CN107629743A - Modified acrylate adhesive, pressure-sensitive adhesive agent and preparation method thereof and adhesive tape and preparation method thereof - Google Patents
Modified acrylate adhesive, pressure-sensitive adhesive agent and preparation method thereof and adhesive tape and preparation method thereof Download PDFInfo
- Publication number
- CN107629743A CN107629743A CN201711045194.7A CN201711045194A CN107629743A CN 107629743 A CN107629743 A CN 107629743A CN 201711045194 A CN201711045194 A CN 201711045194A CN 107629743 A CN107629743 A CN 107629743A
- Authority
- CN
- China
- Prior art keywords
- parts
- pressure
- sensitive adhesive
- preparation
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Modified acrylate adhesive, pressure-sensitive adhesive agent and preparation method thereof and adhesive tape and preparation method thereof, the pressure-sensitive adhesive agent is prepared by II 3~9 parts of 50~80 parts of Modified acrylate adhesive, 3~10 parts of curing agent and solvent.Pressure-sensitive adhesive agent is prepared using electrolyte resistance type Modified acrylate adhesive in the present invention, the adhesive tape made of pressure-sensitive adhesive oxidant layer, buffering base material and the mould release membrance that the pressure-sensitive adhesive agent obtains, during applied to fixation between battery, both there is excellent electrolyte resistance performance, it can guarantee that bonding is permanently effective, and possess pooling feature, can guarantee that the gap between battery and battery is small can be tightly fastened and save space.
Description
Technical field
The present invention relates to assembled battery technical field, in particular to a kind of acrylate adhesive, pressure-sensitive adhesive
And preparation method thereof and adhesive tape and preparation method thereof.
Background technology
With the rapid development of New Energy Industry, increasing new energy battery applications are set in various automobiles and electronics
It is standby.To increase the capacitance of unit, multi-disc assembled battery is one of method for solving single equipment capacitance.Therefore, in order to
In the fixed more cell pieces of space arrangement, and fixation stable between cell piece is that to solve the problems, such as at present.
The content of the invention
In view of this, a kind of Modified acrylate adhesive provided by the invention, pressure-sensitive adhesive agent and preparation method thereof and
Adhesive tape and preparation method thereof, the above-mentioned problems of the prior art and defect are preferably overcome, be modified using electrolyte resistance type
Pressure-sensitive adhesive agent is prepared in acrylate adhesive, the pressure-sensitive adhesive oxidant layer that is obtained by the pressure-sensitive adhesive agent, buffering base material and
Adhesive tape made of mould release membrance, during applied to fixation between battery, both with excellent electrolyte resistance performance, it can guarantee that cohesive length
Phase is effective, and possesses pooling feature, and can guarantee that the gap between battery and battery is small can be tightly fastened and save space.
A kind of Modified acrylate adhesive, cross-linking polymerization system is carried out in organic solvent by the way that its raw material is mixed
It is standby to obtain；The raw material includes by weight：20~30 parts of acrylic monomers, 20~30 parts of methyl methacrylate, propylene
16~28 parts of acid butyl ester, 16~28 parts of Isooctyl acrylate monomer, 10~18 parts of styrene resin, 10~18 parts of isoprene resin and
0.01~1 part of initiator.
Further, the initiator is benzoyl peroxide.
Present invention also offers a kind of preparation method of pressure-sensitive adhesive agent, including：
3~9 parts of organic solvents and 3~10 parts of curing agent are sequentially added into 50~80 parts of Modified acrylate adhesives,
And stirring reaction；The Modified acrylate adhesive is above-mentioned Modified acrylate adhesive.
Further, the curing agent is isocyanates, pyridine, amino resins, band epoxide group resin, aluminium salt class chelating
One or more in thing.
Further, the speed of the stirring is 900~1500r/min.
Present invention also offers a kind of pressure-sensitive adhesive agent, the pressure-sensitive adhesive agent by above-mentioned pressure-sensitive adhesive agent preparation side
Method is prepared.
Present invention also offers a kind of preparation method of adhesive tape, including：
Above-mentioned pressure-sensitive adhesive agent is coated on mould release membrance, then toasted formation pressure-sensitive adhesive oxidant layer；
Buffering base material is fitted in the surface of the adhesive layer.
