CN107554015A - A kind of medicine and food packaging BOPP metallized films and preparation method thereof - Google Patents
A kind of medicine and food packaging BOPP metallized films and preparation method thereof Download PDFInfo
- Publication number
- CN107554015A CN107554015A CN201610506701.1A CN201610506701A CN107554015A CN 107554015 A CN107554015 A CN 107554015A CN 201610506701 A CN201610506701 A CN 201610506701A CN 107554015 A CN107554015 A CN 107554015A
- Authority
- CN
- China
- Prior art keywords
- bopp
- heat
- preparation
- film
- medicine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of medicine and food packaging BOPP metallized films and preparation method thereof.The preparation method comprises the following steps:Sided corona treatment is first carried out on the heat-sealing skin surface of heat-sealing type BOPP film, then carries out corona treatment;Traction winding;Ageing Treatment;Cutting;It is vacuum aluminum-coated.BOPP metallized films have high obstructing performance made from this method, moisture-vapor transmission≤0.2g/ (m in the case of 38 DEG C, 90% relative humidity224h), OTR oxygen transmission rate≤25cm3/(m2·24h);Heat seal strength >=3.0N/15mm of obtained BOPP aluminizers heat cover, play envelope temperature≤115 DEG C.BOPP metallized films made from this method can reach composite flexible pouch and label printing industry standard and the professional standards of YY0236 1996, the packaging material available for fields such as the medicine with high-barrier packing instructions and food simultaneously.
Description
Technical field
The present invention relates to composite soft packaging and the production technical field of label printing industry, more particularly to a kind of medicine and food
Product are packed for BOPP metallized films and preparation method thereof.
Background technology
At present, film base material of being aluminized in the market composite soft packaging and label printing industry often chooses PET (poly terephthalic acids
Glycol ester) and BOPP (bidirectional stretching polypropylene film).Wherein, BOPP has light, inexpensive, nontoxic, moistureproof, printing performance
Well, mist degree is low and decorates the advantages that functional and attention.High-barrier type BOPP base material metallized films are polypropylene films
The high-end product of middle newer type, at present China energy higher to performance requirements such as barrier, adhesive strength of aluminizing, heat-seal strengths
It is few to produce the enterprise of this product, and then larger to its demand both at home and abroad, domestic substantial amounts of high-barrier type BOPP base materials plating
The demand almost all of aluminium film relies on import to meet.
In the market extensively production and application BOPP aluminizers, be that conventional BOPP is process through aluminizing, but its plate
Aluminium lamination fastness with 3M-610 adhesive tapes avulsion detection thing can only achieve it is 85%~90% not de- (i.e. avulsion dealuminzation rate up to 10%~
15%) (3M-610 adhesive tapes are to meet national sector standard to level:Be packed in metallized film BB/T0030-2004
6.12.1 the transparent BOPP pressure-sensitive tapes that peel strength is 2.0N/cm in bar), also it is not reaching to composite flexible pouch and label
Peel strength between internal layer and secondary internal layer after requirement of the printing industry to BOPP aluminizers, i.e. polyester aluminizer and other materials are compound
>=1.0N/15mm (national pharmaceuticals industry standards:4.4th article of regulation in composite membrane for packaging medicine YY0236-1996) water
It is flat to differ greatly.After BOPP aluminizers and other materials common at present is compound, aluminium coated and time outer interlaminar strength are basic
On all≤0.5N/15mm so that BOPP aluminizers purposes and use range are extremely limited.
