CN107628807A - 一种负离子多孔陶瓷材料的制备方法 - Google Patents
一种负离子多孔陶瓷材料的制备方法 Download PDFInfo
- Publication number
- CN107628807A CN107628807A CN201710971043.8A CN201710971043A CN107628807A CN 107628807 A CN107628807 A CN 107628807A CN 201710971043 A CN201710971043 A CN 201710971043A CN 107628807 A CN107628807 A CN 107628807A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- powder
- slurry
- film material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供一种负离子多孔陶瓷材料的制备方法,包括步骤:(1) 按重量配比,将苏州土80~85份、滑石粉5~10份、电气石10~15份、助烧结剂3~5份,混合后进行球磨,制成粉料;(2)将聚乙烯醇溶解于无水乙醇中,待溶解均匀后再加入水和粉料进行搅拌,搅拌同时加入羧甲基纤维素,制成陶瓷浆料;(3)将聚酯海绵切割成陶瓷材料所需形状,浸渍到浆料中,使浆料充满聚酯海绵后,烘干,制成陶瓷生坯;(4)将陶瓷生坯置入电炉中烧结,制成多孔陶瓷。
Description
技术领域
本发明涉及陶瓷领域,具体涉及一种新型陶瓷材料的制备方法。
背景技术
随着人们对家居环境要求的提高,对各种建材的环保健康要求也随之提高,尤其是对于室内空气的要求越来越高。
负离子具有极佳的净化除尘,减少二手烟危害、改善预防呼吸道疾病、改善睡眠、抗氧化、防衰老、清除体内自由基、降低血液粘稠度的效果,在医学界享有“维他氧”“空气维生素”“长寿素”“ 空气维他命”等美称。
发明内容
针对上述问题,本发明提供一种负离子多孔陶瓷材料的制备方法,包括步骤:
(1) 按重量配比,将苏州土80~85份、滑石粉5~10份、电气石10~15份、助烧结剂3~5份,混合后进行球磨,制成粉料;
(2)将聚乙烯醇溶解于无水乙醇中,待溶解均匀后再加入水和粉料进行搅拌,搅拌同时加入羧甲基纤维素,制成陶瓷浆料;
(3)将聚酯海绵切割成陶瓷材料所需形状,浸渍到浆料中,使浆料充满聚酯海绵后,烘干,制成陶瓷生坯;
(4)将陶瓷生坯置入电炉中烧结,制成多孔陶瓷。
优选的,所述助烧结剂为氧化镁。
优选的,步骤(2)中,水和粉料的重量比例为1:0.8。
优选的,在步骤(2)中,搅拌时间90~130分钟。
优选的,步骤(4)中,烧结温度850~930℃。
本发明采用电气石制作浆料,将聚酯海绵浸渍,采用该方法烧制成的陶瓷含有大量电气石,并具有多孔结构以提高电气石与空气的接触面,应用在家具建材的陶瓷产品的制作中,使产品可以散发出大量负离子,有益人体健康。
具体实施方式
为便于本领域技术人员理解本发明,下面将结合具体实施例对本发明作进一步详细描述。
实施例1
(1)按重量配比,将苏州土80份、滑石粉5份、电气石10份、助烧结剂3份,助烧结剂采用氧化镁,混合后进行球磨,制成粉料;
(2)将聚乙烯醇溶解于无水乙醇中,待溶解均匀后再加入水和粉料进行搅拌,水和粉料的重量比例为1:0.8,搅拌时间90分钟,搅拌同时加入羧甲基纤维素,制成陶瓷浆料;
(3)将聚酯海绵切割成陶瓷材料所需形状,浸渍到浆料中,使浆料充满聚酯海绵后,烘干,制成陶瓷生坯;
(4)将陶瓷生坯置入电炉中烧结,烧结温度850℃,制成多孔陶瓷。
实施例2
(1)按重量配比,将苏州土85份、滑石粉10份、电气石15份、助烧结剂5份,助烧结剂采用氧化镁,混合后进行球磨,制成粉料;
(2)将聚乙烯醇溶解于无水乙醇中,待溶解均匀后再加入水和粉料进行搅拌,水和粉料的重量比例为1:0.8,搅拌时间130分钟,搅拌同时加入羧甲基纤维素,制成陶瓷浆料;
(3)将聚酯海绵切割成陶瓷材料所需形状,浸渍到浆料中,使浆料充满聚酯海绵后,烘干,制成陶瓷生坯;
(4)将陶瓷生坯置入电炉中烧结,烧结温度930℃,制成多孔陶瓷。
虽然对本发明的描述是结合以上具体实施例进行的,但是,熟悉本技术领域的人员能够根据上述的内容进行许多替换、修改和变化,是显而易见的。因此,所有这样的替代、改进和变化都包括在附后的权利要求的范围内。
Claims (5)
1.一种负离子多孔陶瓷材料的制备方法,包括步骤:
(1) 按重量配比,将苏州土80~85份、滑石粉5~10份、电气石10~15份、助烧结剂3~5份,混合后进行球磨,制成粉料;
(2)将聚乙烯醇溶解于无水乙醇中,待溶解均匀后再加入水和粉料进行搅拌,搅拌同时加入羧甲基纤维素,制成陶瓷浆料;
(3)将聚酯海绵切割成陶瓷材料所需形状,浸渍到浆料中,使浆料充满聚酯海绵后,烘干,制成陶瓷生坯;
(4)将陶瓷生坯置入电炉中烧结,制成多孔陶瓷。
2.依据权利要求1所述负离子多孔陶瓷材料的制备方法,其特征在于:所述助烧结剂为氧化镁。
3.依据权利要求1所述负离子多孔陶瓷材料的制备方法,其特征在于:步骤(2)中,水和粉料的重量比例为1:0.8。
4.依据权利要求1所述负离子多孔陶瓷材料的制备方法,其特征在于:在步骤(2)中,搅拌时间90~130分钟。
5.依据权利要求1所述负离子多孔陶瓷材料的制备方法,其特征在于:步骤(4)中,烧结温度850~930℃。