Further, the material of the buffering base material is one kind in radiation foaming PE foams, SBR foams and NBR foams.
Further, the thickness of the pressure-sensitive adhesive oxidant layer is 50~100 μm, the thickness of the buffering base material for 50~
100μm。
Present invention also offers a kind of adhesive tape, the adhesive tape is prepared by the preparation method of above-mentioned adhesive tape.
Compared with prior art, a kind of Modified acrylate adhesive of the invention, pressure-sensitive adhesive and preparation method thereof
Beneficial effect with adhesive tape and preparation method thereof is：
(1) pressure-sensitive adhesive agent is prepared using the modified rubber acrylate adhesive of electrolyte resistance type in the present invention, by
Adhesive tape made of pressure-sensitive adhesive oxidant layer, buffering base material and the mould release membrance that the pressure-sensitive adhesive agent obtains, applied to consolidating between battery
Regularly, it both can guarantee that bonding is permanently effective with excellent electrolyte resistance performance, and possess pooling feature, can guarantee that battery
Gap between battery is small to be tightly fastened and save space.
(2) preparation method of pressure-sensitive adhesive agent of the invention and adhesive tape is simple, and production cost is relatively low.
To enable the above objects, features and advantages of the present invention to become apparent, preferred embodiment cited below particularly, and coordinate
Appended accompanying drawing, is described in detail below.
Brief description of the drawings
In order to illustrate the technical solution of the embodiments of the present invention more clearly, below by embodiment it is required use it is attached
Figure is briefly described, it will be appreciated that the following drawings illustrate only certain embodiments of the present invention, therefore be not construed as pair
The restriction of scope, for those of ordinary skill in the art, on the premise of not paying creative work, can also be according to this
A little accompanying drawings obtain other related accompanying drawings.
Fig. 1 is the structural representation of the adhesive tape of one embodiment of the present of invention.
Main element symbol description：
1- adhesive tapes；
100- mould release membrances；
200- pressure-sensitive adhesive oxidant layer；
300- buffers base material.
Embodiment
For the ease of understanding the present invention, technical scheme is elaborated with reference to the mode of embodiment,
Many details are elaborated in the following description in order to fully understand the present invention.
But the invention can be embodied in many other ways as described herein, those skilled in the art can be with
Similar improvement is done in the case of without prejudice to intension of the present invention, therefore the present invention is not limited to the specific embodiments disclosed below.
Unless otherwise defined, all technologies used herein and scientific terminology have and the common skill of art of the present invention
The identical implication that art personnel are generally understood that.When contradiction be present, the definition in this specification is defined.
Term as used herein：
Term "comprising" used herein, " comprising ", " having ", " containing " or its any other deformation, it is intended that covering
Non-exclusionism includes.Wanted for example, composition, step, method, product or device comprising listed elements are not necessarily limited to those
Element, but can include not expressly listed other key elements or such a composition, step, method, product or device it is intrinsic
Key element.
Conjunction " by ... form " exclude any key element do not pointed out, step or component.If be used in claim,
This phrase will make claim be closed, it is not included the material in addition to the material of those descriptions, but relative
Except customary impurities.When phrase " by ... form " be rather than immediately following theme in the clause that appears in claim main body after
When, it is only limited to the key element described in the clause；Other key elements be not excluded as entirety the claim it
Outside.
Equivalent, concentration or other values or parameter are excellent with scope, preferred scope or a series of upper limit preferred values and lower limit
During the Range Representation that choosing value limits, this, which is appreciated that, specifically discloses by any range limit or preferred value and any scope
All scopes that any pairing of lower limit or preferred value is formed, regardless of whether the scope separately discloses.For example, when open
Scope " when 1~5 ", described scope should be interpreted as including scope " 1~4 ", " 1~3 ", " 1~2 ", " 1~2 and 4~
5 ", " 1~3 and 5 " etc..When number range is described herein, unless otherwise indicated, otherwise the scope is intended to include its end
Value and all integers and fraction within the range.
"and/or" is used to represent that one of illustrated situation or both may to occur, for example, A and/or B includes (A
And B) and (A or B)；
In addition, indefinite article " one kind " before key element of the present invention or component and "one" to key element or the quantitative requirement of component
(i.e. occurrence number) unrestriction.Therefore "one" or " one kind " should be read as including one or at least one, well and odd number
The key element or component of form also include plural form, unless the obvious purport of the quantity refers to singulative.