The content of the invention
The technical problems to be solved by the invention are to overcome existing BOPP aluminizers to be difficult to reach composite flexible pouch
And requirement of the label printing industry to BOPP aluminizers, aluminium coated are substantially all≤0.5N/15mm with time outer interlaminar strength,
It is far apart with national pharmaceuticals industry standard YY0236-1996, the defects of medicine and packaging for foodstuff etc. can not be applied to, there is provided one
Kind medicine and food packaging BOPP metallized films and preparation method thereof.The medicine and food packaging BOPP of the present invention is aluminized thin
Film has excellent barrier property, aluminium lamination attachment fastness height and even compact, good stability of the dimension, the coefficient of friction in non-face of aluminizing
It is small, and the medicine of the present invention and food packaging BOPP metallized films have low envelope temperature and high heat-sealing strength, can be used for
The packaging material in the fields such as food and medicine with high-barrier packing instructions.The medicine of the present invention and food packaging BOPP platings
The medicine of excellent quality can be made by selection and the optimization of processing technology to raw material and formula in the preparation method of aluminium film
Product and food packaging BOPP metallized films, client is disclosure satisfy that to shallow reticulated printing adaptability and the particular/special requirement of combination process,
Printing, compound rear barrier are substantially unattenuated, and the preparation method is produced in batches suitable for industrialization.
The present invention solves above-mentioned technical problem by the following technical programs.
The invention provides the preparation method of a kind of medicine and food packaging BOPP metallized films, and it includes following steps
Suddenly:
(1) sided corona treatment is carried out to the heat-sealing skin surfaces of heat-sealing type BOPP base films, the electricity during sided corona treatment
Pole tension is 6.0~10.0kV, and the intensity of the sided corona treatment is 40~45dym/cm, the heat-sealing type BOPP base films
Temperature is 25~40 DEG C, and line speed is 155~185m/min;
(2) plasma treatment, the ginseng of the plasma treatment are carried out to the heat-sealing type BOPP base films through sided corona treatment
Number and condition are as follows:Power is 300~3000W, and operating pressure is 15~35Pa, and the linear velocity of heat-sealing type BOPP base films is
5~25m/min;
(3) plasma treated heat-sealing type BOPP base films are drawn into winding;
(4) Ageing Treatment is carried out to the heat-sealing type BOPP base films after winding, obtains BOPP film;The Ageing Treatment is
Placed 48~72 hours at 25~35 DEG C;
(5) BOPP film is cut;
(6) evaporation boat of vacuum aluminum-plating equipment is preheated to the 70%~93% of equipment setting, aluminium wire transfer rate is 350
~1400mm/min, after equipment winding speed to 3.5~7.5m/s, the BOPP film is carried out it is vacuum aluminum-coated, it is vacuum aluminum-coated
After produce.
In step (1), the heat-sealing type BOPP base films can be the conventional heat-sealing type BOPP base films in this area, its
With a heat-sealing top layer and a sandwich layer.The heat-sealing type BOPP base films are preferably using double-layer coextrusion and biaxial tension
The co-extrusion BOPP film that production technology obtains, the structure of the co-extrusion BOPP film are followed successively by sandwich layer and heat-sealing top layer.In this hair
In a bright better embodiment, PP raw materials used are to be copolymerized PP top layers heat-sealing material in the heat-sealing top layer, in the sandwich layer
PP raw materials used are biaxial tension level and a grade homopolymerization PP of aluminizing.
In step (1), the sided corona treatment causes the surface of the heat-sealing type BOPP base films to form oxidation polarization base,
Make heat-sealing type BOPP base films surface polarization, be easy to improve the printing color of heat-sealing type BOPP base films and compound
When Adhesion property.
In step (3), the method and condition of the winding can be this area conventional method and condition, generally clearance-type
Winding or contact winding, also can use the production line for possessing both winding modes to be wound.
In step (5), the method and condition of the cutting can be this area conventional method and condition.The cutting is general
The cutting machine being integrated using the center that has concurrently, surface drive is carried out.It is preferred that the setup parameter during cutting is as follows:Temperature
For 20~38 DEG C, it is 120~130N/m that BOPP film cutting, which starts initial tension setting value, and former pressure set points are 50~90N/m,
Former wrinkle and strip length are 1500~2800m, and amendment backward pull setting value is 80~160N/m, and pressure set points are after revision
56~66N/m, wrinkle and strip length are 250~400m after revision;Film thickness is less than the 20 μm sides for selecting thickness 0.2mm
Blade, film thickness are 20~35 μm of square blades from thickness 0.4mm, and film thickness is more than 35 μm and selects circular knife, with life
Output meets the product of different user requirement.
