CN107557954A - A kind of uvioresistant water absorbent quick-drying skin toner and its production technology - Google Patents
A kind of uvioresistant water absorbent quick-drying skin toner and its production technology Download PDFInfo
- Publication number
- CN107557954A CN107557954A CN201710762144.4A CN201710762144A CN107557954A CN 107557954 A CN107557954 A CN 107557954A CN 201710762144 A CN201710762144 A CN 201710762144A CN 107557954 A CN107557954 A CN 107557954A
- Authority
- CN
- China
- Prior art keywords
- fiber
- drying
- uvioresistant
- water absorbent
- dyeing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of uvioresistant water absorbent quick-drying skin toner and its production technology, the skin toner is made by following raw material proportioning：80SW mercerized wools 50%, first silk fiber 10%, uvioresistant fiber 15%, terylene 20%, water absorbent quick-drying fiber 5%；The production technology of the skin toner, comprises the following steps：（1）Dyeing process；（2）Spinning process；（3）Weaving process；（4）Finishing process.The present invention not only has the functions such as uvioresistant water-absorbing fast-drying, also the characteristics of embodying mercerized wool and soft and smooth soft warm first silk fiber, feel is soft glutinous, wearability is splendid, fabric produced by the present invention has given full play to uvioresistant, the premium properties of absorbing fast-drying fiber, and first silk fiber application assigns the consumption concept of the green ecological environmental protection of fabric, enriches wool spinning fabric kind, the class and added value of fabric are improved, achieves good market effect.
Description
Technical field
The invention belongs to weaving face fabric preparing technical field, more particularly to a kind of uvioresistant water absorbent quick-drying skin toner and its
Production technology.
Background technology
With the development of modern industry, the ozone layer in atmosphere is constantly being destroyed, and ozone layer is that the earth is best
Umbrella, it can absorb most of ultraviolet from the sun.However, the scientific research of recent two decades and atmospheric seeing are found：
Ozone layer above the Antarctic or even has produced an ozone hole always thinning.Excessive ultraviolet drives straight in, long-term irradiation
Under, acute big injury can be caused to human skin.UV-A, UV-B wave band in ultraviolet can encourage melanin generation, cause skin
Matter aging, or even cause the lesions such as white Inner barriers, cutaneum carcinoma.Therefore, people are also increasingly surging to the product demand of antiultraviolet.Together
When with the raising of people's level of consumption, requirement of the people to clothes snugness of fit also more and more higher, it is desirable to which clothes have dry
Refreshing, ventilative, warming effect.Traditional natural fiber cotton has a preferable hydrophilicity and natural morphosis, but
After being soaked by sweat, it may occur that the phenomenon being pasted onto on human body skin, bring extremely uncomfortable sensation；Conventional polyester fiber due to
The hydrophobic property of itself, it have impact on the comfortableness of fabric.It would therefore be highly desirable to research and develop one kind can antiultraviolet, and comfortable face
Material.
The content of the invention
The invention aims to provide a kind of uvioresistant water absorbent quick-drying skin toner, the exploitation of the product makes full use of
The fibers such as uvioresistant, hydroscopic fast-drying fiber and first silk enhance its feature, improve its wearability, carry as raw material
High product added value, it is the preferable fabric for making high-grade business wear.
In order to realize the purpose of the present invention, the technical scheme of use is：
A kind of uvioresistant water absorbent quick-drying skin toner, is made by following raw material proportioning：80SW mercerized wools 50%, first silk fiber
10%, uvioresistant fiber 15%, terylene 20%, water absorbent quick-drying fiber 5%.
Further, the fineness of the 80SW mercerized wools is 18.5 um, and length 78mm, the fineness of first silk fiber is 2D,
Length is 88mm, and the fineness of uvioresistant fiber is 1.5 D, length 95mm, and the fineness of terylene is 1.5 D, length 95mm,
The fineness of water absorbent quick-drying fiber is 2 D, length 90mm.
Further, the uvioresistant fiber selects FeelCool UV Cut uvioresistants, and water absorbent quick-drying fiber is selected
Cooldry water absorbent quick-drying fibers.
