CN107629363A - 一种防辐射改性材料及其制备方法 - Google Patents
一种防辐射改性材料及其制备方法 Download PDFInfo
- Publication number
- CN107629363A CN107629363A CN201711046865.1A CN201711046865A CN107629363A CN 107629363 A CN107629363 A CN 107629363A CN 201711046865 A CN201711046865 A CN 201711046865A CN 107629363 A CN107629363 A CN 107629363A
- Authority
- CN
- China
- Prior art keywords
- parts
- radiation proof
- material modified
- raw material
- polyvinyl chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种防辐射改性材料及其制备方法,防辐射改性材料包括以下重量份的原料:25份‑35份PVC树脂、20‑35份ABS树脂、3份‑6份紫外线吸收剂、10‑18份硬脂酸锌、1‑6份抗静电剂、0.8‑1.5份防伽马射线剂、0.8‑2.5份增塑剂。本发明的防辐射改性材料通过采用两种不同的树脂材料进行混合,并加入抗静电剂和防辐射剂,具有良好的防静电效果和防辐射效果,环保性能好。
Description
技术领域
本发明涉及高分子材料技术领域,具体涉及一种防辐射改性材料及其制备方法。
背景技术
聚氯乙烯是最早工业化、用途广泛的通用热塑性塑料之一,它具有质量轻、阻燃、耐辐射等优点。但也存在韧性差、受冲击时极易脆裂、热稳定性差、粘度高、流动性差等缺点,在一定程度上限制了其使用,因此不能用作结构材料。辐射对人体的危害性很大,射线具有很强的穿透力,对细胞有杀伤力,因此,研发一种防辐射的改性材料显得尤为重要。
发明内容
本发明所要解决的技术问题是针对现有技术的不足,提供一种防辐射改性材料及其制备方法。
本发明解决上述技术问题的技术方案如下:一种防辐射改性材料,包括以下重量份的原料:25份-35份PVC树脂、20-35份ABS树脂、3份-6份紫外线吸收剂、10-18份硬脂酸锌、1-6份抗静电剂、0.8-1.5份防伽马射线剂、0.8-2.5份增塑剂。
本发明的有益效果是:本发明的防辐射改性材料通过采用两种不同的树脂材料进行混合,并加入抗静电剂和防辐射剂,具有良好的防静电效果和防辐射效果,环保性能好。
在上述技术方案的基础上,本发明还可以做如下改进。
进一步,包括以下重量份的原料:30份ABS树脂、30份ABS树脂、4份紫外线吸收剂、15份硬脂酸锌、3份抗静电剂、1份防伽马射线剂、1.8份增塑剂。
进一步,所述增塑剂是由柠檬酸三乙酯和环氧大豆油以任意比混合得到的混合物。
进一步,所述抗静电剂是由炭黑和碳纤维以1:1混合得到的混合物。
进一步,所述防伽马射线剂为硫酸钡。
一种防辐射改性材料的制备方法,包括以下步骤:
(1)按重量份称取上述的原料,将PVC树脂和ABS树脂均在80-90℃温度下烘烤3-5h备用;
(2)将经过烘烤的PVC树脂和ABS树脂和其余原料放入高速混合机中共混4-9min,混合温度为90-110℃,得到混合物;
(3)将混合物投入到双螺杆挤出机中熔融造粒,制得所述防辐射改性材料。
具体实施方式
以下对本发明的原理和特征进行描述,所举实例只用于解释本发明,并非用于限定本发明的范围。
实施例1
本实施例的一种防辐射改性材料,包括以下重量份的原料:25份PVC树脂、20份ABS树脂、3份紫外线吸收剂、10份硬脂酸锌、1份抗静电剂、0.8份防伽马射线剂、0.8份增塑剂。
本实施例的防辐射改性材料通过采用两种不同的树脂材料进行混合,并加入抗静电剂和防辐射剂,具有良好的防静电效果和防辐射效果,环保性能好。
具体的,所述增塑剂是由柠檬酸三乙酯和环氧大豆油以任意比混合得到的混合物。
具体的,所述抗静电剂是由炭黑和碳纤维以1:1混合得到的混合物。
具体的,所述防伽马射线剂为硫酸钡。
本实施例的防辐射改性材料的制备方法,包括以下步骤:
(1)按重量份称取上述的原料,将PVC树脂和ABS树脂均在80℃温度下烘烤3h备用;
(2)将经过烘烤的PVC树脂和ABS树脂和其余原料放入高速混合机中共混4min,混合温度为90℃,得到混合物;