In step (6), the vacuum aluminum-coated method and other conditions can be this area conventional method and condition.It is described
Vacuum aluminum-coated vacuum is preferably 10-3~10-5Pa。
Present invention also offers a kind of medicine as obtained by above-mentioned preparation method and food packaging BOPP metallized films.
In the present invention, the medicine and food packaging BOPP metallized films include an aluminium lamination, a plating aluminum surface layer, one successively
Sandwich layer and a heat-sealing top layer.It is preferred that PP raw materials used in the plating aluminum surface layer are copolymerized PP, the heat-sealing top layer for level of aluminizing
In used PP raw materials be copolymerization PP top layers heat-sealing material, in the sandwich layer PP raw materials used for biaxial tension level and level of aluminizing it is equal
Poly- PP.
In the present invention, described medicine and food packaging BOPP metallized films are in the case of 38 DEG C, 90% relative humidity
Moisture-vapor transmission≤0.2g/ (m224h), OTR oxygen transmission rate≤25cm3/(m2·24h);Described high-barrier BOPP aluminizes
Heat seal strength >=3.0N/15mm of the heat cover of film, play envelope temperature≤115 DEG C.
It on the basis of common sense in the field is met, above-mentioned each optimum condition, can be combined, it is each preferably real to produce the present invention
Example.
Agents useful for same and raw material of the present invention are commercially available.
The positive effect of the present invention is:
(1) of the invention medicine and food packaging BOPP metallized films have excellent barrier property, 38 DEG C, 90%
Moisture-vapor transmission≤0.2g/ (m in the case of relative humidity224h), OTR oxygen transmission rate≤25cm3/(m2·24h)。
(2) of the invention medicine and food packaging BOPP metallized films have a good aluminium lamination attachment fastness, and aluminium lamination is equal
Even densification.
(3) medicine and food packaging BOPP metallized films of the invention have low envelope temperature, high heat-sealing strength, heat-sealing
Intensity reaches 3N/15mm, plays envelope temperature and is less than 118 DEG C.
(4) good stability of the dimension of medicine of the invention and food packaging BOPP metallized films, the friction in non-face of aluminizing
Coefficient is smaller.
(5) medicine of the invention and food packaging BOPP metallized films are in thickness of coating, uniformity, fastness, winding etc.
Aspect has high quality and high stability.
(6) preparation method of medicine of the invention and food packaging BOPP metallized films by the selections of raw material, match somebody with somebody
Side and the optimization of processing technology, it disclosure satisfy that client to shallow reticulated printing adaptability and the particular/special requirement of combination process, prints, be compound
Barrier is substantially unattenuated afterwards.
(7) medicine and food packaging BOPP base materials aluminizer of the invention can increase China's plastics package high technology content
Product proportion, be advantageous to improve industry product structure, also, high-end BOPP products can not only turn into the one of plastics package enterprise
Individual new profit growth point, import substitutes, can also export goods and earn foreign currency, while can improve the technology of China's PP film industries
Level, economic benefit and social benefit are notable.
Embodiment
The present invention is further illustrated below by the mode of embodiment, but does not therefore limit the present invention to described reality
Apply among a scope.The experimental method of unreceipted actual conditions in the following example, conventionally and condition, or according to business
Product specification selects.
In following embodiments, heat-sealing type BOPP base films used are produced by multi-layer co-extruded technology and obtained, and it has single
The heat-sealing top layer of face heat sealability and BOPP base films sandwich layer (BOPP originals film is purchased from Hubei Si Hong materials Science and Technology Ltd.,
BOPP aluminium plating basement membranes, model:VD-3).