A kind of production technology of uvioresistant water absorbent quick-drying skin toner as described above, comprises the following steps：
（1）Dyeing process
80SW mercerized wools dye:Because mercerized wool is by shelling squama processing, blocking performance comparision is poor, and dyeing dyeing speed is very fast,
It is 20 DEG C, 1 DEG C/min of heating rate to play dye temperature selection, and using low temperature dyeing, it is active to receive plain hair from environment-friendly type import orchid
Dyestuff is dyed, and adds 2% N2 low-temp dyeing accelerants, and wool high-temperature dyeing temperature drops to 90 DEG C from 98 DEG C, and after backwashing is improvement
Feel, add a certain amount of smooth, soft agent, reduce the damage of wool fiber, improve spinning row yielding and yarn it is strong
Power feel.
First silk fiber dyeing:Dyed from reactive dye, add a certain amount of N2 low-temp dyeing accelerants, ensure colouring
Uniform color fastness, to make the smooth adsorption and diffusion of dye molecule to fibrous inside and carrying out set, prolonged dyeing times are to 90 points
Clock, after backwashing workshop section emphasis are controlled to water temperature and drying room temperature, 50-60 DEG C of water temperature, 110-120 DEG C of drying room temperature, make fiber
Lower machine bar is submissive, and moisture regain is uniform, is easy to rear road to unclog and readjust；
Uvioresistant fiber：The fiber is the fiber of viscose glue carrier, is dyed using cotton reactive dye, to ensure antiultraviolet fiber
Color fastness, a certain amount of level dyeing bleeding agent is added in dyeing course；
（2）Spinning process
Combing chooses greatly gauge so as to reduce the quantity of card nailing neps in fiber using light feed quantity, using light quantitative, small drawing-off, septulum
Process configuration away from, low speed, thickness section and filoplume are reduced, improve the bright and clean uniformity of resultant yarn strand, the configuration of rove main technique：
Thick bar weight：0.16g/m, feed strip substance：0.36g/m, ratch：125mm, it is easy to road spinning efficiency after improving,
Silver mixing and crude oil filling 40mL, the grams m of shaping weight 20,5-8 times of drafting multiple, rear spin use compact spinning, used
The low speeds of 7000r/min；
（3）Weaving process
The tension difference between the tension difference and reeled yarn between single thread is strictly controlled during warping, through on-the-spot test single thread
Tension force is in 15CN or so, 1.5 kilograms of beaming tension force, the moderate shaping rounding of beam of a loom even tension elasticity, avoids finished product cloth cover
Occur through shelves and hang through because considering yarn strength, while number is again higher, therefore, 8% HG- is added during warping beaming
The cold slurry agent of 106 warp thread, makes yam surface brighter and cleaner, and cohesive force enhancing, wearability improves, and reduces and breaks end, and 280 turns of warping speed/
Point, small tension receiving coil is used on loom, ensures that weaving is smoothed out；
（4）Finishing process
Technological process：→ braying of singing is → bis- to boil → to absorb water → dries → and middle inspection → ripe repaiies and → middle to examine → rolls soft → middle inspection → decatizing
→ KD tanks steaming → finished product；
First singed in raw cloth and carry out surface fine hair processing, the whole pre-treatment of rewetting, allow uvioresistant fiber fully to be absorbed water in hygrometric state,
Fiber relaxation is allowed to open, to play absorbing fast-drying fiber properties, each road is arranged using hydrophilic auxiliary agent, improves the moisture absorption of fabric
Rapid-curing cutback wearability, technological parameter：Rinse:40 DEG C, 15 ', wash at a high speed:280m/min、30′；Crabbing technique：80 DEG C of temperature,
40 ', middle tension force, pressure 1.4, acid adding 400HAC, machine cooling outside, bath raio 1:8th, anti-adding soda ash 0.5%, meanwhile, 2% on overfeeding under
4%th, 3# burners are burnt thoroughly, and machine 152cm is accurately controlled under upper gate width 154cm, and the cloth cover feel and glossiness for making finished product reach
The state optimal to one.
Further, the preferably Italian import Azithromycin loom of the loom, the most rational technological parameter of use, opening time
315 degree, back rest 1-2, weaving-machine tension 285N, the emphasis pair warp and weft problem of hanging is controlled, and ensures fabric quality.
Further, the uvioresistant fiber selects FeelCool UV Cut uvioresistants, and water absorbent quick-drying fiber is selected
Cooldry water absorbent quick-drying fibers.
The device have the advantages that：
1st, the present invention not only has the functions such as uvioresistant water-absorbing fast-drying, also embodies mercerized wool and first silk fiber is soft and smooth soft warm
Feature, feel is soft glutinous, and wearability is splendid.
