CN107556743A - A kind of high-transparency nylon CPP laminated films - Google Patents
A kind of high-transparency nylon CPP laminated films Download PDFInfo
- Publication number
- CN107556743A CN107556743A CN201711001704.0A CN201711001704A CN107556743A CN 107556743 A CN107556743 A CN 107556743A CN 201711001704 A CN201711001704 A CN 201711001704A CN 107556743 A CN107556743 A CN 107556743A
- Authority
- CN
- China
- Prior art keywords
- parts
- nylon
- cpp
- butyl
- transparency
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-transparency nylon CPP laminated films, by weight, including following raw material components：60 70 parts of nylon, 15 20 parts of CPP resins, 14 20 parts of corundum fine powder, 23 29 parts of glass fibre, 23 parts of gelatin, 14 20 parts of magnesium hypophosphite, di-sec-butyl are to 36 parts of benzene, 37 parts of sepiolite, 9 17 parts of sodium salicylate, 38 parts of kaolin, 10 20 parts of benzoin ethyl ether, 1.2 1.4 parts of butyl titanate, 13 15 parts of tributyl 2-acetylcitrate, 23 parts of diethylene glycol ether acetate alone, 34 parts of glycerine.Nylon composite film prepared by the inventive method improves the transparency of film in the case where not influenceing barrier, so as to improve the visuality of package goods.
Description
Technical field
The present invention relates to CPP film applications, a kind of specific high-transparency nylon-CPP laminated films.
Background technology
In recent years, the functional film packaging material of Devoting Major Efforts To Developing high added value turns into countries in the world plastic package material
Development trend.Functional film generally has a higher technology content, while also with preferable economic benefit and stronger
The market competitiveness, therefore enjoy people to pay close attention to.Current industrialization and significant feature bag in packaging field
Dress film has barrier packaging film, shrink package film, surface protection film, film, antistatic film, the antirust of easily breaking a seal thin
Film, antibacterial film, degradable film etc., functional package film be the important kind of packaging material, often a little particular envelopes
Indispensable material, there is highly important status in plastic package material.Wherein nylon/polyethylene (polypropylene) multilayer
Coex composite membranes (piece) turn into a kind of new packaging material with fastest developing speed in the plastic package material of countries in the world, this
The resistance oxygen that laminated film (piece) has due to it, the function for the steam that blocks water, wrapped in meat product, grain and food, electronic product etc.
Dress field is widely applied.And due to the life of the feature of environmental protection of this production technology, in recent years this kind of laminated film (piece)
Production has also obtained faster development in China.
With the development of the society, higher and higher requirement it is also proposed to the packaging of commodity, the function except requiring packaging
Outside, also require visual good after commodity packaging, people can be accurate, clearly sees the actual state of commodity, especially
High-grade goods.This requires coex composite membranes (piece) with resistance oxygen, outside the function for the steam that blocks water, also to have good
The transparency.
The content of the invention
It is an object of the invention to provide a kind of high-transparency nylon-CPP laminated films.
The purpose of the present invention can be achieved through the following technical solutions：
A kind of high-transparency nylon-CPP laminated films, by weight, including following raw material components：Nylon 60-70 parts,
CPP resin 15-20 parts, corundum fine powder 14-20 parts, glass fibre 23-29 parts, gelatin 2-3 parts, magnesium hypophosphite 14-20 parts, di-secondary
Butyl is to benzene 3-6 parts, sepiolite 3-7 parts, sodium salicylate 9-17 parts, kaolin 3-8 parts, benzoin ethyl ether 10-20 parts, metatitanic acid four
Butyl ester 1.2-1.4 parts, tributyl 2-acetylcitrate 13-15 parts, diethylene glycol ether acetate alone 2-3 parts, glycerine 3-4 parts.
A kind of described high-transparency nylon-CPP laminated films, by weight, including following raw material components：Nylon 65
Part, 18 parts of CPP resins, 20 parts of corundum fine powder, 29 parts of glass fibre, 2 parts of gelatin, 14 parts of magnesium hypophosphite, di-sec-butyl are to benzene 6
Part, 7 parts of sepiolite, 17 parts of sodium salicylate, 8 parts of kaolin, 10 parts of benzoin ethyl ether, 1.4 parts of butyl titanate, acetyl tributyl citrate
13 parts of tributyl, 2 parts of diethylene glycol ether acetate alone, 3 parts of glycerine.
A kind of described high-transparency nylon-CPP laminated films, by weight, including following raw material components：Nylon 65
Part, 20 parts of CPP resins, 16 parts of corundum fine powder, 25 parts of glass fibre, 2 parts of gelatin, 15 parts of magnesium hypophosphite, di-sec-butyl are to benzene 5
Part, 4 parts of sepiolite, 10 parts of sodium salicylate, 6 parts of kaolin, 15 parts of benzoin ethyl ether, 1.3 parts of butyl titanate, acetyl tributyl citrate
14 parts of tributyl, 3 parts of diethylene glycol ether acetate alone, 3 parts of glycerine.
