CN107604106B - Clean tanning method for Tan sheep fur - Google Patents
Clean tanning method for Tan sheep fur Download PDFInfo
- Publication number
- CN107604106B CN107604106B CN201710948032.8A CN201710948032A CN107604106B CN 107604106 B CN107604106 B CN 107604106B CN 201710948032 A CN201710948032 A CN 201710948032A CN 107604106 B CN107604106 B CN 107604106B
- Authority
- CN
- China
- Prior art keywords
- temperature
- stirring
- paddle vat
- discharging
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The application provides a clean tanning method of Tan sheep fur, which adopts a chrome tanning agent to tan the Tan sheep fur and chrome to tan Cr in the Tan sheep fur in comparison with the prior art of Tan sheep fur tanning technology2Is easily oxidized into Cr with carcinogenicity under the conditions of external light, heat, sweat and the like2And the formaldehyde content in the finished product Tan sheep fur seriously exceeds the standard; the application provides a clean tanning method of Tan sheep fur, which adopts an aldehyde-free and chromium-free tanning technology and a biological enzyme degreasing technology, carries out clean tanning on the Tan sheep fur through nine procedures, reduces water consumption by 50 percent, and reduces more than 70 percent of neutral salt, does not use harmful chemicals such as formaldehyde, chromium compounds and the like in the production process, and does not contain chemical components harmful to human bodies such as formaldehyde, hexavalent chromium, forbidden azo dyes and the like.
Description
Technical Field
The invention relates to the technical field of fur tanning, in particular to a clean tanning method for Tan sheep fur.
Background
Three types of tanning agents are mainly adopted for tanning Tan sheep fur. The first category is inorganic salt tanning agent, including chrome tanning agent, titanium tanning agent, silicate and the like; the second category is aldehyde tanning agent, including modified glutaraldehyde, oxazolidine, organic phosphorus, etc.; the third category is tannin extract tanning agent. Wherein, the chrome tanning agent is the most main tanning agent for producing the Tan sheep fur and can endow the Tan sheep fur with good damp-heat stability.
Although the chrome tanned Tan sheep fur has good shrinkage temperature and excellent physical properties, practice shows that Cr in the chrome tanned Tan sheep fur2Easily oxidized under the conditions of external light, heat, sweat and the like to generate Cr with carcinogenicity2And the finished product of Tan sheep hairThe leather has the problems of serious standard exceeding of formaldehyde content and the like.
In recent years, with the development of global economy, people pay more and more attention to the safety problem of Tan sheep fur products, so that a clean tanning method of Tan sheep fur is developed.
Disclosure of Invention
The application provides a clean tanning method of Tan sheep fur, which adopts an aldehyde-free and chromium-free tanning technology and a biological enzyme degreasing technology, reduces water consumption by 50 percent, has more than 70 percent of neutral salt, does not use harmful chemicals such as formaldehyde, chromium compounds and the like in the production process, and does not contain chemical components harmful to human bodies such as formaldehyde, hexavalent chromium, forbidden azo dyes and the like.
The invention provides the following technical scheme:
a clean tanning method of Tan sheep fur comprises the following steps:
s101: adding 250 kg of hot water with the temperature of 41-50 ℃ into a paddle vat, putting 8-10 kg of anhydrous sodium sulphate into the paddle vat, rotationally stirring for 10-20 minutes, putting the anhydrous sodium sulphate into the goat fur after dissolving, rotationally stirring for 10-20 minutes, soaking for 8-12 hours, diluting 2-3 kg of baking soda with 8-10 times of hot water with the temperature of 41-50 ℃ for 8-10 times of the weight, adding the baking soda into the paddle vat, rotationally stirring for 10-20 minutes, soaking for 3-5 hours, diluting 2-3 kg of baking soda with 8-10 times of hot water with the temperature of 41-50 ℃ for 3-3 minutes, adding the baking soda into the paddle vat, and continuously rotationally stirring for 10-20 minutes; adding sodium bicarbonate to adjust pH to 5.6-6.0, stopping the tank, and standing for 18-20 hours; discharging the skin, and discharging all liquid in the paddle vat;
s102: adding 250 kg of hot water with the temperature of 41-50 ℃ into the paddle vat again, dissolving 10 kg-12 kg of wetting agent with 5 kg-10 kg of hot water with the temperature of 41-50 ℃ and then adding the wetting agent into the paddle vat, rotating and stirring for 10 min-20 min, putting the Tan sheep fur obtained in the S101, rotating and stirring for 4 h-6 h, adding 6 kg-7 kg of lactic acid, continuing to rotate and stir for 6 h-8 h, adding the lactic acid to adjust the pH value to 3.8-4.2, stopping the paddle vat, and standing for 18 h-20 h; discharging all liquid in the paddle vat and discharging the skin;
s103: adding 250 kg of hot water with the temperature of 41-50 ℃ into the paddle vat again, adding 2 kg-2.5 kg of biological enzyme, rotationally stirring for 10-20 minutes, putting the Tan sheep fur obtained in the step S102, rotationally stirring for 41-50 minutes, stopping the paddle vat, and discharging all liquid in the paddle vat; adding 250 kg hot water at 41-50 deg.c, rotating and stirring for 10-30 min, stopping the tank, peeling and draining the liquid;
s104: adding 250 kg of hot water with the temperature of 41-50 ℃ into the scratch groove again, dissolving the fatting agent with the weight of 20-30 kg by using 5-10 kg of water with the temperature of 41-50 ℃ and then adding the dissolved fatting agent into the scratch groove, rotationally stirring for 20-25 min, ensuring that the temperature in the scratch groove reaches 41-50 ℃, putting the Tan sheep fur obtained in the step S103, rotationally stirring for 2-2.5 h, adding lactic acid to adjust the pH value to 4.0-4.4, discharging all liquid in the scratch groove, and discharging the skin;
s105: adding 250 kg of hot water with the temperature of 30-40 ℃ into the paddle vat again, adding 5 kg-8 kg of zirconium-aluminum composite tanning agent, rotationally stirring for 10-20 min, adding the Tan sheep fur obtained in the step S104, rotationally stirring for 3-3.5 h, adding 2.5 kg-5 kg of sodium nitrate, and continuously rotationally stirring for 20-30 min; dissolving sodium bicarbonate with a weight of 4 kg in water with a weight of 20 kg and a temperature of 30-40 ℃, adding the water into the paddle vat while continuously rotating and stirring for 25-35 minutes, adding the sodium bicarbonate to adjust the pH value to 5.0-6.0, continuously rotating and stirring for 1-2 hours, and discharging all liquid in the paddle vat; adding 300 kg of hot water at 30-40 ℃, rotating to wash for 15-25 minutes, peeling, and discharging all liquid in the paddle vat;
