杆产品,加工工艺简单,且产品的结构强度、稳定性、韧性及耐腐蚀性大大提升。
Description
【技术领域】
本发明涉及千斤顶调整螺纹杆的技术领域,特别涉及一种千斤顶调整螺纹 杆的生产工艺。
【背景技术】
千斤顶是一种起重设备,用钢性顶举件作为工作装置,通过顶部托座或底 部托爪在行程内顶升重物的轻小起重设备。分机械式和液压式两种,千斤顶主 要用于厂矿、交通运输等部门作为车辆修理及其它起重、支撑等工作。其结构 轻巧坚固、灵活可靠,一人即可携带和操作。千斤顶调整螺纹杆是构成千斤顶 的重要部件。目前的千斤顶调整螺纹杆结构强度低,且在使用过程中易锈蚀, 使用寿命短,为了解决以上问题,有必要提出一种千斤顶调整螺纹杆的生产工 艺。
【发明内容】
本发明的目的在于克服上述现有技术的不足,提供一种千斤顶调整螺纹杆 的生产工艺,其旨在解决现有技术中千斤顶调整螺纹杆结构强度低,且在使用 过程中易锈蚀的技术问题。
为实现上述目的,本发明提出了一种千斤顶调整螺纹杆的生产工艺,包括 以下步骤:
S1、准备材料:选用45K盘圆钢材作为生产千斤顶调整螺纹杆的钢材;
S2、断料处理:将盘圆钢材通过调直机调直,然后送入圆钢断料机中冲切 成规定长度的直条圆钢棒状坯料;
S3、冷镦处理:将圆钢棒状坯料送至冷镦机上进行冷镦成型;
S4、搓丝处理:将冷镦后的圆钢棒状坯料送至搓丝机上进行搓丝,得到螺 纹杆半成品;
S5、热处理:将半成品送进热处理炉内进行热处理工艺;
S6、高温发黑处理:将热处理后的半成品进行高温发黑工艺处理,得到成 品。
作为优选,所述的S5中热处理工艺包括以下步骤:
S5.1、将搓丝后的螺纹杆半成品采用清水清洗,然后送至热处理炉中加热, 保温一段时间后,在淬火池中进行淬火;
S5.2、将一次淬火后的螺纹杆半成品再次送入热处理炉中加热,保温一段时 间后,再在淬火池中进行淬火冷却;
S5.3、对冷却后的螺纹杆半成品采用清水进行清洗;
S5.4、将清洗后的螺纹杆半成品重新送入热处理炉中加热,保温一段时间后, 于空气中自然冷却。
作为优选,所述的S5.1、S5.2及S5.4中热处理炉的加热温度为850℃~900 ℃,保温时间为40~45min。
作为优选,所述的S6中的高温发黑工艺包括以下步骤:
S6.1、将半成品浸入除油槽内采用脱脂剂进行除油处理;
S6.2、将除油后的半成品浸入第一清洗槽内用清水进行清洗;
S6.3、将清洗后的半成品浸入酸洗槽内用盐酸进行酸洗处理;
S6.4、将酸洗后的半成品浸入第二清洗槽内用清水进行清洗;
S6.5、将清洗后的半成品浸入高温发黑槽内采用高温发黑剂进行发黑处理。
作为优选,所述的S6.1中脱脂剂为金属脱脂剂,主要成分有十二烷基磺酸 钠、椰油酰胺基丙基二甲基氧化胺、NaAc、Na2SO4、EDTA、助洗剂、表面活 性剂。
作为优选,所述的S6.5中高温发黑剂采用烧碱、亚硝酸钠和水配制而成, 所述的发黑处理温度为450℃~500℃,处理时间为10~15min。
作为优选,所述的发黑处理温度为475℃,处理时间为12min。
作为优选,所述的盘圆钢材在S2断料处理之前还依次经过酸洗、磷化、皂 化和拉丝处理。