2nd, fabric produced by the present invention has given full play to uvioresistant, the premium properties of absorbing fast-drying fiber, and first silk fiber should
With the consumption concept for the green ecological environmental protection for assigning fabric, wool spinning fabric kind is enriched, the class of fabric is improved and adds
Value, achieves good market effect.
Embodiment
With reference to embodiment, the invention will be further described, but protection scope of the present invention is not limited solely to implement
Example.
The present invention is as follows from the parameter of raw material,
A kind of production technology of uvioresistant water absorbent quick-drying skin toner as described above, comprises the following steps：
（1）Dyeing process
80SW mercerized wools dye:Because mercerized wool is by shelling squama processing, blocking performance comparision is poor, and dyeing dyeing speed is very fast,
It is 20 DEG C, 1 DEG C/min of heating rate to play dye temperature selection, and using low temperature dyeing, it is active to receive plain hair from environment-friendly type import orchid
Dyestuff is dyed, and adds 2% N2 low-temp dyeing accelerants, and wool high-temperature dyeing temperature drops to 90 DEG C from 98 DEG C, and after backwashing is improvement
Feel, add a certain amount of smooth, soft agent, reduce the damage of wool fiber, improve spinning row yielding and yarn it is strong
Power feel.
First silk fiber dyeing:Dyed from reactive dye, add a certain amount of N2 low-temp dyeing accelerants, ensure colouring
Uniform color fastness, to make the smooth adsorption and diffusion of dye molecule to fibrous inside and carrying out set, prolonged dyeing times are to 90 points
Clock, after backwashing workshop section emphasis are controlled to water temperature and drying room temperature, 50-60 DEG C of water temperature, 110-120 DEG C of drying room temperature, make fiber
Lower machine bar is submissive, and moisture regain is uniform, is easy to rear road to unclog and readjust；
Uvioresistant fiber：The fiber is the fiber of viscose glue carrier, is dyed using cotton reactive dye, to ensure antiultraviolet fiber
Color fastness, a certain amount of level dyeing bleeding agent is added in dyeing course；
（2）Spinning process
Combing chooses greatly gauge so as to reduce the quantity of card nailing neps in fiber using light feed quantity, using light quantitative, small drawing-off, septulum
Process configuration away from, low speed, thickness section and filoplume are reduced, improve the bright and clean uniformity of resultant yarn strand, the configuration of rove main technique：
Thick bar weight：0.16g/m, feed strip substance：0.36g/m, ratch：125mm, it is easy to road spinning efficiency after improving,
Silver mixing and crude oil filling 40mL, the grams m of shaping weight 20,5-8 times of drafting multiple, rear spin use compact spinning, used
The low speeds of 7000r/min；
（3）Weaving process
The tension difference between the tension difference and reeled yarn between single thread is strictly controlled during warping, through on-the-spot test single thread
Tension force is in 15CN or so, 1.5 kilograms of beaming tension force, the moderate shaping rounding of beam of a loom even tension elasticity, avoids finished product cloth cover
Occur through shelves and hang through because considering yarn strength, while number is again higher, therefore, 8% HG- is added during warping beaming
The cold slurry agent of 106 warp thread, makes yam surface brighter and cleaner, and cohesive force enhancing, wearability improves, and reduces and breaks end, and 280 turns of warping speed/
Point, small tension receiving coil is used on loom, ensures that weaving is smoothed out, the preferably Italian import Azithromycin loom of loom, using most closing
The technological parameter of reason, 315 degree, back rest 1-2, weaving-machine tension 285N of opening time, the emphasis pair warp and weft problem of hanging is controlled, and is ensured
Fabric quality；
（4）Finishing process
Technological process：→ braying of singing is → bis- to boil → to absorb water → dries → and middle inspection → ripe repaiies and → middle to examine → rolls soft → middle inspection → decatizing
→ KD tanks steaming → finished product；
First singed in raw cloth and carry out surface fine hair processing, the whole pre-treatment of rewetting, allow uvioresistant fiber fully to be absorbed water in hygrometric state,
Fiber relaxation is allowed to open, to play absorbing fast-drying fiber properties, each road is arranged using hydrophilic auxiliary agent, improves the moisture absorption of fabric
Rapid-curing cutback wearability, technological parameter：Rinse:40 DEG C, 15 ', wash at a high speed:280m/min、30′；Crabbing technique：80 DEG C of temperature,
40 ', middle tension force, pressure 1.4, acid adding 400HAC, machine cooling outside, bath raio 1:8th, anti-adding soda ash 0.5%, meanwhile, 2% on overfeeding under
4%th, 3# burners are burnt thoroughly, and machine 152cm is accurately controlled under upper gate width 154cm, and the cloth cover feel and glossiness for making finished product reach
The state optimal to one.
