CN107587024A - A kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide - Google Patents
A kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide Download PDFInfo
- Publication number
- CN107587024A CN107587024A CN201710846853.0A CN201710846853A CN107587024A CN 107587024 A CN107587024 A CN 107587024A CN 201710846853 A CN201710846853 A CN 201710846853A CN 107587024 A CN107587024 A CN 107587024A
- Authority
- CN
- China
- Prior art keywords
- vanadium nitride
- alloy
- iron oxide
- vanadic anhydride
- prepared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide, this method comprises the following steps:(1) vanadic anhydride, activated carbon, iron oxide are mixed with water, mixture is made;(2) mixture obtained by step (1) is placed in the heating furnace with the protection of inert gas and heated, and be incubated;(3) mixture in step (2) is continued into heat temperature raising and be incubated;(4) mixture in step (3) is cooled down, obtains primary vanadium nitride;(5) primary vanadium nitride is crushed, adds polyethylene glycol, mixed, alloy of vanadium nitride is obtained after suppressing balling-up.Compared with prior art, the low in raw material price that the present invention uses, is easily obtained;The method of the invention flow is simple, easily operated, is easy to large-scale promotion, significantly improves labor productivity;Reaction temperature of the present invention is low, and energy consumption is low.The present invention is carried out under non-vacuum condition, and equipment is simple, stability is strong, equipment investment is few.
Description
Technical field
The invention belongs to field of metallurgy, prepares vanadium nitride with vanadic anhydride and iron oxide more particularly, to one kind and closes
The method of gold.
Background technology
Vanadium nitride, alias VN alloy, it is that only China and country of two, the U.S. can at present than the metallurgical technology of higher-end
With production, and the enterprise that can produce and few.
VN alloy is a kind of novel alloy additive, can substitute the production that vanadium iron is used for micro alloyed steel.Vanadium nitride
The comprehensive mechanical performances such as intensity, toughness, ductility and the thermal fatigue resistance of steel can be improved by making an addition in steel, and it is good to have steel
Solderability.In the case where reaching same intensity, addition vanadium nitride can save vanadium addition 30-40%, and then reduce cost.
By taking construction industry as an example, using the new three-level reinforcing bar of VN alloy technology production, because its intensity improves, not only strengthen
The security of building, shock resistance, but also can than saved using two level reinforcing bar 10%~15% steel.Only this one
, China can lack with about 7,500,000 tons of reinforcing bar every year, accordingly exploit about 12,400,000 tons of iron ore concentrate less, save 6,600,000 tons of coal,
Related 3,300,000 tons of auxiliary material is saved, while substantially reduce the number the discharge of the waste gas such as carbon dioxide and sulfur dioxide, receives resource
Save the double benefit with environmental protection.VN alloy can be used for structural steel, tool steel, pipe line steel, in reinforcing bar and cast iron.Vanadium nitrogen
Alloyapplication can carry out effective vanadium, nitrogen microalloying simultaneously in Aldecor, promote carbon, vanadium, nitrification in steel
The precipitation of thing, more effectively play sedimentation reinforcing and Grain refinement.VN alloy feature:VN alloy has more than vanadium iron
It is effective to strengthen and Grain refinement, can save vanadium addition using VN alloy, under the conditions of same intensity VN alloy with
Vanadium iron compares the vanadium that can save 20-40%.Vanadium, nitrogen recovery rate stabilization are more beneficial for using VN alloy, reduces the performance ripple of steel
It is dynamic.Particularly convenient using VN alloy, loss is few.Packed using high strength moistureproof, can directly enter stove.
The content of the invention
Must operate under vacuo it is an object of the invention to solving to prepare vanadium nitride in the prior art, flow it is complicated, no
The problem of easily operated.
To achieve these goals, the present invention provides a kind of side that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide
Method, this method comprise the following steps:
(1) vanadic anhydride, activated carbon, iron oxide are mixed with water, mixture is made;
(2) mixture obtained by step (1) is placed in the heating furnace with the protection of inert gas and heated, and be incubated;
(3) mixture in step (2) is continued into heat temperature raising and be incubated;
(4) mixture in step (3) is cooled down, obtains primary vanadium nitride;
(5) primary vanadium nitride is crushed, adds polyethylene glycol, mixed, alloy of vanadium nitride is obtained after suppressing balling-up.
In step (1) of the present invention, the vanadic anhydride, activated carbon, the weight ratio of iron oxide and water are 100:10-35:
5-10:2-6.
As the preferred embodiment of the present invention, the vanadic anhydride is powdery.
As the preferred embodiment of the present invention, in step (1), the vanadic anhydride, activated carbon, iron oxide and water
Weight ratio is 100:25-35:5-10:4-6.
As the preferred embodiment of the present invention, the inert gas is nitrogen.
In step (2) of the present invention, heating-up temperature is 580-600 DEG C, and preferably 590-600 DEG C, optimal is 600 DEG C.
In step (2) of the present invention, soaking time is preferably 0.5-3h.
In step (3) of the present invention, the temperature of insulation is preferably 1000-1200 DEG C.
In step (4) of the present invention, the temperature of cooling is preferably 10-40 DEG C.