ZrO in the zirconium-aluminum composite tanning agent2With Al2O3The weight ratio of: ZrO (ZrO)2:Al2O3=100:25-100:100;
S106: adding 250 kg of warm water with the temperature of 10-20 ℃ into the paddle vat again, adding 1 kg-1.5 kg of hydrogen peroxide with the concentration of 35-40% into the paddle vat, and stirring for 10-20 minutes in a rotating manner; putting the Tan sheep fur obtained in the step S105, rotating and stirring for 30-40 minutes, and discharging all liquid in the paddle vat; adding 300 kg warm water at 10-20 deg.C, washing for 10-20 min, discharging all liquid in the groove, and peeling;
s107: adding 250 kg of hot water with the temperature of 55-60 ℃ into the paddle vat again, dissolving and adding the fatting agent with the weight of 20-25 kg into the paddle vat by using 10-20 kg of hot water with the temperature of 55-60 ℃, rotationally stirring for 15-20 minutes, ensuring that the temperature in the paddle vat reaches 55-60 ℃, putting the Tan sheep fur obtained in the S106, rotationally stirring for 1-2 hours, and adding lactic acid to adjust the pH to 4.0-5.0; discharging the skin, and discharging all liquid in the paddle vat;
s108: adding 250 kg of hot water with the temperature of 40-45 ℃ into the paddle vat again, dissolving the excellent yellow ether yeast powder polymer with the weight of 10 kg-15 kg by using 10 kg-20 kg of hot water with the temperature of 40-45 ℃, adding the dissolved excellent yellow ether yeast powder polymer into the paddle vat, rotationally stirring for 5-15 minutes, adding the Tan sheep fur obtained in the step S107, rotationally stirring for 3-5 hours, adding lactic acid to adjust the pH to 4.0-5.0; stopping the groove, standing for 18-20 hours, discharging all liquid in the groove, and peeling;
s109: shaking and throwing the sheepskin, placing the sheepskin on a plate frame for binding, moving the sheepskin on a flat land, and naturally drying the sheepskin at a daily temperature of 18-25 ℃;
after natural drying, the Tan sheep fur is disassembled from the plate frame and is placed in a shady and cool place with four ventilated sides for 18-20 hours.
Optionally, the S101: adding 250 kg of hot water with the temperature of 45 ℃ into a paddle vat, putting 8 kg of anhydrous sodium sulphate into the paddle vat, rotationally stirring for 15 minutes, putting the anhydrous sodium sulphate into Tan sheep fur after dissolving, rotationally stirring for 15 minutes, soaking for 8-12 hours, diluting baking soda with the weight of 2 kg with the hot water with the temperature of 45 ℃, adding the baking soda into the paddle vat, rotationally stirring for 15 minutes, soaking for 3-5 hours, diluting the baking soda with the weight of 8-10 times of the weight of 45 ℃ of hot water, adding the baking soda into the paddle vat, and continuously rotationally stirring for 15 minutes; adding sodium bicarbonate to adjust pH to 5.6-6.0, stopping the tank, and standing for 18-20 hours; discharging the skin and discharging all the liquid in the paddle vat.
Optionally, the S102: adding 250 kg of hot water with the temperature of 45 ℃ into the paddle vat again, dissolving 10 kg of wetting agent with 8 kg of hot water with the temperature of 45 ℃ and then adding the wetting agent into the paddle vat, rotationally stirring for 15 minutes, adding the Tan sheep fur obtained in the step S101, rotationally stirring for 4 to 6 hours, adding 6 kg to 7 kg of lactic acid, continuously rotationally stirring for 6 to 8 hours, adding the lactic acid to adjust the pH value to be 3.8 to 4.2, stopping the paddle vat, and standing for 18 to 20 hours; discharging all liquid in the paddle vat and discharging the skin.
Optionally, the step S103: adding 250 kg of hot water with the temperature of 45 ℃ into the paddle vat again, adding 2 kg of biological enzyme, rotationally stirring for 15 minutes, adding the Tan sheep fur obtained in the step S102, rotationally stirring for 45 minutes, stopping the paddle vat, and discharging all liquid in the paddle vat; adding 250 kg hot water at 45 deg.C, stirring for 10-30 min, stopping the tank, discharging peel, and discharging the liquid.
Alternatively, S104: adding 250 kg of hot water with the temperature of 45 ℃ into the paddle vat again, dissolving 25 kg of fatting agent with 10 kg of water with the temperature of 45 ℃, adding the dissolved fatting agent into the paddle vat, rotationally stirring for 20-25 min, ensuring that the temperature in the paddle vat reaches 41-50 ℃, adding the Tan sheep fur obtained in the step S103, rotationally stirring for 2-2.5 h, adding lactic acid to adjust the pH value to 4.0-4.4, discharging all liquid in the paddle vat, and discharging the skin.
Optionally, the S105: adding 250 kg of hot water with the temperature of 35 ℃ into the paddle vat again, adding 5 kg-8 kg of zirconium-aluminum composite tanning agent, rotationally stirring for 10 min-20 min, adding the Tan sheep fur obtained in the step S104, rotationally stirring for 3 h-3.5 h, adding 2.5 kg-5 kg of sodium nitrate, and continuously rotationally stirring for 20 min-30 min; dissolving 4 kg of sodium bicarbonate in 20 kg of water at the temperature of 35 ℃, adding the solution into a paddle vat while continuously rotating and stirring for 25-35 minutes, adding the sodium bicarbonate to adjust the pH value to 5.0-6.0, continuously rotating and stirring for 1-2 hours, and discharging all liquid in the paddle vat; adding 300 kg of hot water with the temperature of 40 ℃ again, rotating and washing for 15-25 minutes, peeling, and discharging all liquid in the paddle vat;
ZrO in the zirconium-aluminum composite tanning agent2With Al2O3The weight ratio of: ZrO (ZrO)2:Al2O3=100:25-100:100。
Optionally, ZrO in the zirconium-aluminum composite tanning agent2With Al2O3The weight ratio of: ZrO (ZrO)2:Al2O3=100:35-100:85。
Optionally, the S106: adding 250 kg of warm water with the temperature of 10-20 ℃ into the paddle vat again, adding 1 kg-1.5 kg of hydrogen peroxide with the concentration of 35% into the paddle vat, and stirring for 15 minutes in a rotating way; putting the Tan sheep fur obtained in the step S105, rotating and stirring for 30-40 minutes, and discharging all liquid in the paddle vat; adding 300 kg warm water with the temperature of 10-20 ℃, rotating and washing for 10-20 minutes, discharging all liquid in the paddle vat, and peeling.