(3)将混合物投入到双螺杆挤出机中熔融造粒,制得所述防辐射改性材料。
实施例2
本实施例的一种防辐射改性材料,包括以下重量份的原料:30份ABS树脂、30份ABS树脂、4份紫外线吸收剂、15份硬脂酸锌、3份抗静电剂、1份防伽马射线剂、1.8份增塑剂。
本实施例的防辐射改性材料通过采用两种不同的树脂材料进行混合,并加入抗静电剂和防辐射剂,具有良好的防静电效果和防辐射效果,环保性能好。
具体的,所述增塑剂是由柠檬酸三乙酯和环氧大豆油以任意比混合得到的混合物。
具体的,所述抗静电剂是由炭黑和碳纤维以1:1混合得到的混合物。
具体的,所述防伽马射线剂为硫酸钡。
本实施例的防辐射改性材料的制备方法,包括以下步骤:
(1)按重量份称取上述的原料,将PVC树脂和ABS树脂均在85℃温度下烘烤4h备用;
(2)将经过烘烤的PVC树脂和ABS树脂和其余原料放入高速混合机中共混6min,混合温度为100℃,得到混合物;
(3)将混合物投入到双螺杆挤出机中熔融造粒,制得所述防辐射改性材料。
实施例3
本实施例的一种防辐射改性材料,包括以下重量份的原料:35份PVC树脂、35份ABS树脂、6份紫外线吸收剂、18份硬脂酸锌、6份抗静电剂、1.5份防伽马射线剂、2.5份增塑剂。
本实施例的防辐射改性材料通过采用两种不同的树脂材料进行混合,并加入抗静电剂和防辐射剂,具有良好的防静电效果和防辐射效果,环保性能好。
具体的,所述增塑剂是由柠檬酸三乙酯和环氧大豆油以任意比混合得到的混合物。
具体的,所述抗静电剂是由炭黑和碳纤维以1:1混合得到的混合物。
具体的,所述防伽马射线剂为硫酸钡。
本实施例的防辐射改性材料的制备方法,包括以下步骤:
(1)按重量份称取上述的原料,将PVC树脂和ABS树脂均在90℃温度下烘烤5h备用;
(2)将经过烘烤的PVC树脂和ABS树脂和其余原料放入高速混合机中共混9min,混合温度为110℃,得到混合物;
(3)将混合物投入到双螺杆挤出机中熔融造粒,制得所述防辐射改性材料。
对比例1
一种防辐射改性材料,包括以下重量份的原料:35份PVC树脂、35份ABS树脂、6份紫外线吸收剂、6份抗静电剂、1.5份防伽马射线剂、2.5份增塑剂。制备方法与实施例3相同。
对比例2
一种防辐射改性材料,包括以下重量份的原料:35份PVC树脂、35份ABS树脂、6份紫外线吸收剂、18份硬脂酸锌、6份抗静电剂、1.5份防伽马射线剂。制备方法与实施例3相同。
本实施例1-3和对比例1-2中的改性材料的机械物理性能如表1所示。
表1改性材料性能测试
测试项目 | 实施例1 | 实施例2 | 实施例3 | 对比例1 | 对比例2 |
断裂伸长率(%) | 297 | 301 | 289 | 245 | 249 |
防伽马辐射 | 91% | 95% | 94% | 74% | 78% |
防电磁辐射 | 89% | 87% | 86% | 64% | 68% |
由表1可知,本实施例的防辐射改性材料的防辐射效果好、环保,且耐温和耐候性能优良,强度高,抗冲击性能优异。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (6)
1.一种防辐射改性材料,其特征在于,包括以下重量份的原料:25份-35份PVC树脂、20-35份ABS树脂、3份-6份紫外线吸收剂、10-18份硬脂酸锌、1-6份抗静电剂、0.8-1.5份防伽马射线剂、0.8-2.5份增塑剂。
2.根据权利要求1所述一种防辐射改性材料,其特征在于,包括以下重量份的原料:30份ABS树脂、30份ABS树脂、4份紫外线吸收剂、15份硬脂酸锌、3份抗静电剂、1份防伽马射线剂、1.8份增塑剂。
3.根据权利要求1或2所述一种防辐射改性材料,其特征在于,所述增塑剂是由柠檬酸三乙酯和环氧大豆油以任意比混合得到的混合物。
4.根据权利要求1或2所述一种防辐射改性材料,其特征在于,所述抗静电剂是由炭黑和碳纤维以1:1混合得到的混合物。
5.根据权利要求1或2所述一种防辐射改性材料,其特征在于,所述防伽马射线剂为硫酸钡。
6.一种防辐射改性材料的制备方法,其特征在于,包括以下步骤:
(1)按重量份称取权利要求1至5任一项所述的原料,将PVC树脂和ABS树脂均在80-90℃温度下烘烤3-5h备用;
(2)将经过烘烤的PVC树脂和ABS树脂和其余原料放入高速混合机中共混4-9min,混合温度为90-110℃,得到混合物;
(3)将混合物投入到双螺杆挤出机中熔融造粒,制得所述防辐射改性材料。