Embodiment 1
A kind of preparation method of medicine and food packaging BOPP metallized films:
(1) sided corona treatment:Sided corona treatment is carried out in the heat-sealing skin surface of heat-sealing type BOPP base films, its heat cover
Heat seal strength >=3.0N/15mm, heat-sealing type BOPP base films are by between 8.0KV two electrodes, sided corona treatment intensity is
40dym/cm, film temperature are 35 DEG C, line speed 170m/min;
(2) plasma treatment:Plasma treatment power 1200W is set, working gas is oxygen, operating pressure 25Pa,
The linear velocity of heat-sealing type BOPP base films is 15m/min;
(3) traction winding:Winding is carried out on winder, is wound using clearance-type;
(4) Ageing Treatment:Heat-sealing type BOPP base films after winding place 60h at a temperature of 35 DEG C, obtain BOPP film;
(5) cut:The cutting machine being integrated using the center that has concurrently, surface drive, temperature are 28 DEG C, and BOPP film cutting is opened
Dynamic initial tension setting value is 125N/m, and former pressure set points are 60N/m, and former wrinkle and strip length are 1800m, corrects backward pull
Setting value is 120N/m, and pressure set points are 60N/m after revision, and wrinkle and strip length are 320m after revision, and film thickness is
More than 35 μm are selected circular knife;
(6) it is vacuum aluminum-coated:BOPP film is inserted into plastic sheeting vacuum aluminum-plating equipment, and (equipment is purchased from German Lay treasured photoelectricity skill
Art Co., Ltd, the type packaging material web coating systems of PRO-M 2100), vacuumize and reach high vacuum levels (10-4Pa), will steam
Hair boat, which is opened, to be preheated between 90% (equipment setting), is then turned on aluminium wire transmission (speed control is in 900mm/min), is started and set
The standby speed that is wound to starts to be deposited after 4.5m/s, to open equipment baffle plate, and aluminium steam condenses to the main surface of drawing a bow to the full of cooling and do not stop to wind
BOPP film surface, produced after vacuum aluminum-coated.
The present embodiment product 3M-610 adhesive tape tests, avulsion dealuminzation rate≤1%.
The present embodiment product is through national pharmaceuticals industry standard:The 4.4th article in composite membrane for packaging medicine YY0236-1996
Regulation assay method measures, heat seal strength >=3.0N/15mm of the heat cover of BOPP metallized films, plays envelope temperature≤115 DEG C, medicine
Product and food packaging BOPP metallized films moisture-vapor transmission≤0.2g/ (m in the case of 38 DEG C, 90% relative humidity2·
24h), OTR oxygen transmission rate≤25cm3/(m2·24h)。
Embodiment 2
A kind of preparation method of medicine and food packaging BOPP metallized films:
(1) sided corona treatment:Sided corona treatment is carried out in the heat-sealing skin surface of heat-sealing type BOPP base films, its heat cover
Heat seal strength >=3.5N/15mm, heat-sealing type BOPP base films are by between 7.5KV two electrodes, sided corona treatment intensity is
45dym/cm, film temperature are 30 DEG C, line speed 165m/min;
(2) plasma treatment:Plasma treatment power 1000W is set, working gas is oxygen, operating pressure 35Pa,
The linear velocity of heat-sealing type BOPP base films is 10m/min;
(3) traction winding:Winding is carried out on winder, is wound using clearance-type;
(4) Ageing Treatment:Heat-sealing type BOPP base films after winding place 72h at a temperature of 30 DEG C, obtain BOPP film;
(5) cut:The cutting machine being integrated using the center that has concurrently, surface drive, temperature are 35 DEG C, and BOPP film cutting is opened
Dynamic initial tension setting value is 130N/m, and former pressure set points are 60N/m, and former wrinkle and strip length are 2000m, corrects backward pull
Setting value is 140N/m, and pressure set points are 65N/m after revision, and wrinkle and strip length are 380m after revision, and film thickness is
20~35 μm of square blades from thickness 0.4mm;
(6) it is vacuum aluminum-coated:BOPP film is inserted into plastic sheeting vacuum aluminum-plating equipment, and (equipment is purchased from German Lay treasured photoelectricity skill
Art Co., Ltd, the type packaging material web coating systems of PRO-M 2100), vacuumize and reach high vacuum levels (10-3Pa), will steam
Hair boat, which is opened, to be preheated between 89% (equipment setting), is then turned on aluminium wire transmission (speed control is in 750mm/min), is started and set
The standby speed that is wound to starts to be deposited after 4.5m/s, to open equipment baffle plate, and aluminium steam condenses to the main surface of drawing a bow to the full of cooling and do not stop to wind
BOPP film surface, produced after vacuum aluminum-coated.