Optionally, the step S109: shaking and throwing the sheepskin, placing the sheepskin on a plate frame for binding, moving the sheepskin on a flat land, and naturally drying the sheepskin at a daily temperature of 20 ℃;
after natural drying, the Tan sheep fur is disassembled from the plate frame and is placed in a shady and cool place with four ventilated sides for 20 hours.
According to the technical scheme, the application provides the clean tanning method of the Tan sheep fur, compared with the prior art that the Tan sheep fur is tanned by adopting a chromium tanning agent in the Tan sheep fur tanning technology, Cr in the Tan sheep fur is tanned by chromium2Is easily oxidized into Cr with carcinogenicity under the conditions of external light, heat, sweat and the like2And the formaldehyde content in the finished product Tan sheep fur seriously exceeds the standard; the application provides a clean tanning method of Tan sheep fur, which adopts an aldehyde-free and chromium-free tanning technology and a biological enzyme degreasing technology, reduces water consumption by 50 percent, and has more than 70 percent of neutral saltHarmful chemicals such as formaldehyde, chromium compounds and the like are not used in the production process, and the product does not contain chemical components harmful to human bodies such as formaldehyde, hexavalent chromium, forbidden azo dyes and the like.
Drawings
In order to more clearly explain the technical solution of the present application, the drawings needed to be used in the embodiments will be briefly described below, and it is obvious to those skilled in the art that other drawings can be obtained according to the drawings without any creative effort.
FIG. 1 is a process flow chart of a clean tanning method for Tan sheep fur.
Detailed Description
The present invention is illustrated below by way of examples, which should be understood as being illustrative of the present invention and not limiting thereof. The scope and core content of the invention are to be determined by the claims.
The scoring groove is an important device for wet processing of leathers and furs. The method is mainly used for the procedures of soaking, degreasing, liming, deliming, enzymatic softening, tanning and the like. The processing machine is divided into a wooden groove, a glass fiber reinforced plastic groove and a cement groove according to manufacturing materials, is semicircular, is provided with a wooden stirring paddle and is driven by a motor to rotate forwards and backwards, and is used for stirring operation liquid, stirring skin and accelerating the processing process. A steam pipe and a water pipe are additionally arranged, so that heating and water injection are facilitated. The movable cover is arranged on the upper surface of the cup body, so that liquid can be prevented from splashing or cooling; and a liquid outlet is arranged below the groove for discharging the operation waste liquid.
The biological enzyme treatment process is recognized as a green production process meeting the requirement of environmental protection, improves the wearability of textiles, and is also beneficial to the protection of ecological environmental protection because of no toxicity, no harm, small dosage, biodegradable wastewater and no pollution. Meanwhile, the biological enzyme is also applied to the field of treating indoor decoration pollution, and can eliminate the pollution of peculiar smell, formaldehyde and the like generated by indoor decoration through phagocytosis and decomposition.
The Tan sheep fur contains fibrin and non-fibrous protein which are present in fiber gaps and epidermis, although the content of the protein is low, if the protein is not removed, the Tan sheep fur is stiff and crisp. Therefore, the Tan sheep fur can be treated by using the biological enzyme.
The preparation method of the excellent yellow ether yeast powder polymer comprises the following steps: processing the millet produced in the current year, peeling, washing rice grains with normal-temperature clear water, and processing the rice grains according to the following steps: the weight ratio of water to 1:0.9-1.1, firstly putting a part of the obtained rice grains into a ceramic container, adding a part of clear water heated to 30-40 ℃, fully stirring to soak the rice grains in water, then sealing, fermenting for 108-hour at the normal temperature of 25-30 ℃, then pouring out the fully fermented rice grains, drying in the shade at the normal temperature, and grinding into powder.
The application provides a clean tanning method for Tan sheep fur, the specific process flow is shown in figure 1, an aldehyde-free and chromium-free tanning technology and a biological enzyme degreasing technology are adopted, the water consumption is reduced by 50%, the neutral salt is reduced by more than 70%, harmful chemicals such as formaldehyde, chromium compounds and the like are not used in the production process, and the product does not contain chemical components harmful to human bodies such as formaldehyde, hexavalent chromium, forbidden azo dyes and the like.