Beneficial effects of the present invention：Nylon composite film prepared by the inventive method carries in the case where not influenceing barrier
The high transparency of film, so as to improve the visuality of package goods.
Embodiment
The present invention is described in further detail with reference to specific embodiment.
Embodiment 1
A kind of high-transparency nylon-CPP laminated films, by weight, including following raw material components：60 parts of nylon, CPP trees
15 parts of fat, 14 parts of corundum fine powder, 23 parts of glass fibre, 2 parts of gelatin, 14 parts of magnesium hypophosphite, di-sec-butyl are to 3 parts of benzene, sepiolite 3
Part, 9 parts of sodium salicylate, 3 parts of kaolin, 10 parts of benzoin ethyl ether, 1.2 parts of butyl titanate, 13 parts of tributyl 2-acetylcitrate,
2 parts of diethylene glycol ether acetate alone, 3 parts of glycerine.
Embodiment 2
A kind of high-transparency nylon-CPP laminated films, by weight, including following raw material components：70 parts of nylon, CPP trees
20 parts of fat, 20 parts of corundum fine powder, 29 parts of glass fibre, 3 parts of gelatin, 20 parts of magnesium hypophosphite, di-sec-butyl are to 6 parts of benzene, sepiolite 7
Part, 17 parts of sodium salicylate, 8 parts of kaolin, 20 parts of benzoin ethyl ether, 1.4 parts of butyl titanate, tributyl 2-acetylcitrate 15
Part, 3 parts of diethylene glycol ether acetate alone, 4 parts of glycerine.
Embodiment 3
A kind of high-transparency nylon-CPP laminated films, by weight, including following raw material components：65 parts of nylon, CPP trees
20 parts of fat, 16 parts of corundum fine powder, 25 parts of glass fibre, 2 parts of gelatin, 15 parts of magnesium hypophosphite, di-sec-butyl are to 5 parts of benzene, sepiolite 4
Part, 10 parts of sodium salicylate, 6 parts of kaolin, 15 parts of benzoin ethyl ether, 1.3 parts of butyl titanate, tributyl 2-acetylcitrate 14
Part, 3 parts of diethylene glycol ether acetate alone, 3 parts of glycerine.
Above content is only citing made for the present invention and explanation, and affiliated those skilled in the art are to being retouched
The specific embodiment stated is made various modifications or supplement or substituted using similar mode, without departing from the design of invention
Or surmount scope defined in the claims, protection scope of the present invention all should be belonged to.
Claims (3)
- A kind of 1. high-transparency nylon-CPP laminated films, it is characterised in that by weight, including following raw material components：Nylon 60-70 parts, CPP resin 15-20 parts, corundum fine powder 14-20 parts, glass fibre 23-29 parts, gelatin 2-3 parts, magnesium hypophosphite 14- 20 parts, di-sec-butyl is to benzene 3-6 parts, sepiolite 3-7 parts, sodium salicylate 9-17 parts, kaolin 3-8 parts, benzoin ethyl ether 10-20 Part, butyl titanate 1.2-1.4 parts, tributyl 2-acetylcitrate 13-15 parts, diethylene glycol ether acetate alone 2-3 parts, glycerine 3-4 parts.
- A kind of 2. high-transparency nylon-CPP laminated films according to claim 1, it is characterised in that by weight, bag Include following raw material components：65 parts of nylon, 18 parts of CPP resins, 20 parts of corundum fine powder, 29 parts of glass fibre, 2 parts of gelatin, hypophosphorous acid 14 parts of magnesium, di-sec-butyl are to 6 parts of benzene, 7 parts of sepiolite, 17 parts of sodium salicylate, 8 parts of kaolin, 10 parts of benzoin ethyl ether, metatitanic acid four 1.4 parts of butyl ester, 13 parts of tributyl 2-acetylcitrate, 2 parts of diethylene glycol ether acetate alone, 3 parts of glycerine.
- A kind of 3. high-transparency nylon-CPP laminated films according to claim 1, it is characterised in that by weight, bag Include following raw material components：65 parts of nylon, 20 parts of CPP resins, 16 parts of corundum fine powder, 25 parts of glass fibre, 2 parts of gelatin, hypophosphorous acid 15 parts of magnesium, di-sec-butyl are to 5 parts of benzene, 4 parts of sepiolite, 10 parts of sodium salicylate, 6 parts of kaolin, 15 parts of benzoin ethyl ether, metatitanic acid four 1.3 parts of butyl ester, 14 parts of tributyl 2-acetylcitrate, 3 parts of diethylene glycol ether acetate alone, 3 parts of glycerine.