本发明的有益效果:与现有技术相比,本发明提供的一种千斤顶调整螺纹 杆的生产工艺,采用45K盘圆钢材依次通过断料处理、冷镦处理、搓丝处理、 热处理和高温发黑处理,得到千斤顶调整螺纹杆产品,加工工艺简单,且产品 的结构强度、稳定性、韧性及耐腐蚀性大大提升。
本发明的特征及优点将通过实施例进行详细说明。
【具体实施方式】
为使本发明的目的、技术方案和优点更加清楚明了,下面通过实施例,对 本发明进行进一步详细说明。但是应该理解,此处所描述的具体实施例仅仅用 以解释本发明,并不用于限制本发明的范围。此外,在以下说明中,省略了对 公知结构和技术的描述,以避免不必要地混淆本发明的概念。
本发明实施例提供一种千斤顶调整螺纹杆的生产工艺,包括以下步骤:
S1、准备材料:选用45K盘圆钢材作为生产千斤顶调整螺纹杆的钢材。
S2、断料处理:将盘圆钢材通过调直机调直,然后送入圆钢断料机中冲切 成规定长度的直条圆钢棒状坯料。
在本发明实施例中,盘圆钢材在S2断料处理之前还依次经过酸洗、磷化、 皂化和拉丝处理。通过酸洗工艺去除钢材表面上的氧化皮和锈蚀物;通过磷化 工艺使钢材表面生成磷化膜,提供保护,在一定程度上防止被腐蚀,在后续的 冷镦过程中起减摩润滑作用;通过皂化工艺,使钢材表面形成硬脂酸锌,起润 滑作用,方便加工;通过拉丝处理工艺,使得钢材的直径拉伸至统一,提高了 产品质量的均一性。
S3、冷镦处理:将圆钢棒状坯料送至冷镦机上进行冷镦成型。
S4、搓丝处理:将冷镦后的圆钢棒状坯料送至搓丝机上进行搓丝,得到螺 纹杆半成品。
S5、热处理:将半成品送进热处理炉内进行热处理工艺:
S5.1、将搓丝后的螺纹杆半成品采用清水清洗,然后送至热处理炉中加热, 保温一段时间后,在淬火池中进行淬火;
S5.2、将一次淬火后的螺纹杆半成品再次送入热处理炉中加热,保温一段 时间后,再在淬火池中进行淬火冷却;
S5.3、对冷却后的螺纹杆半成品采用清水进行清洗;
S5.4、将清洗后的螺纹杆半成品重新送入热处理炉中加热,保温一段时间 后,于空气中自然冷却。
其中,S5.1、S5.2及S5.4中的热处理炉的加热温度为850℃~900℃,保 温时间为40~45min。
在本发明实施例中,采用二次淬火工艺与回火工艺,大大提升了工件的整 体性能的稳定性,同时提高了工件的韧性。
S6、高温发黑处理:将热处理后的半成品进行高温发黑工艺处理,得到成 品,高温发黑工艺包括以下步骤:
S6.1、将半成品浸入除油槽内采用脱脂剂进行除油处理;
S6.2、将除油后的半成品浸入第一清洗槽内用清水进行清洗;
S6.3、将清洗后的半成品浸入酸洗槽内用盐酸进行酸洗处理;
S6.4、将酸洗后的半成品浸入第二清洗槽内用清水进行清洗;
S6.5、将清洗后的半成品浸入高温发黑槽内采用高温发黑剂进行发黑处理。
其中,S6.1中脱脂剂为金属脱脂剂,主要成分有十二烷基磺酸钠、椰油酰 胺基丙基二甲基氧化胺、NaAc(醋酸钠)、Na2SO4、EDTA(乙二胺四乙酸)、 助洗剂、表面活性剂;S6.5中高温发黑剂采用烧碱、亚硝酸钠和水配制而成, 所述的发黑处理温度为450℃~500℃,处理时间为10~15min,优选,发黑处 理温度为475℃,处理时间为12min。