The first embodiment is as follows:
a clean tanning method of Tan sheep fur comprises the following steps:
s101: adding 250 kg of hot water with the temperature of 48 ℃ into a paddle vat, putting 9 kg of anhydrous sodium sulphate into the paddle vat, rotationally stirring for 20 minutes, putting the dissolved anhydrous sodium sulphate into the sheep fur, rotationally stirring for 20 minutes, soaking for 12 hours, diluting 3 kg of baking soda with 10 times of hot water with the temperature of 48 ℃, adding the diluted baking soda into the paddle vat, rotationally stirring for 18 minutes, soaking for 3 hours, diluting 2.8 kg of baking soda with 10 times of hot water with the temperature of 48 ℃, adding the diluted baking soda into the paddle vat, and continuously rotationally stirring for 18 minutes; adding sodium bicarbonate to adjust the pH value to 5.9, stopping the tank, and standing for 19 hours; discharging the skin, and discharging all liquid in the paddle vat;
s102: adding 250 kg of hot water with the temperature of 48 ℃ into the paddle vat again, dissolving 12 kg of wetting agent by 10 kg of hot water with the temperature of 48 ℃, adding the wetting agent into the paddle vat, rotationally stirring for 20 minutes, adding the Tan sheep fur obtained in the step S101, rotationally stirring for 6 hours, adding 6.8 kg of lactic acid, continuously rotationally stirring for 7 hours, adding the lactic acid to adjust the pH value to 3.8, stopping the paddle vat, and standing for 18 hours; discharging all liquid in the paddle vat and discharging the skin;
s103: adding 250 kg of hot water with the temperature of 45 ℃ into the paddle vat again, adding 2 kg of biological enzyme, rotationally stirring for 20 minutes, adding the Tan sheep fur obtained in the step S102, rotationally stirring for 45 minutes, stopping the paddle vat, and discharging all liquid in the paddle vat; adding 250 kg hot water at 45 deg.C, stirring for 30 min, stopping the tank, discharging peel, and discharging all liquid in the tank;
s104: adding 250 kg of hot water with the temperature of 43 ℃ into the paddle vat again, dissolving 25 kg of fatting agent with 5 kg of water with the temperature of 43 ℃ into the paddle vat, rotating and stirring for 20 minutes to ensure that the temperature in the paddle vat reaches 43 ℃, putting the sheep fur obtained in the step S103 into the paddle vat, rotating and stirring for 2.5 hours, adding lactic acid to adjust the pH value to 4.0, discharging all liquid in the paddle vat, and discharging the skin;
s105: adding 250 kg of hot water with the temperature of 30 ℃ into the paddle tank again, adding 6 kg of zirconium-aluminum composite tanning agent, rotationally stirring for 20 minutes, adding the Tan sheep fur obtained in the step S104, rotationally stirring for 3.5 hours, adding 5 kg of sodium nitrate, and continuously rotationally stirring for 30 minutes; dissolving sodium bicarbonate 4 kg in water 20 kg at 30 deg.C, adding into the paddle during stirring for 25 min, adding sodium bicarbonate to adjust pH to 5.0, stirring for 1 hr, and discharging the liquid; adding 300 kg of hot water at 30 ℃, rotating to wash for 25 minutes, peeling, and discharging all liquid in the paddle vat;
ZrO in the zirconium-aluminum composite tanning agent2With Al2O3The weight ratio of: ZrO (ZrO)2:Al2O3=100:75;
S106: adding 250 kg of warm water with the temperature of 20 ℃ into the paddle vat again, adding 1 kg of hydrogen peroxide with the concentration of 40% into the paddle vat, and stirring for 10 minutes in a rotating way; putting the Tan sheep fur obtained in the step S105, rotating and stirring for 30 minutes, and discharging all liquid in the paddle vat; adding 300 kg warm water at 10 deg.C, washing for 15 min, discharging all liquid in the groove, and peeling;
s107: adding 250 kg of hot water with the temperature of 55 ℃ into the paddle vat again, dissolving 23 kg of fatting agent into the paddle vat by using 10 kg of hot water with the temperature of 55 ℃, stirring for 15 minutes in a rotating manner, then putting the Tan sheep fur obtained in the step S106 into the paddle vat when the temperature in the paddle vat reaches 55 ℃, stirring for 1 hour in a rotating manner, and adding lactic acid to adjust the pH value to 4.0; discharging the skin, and discharging all liquid in the paddle vat;
s108: adding 250 kg of hot water with the temperature of 45 ℃ into the paddle vat again, dissolving 10 kg of excellent yellow ether yeast powder polymer with 10 kg of hot water with the temperature of 45 ℃, adding the dissolved excellent yellow ether yeast powder polymer into the paddle vat, rotationally stirring the dissolved excellent yellow ether yeast powder polymer for 15 minutes, adding the Tan sheep fur obtained in the step S107, rotationally stirring the obtained excellent yellow ether yeast powder polymer for 5 hours, adding lactic acid, and adjusting the pH value to 4.5; stopping the groove, standing for 18 hours, discharging all liquid in the groove, and peeling;
s109: shaking and throwing the sheepskin, placing the sheepskin on a plate frame for binding, moving the sheepskin on a flat land, and naturally drying the sheepskin at a daily temperature of 18 ℃;
after natural drying, the Tan sheep fur is disassembled from the plate frame and is placed in a shady and cool place with four ventilated sides for 18 hours.
Example two:
a clean tanning method of Tan sheep fur comprises the following steps:
s101: adding 250 kg of hot water with the temperature of 45 ℃ into a paddle vat, putting 9 kg of anhydrous sodium sulphate into the paddle vat, rotationally stirring for 15 minutes, putting the dissolved anhydrous sodium sulphate into the sheep fur, rotationally stirring for 15 minutes, soaking for 80 hours, diluting 2.5 kg of baking soda with 9 times of hot water with the temperature of 45 ℃ and then adding into the paddle vat, rotationally stirring for 15 minutes, soaking for 4 hours, diluting 2.5 kg of baking soda with 9 times of hot water with the temperature of 45 ℃ and then adding into the paddle vat, and continuing to rotationally stir for 15 minutes; adding sodium bicarbonate to adjust the pH value to 5.8, stopping the tank, and standing for 20 hours; discharging the skin, and discharging all liquid in the paddle vat;
s102: adding 250 kg of hot water with the temperature of 45 ℃ into the paddle vat again, dissolving 11 kg of wetting agent with 10 kg of hot water with the temperature of 45 ℃ and then adding the wetting agent into the paddle vat, rotationally stirring for 15 minutes, adding the Tan sheep fur obtained in the step S101, rotationally stirring for 4 hours, adding 7 kg of lactic acid, continuously rotationally stirring for 6 hours, adding the lactic acid to adjust the pH value to 4, stopping the paddle vat, and standing for 19 hours; discharging all liquid in the paddle vat and discharging the skin;
s103: adding 250 kg of hot water with the temperature of 40 ℃ into the paddle vat again, adding 2 kg of biological enzyme, rotationally stirring for 20 minutes, adding the Tan sheep fur obtained in the step S102, rotationally stirring for 40 minutes, stopping the paddle vat, and discharging all liquid in the paddle vat; adding 250 kg hot water at 40 deg.C, stirring for 30 min, stopping the tank, discharging peel, and discharging all liquid in the tank;
s104: adding 250 kg of hot water with the temperature of 50 ℃ into the paddle vat again, dissolving 30 kg of fatting agent with 5 kg of water with the temperature of 50 ℃ into the paddle vat, rotating and stirring for 25 minutes, ensuring that the temperature in the paddle vat reaches 50 ℃, putting the Tan sheep fur obtained in the step S103, rotating and stirring for 2.5 hours, adding lactic acid to adjust the pH value to 4.4, discharging all liquid in the paddle vat, and discharging the skin;
