CN107573524A - 一种色母粒 - Google Patents
一种色母粒 Download PDFInfo
- Publication number
- CN107573524A CN107573524A CN201710690716.2A CN201710690716A CN107573524A CN 107573524 A CN107573524 A CN 107573524A CN 201710690716 A CN201710690716 A CN 201710690716A CN 107573524 A CN107573524 A CN 107573524A
- Authority
- CN
- China
- Prior art keywords
- masterbatch
- carrier
- lldpe
- masterbatch according
- dispersant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种色母粒,属于高分子材料技术领域,可解决现有技术中色母粒分散性不好,着色差,对母料性能影响较大的问题,包括如下质量分数的组分:45‑50%的色粉,35‑45%的第一种载体,5‑10%的第二种载体,1‑5%的分散剂。用密炼机将其搅拌混合,搅拌呈块状后将其取出,放入双螺杆挤出机中进行熔融、挤出、切粒,得到色母粒。使用本发明的色母粒后,既满足了对颜色的要求,又不会影响母料的性能。
Description
技术领域
本发明属于高分子材料技术领域,具体涉及一种色母粒。
背景技术
色母粒由高比例的颜料或添加剂与热塑性树脂,经良好分散而成的塑料着色剂,其所选用的树脂对着色剂具有良好润湿和分散作用,并且与被着色材料具有良好的相容性,因此,色母粒有着广泛的用途,尤其是塑料中,但是随着色母粒广泛的应用,对色母粒也提出更好的要求,现有技术中的色母粒使用后分散性不好,着色差,对母料性能影响较大。
发明内容
本发明针对现有技术中色母粒分散性不好,着色差,对母料性能影响较大的问题,提供一种色母粒。
本发明采用如下技术方案:
一种色母粒,包括如下质量分数的组分:45-50%的色粉,35-45%的第一种载体,5-10%的第二种载体,1-5%的分散剂。
优选地,本发明的色母粒,包括如下质量分数的组分:50%的色粉,35%的第一种载体,10%的第二种载体,5%的分散剂。
所述色粉为炭黑。
所述第一种载体为线型低密度聚乙烯LLDPE。
所述第二种载体为EVA弹性体。
所述分散剂为N,N'-乙撑双硬脂酰胺。
所述线型低密度聚乙烯的分子量为15000-200000。
优选地,所述线型低密度聚乙烯的分子量为15000-150000。
优选地,所述线型低密度聚乙烯的分子量为15000-50000。
将本发明的各组分进行搅拌、混合、密炼、熔融、挤出、制粒步骤而制得该色母粒,关于搅拌、混合、密炼、熔融、挤出、制粒的操作条件为本领域技术人员所公知技术,可选择合适条件来实施本发明。
本发明的有益效果如下:
1. 本发明色母粒在PP、ABS、PC/ABS等材料中都具有极佳的分散性,并且使用的分散剂不会影响母料的性能。环保、无毒、无味产品表面光滑亮泽,不会出现色点和色纹等现象,且同时具有高黑度,不褪色等优点。
2. 本发明一款通用型黑母粒,使用聚乙烯做载体,可以使用于聚乙烯、聚丙烯、热塑性弹性体等材料,通过添加EVA弹性体对母粒的处理,可以使用ABS、PC/ABS、PC、POM等材料中,可以很好的解决大部分客户的使用要求。
3. 本发明的分散性和黑度超过同类型的进口产品,可以完全取代进口产品的使用。
附图说明
图1为本发明制备工艺流程图。
具体实施方式
1. 本发明所用色粉为山西佩格特公司生产的HTC1#A炭黑,具有以下性能:
牌号 | 粒径nm | BET m2/g | 吸收值cm3/100g | 吸碘值g/kg | 着色力 | pH值 | 流动度 | 杂质 | 挥发份% |
HTC1#A | 22 | 165 | 55 | 160 | 135 | 7~7.5 | 25 | 无 | 1.5 |
2. 载体是可以均匀地与色粉混合者,第一种载体优选为分子量较低的聚烯烃,优选的分子量的范围为15000至200000,更优选的分子量范围为15000至150000,最优选的分子量范围为15000至50000,选择线性低密度聚乙烯。其分子式为[-CH2-CH2]n-。