在本发明实施例中,高温发黑处理的目的是使工件的表面产生一层氧化膜, 以隔绝空气,达到防锈的效果。
本发明一种千斤顶调整螺纹杆的生产工艺,采用45K盘圆钢材依次通过断 料处理、冷镦处理、搓丝处理、热处理和高温发黑处理,得到千斤顶调整螺纹 杆产品,加工工艺简单,且产品的结构强度、稳定性、韧性及耐腐蚀性大大提 升。
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发 明的精神和原则之内所作的任何修改、等同替换或改进等,均应包含在本发明 的保护范围之内。
Claims (8)
1.一种千斤顶调整螺纹杆的生产工艺,其特征在于:包括以下步骤:
S1、准备材料:选用45K盘圆钢材作为生产千斤顶调整螺纹杆的钢材;
S2、断料处理:将盘圆钢材通过调直机调直,然后送入圆钢断料机中冲切成规定长度的直条圆钢棒状坯料;
S3、冷镦处理:将圆钢棒状坯料送至冷镦机上进行冷镦成型;
S4、搓丝处理:将冷镦后的圆钢棒状坯料送至搓丝机上进行搓丝,得到螺纹杆半成品;
S5、热处理:将半成品送进热处理炉内进行热处理工艺;
S6、高温发黑处理:将热处理后的半成品进行高温发黑工艺处理,得到成品。
2.如权利要求1所述的一种千斤顶调整螺纹杆的生产工艺,其特征在于:所述的S5中热处理工艺包括以下步骤:
S5.1、将搓丝后的螺纹杆半成品采用清水清洗,然后送至热处理炉中加热,保温一段时间后,在淬火池中进行淬火;
S5.2、将一次淬火后的螺纹杆半成品再次送入热处理炉中加热,保温一段时间后,再在淬火池中进行淬火冷却;
S5.3、对冷却后的螺纹杆半成品采用清水进行清洗;
S5.4、将清洗后的螺纹杆半成品重新送入热处理炉中加热,保温一段时间后,于空气中自然冷却。
3.如权利要求2所述的一种千斤顶调整螺纹杆的生产工艺,其特征在于:所述的S5.1、S5.2及S5.4中热处理炉的加热温度为850℃~900℃,保温时间为40~45min。
4.如权利要求1所述的一种千斤顶调整螺纹杆的生产工艺,其特征在于:所述的S6中的高温发黑工艺包括以下步骤:
S6.1、将半成品浸入除油槽内采用脱脂剂进行除油处理;
S6.2、将除油后的半成品浸入第一清洗槽内用清水进行清洗;
S6.3、将清洗后的半成品浸入酸洗槽内用盐酸进行酸洗处理;
S6.4、将酸洗后的半成品浸入第二清洗槽内用清水进行清洗;
S6.5、将清洗后的半成品浸入高温发黑槽内采用高温发黑剂进行发黑处理。
5.如权利要求4所述的一种千斤顶调整螺纹杆的生产工艺,其特征在于:所述的S6.1中脱脂剂为金属脱脂剂,主要成分有十二烷基磺酸钠、椰油酰胺基丙基二甲基氧化胺、NaAc、Na2SO4、EDTA、助洗剂、表面活性剂。
6.如权利要求4所述的一种千斤顶调整螺纹杆的生产工艺,其特征在于:所述的S6.5中高温发黑剂采用烧碱、亚硝酸钠和水配制而成,所述的发黑处理温度为450℃~500℃,处理时间为10~15min。
7.如权利要求6所述的一种千斤顶调整螺纹杆的生产工艺,其特征在于:所述的发黑处理温度为475℃,处理时间为12min。
8.如权利要求1所述的一种千斤顶调整螺纹杆的生产工艺,其特征在于:所述的盘圆钢材在S2断料处理之前还依次经过酸洗、磷化、皂化和拉丝处理。