s105: adding 250 kg of hot water with the temperature of 30 ℃ into the paddle vat again, adding 5 kg of zirconium-aluminum composite tanning agent, rotationally stirring for 15 minutes, adding the Tan sheep fur obtained in the step S104, rotationally stirring for 3.5 hours, adding 5 kg of sodium nitrate, and continuously rotationally stirring for 20 minutes; dissolving sodium bicarbonate 4 kg in water 20 kg at 30 deg.C, adding into the paddle during stirring for 25 min, adding sodium bicarbonate to adjust pH to 5.0, stirring for 1 hr, and discharging the liquid; adding 300 kg of hot water at 30 ℃, rotating to wash for 25 minutes, peeling, and discharging all liquid in the paddle vat;
the above-mentionedZrO in zirconium-aluminum composite tanning agent2With Al2O3The weight ratio of: ZrO (ZrO)2:Al2O3=100:25;
S106: adding 250 kg of warm water with the temperature of 20 ℃ into the paddle vat again, adding 1 kg of hydrogen peroxide with the concentration of 35% into the paddle vat, and stirring for 20 minutes in a rotating manner; putting the beach sheep fur obtained in the step S105, rotating and stirring for 38 minutes, and discharging all liquid in the paddle vat; adding 300 kg warm water at 20 deg.C, washing for 20 min, discharging all liquid in the groove, and peeling;
s107: adding 250 kg of hot water with the temperature of 55 ℃ into the paddle vat again, dissolving the fatting agent with the weight of 20 kg into the paddle vat by using 10 kg of hot water with the temperature of 55 ℃, stirring for 15 minutes in a rotating way, putting the Tan sheep fur obtained in the step S106 into the paddle vat when the temperature in the paddle vat reaches 55 ℃, stirring for 1 hour in a rotating way, and adding lactic acid to adjust the pH value to 4.0; discharging the skin, and discharging all liquid in the paddle vat;
s108: adding 250 kg of hot water with the temperature of 40 ℃ into the paddle vat again, dissolving 12 kg of excellent yellow ether yeast powder polymer by using 10 kg of hot water with the temperature of 40 ℃, adding the dissolved excellent yellow ether yeast powder polymer into the paddle vat, rotationally stirring the dissolved excellent yellow ether yeast powder polymer for 15 minutes, adding the Tan sheep fur obtained in the step S107, rotationally stirring the obtained excellent yellow ether yeast powder polymer for 5 hours, adding lactic acid, and adjusting the pH value to 4.5; stopping the groove, standing for 18 hours, discharging all liquid in the groove, and peeling;
s109: shaking and throwing the sheepskin, placing the sheepskin on a plate frame for binding, moving the sheepskin on a flat land, and naturally drying the sheepskin at a daily temperature of 25 ℃;
after natural drying, the Tan sheep fur is disassembled from the plate frame and is placed in a shady and cool place with four ventilated sides for 20 hours.
Example three:
a clean tanning method of Tan sheep fur comprises the following steps:
s101: adding 250 kg of hot water with the temperature of 41 ℃ into a paddle vat, putting 8 kg-10 kg of anhydrous sodium sulphate into the paddle vat, rotationally stirring for 10 minutes, putting the anhydrous sodium sulphate into Tan sheep fur after dissolving, rotationally stirring for 10 minutes, soaking for 8 hours, diluting 2 kg of baking soda with 8 times of hot water with the temperature of 41 ℃ and then adding into the paddle vat, rotationally stirring for 10 minutes, soaking for 3 hours, diluting 2 kg of baking soda with 8 times of hot water with the temperature of 41 ℃ to 50 ℃, adding into the paddle vat, and continuously rotationally stirring for 10 minutes to 20 minutes; adding sodium bicarbonate to adjust pH to 5.6-6.0, stopping the tank, and standing for 18-20 hours; discharging the skin, and discharging all liquid in the paddle vat;
s102: adding 250 kg of hot water with the temperature of 41 ℃ into the paddle vat again, dissolving 10 kg of wetting agent with 5 kg of hot water with the temperature of 41 ℃ and then adding the wetting agent into the paddle vat, rotationally stirring for 10 minutes, adding the Tan sheep fur obtained in the step S101, rotationally stirring for 4 hours, adding 6 kg of lactic acid, continuously rotationally stirring for 6 hours, adding the lactic acid to adjust the pH value to 3.8, stopping the paddle vat, and standing for 18 hours; discharging all liquid in the paddle vat and discharging the skin;
s103: adding 250 kg of hot water with the temperature of 41 ℃ into the paddle vat again, adding 2 kg of biological enzyme, rotationally stirring for 10 minutes, adding the Tan sheep fur obtained in the step S102, rotationally stirring for 41 minutes, stopping the paddle vat, and discharging all liquid in the paddle vat; adding 250 kg hot water at 41 deg.C, stirring for 10 min, stopping the tank, discharging peel, and discharging all liquid in the tank;
s104: adding 250 kg of hot water with the temperature of 41 ℃ into the paddle vat again, dissolving the fatting agent with the weight of 20 kg by using 5 kg of water with the temperature of 41 ℃ and then adding the dissolved fatting agent into the paddle vat, rotating and stirring for 20 minutes, ensuring that the temperature in the paddle vat reaches 41 ℃, putting the Tan sheep fur obtained in the step S103, rotating and stirring for 2 hours, adding lactic acid to adjust the pH value to 4.0, discharging all liquid in the paddle vat, and discharging the skin;
s105: adding 250 kg of hot water with the temperature of 30 ℃ into the paddle vat again, adding 5 kg of zirconium-aluminum composite tanning agent, rotationally stirring for 10 minutes, adding the Tan sheep fur obtained in the step S104, rotationally stirring for 3 hours, adding 2.5 kg of sodium nitrate, and continuously rotationally stirring for 20 minutes; dissolving sodium bicarbonate 4 kg in water 20 kg at 30 deg.C, adding into the paddle during stirring for 25 min, adding sodium bicarbonate to adjust pH to 5.0, stirring for 1 hr, and discharging the liquid; adding 300 kg of hot water at 30 ℃, rotating and washing for 15 minutes, peeling, and discharging all liquid in the paddle vat;
ZrO in the zirconium-aluminum composite tanning agent2With Al2O3The weight ratio of: ZrO (ZrO)2:Al2O3=100:100;
S106: adding 250 kg of warm water with the temperature of 10 ℃ into the paddle vat again, adding 1 kg of hydrogen peroxide with the concentration of 35% into the paddle vat, and stirring for 10 minutes in a rotating manner; putting the Tan sheep fur obtained in the step S105, rotating and stirring for 30 minutes, and discharging all liquid in the paddle vat; adding 300 kg warm water at 10 deg.C, washing for 10 min, discharging all liquid in the groove, and peeling;
s107: adding 250 kg of hot water with the temperature of 55 ℃ into the paddle vat again, dissolving the fatting agent with the weight of 20 kg into the paddle vat by using 10 kg of hot water with the temperature of 55 ℃, stirring for 15 minutes in a rotating way, ensuring that the temperature in the paddle vat reaches 55 ℃, putting the beach sheep fur obtained in the step S106 into the paddle vat, stirring for 1 hour in a rotating way, and adding lactic acid to adjust the pH value to 4.0; discharging the skin, and discharging all liquid in the paddle vat;
s108: adding 250 kg of hot water with the temperature of 40 ℃ into the paddle vat again, dissolving 10 kg of excellent yellow ether yeast powder polymer with 10 kg of hot water with the temperature of 40 ℃, adding the dissolved excellent yellow ether yeast powder polymer into the paddle vat, rotationally stirring the dissolved excellent yellow ether yeast powder polymer for 5 minutes, adding the Tan sheep fur obtained in the step S107, rotationally stirring the obtained excellent yellow ether yeast powder polymer for 3 hours, adding lactic acid, and adjusting the pH value to 4.0; stopping the groove, standing for 18 hours, discharging all liquid in the groove, and peeling;
s109: shaking and throwing the sheepskin, placing the sheepskin on a plate frame for binding, moving the sheepskin on a flat land, and naturally drying the sheepskin at a daily temperature of 18 ℃;
after natural drying, the Tan sheep fur is disassembled from the plate frame and is placed in a shady and cool place with four ventilated sides for 20 hours.