A kind of Modified acrylate adhesive, cross-linking polymerization system is carried out in organic solvent by the way that its raw material is mixed
It is standby to obtain；
The raw material includes by weight：
Such as 20 parts, 23 parts, 25 parts, 28 parts or 30 parts of 20~30 parts of acrylic monomers；
Such as 20 parts, 23 parts, 25 parts, 28 parts or 30 parts of 20~30 parts of methyl methacrylate；
Such as 16 parts, 18 parts, 20 parts, 23 parts, 25 parts or 28 parts of 16~28 parts of butyl acrylate；
Such as 16 parts, 18 parts, 20 parts, 23 parts, 25 parts or 28 parts of 16~28 parts of Isooctyl acrylate monomer；
Such as 10 parts, 11 parts, 12 parts, 13 parts, 14 parts, 15 parts, 16 parts, 17 parts or 18 parts of 10~18 parts of styrene resin；
10~18 parts of isoprene resin is such as 10 parts, 11 parts, 12 parts, 13 parts, 14 parts, 15 parts, 16 parts, 17 parts or 18 parts
Deng；
With such as 0.01 part, 0.05 part, 0.1 part, 0.2 part, 0.3 part, 0.5 part, 0.7 part, 0.9 part of 0.01~1 part of initiator
Or 1 part etc.；
The dosage of above-mentioned organic solvent is 1 times of said components raw material gross weight, and the organic solvent is preferably ethyl acetate,
It can certainly be other organic solvents such as isopropanol etc..
Preferably, the initiator is benzoyl peroxide；It is described to draw but the present invention is not intended to limit the species of initiator
Other various initiators that hair agent can also be known to the skilled person.
The temperature of above-mentioned copolymerzation with cross-linking reaction is preferably 80 DEG C.
Present invention also offers a kind of preparation method of pressure-sensitive adhesive agent, including：
3~9 parts of organic solvents and 3~10 parts of curing agent are sequentially added into 50~80 parts of Modified acrylate adhesives,
And stirring reaction.The Modified acrylate adhesive is above-mentioned Modified acrylate adhesive.
The parts by weight of the Modified acrylate adhesive can specifically be enumerated as 50 parts, 55 parts, 60 parts, 65 parts, 70 parts,
75 parts or 80 parts etc.；The parts by weight of the curing agent can specifically be enumerated as 3 parts, 4 parts, 5 parts, 6 parts, 7 parts, 8 parts, 9 parts or 10
Part etc.；The parts by weight of the organic solvent can specifically be enumerated as 3 parts, 4 parts, 5 parts, 6 parts, 7 parts, 8 parts or 9 parts etc., and this is organic
Solvent is preferably ethyl acetate, naturally it is also possible to for other organic solvents such as isopropanol etc..
Preferably, the curing agent is isocyanates, pyridine, amino resins, band epoxide group resin, aluminium salt class chelate
In one or more；Certainly, other crosslinking agents that the curing agent can be also known to the skilled person.
Preferably, the speed of the stirring be 900~1500r/min such as 900r/min, 1000r/min, 1100r/min,
1200r/min, 1300r/min, 1400r/min or 1500r/min etc..
Present invention also offers a kind of pressure-sensitive adhesive agent, pressure-sensitive adhesive agent described in the pressure-sensitive adhesive agent is by above-mentioned pressure-sensitive
The preparation method of adhesive is prepared.
Present invention also offers a kind of preparation method of adhesive tape 1, including：
Above-mentioned pressure-sensitive adhesive agent is coated on mould release membrance 100, then toasted formation pressure-sensitive adhesive oxidant layer 200；
Buffering base material 300 is fitted in the surface of the pressure-sensitive adhesive oxidant layer 200.
Preferably, the baking temperature be 80~150 DEG C as 80 DEG C, 90 DEG C, 100 DEG C, 110 DEG C, 120 DEG C, 130 DEG C, 140
DEG C or 150 DEG C etc..
Preferably, the mould release membrance 100 uses PET separated type materials.
Preferably, the material of the buffering base material 300 is one kind of radiation foaming PE foams, SBR foams and NBR foams.
More preferably, the material of the buffering base material 300 is radiation foaming PE foams.The compression performance of radiation foaming PE foams
As shown in table 1.
