CN107603002A - A kind of improved polypropylene foamed plate - Google Patents
A kind of improved polypropylene foamed plate Download PDFInfo
- Publication number
- CN107603002A CN107603002A CN201610552547.1A CN201610552547A CN107603002A CN 107603002 A CN107603002 A CN 107603002A CN 201610552547 A CN201610552547 A CN 201610552547A CN 107603002 A CN107603002 A CN 107603002A
- Authority
- CN
- China
- Prior art keywords
- parts
- foamed plate
- polypropylene foamed
- crosslinking agent
- improved polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of improved polypropylene foamed plate, its raw material composition meter in parts by weight includes:2~5 parts of trimethylol-propane trimethacrylate, 0.5~1.5 part of crosslinking agent, 0.5~2 part of foaming agent, 8~15 parts of ultra-high molecular weight polyethylene, 0.1~1 part of acrylonitrile butadient styrene, 65~80 parts of polypropylene, 2~6 parts of nucleator.The present invention is simple containing improved polypropylene foamed plate component, by adding acrylonitrile butadient styrene and ultra-high molecular weight polyethylene, increase the tensile resistance and deformability of melt polypropylene, reduce melt in expansion process and rupture too early, make cell size uniform, reduce holes rate.
Description
Technical field
The present invention relates to foaming plate technical field, and in particular to a kind of improved polypropylene foamed plate.
Background technology
Expanded polypropylene has the advantages of notable, such as mechanical property is more excellent, has higher temperature tolerance and insulation
Thermal insulation, elastic recovery is more preferable, in addition it or a kind of green material that can be degraded in nature etc., plurality of advantages
Determine that polypropylene foam can apply to wider field, such as the buffer packaging material as advanced electronic electrical equipment
The heat insulator of material, hot water pipeline etc., the heat insulating energy saving material of building field, and the buffering energy-absorbing material of automotive field
Deng.But because polyacrylic melt strength is low, strain hardening behavior is weak, and polyacrylic fusing point and softening point temperature it is non-
Very close to viscosity significantly declines after temperature exceedes its fusing point, so as to cause general purpose polypropylene to be foamed.Improve
Polyacrylic expandable, improving its melt strength in other words has a variety of methods, such as improves molecular weight, widens molecular weight point
Cloth or introducing side chain etc. are all effective approach.The expanded material of preferable foam structure is obtained, it is necessary to which structure is extremely complex
Accurate extrusion foaming device, and also have strict requirements for extrusion foaming technique, once process conditions slightly offset from
Setting value extrusion foaming will fail so that foaming body abscess is excessive, cell size is uneven, holes rate is higher and foams not
A series of problems, such as stable.
The content of the invention
It is an object of the invention to overcome defect present in prior art, there is provided a kind of improved polypropylene expanded plate
Material, the sheet material make cell size uniform, reduce holes rate by raw material configuration.
To realize above-mentioned technique effect, the technical scheme is that:A kind of improved polypropylene foamed plate, its feature
It is, its raw material composition meter in parts by weight includes:2~5 parts of trimethylol-propane trimethacrylate, crosslinking agent 0.5~
1.5 parts, 0.5~2 part of foaming agent, 8~15 parts of ultra-high molecular weight polyethylene, acrylonitrile-butadiene-styrene copolymer 0.1~1
Part, 65~80 parts of polypropylene, 2~6 parts of nucleator.
Preferable technical scheme is that crosslinking agent is selected from benzoyl peroxide, cumyl peroxide and tertiary base peroxidating
At least one of hexane.
Preferable technical scheme is also to contain 0.5~1 part of assistant crosslinking agent, the assistant crosslinking agent in polypropylene foamed plate
For divinylbenzene or Triallyl isocyanurate.
Preferable technical scheme is that polyacrylic melt index is 0.5~1.5g/10min, and ultra-high molecular weight polyethylene melts
It is 1~3g/10min to melt index.
Preferable technical scheme is that nucleator is nano titanium oxide, nano-calcium carbonate, nano imvite or nano-talc
Powder.
Preferable technical scheme is foaming agent 4, and 4- OBSHs or azodicarbonamide and zinc oxide are total to
Mixed thing, the percentage by weight of zinc oxide is 5~20% in blend.
The advantages of the present invention are:
The present invention is simple containing improved polypropylene foamed plate component, is copolymerized by adding acrylonitrile-butadiene-styrene (ABS)
Thing and ultra-high molecular weight polyethylene, increase the tensile resistance and deformability of melt polypropylene, reduce melt in expansion process
Rupture too early, makes cell size uniform, reduces holes rate.