Example four:
a clean tanning method of Tan sheep fur comprises the following steps:
s101: adding 250 kg of hot water with the temperature of 50 ℃ into a paddle vat, putting 10 kg of anhydrous sodium sulphate into the paddle vat, rotationally stirring for 20 minutes, putting the dissolved anhydrous sodium sulphate into the sheep fur, rotationally stirring for 20 minutes, soaking for 12 hours, diluting 3 kg of baking soda with 10 times of hot water with the temperature of 50 ℃, adding the diluted baking soda into the paddle vat, rotationally stirring for 20 minutes, soaking for 5 hours, diluting 3 kg of baking soda with 10 times of hot water with the temperature of 50 ℃, adding the diluted baking soda into the paddle vat, and continuously rotationally stirring for 20 minutes; adding sodium bicarbonate to adjust the pH value to 6.0, stopping the tank, and standing for 20 hours; discharging the skin, and discharging all liquid in the paddle vat;
s102: adding 250 kg of hot water with the temperature of 50 ℃ into the paddle vat again, dissolving 12 kg of wetting agent with 10 kg of hot water with the temperature of 50 ℃ and then adding the wetting agent into the paddle vat, rotationally stirring for 20 minutes, adding the Tan sheep fur obtained in the step S101, rotationally stirring for 6 hours, adding 7 kg of lactic acid, continuously rotationally stirring for 8 hours, adding the lactic acid to adjust the pH value to 4.2, stopping the paddle vat, and standing for 20 hours; discharging all liquid in the paddle vat and discharging the skin;
s103: adding 250 kg of hot water with the temperature of 50 ℃ into the paddle vat again, adding 2.5 kg of biological enzyme, rotationally stirring for 20 minutes, adding the Tan sheep fur obtained in the step S102, rotationally stirring for 50 minutes, stopping the paddle vat, and discharging all liquid in the paddle vat; adding 250 kg hot water at 50 deg.C, stirring for 100 min, stopping the tank, discharging peel, and discharging all liquid in the tank;
s104: adding 250 kg of hot water with the temperature of 50 ℃ into the paddle vat again, dissolving 30 kg of fatting agent with 10 kg of water with the temperature of 50 ℃ into the paddle vat, rotating and stirring for 25 minutes, ensuring that the temperature in the paddle vat reaches 50 ℃, putting the Tan sheep fur obtained in the step S103, rotating and stirring for 2.5 hours, adding lactic acid to adjust the pH value to 4.4, discharging all liquid in the paddle vat, and discharging the skin;
s105: adding 250 kg of hot water with the temperature of 40 ℃ into the paddle vat again, adding 8 kg of zirconium-aluminum composite tanning agent, rotationally stirring for 20 minutes, adding the Tan sheep fur obtained in the step S104, rotationally stirring for 3.5 hours, adding 5 kg of sodium nitrate, and continuously rotationally stirring for 30 minutes; dissolving sodium bicarbonate 4 kg in water 20 kg at 40 deg.C, adding into the paddle vat while stirring for 35 min, adding sodium bicarbonate to adjust pH to 6.0, stirring for 2 hr, and discharging the liquid; adding 300 kg hot water at 40 deg.C, rotating to wash for 25 min, peeling, and discharging all liquid in the groove;
ZrO in the zirconium-aluminum composite tanning agent2With Al2O3The weight ratio of: ZrO (ZrO)2:Al2O3=100:85;
S106: adding 250 kg of warm water with the temperature of 20 ℃ into the paddle vat again, adding 1 kg of hydrogen peroxide with the concentration of 38% into the paddle vat, and stirring for 20 minutes in a rotating manner; putting the beach sheep fur obtained in the step S105, rotating and stirring for 40 minutes, and discharging all liquid in the paddle vat; adding 300 kg warm water at 20 deg.C, washing for 20 min, discharging all liquid in the groove, and peeling;
s107: adding 250 kg of hot water with the temperature of 55 ℃ into the paddle vat again, dissolving the fatting agent with the weight of 20 kg into the paddle vat by using 10 kg of hot water with the temperature of 60 ℃, stirring for 15 minutes in a rotating way, ensuring that the temperature in the paddle vat reaches 55 ℃, putting the beach sheep fur obtained in the step S106 into the paddle vat, stirring for 1 hour in a rotating way, and adding lactic acid to adjust the pH value to 4.0; discharging the skin, and discharging all liquid in the paddle vat;
s108: adding 250 kg of hot water with the temperature of 40 ℃ into the paddle vat again, dissolving 10 kg of excellent yellow ether yeast powder polymer by using 10 kg of hot water with the temperature of 40 ℃, adding the solution into the paddle vat, rotationally stirring the solution for 5 minutes, adding the Tan sheep fur obtained in the step S107, rotationally stirring the solution for 3 hours, adding lactic acid, and adjusting the pH value to 4.0-5.0; stopping the groove, standing for 18 hours, discharging all liquid in the groove, and peeling;
s109: shaking and throwing the sheepskin, placing the sheepskin on a plate frame for binding, moving the sheepskin on a flat land, and naturally drying the sheepskin at a daily temperature of 18 ℃;
after natural drying, the Tan sheep fur is disassembled from the plate frame and is placed in a shady and cool place with four ventilated sides for 18 hours.