The present embodiment product 3M-610 adhesive tape tests, avulsion dealuminzation rate≤1.2%.
The present embodiment product is through national pharmaceuticals industry standard:The 4.4th article in composite membrane for packaging medicine YY0236-1996
Regulation assay method measures, heat seal strength >=3.5N/15mm of the heat cover of BOPP metallized films, plays envelope temperature≤115 DEG C, medicine
Product and food packaging BOPP metallized films moisture-vapor transmission≤0.2g/ (m in the case of 38 DEG C, 90% relative humidity2·
24h), OTR oxygen transmission rate≤25cm3/(m2·24h)。
Embodiment 3
A kind of preparation method of medicine and food packaging BOPP metallized films:
(1) sided corona treatment:Sided corona treatment is carried out in the heat-sealing skin surface of heat-sealing type BOPP base films, its heat cover
Heat seal strength >=4.0N/15mm, heat-sealing type BOPP base films are by between 8.5KV two electrodes, sided corona treatment intensity is
45dym/cm, film temperature are 35 DEG C, line speed 180m/min;
(2) plasma treatment:Plasma treatment power 1400W is set, working gas is oxygen, operating pressure 45Pa,
The linear velocity of heat-sealing type BOPP base films is 20m/min;
(3) traction winding:Winding is carried out on winder, is wound using contact;
(4) Ageing Treatment:Heat-sealing type BOPP base films after winding place 48h at a temperature of 35 DEG C, obtain BOPP film;
(5) cut:The cutting machine being integrated using the center that has concurrently, surface drive, temperature are 38 DEG C, and BOPP film cutting is opened
Dynamic initial tension setting value is 125N/m, and former pressure set points are 60N/m, and former wrinkle and strip length are 2500m, corrects backward pull
Setting value is 150N/m, and pressure set points are 65N/m after revision, and wrinkle and strip length are 390m after revision, and film thickness is
20~35 μm of square blades from thickness 0.4mm;
(6) it is vacuum aluminum-coated:BOPP film is inserted into plastic sheeting vacuum aluminum-plating equipment, and (equipment is purchased from German Lay treasured photoelectricity skill
Art Co., Ltd, the type packaging material web coating systems of PRO-M 2100), vacuumize and reach high vacuum levels (10-5Pa), will steam
Hair boat, which is opened, to be preheated between 80% (equipment setting), is then turned on aluminium wire transmission (speed control is in 1100mm/min), is started
Equipment is wound to speed and starts to be deposited after 4.5m/s, to open equipment baffle plate, and aluminium steam condenses to the main surface of drawing a bow to the full of cooling and do not stop to roll up
Around BOPP film surface, produced after vacuum aluminum-coated.
The present embodiment product 3M-610 adhesive tape tests, avulsion dealuminzation rate≤1.5%.
The present embodiment product is through national pharmaceuticals industry standard:The 4.4th article in composite membrane for packaging medicine YY0236-1996
Regulation assay method measures, heat seal strength >=4.0N/15mm of the heat cover of BOPP metallized films, plays envelope temperature≤115 DEG C, medicine
Product and food packaging BOPP metallized films moisture-vapor transmission≤0.2g/ (m in the case of 38 DEG C, 90% relative humidity2·
24h), OTR oxygen transmission rate≤25cm3/(m2·24h)。
Embodiment 4
A kind of preparation method of medicine and food packaging BOPP metallized films:
(1) sided corona treatment:Sided corona treatment is carried out in the heat-sealing skin surface of heat-sealing type BOPP base films, its heat cover
Heat seal strength >=4.5N/15mm, heat-sealing type BOPP base films are by between 8.0KV two electrodes, sided corona treatment intensity is
45dym/cm, film temperature are 40 DEG C, line speed 185m/min;
(2) plasma treatment:Plasma treatment power 2000W is set, working gas is oxygen, operating pressure 50Pa,
The linear velocity of heat-sealing type BOPP base films is 25m/min;
(3) traction winding:Winding is carried out on winder, is wound using contact;
(4) Ageing Treatment:Heat-sealing type BOPP base films after winding place 60h at a temperature of 30 DEG C, obtain BOPP film;
(5) cut:The cutting machine being integrated using the center that has concurrently, surface drive, temperature are 38 DEG C, and BOPP film cutting is opened
Dynamic initial tension setting value is 130N/m, and former pressure set points are 60N/m, and former wrinkle and strip length are 2800m, corrects backward pull
Setting value is 160N/m, and pressure set points are 66N/m after revision, and wrinkle and strip length are 400m after revision, and film thickness is
20~35 μm of square blades from thickness 0.4mm;
(6) it is vacuum aluminum-coated:BOPP film is inserted into plastic sheeting vacuum aluminum-plating equipment, and (equipment is purchased from German Lay treasured photoelectricity skill
Art Co., Ltd, the type packaging material web coating systems of PRO-M 2100), vacuumize and reach high vacuum levels (10-5Pa), will steam
Hair boat, which is opened, to be preheated between 93% (equipment setting), is then turned on aluminium wire transmission (speed control is in 1400mm/min), is started
Equipment is wound to speed and starts to be deposited after 5.5m/s, to open equipment baffle plate, and aluminium steam condenses to the main surface of drawing a bow to the full of cooling and do not stop to roll up
Around BOPP film surface, produced after vacuum aluminum-coated.
