CN107556635A - A kind of fill material and its manufacture method for being used to manufacture toilet bottom basin - Google Patents
A kind of fill material and its manufacture method for being used to manufacture toilet bottom basin Download PDFInfo
- Publication number
- CN107556635A CN107556635A CN201710773884.8A CN201710773884A CN107556635A CN 107556635 A CN107556635 A CN 107556635A CN 201710773884 A CN201710773884 A CN 201710773884A CN 107556635 A CN107556635 A CN 107556635A
- Authority
- CN
- China
- Prior art keywords
- manufacture
- fill material
- bottom basin
- polyethers
- polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of fill material and its manufacture method for being used to manufacture toilet bottom basin that can reduce production cost, the fill material includes PU, polyester, polyethers, reinforcing agent and packing material, wherein account for by weight, PU accountings 10% 25%, polyester accounting 3% 15%, polyethers accounting 2% 12%, reinforcing agent is quartz sand and weight accounting is 35% 75%, and packing material includes expandable polystyrene pellet；Its manufacture method, comprises the following steps：A, polyester, polyethers, PU, reinforcing agent and packing material are weighed in proportion；B, the polyester and polyethers weighed step A adds uniform stirring in mixer, is made into the first mixed slurry；C, the reinforcing agent and PU that step A is weighed are added in the first mixed slurry obtained to step B, is then stirred, mixing time is no less than 1 minute, is made into the second mixed slurry；D, packing material is added in the second mixed slurry obtained to step C, then stirred, mixing time is no less than 30 seconds.
Description
【Technical field】
The present invention relates to bathroom field, especially a kind of fill material and its manufacturer for being used to manufacture toilet bottom basin
Method.
【Background technology】
Traditional use in toilet bottom basin, the asking there is slow release toxic monomers during the manufacturing and use
Topic；And when in use because in-between cavity is without enriching, cause that when people steps down in a kind of vacantly sense can be produced above.Pin of the present invention
To it is such the problem of develop and a kind of toxic and harmful gas, and the bottom that bottom is completely substantial do not discharged during the manufacturing
Basin, and expandable polystyrene (EPS) reclaimed materials by one of " white pollution " etc. is used as inserts, carries out recovery profit again
Produced with and applied to bottom basin, both reduced production cost, add way again for the recycling of recyclable material as EPS
Footpath.
【The content of the invention】
The technical problem to be solved in the present invention is to provide a kind of fill material and its manufacture for being used to manufacture toilet bottom basin
Method, benefit of the fill material using new resin compounded system substitution compound glass fiber with unsaturated-resin system as bottom basin
The chemical formulation of strong material, solve to exist during the manufacturing and use asking for slowly release toxic monomers and intermediate void
Topic, meanwhile, production cost is also reduced, is again EPS pellets, waste old pellet and Scrap-FRP, waste and scrap etc. increase
The approach of a recycling is added.
The object of the present invention is achieved like this：
A kind of fill material for being used to manufacture toilet bottom basin, including PU, polyester, polyethers, reinforcing agent and packing material, institute
The weight accounting for stating PU is 10%-25%, and the weight accounting of the polyester is 3%-15%, and the weight accounting of the polyethers is
2%-12%, the reinforcing agent is quartz sand and weight accounting is 35%-75%, and the packing material includes expandability polyphenyl second
Alkene pellet.
A kind of fill material for being used to manufacture toilet bottom basin as described above, the packing material also include waste old
One or more in pellet, Scrap-FRP or waste and scrap.
A kind of fill material for being used to manufacture toilet bottom basin as described above, the PU be PM200 and/or 5005 and/
Or PAPI135C.
A kind of fill material for being used to manufacture toilet bottom basin as described above, the polyester is DH-3380.
A kind of fill material for being used to manufacture toilet bottom basin as described above, the polyethers is ZSN-330.
A kind of fill material for being used to manufacture toilet bottom basin as described above, the mesh number of the quartz sand is 30-80 mesh.
A kind of manufacture method for being used to manufacture the fill material of toilet bottom basin, using fill material as described above, bag
Include following steps：
A, polyester, polyethers, PU, reinforcing agent and packing material are weighed in proportion；
B, the polyester and polyethers weighed step A adds uniform stirring in mixer, is made into the first mixed slurry；
C, the reinforcing agent and PU that step A is weighed are added in the first mixed slurry obtained to step B, then stirring is equal
Even, mixing time is no less than 1 minute, is made into the second mixed slurry；
D, packing material is added in the second mixed slurry obtained to step C, then stirred, mixing time is no less than
30 seconds.