According to the technical scheme, the application provides the clean tanning method of the Tan sheep fur, compared with the prior art that the Tan sheep fur is tanned by adopting a chromium tanning agent in the Tan sheep fur tanning technology, Cr in the Tan sheep fur is tanned by chromium2Is easily oxidized into Cr with carcinogenicity under the conditions of external light, heat, sweat and the like2And the formaldehyde content in the finished product Tan sheep fur seriously exceeds the standard; the application provides a clean tanning method of Tan sheep fur, which adopts an aldehyde-free and chromium-free tanning technology and a biological enzyme degreasing technology, reduces water consumption by 50 percent, has more than 70 percent of neutral salt, does not use harmful chemicals such as formaldehyde, chromium compounds and the like in the production process, and does not contain chemical components harmful to human bodies such as formaldehyde, hexavalent chromium, forbidden azo dyes and the like.
It will be understood that the invention is not limited to the precise arrangements described above and that various modifications and changes may be made without departing from the scope thereof. The scope of the invention is limited only by the appended claims.
And various modifications and changes may be made in the scope thereof. The scope of the invention is limited only by the appended claims.
Claims (9)
1. A clean tanning method of Tan sheep fur is characterized by comprising the following steps:
s101: adding 250 kg of hot water with the temperature of 41-50 ℃ into a paddle vat, putting 8-10 kg of anhydrous sodium sulphate into the paddle vat, rotationally stirring for 10-20 minutes, putting the anhydrous sodium sulphate into the goat fur after dissolving, rotationally stirring for 10-20 minutes, soaking for 8-12 hours, diluting 2-3 kg of baking soda with 8-10 times of hot water with the temperature of 41-50 ℃ for 8-10 times of the weight, adding the baking soda into the paddle vat, rotationally stirring for 10-20 minutes, soaking for 3-5 hours, diluting 2-3 kg of baking soda with 8-10 times of hot water with the temperature of 41-50 ℃ for 3-3 minutes, adding the baking soda into the paddle vat, and continuously rotationally stirring for 10-20 minutes; adding sodium bicarbonate to adjust pH to 5.6-6.0, stopping the tank, and standing for 18-20 hours; discharging the skin, and discharging all liquid in the paddle vat;
s102: adding 250 kg of hot water with the temperature of 41-50 ℃ into the paddle vat again, dissolving 10 kg-12 kg of wetting agent with 5 kg-10 kg of hot water with the temperature of 41-50 ℃ and then adding the wetting agent into the paddle vat, rotating and stirring for 10 min-20 min, putting the Tan sheep fur obtained in the S101, rotating and stirring for 4 h-6 h, adding 6 kg-7 kg of lactic acid, continuing to rotate and stir for 6 h-8 h, adding the lactic acid to adjust the pH value to 3.8-4.2, stopping the paddle vat, and standing for 18 h-20 h; discharging all liquid in the paddle vat and discharging the skin;
s103: adding 250 kg of hot water with the temperature of 41-50 ℃ into the paddle vat again, adding 2 kg-2.5 kg of biological enzyme, rotationally stirring for 10-20 minutes, putting the Tan sheep fur obtained in the step S102, rotationally stirring for 41-50 minutes, stopping the paddle vat, and discharging all liquid in the paddle vat; adding 250 kg hot water at 41-50 deg.c, rotating and stirring for 10-30 min, stopping the tank, peeling and draining the liquid;
s104: adding 250 kg of hot water with the temperature of 41-50 ℃ into the scratch groove again, dissolving the fatting agent with the weight of 20-30 kg by using 5-10 kg of water with the temperature of 41-50 ℃ and then adding the dissolved fatting agent into the scratch groove, rotationally stirring for 20-25 min, ensuring that the temperature in the scratch groove reaches 41-50 ℃, putting the Tan sheep fur obtained in the step S103, rotationally stirring for 2-2.5 h, adding lactic acid to adjust the pH value to 4.0-4.4, discharging all liquid in the scratch groove, and discharging the skin;
s105: adding 250 kg of hot water with the temperature of 30-40 ℃ into the paddle vat again, adding 5 kg-8 kg of zirconium-aluminum composite tanning agent, rotationally stirring for 10-20 min, adding the Tan sheep fur obtained in the step S104, rotationally stirring for 3-3.5 h, adding 2.5 kg-5 kg of sodium nitrate, and continuously rotationally stirring for 20-30 min; dissolving sodium bicarbonate with a weight of 4 kg in water with a weight of 20 kg and a temperature of 30-40 ℃, adding the water into the paddle vat while continuously rotating and stirring for 25-35 minutes, adding the sodium bicarbonate to adjust the pH value to 5.0-6.0, continuously rotating and stirring for 1-2 hours, and discharging all liquid in the paddle vat; adding 300 kg of hot water at 30-40 ℃, rotating to wash for 15-25 minutes, peeling, and discharging all liquid in the paddle vat;
ZrO in the zirconium-aluminum composite tanning agent2With Al2O3The weight ratio of: ZrO (ZrO)2:Al2O3=100:25-100:100;
S106: adding 250 kg of warm water with the temperature of 10-20 ℃ into the paddle vat again, adding 1 kg-1.5 kg of hydrogen peroxide with the concentration of 35-40% into the paddle vat, and stirring for 10-20 minutes in a rotating manner; putting the Tan sheep fur obtained in the step S105, rotating and stirring for 30-40 minutes, and discharging all liquid in the paddle vat; adding 300 kg warm water at 10-20 deg.C, washing for 10-20 min, discharging all liquid in the groove, and peeling;
s107: adding 250 kg of hot water with the temperature of 55-60 ℃ into the paddle vat again, dissolving and adding the fatting agent with the weight of 20-25 kg into the paddle vat by using 10-20 kg of hot water with the temperature of 55-60 ℃, rotationally stirring for 15-20 minutes, ensuring that the temperature in the paddle vat reaches 55-60 ℃, putting the Tan sheep fur obtained in the S106, rotationally stirring for 1-2 hours, and adding lactic acid to adjust the pH to 4.0-5.0; discharging the skin, and discharging all liquid in the paddle vat;
s108: adding 250 kg of hot water with the temperature of 40-45 ℃ into the paddle vat again, dissolving the excellent yellow ether yeast powder polymer with the weight of 10 kg-15 kg by using 10 kg-20 kg of hot water with the temperature of 40-45 ℃, adding the dissolved excellent yellow ether yeast powder polymer into the paddle vat, rotationally stirring for 5-15 minutes, adding the Tan sheep fur obtained in the step S107, rotationally stirring for 3-5 hours, adding lactic acid to adjust the pH to 4.0-5.0; stopping the groove, standing for 18-20 hours, discharging all liquid in the groove, and peeling;
s109: shaking and throwing the sheepskin, placing the sheepskin on a plate frame for binding, moving the sheepskin on a flat land, and naturally drying the sheepskin at a daily temperature of 18-25 ℃;
after natural drying, the Tan sheep fur is disassembled from the plate frame and is placed in a shady and cool place with four ventilated sides for 18-20 hours.