Embodiment
With reference to embodiment, the embodiment of the present invention is further described.Following examples are only used for more
Add and clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
Embodiment 1
The improved polypropylene foamed plate of embodiment 1, its raw material composition meter in parts by weight include:Trimethylolpropane
2 parts of trimethyl acrylic ester, 1.5 parts of crosslinking agent, 0.5 part of foaming agent, 15 parts of ultra-high molecular weight polyethylene, acrylonitrile-butadiene-
Styrol copolymer 0.1,80 parts of polypropylene, 2 parts of nucleator.
Crosslinking agent is benzoyl peroxide.Also contain 0.5~1 part of assistant crosslinking agent, assistant crosslinking agent in polypropylene foamed plate
For divinylbenzene.
Polyacrylic melt index is 0.5g/10min, and ultra-high molecular weight polyethylene melt index is 3g/10min.
Nucleator is nano titanium oxide.Foaming agent is 4,4- OBSHs.
Embodiment 2
The difference of embodiment 2 and embodiment 1 is that improved polypropylene foamed plate, its raw material forms in parts by weight
Meter includes:5 parts of trimethylol-propane trimethacrylate, 0.5 part of crosslinking agent, 2 parts of foaming agent, ultra-high molecular weight polyethylene 8
Part, 1 part of acrylonitrile-butadiene-styrene copolymer, 65 parts of polypropylene, 6 parts of nucleator.
Crosslinking agent is that cumyl peroxide and tertiary base butylperoxyhexane etc. mix again.
Also contain 1 part of assistant crosslinking agent in polypropylene foamed plate, assistant crosslinking agent is Triallyl isocyanurate.
Polyacrylic melt index is 1.5g/10min, and ultra-high molecular weight polyethylene melt index is 1g/10min.
Nucleator is nano-calcium carbonate.
Foaming agent is the blend of azodicarbonamide and zinc oxide, and the percentage by weight of zinc oxide is 5% in blend.
Embodiment 3
The difference of embodiment 3 and embodiment 1 is that improved polypropylene foamed plate, its raw material forms in parts by weight
Meter includes:3.5 parts of trimethylol-propane trimethacrylate, 1 part of crosslinking agent, 1.2 parts of foaming agent, ultra-high molecular weight polyethylene
11 parts, 0.5 part of acrylonitrile-butadiene-styrene copolymer, 72 parts of polypropylene, 4 parts of nucleator.
Crosslinking agent is to select tertiary base butylperoxyhexane.Also contain 1 part of assistant crosslinking agent in polypropylene foamed plate, assistant crosslinking agent is
Divinylbenzene.
Polyacrylic melt index is 1g/10min, and ultra-high molecular weight polyethylene melt index is 2g/10min.
Nucleator is nanomete talc powder.Foaming agent is the blend of azodicarbonamide and zinc oxide, is aoxidized in blend
The percentage by weight of zinc is 20%.
Comparative example:Acrylonitrile-butadiene-styrene copolymer and ultra-high molecular weight polyethylene, group are added without in comparative example
Into same embodiment 1, two kinds of components of acrylonitrile-butadiene-styrene copolymer and ultra-high molecular weight polyethylene are replaced with polypropylene.
Composite board carries out holes rate test obtained by embodiment and comparative example.
Test result:The holes rate of embodiment 1-3 samples is less than comparative example, the abscess pore size of embodiment 1-3 samples
Evenly.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, some improvements and modifications can also be made, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of improved polypropylene foamed plate, it is characterised in that its raw material composition meter in parts by weight includes:Trihydroxy methyl
2~5 parts of propane trimethyl acrylic ester, 0.5~1.5 part of crosslinking agent, 0.5~2 part of foaming agent, ultra-high molecular weight polyethylene 8~
15 parts, 0.1~1 part of acrylonitrile-butadiene-styrene copolymer, 65~80 parts of polypropylene, 2~6 parts of nucleator.
2. improved polypropylene foamed plate according to claim 1, it is characterised in that crosslinking agent is selected from benzoyl peroxide
At least one of formyl, cumyl peroxide and tertiary base butylperoxyhexane.
3. improved polypropylene foamed plate according to claim 1, it is characterised in that also contain in polypropylene foamed plate
There is 0.5~1 part of assistant crosslinking agent, the assistant crosslinking agent is divinylbenzene or Triallyl isocyanurate.
4. improved polypropylene foamed plate according to claim 1, it is characterised in that polyacrylic melt index is
0.5~1.5g/10min, ultra-high molecular weight polyethylene melt index are 1~3g/10min.
5. improved polypropylene foamed plate according to claim 1, it is characterised in that nucleator is nanometer titanium dioxide
Titanium, nano-calcium carbonate, nano imvite or nanomete talc powder.
6. improved polypropylene foamed plate according to claim 1, it is characterised in that foaming agent 4, the double benzene of 4- oxos
The blend of sulfohydrazide or azodicarbonamide and zinc oxide, the percentage by weight of zinc oxide is 5~20% in blend.