The present embodiment product 3M-610 adhesive tape tests, avulsion dealuminzation rate≤1.5%.
The present embodiment product is through national pharmaceuticals industry standard:The 4.4th article in composite membrane for packaging medicine YY0236-1996
Regulation assay method measures, heat seal strength >=4.5N/15mm of the heat cover of BOPP metallized films, plays envelope temperature≤115 DEG C, medicine
Product and food packaging BOPP metallized films moisture-vapor transmission≤0.2g/ (m in the case of 38 DEG C, 90% relative humidity2·
24h), OTR oxygen transmission rate≤25cm3/(m2·24h)。
Comparative example 1
Prepare a kind of medicine and food packaging BOPP metallized films:Without sided corona treatment, but other conditions are the same as real
Apply example 1.
After testing, its aluminium coated fastness is generally less than the aluminium coated fastness 10% of embodiment 1 to obtained BOPP aluminizers product
More than, obtained BOPP aluminizers product 3M-610 adhesive tape tests, avulsion dealuminzation rate≤89%.Obtained BOPP aluminizers production
Product are through national pharmaceuticals industry standard:The 4.4th article of regulation assay method measures in composite membrane for packaging medicine YY0236-1996,
Heat seal strength >=2.5N/15mm of heat-sealing type BOPP film heat cover, play envelope temperature≤115 DEG C, high barrier aluminum-plating type BOPP base materials
Film moisture-vapor transmission≤2.0g/ (m in the case of 38 DEG C, 90% relative humidity224h), OTR oxygen transmission rate≤225cm3/
(m2·24h)。
Comparative example 2
Prepare a kind of medicine and food packaging BOPP metallized films:Without corona treatment, but other conditions
With embodiment 1.
Obtained BOPP aluminizers product after testing, its aluminium coated fastness generally less than the aluminium coated fastness 8% of embodiment 1 with
On, obtained BOPP aluminizers product 3M-610 adhesive tape tests, avulsion dealuminzation rate≤91%.Obtained BOPP aluminizers product
Through national pharmaceuticals industry standard:The 4.4th article of regulation assay method measures in composite membrane for packaging medicine YY0236-1996, heat
Heat seal strength >=2.5N/15mm of envelope type BOPP film heat cover, plays envelope temperature≤115 DEG C, and high barrier aluminum-plating type BOPP base materials are thin
Film moisture-vapor transmission≤0.75g/ (m in the case of 38 DEG C, 90% relative humidity224h), OTR oxygen transmission rate≤75cm3/
(m2·24h)。
Comparative example 3
Prepare a kind of medicine and food packaging BOPP metallized films:Without Wetted constructures, but other conditions are the same as real
Apply example 1.
