CN107604221A - 一种高强度抗氧化铝合金材料及其制备方法 - Google Patents

一种高强度抗氧化铝合金材料及其制备方法 Download PDF

Info

Publication number
CN107604221A
CN107604221A CN201710999472.6A CN201710999472A CN107604221A CN 107604221 A CN107604221 A CN 107604221A CN 201710999472 A CN201710999472 A CN 201710999472A CN 107604221 A CN107604221 A CN 107604221A
Authority
CN
China
Prior art keywords
temperature
aluminum alloy
alloy materials
magnesium
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710999472.6A
Other languages
English (en)
Inventor
魏道金
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xuzhou Xuanyuan Aluminum Co Ltd
Original Assignee
Xuzhou Xuanyuan Aluminum Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xuzhou Xuanyuan Aluminum Co Ltd filed Critical Xuzhou Xuanyuan Aluminum Co Ltd
Priority to CN201710999472.6A priority Critical patent/CN107604221A/zh
Publication of CN107604221A publication Critical patent/CN107604221A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高强度抗氧化铝合金材料及其制备方法，所述材料按以下重量百分比组成：0.5‑1的铜，1‑1.5的钛，3‑5的硅，2‑3的铁，1‑1.4的镁，0.02‑0.04的钒，0.5‑0.7的锌，0.3‑0.7的硼，其余为铝和不可避免的杂质。具体制备方法如下：步骤一、将纯铝锭放入锅炉内加热至熔化状态，加热温度为420‑440℃，加热时间为35‑45分钟；步骤二、进行脱杂质和脱氧处理；步骤三、依次放入铜，钛，硅，铁，镁，钒，锌，硼，加热温度为550‑600℃，保温1‑1.5小时；步骤四、再次加热至650‑680℃，保温2‑3小；步骤五、降温，然后在温度450‑500℃下进行两次热轧，待温度自然冷却至室温时再进行冷轧定型。本发明所得铝合金材料具有抗氧化性，耐腐蚀性的特点，可延长铝合金材料的使用寿命。

Description

一种高强度抗氧化铝合金材料及其制备方法
技术领域
本发明涉及一种高强度抗氧化铝合金材料及其制备方法，属于铝合金制备技术领域。
背景技术
铝合金是用途广泛的常用有色金属，具有很高的塑性、重量轻、易于加工等特点，广泛应用在工业生产中。但是，由于纯的铝很软，强度不大，在潮湿空气中易被氧化而变暗，失去金属的光泽，不仅影响使用寿命，而且还影响美观，因此需对铝合金的抗氧化处理进一步改进。
发明内容
本发明为解决上述问题，提供了一种高强度抗氧化铝合金材料及其制备方法。
本发明的目的是通过以下技术方案实现的：
一种高强度抗氧化铝合金材料及其制备方法，所述材料按以下重量百分比组成：0.5-1的铜，1-1.5的钛，3-5的硅，2-3的铁，1-1.4的镁，0.02-0.04的钒，0.5-0.7的锌，0.3-0.7的硼，其余为铝和不可避免的杂质。
具体制备方法如下：
步骤一、将纯铝锭放入锅炉内加热至熔化状态，加热温度为420-440℃，加热时间为35-45分钟；
步骤二、进行脱杂质和脱氧处理；
步骤三、依次放入铜，钛，硅，铁，镁，钒，锌，硼，加热温度为550-600℃，保温1-1.5小时；
步骤四、再次加热至650-680℃，保温2-3小；
步骤五、降温，然后在温度450-500℃下进行两次热轧，待温度自然冷却至室温时再进行冷轧定型。
本发明的有益效果是：本发明所得铝合金材料具有抗氧化性，耐腐蚀性的特点，可延长铝合金材料的使用寿命。
具体实施方式
实施例一
本发明所述的一种高强度抗氧化铝合金材料及其制备方法，所述材料按以下重量百分比组成：0.5的铜，1的钛，3的硅，2的铁，1的镁，0.02的钒，0.5的锌，0.3的硼，其余为铝和不可避免的杂质。
具体制备方法如下：
步骤一、将纯铝锭放入锅炉内加热至熔化状态，加热温度为420℃，加热时间为35分钟；
步骤二、进行脱杂质和脱氧处理；
步骤三、依次放入铜，钛，硅，铁，镁，钒，锌，硼，加热温度为550-600℃，保温1小时；
步骤四、再次加热至650℃，保温2小；
步骤五、降温，然后在温度450℃下进行两次热轧，待温度自然冷却至室温时再进行冷轧定型。
实施例2
本发明所述的一种高强度抗氧化铝合金材料及其制备方法，所述材料按以下重量百分比组成：1的铜，1.5的钛，5的硅，3的铁，1.4的镁，0.04的钒，0.7的锌，0.7的硼，其余为铝和不可避免的杂质。
具体制备方法如下：
步骤一、将纯铝锭放入锅炉内加热至熔化状态，加热温度为440℃，加热时间为45分钟；
步骤二、进行脱杂质和脱氧处理；
步骤三、依次放入铜，钛，硅，铁，镁，钒，锌，硼，加热温度为600℃，保温1.5小时；
步骤四、再次加热至680℃，保温3小；
步骤五、降温，然后在温度500℃下进行两次热轧，待温度自然冷却至室温时再进行冷轧定型。
实施例3
本发明所述的一种高强度抗氧化铝合金材料及其制备方法，所述材料按以下重量百分比组成：0.8的铜，1.2的钛，4的硅，2.5的铁，1.2的镁，0.03的钒，0.6的锌，0.5的硼，其余为铝和不可避免的杂质。
具体制备方法如下：
步骤一、将纯铝锭放入锅炉内加热至熔化状态，加热温度为430℃，加热时间为40分钟；
步骤二、进行脱杂质和脱氧处理；
步骤三、依次放入铜，钛，硅，铁，镁，钒，锌，硼，加热温度为575℃，保温1.3小时；
步骤四、再次加热至665℃，保温2.5小；
步骤五、降温，然后在温度475℃下进行两次热轧，待温度自然冷却至室温时再进行冷轧定型。

Claims (2)

1.一种高强度抗氧化铝合金材料及其制备方法，其特征在于，所述材料按以下重量百分比组成：0.5-1的铜，1-1.5的钛，3-5的硅，2-3的铁，1-1.4的镁，0.02-0.04的钒，0.5-0.7的锌，0.3-0.7的硼，其余为铝和不可避免的杂质。具体制备方法如下：步骤一、将纯铝锭放入锅炉内加热至熔化状态，加热温度为420-440℃，加热时间为35-45分钟；步骤二、进行脱杂质和脱氧处理；步骤三、依次放入铜，钛，硅，铁，镁，钒，锌，硼，加热温度为550-600℃，保温1-1.5小时；步骤四、再次加热至650-680℃，保温2-3小；步骤五、降温，然后在温度450-500℃下进行两次热轧，待温度自然冷却至室温时再进行冷轧定型。
2.根据权利要求1所述的一种高强度抗氧化铝合金材料及其制备方法，其特征在于，所述的镁、钒、锌分别以镁铝合金、钒铝合金、锌铝合金的方式加入。
CN201710999472.6A 2017-10-24 2017-10-24 一种高强度抗氧化铝合金材料及其制备方法 Pending CN107604221A (zh)