The radiation foaming PE foam compression performances of table 1
| Compression ratio | 5% | 50% | 75% |
| Bounce (Kg) | 0.1~0.5 | 5.0~7.0 | 10.0~13.0 |
Preferably, the thickness of the mould release membrance 100 is 25~50 μm such as 25 μm, 30 μm, 35 μm, 40 μm, 45 μm or 50 μm
Deng；The thickness of the pressure-sensitive adhesive oxidant layer 200 is 50~100 μm such as 50 μm, 60 μm, 70 μm, 80 μm, 90 μm or 100 μm；Institute
The thickness for stating buffering base material 300 is 100~500 μm such as 100 μm, 200 μm, 300 μm, 400 μm or 500 μm.
Present invention also offers a kind of adhesive tape 1, the adhesive tape 1 is prepared by the preparation method of above-mentioned adhesive tape 1.The glue
Mould release membrance 100, pressure-sensitive adhesive oxidant layer 200 and buffering base material 300 including stacking gradually with 1.
Seen from the above description, pressure is prepared using the modified rubber acrylate adhesive of electrolyte resistance type in the present invention
Quick adhesive, the adhesive tape made of pressure-sensitive adhesive oxidant layer 200, buffering base material 300 and the mould release membrance 100 that the pressure-sensitive adhesive agent obtains
1, thickness of thin, during applied to fixation between battery,
Both there is excellent electrolyte resistance performance, can guarantee that bonding is permanently effective, and possess pooling feature, can guarantee that electricity
Gap between pond and battery is small to be tightly fastened and save space.
For the ease of understanding the present invention, technical scheme is further illustrated with reference to embodiment.Applicant
Statement, the present invention illustrate the detailed process equipment of the present invention and technological process, but not office of the invention by above-described embodiment
It is limited to above-mentioned detailed process equipment and technological process, that is, does not mean that the present invention should rely on above-mentioned detailed process equipment and technique stream
Cheng Caineng is implemented.Person of ordinary skill in the field is it will be clearly understood that any improvement in the present invention, to each original of product of the present invention
The equivalence replacement of material and the addition of auxiliary element, the selection of concrete mode etc., all fall within protection scope of the present invention and open model
Within enclosing.
Embodiment 1
Step 1：By 20 parts of acrylic monomers, 20 parts of methyl methacrylates, 28 parts of butyl acrylates, 16 parts of acrylic acid
Different monooctyl ester, 18 parts of styrene resins, 1 times of 10 parts of isoprene resins, 0.01 part of initiator and said components raw material gross weight
The ethyl acetate of dosage, copolymerzation with cross-linking reaction is carried out under the conditions of 80 DEG C, obtains electrolyte resistance type Modified acrylate adhesive.
Step 2：3 parts of ethyl acetate are added in 50 parts of above-mentioned Modified acrylate adhesive, and use homogenizer
10min is stirred with 900r/min mixing speed.
Step 3：3 parts of isocyanates are added in above-mentioned solution, and with homogenizer with 900r/min mixing speed
10min is stirred, obtains pressure-sensitive adhesive agent.
Step 4：Above-mentioned pressure-sensitive adhesive agent is coated on a mould release membrance 100, is sent into the hot-air oven that temperature is 80 DEG C
Baking, form pressure-sensitive adhesive oxidant layer 200.
Step 5：Radiation foaming PE foam buffering base materials 300 are fitted in the surface of above-mentioned pressure-sensitive adhesive oxidant layer 200, received
Parent roll, adhesive tape 1 is made.
Embodiment 2
Step 1：By 23 parts of acrylic monomers, 23 parts of methyl methacrylates, 25 parts of butyl acrylates, 18 parts of acrylic acid
Different monooctyl ester, 16 parts of styrene resins, 1 times of 12 parts of isoprene resins, 0.1 part of initiator and said components raw material gross weight use
The ethyl acetate of amount, copolymerzation with cross-linking reaction is carried out under the conditions of 80 DEG C, obtains electrolyte resistance type Modified acrylate adhesive.
Step 2：5 parts of ethyl acetate are added in 60 parts of above-mentioned Modified acrylate adhesive, and use homogenizer
9min is stirred with 1000r/min mixing speed.