Compared with prior art, the present invention has following features：
1st, bottom basin fill material polymerize to form cross-linked structure based on PU with polyester, polyethers so that the knot of product
Structure is stable to be enriched, and is not susceptible to deformation；
2nd, toxic and harmful gas is not discharged during manufacturing, and by the expandability polyphenyl second of one of " white pollution "
Alkene (EPS) reclaimed materials etc. is used as inserts, is recycled again, both reduces production cost, is as EPS, waste and old rubber again
The recycling of the waste and scraps such as micelle material, Scrap-FRP adds approach；
3rd, the reinforcing agent that the present invention uses is the quartz sand of 30-80 mesh, and the use of quartz sand enhances the structural capacity of bottom basin
And intensity, and cause bottom basin to have fire prevention high temperature-proof ability to a certain extent；
4th, present invention green, environmental protection, operating procedure is simple, and raw material is easy to get, is cheap, is applicable most of filled-type bottom basin
Industrialized production.
【Embodiment】
A kind of manufacture method for being used to manufacture the fill material of toilet bottom basin：
A, polyester, polyethers, PU, reinforcing agent and packing material are weighed in proportion, wherein, PU is PAPI135C and weight accounting
For 25%, polyester is DH-3380 and weight accounting is 3%, and polyethers is ZSN-330 and weight accounting is 2%, and reinforcing agent is 30 mesh
Quartz sand and weight accounting be 35%, packing material is expandable polystyrene and weight accounting is 35%；
B, the polyester and polyethers weighed step A adds uniform stirring in mixer, is made into the first mixed slurry；
C, reinforcing agent and PU that step A is weighed at the uniform velocity are added in the first mixed slurry obtained to step B, then uniformly
Stirring 1 minute, is made into the second mixed slurry；
D, packing material is at the uniform velocity added in the second mixed slurry obtained to step C, then uniform stirring 30 seconds, obtains
Three mixed slurries, the 3rd mixed slurry is poured into and put well in the thick stick mould of bottom basin shell, uniformly scratched slurry with mud guard
Everywhere, compacting, cover mold pressurization, pressure process continues 2h to be stripped bottom basin, and toilet bottom basin is made in mould.
If it is worth noting that, the PAPI135C weight accounting 10% weighed in step A, DH-3380 weight accounting 15%,
ZSN-330 weight accounting 12%, quartz sand weight accounting are 55%, expandable polystyrene weight accounting 8%, can also reach phase
The effect answered.
Claims (7)
1. a kind of fill material for being used to manufacture toilet bottom basin, it is characterised in that including PU, polyester, polyethers, reinforcing agent and fill out
Fill material, the weight accounting of the PU is 10%-25%, and the weight accounting of the polyester is 3%-15%, the weight of the polyethers
Amount accounting is 2%-12%, and the reinforcing agent is quartz sand and weight accounting is 35%-75%, and the packing material includes sending out
Property polystyrene pellets.
A kind of 2. fill material for being used to manufacture toilet bottom basin according to claim 1, it is characterised in that the filling
Material also includes waste old pellet and/or Scrap-FRP.
A kind of 3. fill material for being used to manufacture toilet bottom basin according to claim 1 or 2, it is characterised in that the PU
For PM200 and/or 5005 and/or PAPI135C.
4. a kind of fill material for being used to manufacture toilet bottom basin according to claim 1 or 2, it is characterised in that described poly-
Ester is DH-3380.
5. a kind of fill material for being used to manufacture toilet bottom basin according to claim 1 or 2, it is characterised in that described poly-
Ether is ZSN-330.
A kind of 6. fill material for being used to manufacture toilet bottom basin according to claim 1 or 2, it is characterised in that the stone
The mesh number of sand is 30-80 mesh.
A kind of 7. manufacture method for being used to manufacture the fill material of toilet bottom basin, using the filling as described in claim 1 to 6
Material, it is characterised in that comprise the following steps：
A, polyester, polyethers, PU, reinforcing agent and packing material are weighed in proportion；
B, the polyester and polyethers weighed step A adds uniform stirring in mixer, is made into the first mixed slurry；
C, the reinforcing agent and PU that step A is weighed are added in the first mixed slurry obtained to step B, then stirs, stirs
The time is mixed no less than 1 minute, is made into the second mixed slurry；
D, packing material is added in the second mixed slurry obtained to step C, then stirred, mixing time is no less than 30
Second.