The fabric selects FeelCool UV Cut uvioresistants and Cooldry water absorbent quick-drying fibers, is produced in absorbing fast-drying
On the basis of product, the brand-new material of high-tech is incorporated, uvioresistant and moisture absorption sweat discharging functions is had concurrently, ultraviolet can be effectively isolated, protected
Sheath skin, while have and can reach ventilative dry and comfortable effect, allow skin freely to breathe.Anti- UV effects：The special core sheath of the fiber
Structure is that the higher super blunt finish matter containing titanium dioxide is coated in general semi-gloss raw material so that UVResistant effect and permeation-proof
Given full play to depending on effect；Absorbing fast-drying：Fibrous inside groove can absorb the sweat of skin surface rapidly, and transmit rapidly
Dissipated to skin surface, make body dry and comfortable comfortable.Meanwhile used first silk fiber is the closure using pure timber as raw material
Manage dissolution type production, more than 99% solvent circulation, product be can 100% natural degradation pollution-free regenerated celulose fibre.It is simultaneous
The comfortable ventilating of tool natural fiber and the intensity of chemical fibre are durable, and it is cellulose that it, which is mainly formed as cotton or viscose glue, its
Molecular weight and crystallinity have good hygroscopicity, dry and wet intensity is big, initial modulus is high, is received in water between cotton and viscose glue
The features such as shrinkage is small, good stability of the dimension, its structure is more smooth than cotton, have cotton comfortableness, make skin have it is nice and cool, smooth,
Dry comfort；Feel with silk, fine and smooth soft and smooth, gloss is soft, such as second layer skin sense；It is very refreshing with hair, hand
Sense is fine and smooth, it is soft, have a muscles and bones sense, quality is plentiful, fluffy；The intensity of drapability, terylene with viscose glue, drapability is good, quick-drying,
The characteristic such as do not crease easily, easily arrange.
Our company is detected to obtained fabric according to standard GB/T/T 26382-2011, and testing result is as follows：
A, finishing 4-5 levels;
B, anti-fluffing and anti-pilling 4-5 levels；
C, colour fasteness to rubbing >=4 grade；
D, shrink≤1.5%.
From test result, the indices of product meet GB/T 26382-2011 countries examination criteria.
Uvioresistant absorbing fast-drying skin toner is the new direction for leading the high-grade functional fabric development of spinning environmental protection, and the product is peculiar
Feature lead the consumption guidance of people, be well received by consumers.The product has good dimensional stability, wear-resisting
Property is good, is detected through authoritative institution：UPF≥50；Drip diffusion time≤5s；Vapor transfer rate >=8000/g (㎡ .d), product market is opened
Value of making an offer is high, has a extensive future.
Finally it should be noted that：Above example only not limits technology described in the invention to illustrate the present invention
Scheme；Therefore, although this specification with reference to above-mentioned each embodiment to present invention has been detailed description, this
Field it is to be appreciated by one skilled in the art that still can be modified to the present invention or equivalent substitution；And all do not depart from this
The technical scheme of the spirit and scope of invention and its improvement, it all should cover in scope of the presently claimed invention.
Claims (6)
1. a kind of uvioresistant water absorbent quick-drying skin toner, it is characterised in that be made by following raw material proportioning：80SW mercerized wools
50%, first silk fiber 10%, uvioresistant fiber 15%, terylene 20%, water absorbent quick-drying fiber 5%.
A kind of 2. uvioresistant water absorbent quick-drying skin toner according to claim 1, it is characterised in that the 80SW mercerisings sheep
The fineness of hair is 18.5um, length 78mm, and the fineness of first silk fiber is 2D, length 88mm, the fineness of uvioresistant fiber
For 1.5D, length 95mm, the fineness of terylene is 1.5D, and length 95mm, the fineness of water absorbent quick-drying fiber is 2D, and length is
90mm。
3. according to a kind of any described uvioresistant water absorbent quick-drying skin toner of claim 1 or 2, it is characterised in that described anti-
Ultraviolet line fiber selects FeelCool UV Cut uvioresistants, and water absorbent quick-drying fiber selects Cooldry water absorbent quick-drying fibers.