Step 3：5 parts of isocyanates are added in above-mentioned solution, and with homogenizer with 1000r/min stirring speed
Degree stirring 9min, obtains pressure-sensitive adhesive agent.
Step 4：Above-mentioned pressure-sensitive adhesive agent is coated on a mould release membrance 100, is sent into the hot-air oven that temperature is 80 DEG C
Baking, form pressure-sensitive adhesive oxidant layer 200.
Step 5：Radiation foaming PE foam buffering base materials 300 are fitted in the surface of above-mentioned pressure-sensitive adhesive oxidant layer 200, received
Parent roll, adhesive tape 1 is made.
Embodiment 3
Step 1：By 25 parts of acrylic monomers, 25 parts of methyl methacrylates, 23 parts of butyl acrylates, 20 parts of acrylic acid
Different monooctyl ester, 15 parts of styrene resins, 1 times of 14 parts of isoprene resins, 0.3 part of initiator and said components raw material gross weight use
The ethyl acetate of amount, copolymerzation with cross-linking reaction is carried out under the conditions of 80 DEG C, obtains electrolyte resistance type Modified acrylate adhesive.
Step 2：6 parts of ethyl acetate are added in 65 parts of above-mentioned Modified acrylate adhesive, and use homogenizer
8min is stirred with 1100r/min mixing speed.
Step 3：6 parts of isocyanates are added in above-mentioned solution, and with homogenizer with 1100r/min stirring speed
Degree stirring 7min, obtains pressure-sensitive adhesive agent.
Step 4：Above-mentioned pressure-sensitive adhesive agent is coated on a mould release membrance 100, is sent into the hot-air oven that temperature is 80 DEG C
Baking, form pressure-sensitive adhesive oxidant layer 200.
Step 5：Radiation foaming PE foam buffering base materials 300 are fitted in the surface of above-mentioned pressure-sensitive adhesive oxidant layer 200, received
Parent roll, adhesive tape 1 is made.
Embodiment 4
Step 1：By 28 parts of acrylic monomers, 28 parts of methyl methacrylates, 20 parts of butyl acrylates, 23 parts of acrylic acid
Different monooctyl ester, 13 parts of styrene resins, 1 times of 15 parts of isoprene resins, 0.5 part of initiator and said components raw material gross weight use
The ethyl acetate of amount, copolymerzation with cross-linking reaction is carried out under the conditions of 80 DEG C, obtains electrolyte resistance type Modified acrylate adhesive.
Step 2：7 parts of ethyl acetate are added in 70 parts of above-mentioned Modified acrylate adhesive, and use homogenizer
8min is stirred with 1200r/min mixing speed.
Step 3：8 parts of isocyanates are added in above-mentioned solution, and with homogenizer with 1200r/min stirring speed
Degree stirring 8min, obtains pressure-sensitive adhesive agent.
Step 4：Above-mentioned pressure-sensitive adhesive agent is coated on a mould release membrance 100, is sent into the hot-air oven that temperature is 80 DEG C
Baking, form pressure-sensitive adhesive oxidant layer 200.
Step 5：Radiation foaming PE foam buffering base materials 300 are fitted in the surface of above-mentioned pressure-sensitive adhesive oxidant layer 200, received
Parent roll, adhesive tape 1 is made.
Embodiment 5
Step 1：By 30 parts of acrylic monomers, 30 parts of methyl methacrylates, 18 parts of butyl acrylates, 25 parts of acrylic acid
Different monooctyl ester, 12 parts of styrene resins, 1 times of 16 parts of isoprene resins, 0.7 part of initiator and said components raw material gross weight use
The ethyl acetate of amount, copolymerzation with cross-linking reaction is carried out under the conditions of 80 DEG C, obtains electrolyte resistance type Modified acrylate adhesive.
Step 2：9 parts of ethyl acetate are added in 80 parts of above-mentioned Modified acrylate adhesive, and use homogenizer
5min is stirred with 1500r/min mixing speed.
Step 3：10 parts of isocyanates are added in above-mentioned solution, and with homogenizer with 1500r/min stirring speed
Degree stirring 5min, obtains pressure-sensitive adhesive agent.
Step 4：Above-mentioned pressure-sensitive adhesive agent is coated on a mould release membrance 100, is sent into the hot-air oven that temperature is 80 DEG C
Baking, form pressure-sensitive adhesive oxidant layer 200.