其性能与LDPE相比,具有较高的软化温度和熔融温度,有强度大、韧性好、刚性大、耐热、耐寒性好等优点,还具有良好的耐环境应力开裂性,耐冲击强度、耐撕裂强度等性能。并可耐酸、碱、有机溶剂等。
第二种载体选择EVA弹性体,由乙烯和乙酸乙烯共聚而得,一般乙酸乙烯含量在5%-40%,由于EVA在分子链中引入乙酸乙烯单体,从而降低了高结晶度,提高了韧性、抗冲击性、填料相溶性,使产品可以在多种材料中使用,并且不影响材料的其他性能。其结构式如下:
。
3. 分散剂选用N,N'-乙撑双硬脂酰胺,与树脂相溶性好,其化学性质稳定、电性能良好,在色母粒中可以对色粉起到分散作用,并具有十分优异的外部润滑和内部润滑作用。作为内润滑剂,它减少树脂分子链的内摩擦力,提高聚合物的流动性,改进制品表面光洁度。作为外润滑剂,它可作为其在挤出、压延、注射加工中的润滑剂。可提高加工效率,防止和克服薄膜、管材、片材、颗粒粘结,提高成品的平滑度和光泽度,改善成品外观。
本发明选用的N,N'-乙撑双硬脂酰胺为日本花王EB-FF,具有以下性能:
外观(25℃) | 颜色 | 酸值gKOH/g | 胺值mgKOH/g | 熔点℃ | 挥发成分% | 颗粒尺寸% |
白色超细粉末 | 5max | 10max | 2.5max | 141.5-146.5闪点(闭杯) | 0.5max | 91min过200目 |
4. 制备方法:称取各组分,用密炼机将其搅拌混合,密炼机温度为130摄氏度,搅拌呈块状后将其取出,放入双螺杆挤出机中进行熔融、挤出、切粒。
5. 实施例
实施例1,一种色母粒,包括如下质量分数的组分:50kg的炭黑,35kg的LLDPE,10kg的EVA弹性体,5kg的N,N'-乙撑双硬脂酰胺。
实施例2,一种色母粒,包括如下质量分数的组分:45kg的炭黑,45kg的LLDPE,5kg的EVA弹性体,5kg的N,N'-乙撑双硬脂酰胺。
实施例3,一种色母粒,包括如下质量分数的组分:50kg的炭黑,40kg的LLDPE,9kg的EVA弹性体,1kg的N,N'-乙撑双硬脂酰胺。
实施例4,一种色母粒,包括如下质量分数的组分:47.5kg的炭黑,40kg的LLDPE,7.5kg的EVA弹性体,5kg的N,N'-乙撑双硬脂酰胺。
实施例5,一种色母粒,包括如下质量分数的组分:47.5kg的炭黑,45kg的LLDPE,5kg的EVA弹性体,2.5kg的N,N'-乙撑双硬脂酰胺。
6. 将本发明各实施例与卡博特母粒UN2014性能对比。
(1)黑度数据对比,使用X-rite Ci4200仪器。
从上表中可以看出(L值越小颜色越黑),本发明色母粒的黑度完全超越同类型进口产品UN2014。其中,ABS树脂是奇美公司ABS PA757;PP树脂是上海赛科石油化工,规格是S2040。
(2)熔融数据对比,使用苏州方特电子科技有限公司 FTRH-400仪器。
(3)滤压值对比
从对比的数据中可以看出,炭黑含量减少,分散性增加(滤压值变小)会影响产品的黑度下降(L值变大);分散剂变少,会影响产品的分散性能。
(4)本发明色母粒在PC/ABS中,对母料物性的影响
从上表中,可以看出,添加本发明色母粒后,对母料的冲击性能影响很小。
Claims (9)
1.一种色母粒,其特征在于:包括如下质量分数的组分:45-50%的色粉,35-45%的第一种载体,5-10%的第二种载体,1-5%的分散剂。
2.根据权利要求1所述的一种色母粒,其特征在于:包括如下质量分数的组分:50%的色粉,35%的第一种载体,10%的第二种载体,5%的分散剂。
3.根据权利要求1或2所述的一种色母粒,其特征在于:所述色粉为炭黑。
4.根据权利要求1所述的一种色母粒,其特征在于:所述第一种载体为线型低密度聚乙烯LLDPE。
5.根据权利要求1或2所述的一种色母粒,其特征在于:所述第二种载体为EVA弹性体。
6.根据权利要求1或2所述的一种色母粒,其特征在于:所述分散剂为N,N'-乙撑双硬脂酰胺。
7.根据权利要求4所述的一种色母粒,其特征在于:所述线型低密度聚乙烯的分子量为15000-200000。
8.根据权利要求7所述的一种色母粒,其特征在于:所述线型低密度聚乙烯的分子量为15000-150000。
9.根据权利要求8所述的一种色母粒,其特征在于:所述线型低密度聚乙烯的分子量为15000-50000。