A kind of 4. production technology of uvioresistant water absorbent quick-drying skin toner according to claim 1, it is characterised in that including
Following steps：
(1) dyeing process
80SW mercerized wools dye:Because mercerized wool is by shelling squama processing, blocking performance comparision is poor, and dyeing dyeing speed is very fast,
It is 20 DEG C, 1 DEG C/min of heating rate to play dye temperature selection, and using low temperature dyeing, it is active to receive plain hair from environment-friendly type import orchid
Dyestuff is dyed, and adds 2% N2 low-temp dyeing accelerants, and wool high-temperature dyeing temperature drops to 90 DEG C from 98 DEG C, and after backwashing is to change
Kind feel, add a certain amount of smooth, soft agent, reduce the damage of wool fiber, improves the row yielding and yarn of spinning
Strength feel.
First silk fiber dyeing:Dyed from reactive dye, add a certain amount of N2 low-temp dyeing accelerants, ensure that colouring is uniform
Color fastness, to make the smooth adsorption and diffusion of dye molecule to fibrous inside and carrying out set, prolonged dyeing times were by 90 minutes, after backwashing
Workshop section's emphasis is controlled to water temperature and drying room temperature, 50-60 DEG C of water temperature, 110-120 DEG C of drying room temperature, makes machine bar under fiber soft
Suitable, moisture regain is uniform, is easy to rear road to unclog and readjust；
Uvioresistant fiber：The fiber is the fiber of viscose glue carrier, is dyed using cotton reactive dye, to ensure antiultraviolet fiber
Color fastness, a certain amount of level dyeing bleeding agent is added in dyeing course；
(2) spinning process
Combing chooses greatly gauge so as to reduce the quantity of card nailing neps in fiber using light feed quantity, using light quantitative, small drawing-off, septulum
Process configuration away from, low speed, thickness section and filoplume are reduced, improve the bright and clean uniformity of resultant yarn strand, the configuration of rove main technique：
Thick bar weight：0.16g/m, feed strip substance：0.36g/m, ratch：125mm, it is easy to road spinning efficiency after improving,
Silver mixing and crude oil filling 40mL, the grams m of shaping weight 20,5-8 times of drafting multiple, rear spin use compact spinning, used
The low speeds of 7000r/min；
(3) weaving process
The tension difference between the tension difference and reeled yarn between single thread is strictly controlled during warping, through on-the-spot test single thread
Tension force is in 15CN or so, 1.5 kilograms of beaming tension force, the moderate shaping rounding of beam of a loom even tension elasticity, avoids finished product cloth cover
Occur through shelves and hang through because considering yarn strength, while number is again higher, therefore, 8% is added during warping beaming
The cold slurry agent of HG-106 warp thread, makes yam surface brighter and cleaner, and cohesive force enhancing, wearability improves, and reduces broken end, warping speed 280
Rev/min, small tension receiving coil is used on loom, ensures that weaving is smoothed out；
(4) finishing process
Technological process：→ braying of singing is → bis- to boil → to absorb water → dries → and middle inspection → ripe repaiies and → middle to examine → rolls soft → middle inspection → decatizing
→ KD tanks steaming → finished product；
First singed in raw cloth and carry out surface fine hair processing, the whole pre-treatment of rewetting, allow uvioresistant fiber fully to be absorbed water in hygrometric state,
Fiber relaxation is allowed to open, to play absorbing fast-drying fiber properties, each road is arranged using hydrophilic auxiliary agent, improves the moisture absorption of fabric
Rapid-curing cutback wearability, technological parameter：Rinse:40 DEG C, 15 ', wash at a high speed:280m/min、30′；Crabbing technique：80 DEG C of temperature,
40 ', middle tension force, pressure 1.4, acid adding 400HAC, machine cooling outside, bath raio 1:8th, anti-adding soda ash 0.5%, meanwhile, 2% on overfeeding under
4%th, 3# burners are burnt thoroughly, and machine 152cm is accurately controlled under upper gate width 154cm, and the cloth cover feel and glossiness for making finished product reach
The state optimal to one.
5. the production technology of a kind of uvioresistant water absorbent quick-drying skin toner according to claim 4, it is characterised in that described
The preferably Italian import Azithromycin loom of loom, the most rational technological parameter of use, 315 degree, back rest 1-2 of opening time, loom
Tension force 285N, the emphasis pair warp and weft problem of hanging are controlled, and ensure fabric quality.
6. the production technology of a kind of uvioresistant water absorbent quick-drying skin toner according to claim 4, it is characterised in that described
Uvioresistant fiber selects FeelCool UV Cut uvioresistants, and water absorbent quick-drying fiber selects Cooldry water absorbent quick-drying fibers.