Step 5：Radiation foaming PE foam buffering base materials 300 are fitted in the surface of above-mentioned pressure-sensitive adhesive oxidant layer 200, received
Parent roll, adhesive tape 1 is made.
Embodiment 6
Step 1：By 20 parts of acrylic monomers, 20 parts of methyl methacrylates, 28 parts of butyl acrylates, 28 parts of acrylic acid
Different monooctyl ester, 10 parts of styrene resins, 1 times of 18 parts of isoprene resins, 1 part of initiator and said components raw material gross weight dosage
Ethyl acetate, under the conditions of 80 DEG C carry out copolymerzation with cross-linking reaction, obtain electrolyte resistance type Modified acrylate adhesive.
Step 2：8 parts of ethyl acetate are added in 75 parts of above-mentioned Modified acrylate adhesive, and use homogenizer
6min is stirred with 1400r/min mixing speed.
Step 3：8 parts of isocyanates are added in above-mentioned solution, and with homogenizer with 1400r/min stirring speed
Degree stirring 6min, obtains pressure-sensitive adhesive agent.
Step 4：Above-mentioned pressure-sensitive adhesive agent is coated on a mould release membrance 100, is sent into the hot-air oven that temperature is 80 DEG C
Baking, form pressure-sensitive adhesive oxidant layer 200.
Step 5：Radiation foaming PE foam buffering base materials 300 are fitted in the surface of above-mentioned pressure-sensitive adhesive oxidant layer 200, received
Parent roll, adhesive tape 1 is made.
The preferred embodiments of the present invention are above are only, are not intended to limit the invention, for those skilled in the art
For member, inventive formulation and preparation technology can have various modifications and variations.Within the spirit and principles of the invention, institute
Any modification, equivalent substitution and improvements of work etc., should be included in the scope of the protection.
Claims (10)
- A kind of 1. Modified acrylate adhesive, it is characterised in that：It is crosslinked in organic solvent by the way that its raw material is mixed Polymerisation is prepared；The raw material includes by weight：20~30 parts of acrylic monomers, methyl methacrylate 20~ 30 parts, 16~28 parts of butyl acrylate, 16~28 parts of Isooctyl acrylate monomer, 10~18 parts of styrene resin, isoprene resin 10~18 parts and 0.01~1 part of initiator.
- 2. Modified acrylate adhesive according to claim 1, it is characterised in that：The initiator is benzoyl peroxide first Acyl.
- A kind of 3. preparation method of pressure-sensitive adhesive agent, it is characterised in that：Including：3~9 parts of organic solvents and 3~10 parts of curing agent are sequentially added into 50~80 parts of Modified acrylate adhesives, and are stirred Mix reaction；The Modified acrylate adhesive is the Modified acrylate adhesive described in claim 1 or 2.
- 4. the preparation method of pressure-sensitive adhesive agent according to claim 3, it is characterised in that：The curing agent is isocyanic acid Ester, pyridine, amino resins, with the one or more in epoxide group resin, aluminium salt class chelate.
- 5. the preparation method of pressure-sensitive adhesive agent according to claim 3, it is characterised in that：The speed of the stirring is 900 ~1500r/min.
- A kind of 6. pressure-sensitive adhesive agent, it is characterised in that：The pressure-sensitive adhesive agent is as pressure-sensitive described in any one of claim 3~5 The preparation method of adhesive is prepared.
- A kind of 7. preparation method of adhesive tape, it is characterised in that：Including：Pressure-sensitive adhesive agent described in claim 6 is coated on mould release membrance, then toasted formation pressure-sensitive adhesive oxidant layer；Buffering base material is fitted in the surface of the adhesive layer.
- 8. the preparation method of adhesive tape according to claim 7, it is characterised in that：The material of the buffering base material is sent out for radiation Steep one kind in PE foams, SBR foams and NBR foams.
- 9. the preparation method of adhesive tape according to claim 7, it is characterised in that：The thickness of the pressure-sensitive adhesive oxidant layer is 50 ~100 μm, the thickness of the buffering base material is 50~100 μm.
- A kind of 10. adhesive tape, it is characterised in that：Preparation method system of the adhesive tape as the adhesive tape described in any one of claim 7~9 It is standby to obtain.