Obtained BOPP aluminizers product after testing, its aluminium coated fastness generally less than the aluminium coated fastness 6% of embodiment 1 with
On, obtained BOPP aluminizers product 3M-610 adhesive tape tests, avulsion dealuminzation rate≤93%.Obtained BOPP aluminizers product
Through national pharmaceuticals industry standard:The 4.4th article of regulation assay method measures in composite membrane for packaging medicine YY0236-1996, heat
Heat seal strength >=2.5N/15mm of envelope type BOPP film heat cover, plays envelope temperature≤115 DEG C, and high barrier aluminum-plating type BOPP base materials are thin
Film moisture-vapor transmission≤0.5g/ (m in the case of 38 DEG C, 90% relative humidity224h), OTR oxygen transmission rate≤55cm3/
(m2·24h)。
The foregoing examples are merely illustrative of the technical concept and features of the invention, its object is to allow the person skilled in the art to be
Present disclosure can be understood and implemented according to this, it is not intended to limit the scope of the present invention.It is all smart according to the present invention
The equivalent transformation or modification that refreshing essence is done, should all be included within the scope of the present invention.
Claims (8)
1. the preparation method of a kind of medicine and food packaging BOPP metallized films, it is characterised in that it comprises the steps:
(1) sided corona treatment is carried out to the heat-sealing skin surfaces of heat-sealing type BOPP base films, the electrode electricity during sided corona treatment
Press as 6.0~10.0kV, the intensity of the sided corona treatment is 40~45dym/cm, the temperature of the heat-sealing type BOPP base films
For 25~40 DEG C, line speed is 155~185m/min;
(2) to through sided corona treatment heat-sealing type BOPP base films carry out plasma treatment, the parameter of the plasma treatment and
Condition is as follows:Power is 300~3000W, and operating pressure is 15~35Pa, the linear velocities of heat-sealing type BOPP base films for 5~
25m/min;
(3) plasma treated heat-sealing type BOPP base films are drawn into winding;
(4) Ageing Treatment is carried out to the heat-sealing type BOPP base films after winding, obtains BOPP film;The Ageing Treatment is 25
Placed 48~72 hours at~35 DEG C;
(5) BOPP film is cut;
(6) by the evaporation boat of vacuum aluminum-plating equipment be preheated to equipment setting 70%~93%, aluminium wire transfer rate be 350~
1400mm/min, after equipment winding speed to 3.5~7.5m/s, the BOPP film is carried out it is vacuum aluminum-coated, after vacuum aluminum-coated
Produce.
2. preparation method as claimed in claim 1, it is characterised in that in step (1), the heat-sealing type BOPP base films are
The co-extrusion BOPP film obtained using the production technology of double-layer coextrusion and biaxial tension.
3. preparation method as claimed in claim 2, it is characterised in that in step (1), the structure of the co-extrusion BOPP film is
Sandwich layer and heat-sealing top layer, the PP raw materials sealed used in top layer are that the heat-sealing of copolymerization PP top layers is expected, used in the sandwich layer
PP raw materials are biaxial tension level and a grade homopolymerization PP of aluminizing.
4. preparation method as claimed in claim 1, it is characterised in that in step (3), the winding winds or connect for clearance-type
Touch is wound.
5. preparation method as claimed in claim 1, it is characterised in that in step (5), the cutting, which uses, has center, table concurrently
The cutting machine that face driving is integrated is carried out.
6. preparation method as claimed in claim 5, it is characterised in that in step (5), the setup parameter during cutting is such as
Under:Temperature is 20~38 DEG C, and it is 120~130N/m that BOPP film cutting, which starts initial tension setting value, and former pressure set points are 50
~90N/m, former wrinkle and strip length are 1500~2800m, and amendment backward pull setting value is 80~160N/m, pressure after revision
Setting value is 56~66N/m, and wrinkle and strip length are 250~400m after revision;Film thickness is less than 20 μm and selects thickness
0.2mm square blade, film thickness are 20~35 μm of square blades from thickness 0.4mm, and film thickness is more than 35 μm from circle
Blade.
7. preparation method as claimed in claim 1, it is characterised in that in step (6), the vacuum aluminum-coated vacuum is 10-3~10-5Pa。
8. a kind of medicine as obtained by the preparation method as described in any one of claim 1~7 and food packaging BOPP aluminize
Film.