2. The clean tanning method of beach sheep fur according to claim 1, characterized in that: the step S101: adding 250 kg of hot water with the temperature of 45 ℃ into a paddle vat, putting 8 kg of anhydrous sodium sulphate into the paddle vat, rotationally stirring for 15 minutes, putting the anhydrous sodium sulphate into Tan sheep fur after dissolving, rotationally stirring for 15 minutes, soaking for 8-12 hours, diluting baking soda with the weight of 2 kg with the hot water with the temperature of 45 ℃, adding the baking soda into the paddle vat, rotationally stirring for 15 minutes, soaking for 3-5 hours, diluting the baking soda with the weight of 8-10 times of the weight of 45 ℃ of hot water, adding the baking soda into the paddle vat, and continuously rotationally stirring for 15 minutes; adding sodium bicarbonate to adjust pH to 5.6-6.0, stopping the tank, and standing for 18-20 hours; discharging the skin and discharging all the liquid in the paddle vat.
3. The clean tanning method of beach sheep fur according to claim 1, characterized in that: the step S102: adding 250 kg of hot water with the temperature of 45 ℃ into the paddle vat again, dissolving 10 kg of wetting agent with 8 kg of hot water with the temperature of 45 ℃ and then adding the wetting agent into the paddle vat, rotationally stirring for 15 minutes, adding the Tan sheep fur obtained in the step S101, rotationally stirring for 4 to 6 hours, adding 6 kg to 7 kg of lactic acid, continuously rotationally stirring for 6 to 8 hours, adding the lactic acid to adjust the pH value to be 3.8 to 4.2, stopping the paddle vat, and standing for 18 to 20 hours; discharging all liquid in the paddle vat and discharging the skin.
4. The clean tanning method of beach sheep fur according to claim 1, characterized in that: the step S103: adding 250 kg of hot water with the temperature of 45 ℃ into the paddle vat again, adding 2 kg of biological enzyme, rotationally stirring for 15 minutes, adding the Tan sheep fur obtained in the step S102, rotationally stirring for 45 minutes, stopping the paddle vat, and discharging all liquid in the paddle vat; adding 250 kg hot water at 45 deg.C, stirring for 10-30 min, stopping the tank, discharging peel, and discharging the liquid.
5. The clean tanning method of beach sheep fur according to claim 1, characterized in that: s104: adding 250 kg of hot water with the temperature of 45 ℃ into the paddle vat again, dissolving 25 kg of fatting agent with 10 kg of water with the temperature of 45 ℃, adding the dissolved fatting agent into the paddle vat, rotationally stirring for 20-25 min, ensuring that the temperature in the paddle vat reaches 41-50 ℃, adding the Tan sheep fur obtained in the step S103, rotationally stirring for 2-2.5 h, adding lactic acid to adjust the pH value to 4.0-4.4, discharging all liquid in the paddle vat, and discharging the skin.
6. The clean tanning method of beach sheep fur according to claim 1, characterized in that: the step S105: adding 250 kg of hot water with the temperature of 35 ℃ into the paddle vat again, adding 5 kg-8 kg of zirconium-aluminum composite tanning agent, rotationally stirring for 10 min-20 min, adding the Tan sheep fur obtained in the step S104, rotationally stirring for 3 h-3.5 h, adding 2.5 kg-5 kg of sodium nitrate, and continuously rotationally stirring for 20 min-30 min; dissolving 4 kg of sodium bicarbonate in 20 kg of water at the temperature of 35 ℃, adding the water into the paddle vat while continuously rotating and stirring for 25-35 minutes, adding the sodium bicarbonate to adjust the pH value to 5.0-6.0, continuously rotating and stirring for 1-2 hours, and discharging all liquid in the paddle vat; adding 300 kg of hot water with the temperature of 40 ℃ again, rotating and washing for 15-25 minutes, peeling, and discharging all liquid in the paddle vat;
ZrO in the zirconium-aluminum composite tanning agent2With Al2O3The weight ratio of: ZrO (ZrO)2:Al2O3=100:25-100:100。
7. A clean tanning method of Tan sheep fur as claimed in claim 6The method is characterized in that: ZrO in the zirconium-aluminum composite tanning agent2With Al2O3The weight ratio of: ZrO (ZrO)2:Al2O3=100:35-100:85。
8. The clean tanning method of beach sheep fur according to claim 1, characterized in that: the S106: adding 250 kg of warm water with the temperature of 10-20 ℃ into the paddle vat again, adding 1 kg-1.5 kg of hydrogen peroxide with the concentration of 35% into the paddle vat, and stirring for 15 minutes in a rotating way; putting the Tan sheep fur obtained in the step S105, rotating and stirring for 30-40 minutes, and discharging all liquid in the paddle vat; adding 300 kg warm water with the temperature of 10-20 ℃, rotating to wash for 10-20 minutes, discharging all liquid in the paddle vat, and peeling.
9. The clean tanning method of beach sheep fur according to any one of claims 1 to 8, characterized in that: the step S109: shaking and throwing the sheepskin, placing the sheepskin on a plate frame for binding, moving the sheepskin on a flat land, and naturally drying the sheepskin at a daily temperature of 20 ℃;
after natural drying, the Tan sheep fur is disassembled from the plate frame and is placed in a shady and cool place with four ventilated sides for 20 hours.