In step (5) of the present invention, the pressure for suppressing balling-up is preferably 15-20Mpa.
Beneficial effects of the present invention:
(1) low in raw material price that the present invention uses, is easily obtained.
(2) the method for the invention flow is simple, easily operated, is easy to large-scale promotion, significantly improves labor productivity.
(3) reaction temperature of the present invention is low, and energy consumption is low.
(4) present invention is carried out under non-vacuum condition, and equipment is simple, stability is strong, equipment investment is few.
Other features and advantages of the present invention will be described in detail in subsequent specific embodiment part.
Embodiment
The preferred embodiment of the present invention is described in more detail below.Although the following describe being preferable to carry out for the present invention
Mode, however, it is to be appreciated that may be realized in various forms the present invention without should be limited by embodiments set forth herein.Phase
Instead, there is provided these embodiments be in order that the present invention is more thorough and complete, and can be by the scope of the present invention intactly
It is communicated to those skilled in the art.
Embodiment 1:
A kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide, this method comprise the following steps:
(1) vanadic anhydride, activated carbon, iron oxide of powdery are mixed with water, mixture is made;
(2) mixture obtained by step (1) is placed in the heating furnace with the protection of nitrogen and heated, and be incubated;
(3) mixture in step (2) is continued into heat temperature raising and be incubated;
(4) mixture in step (3) is cooled down, obtains primary vanadium nitride;
(5) primary vanadium nitride is crushed, adds polyethylene glycol, mixed, alloy of vanadium nitride is obtained after suppressing balling-up.
In step (1) of the present invention, the vanadic anhydride, activated carbon, the weight ratio of iron oxide and water are 100:10:5:2.
In step (2) of the present invention, heating-up temperature is 590 DEG C.
In step (2), soaking time 0.5h.
In step (3), the temperature of insulation is 1000 DEG C.
In step (4), the temperature of cooling is 10 DEG C.
In step (5), the pressure for suppressing balling-up is 15Mpa.
Embodiment 2:
A kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide, this method comprise the following steps:
(1) vanadic anhydride, activated carbon, iron oxide of powdery are mixed with water, mixture is made;
(2) mixture obtained by step (1) is placed in the heating furnace with the protection of nitrogen and heated, and be incubated;
(3) mixture in step (2) is continued into heat temperature raising and be incubated;
(4) mixture in step (3) is cooled down, obtains primary vanadium nitride;
(5) primary vanadium nitride is crushed, adds polyethylene glycol, mixed, alloy of vanadium nitride is obtained after suppressing balling-up.
In step (1) of the present invention, the vanadic anhydride, activated carbon, the weight ratio of iron oxide and water are 100:35:10:
6。
In step (2) of the present invention, heating-up temperature be 600 DEG C,
In step (2) of the present invention, soaking time 3h.
In step (3) of the present invention, the temperature of insulation is 1200 DEG C.
In step (4) of the present invention, the temperature of cooling is 40 DEG C.
In step (5) of the present invention, the pressure for suppressing balling-up is 20Mpa.
It is described above various embodiments of the present invention, described above is exemplary, and non-exclusive, and
It is not limited to disclosed each embodiment.In the case of without departing from the scope and spirit of illustrated each embodiment, for this skill
Many modifications and changes will be apparent from for the those of ordinary skill in art field.
Claims (10)
- A kind of 1. method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide, it is characterised in that this method includes following Step:(1) vanadic anhydride, activated carbon, iron oxide are mixed with water, mixture is made;(2) mixture obtained by step (1) is placed in the heating furnace with the protection of inert gas and heated, and be incubated;(3) mixture in step (2) is continued into heat temperature raising and be incubated;(4) mixture in step (3) is cooled down, obtains primary vanadium nitride;(5) primary vanadium nitride is crushed, adds polyethylene glycol, mixed, alloy of vanadium nitride is obtained after suppressing balling-up.
- 2. a kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide according to claim 1, wherein, step Suddenly in (1), the vanadic anhydride, activated carbon, the weight ratio of iron oxide and water are 100:10-35:5-10:2-6.
- 3. a kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide according to claim 1, wherein, institute It is powdery to state vanadic anhydride.
- 4. a kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide according to claim 1, wherein, step Suddenly in (1), the vanadic anhydride, activated carbon, the weight ratio of iron oxide and water are 100:25-35:5-10:4-6.
- 5. a kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide according to claim 1, wherein, institute It is nitrogen to state inert gas.
- 6. a kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide according to claim 1, wherein, step Suddenly in (2), heating-up temperature is 580-600 DEG C.
- 7. a kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide according to claim 1, wherein, step Suddenly in (2), soaking time 0.5-3h.
- 8. a kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide according to claim 1, wherein, step Suddenly in (3), the temperature of insulation is 1000-1200 DEG C.
- 9. a kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide according to claim 1, wherein, step Suddenly in (4), the temperature of cooling is 10-40 DEG C.
- 10. a kind of method that alloy of vanadium nitride is prepared with vanadic anhydride and iron oxide according to claim 1, wherein, In step (5), the pressure for suppressing balling-up is 15-20Mpa.