CN107513650A - Intelligent atomizer metal mesh sheet - Google Patents
Intelligent atomizer metal mesh sheet Download PDFInfo
- Publication number
- CN107513650A CN107513650A CN201710784194.2A CN201710784194A CN107513650A CN 107513650 A CN107513650 A CN 107513650A CN 201710784194 A CN201710784194 A CN 201710784194A CN 107513650 A CN107513650 A CN 107513650A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass fraction
- metal mesh
- mesh sheet
- intelligent atomizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses intelligent atomizer metal mesh sheet, its raw material composition is:Aluminium-manganese glass powder:34 parts;Magnesium:10 16 parts;Zirconium:12 parts;Binding agent:1 1.5 parts;Nickel:46 parts;Hafnium:1 1.5 parts;Titanium alloy:1.5 2.5 parts;Chromium:35 parts;Cosolvent:1.5 2.5 parts;Above-mentioned number is mass fraction.It is preferred that the aluminium-manganese glass powder is 3.5 parts, number is mass fraction.It is preferred that the magnesium is 14 parts, number is mass fraction.It is preferred that the titanium alloy is 2 parts, number is mass fraction.The beneficial effects of the invention are as follows:Using the formula of complexity, service life is improved, service life surpasses 3000 hours, reduces and changes number.
Description
Technical field
The present invention relates to a kind of intelligent atomizer metal mesh sheet.
Background technology
Atomizing piece is the significant components of intelligent atomizer, and it is made up of metal mesh sheet and piezoelectric ceramics, existing metal
Mesh sheet, service life about 3000 hours, it is necessary to be changed after long-time use, service life need to be improved.
The content of the invention
In view of the above-mentioned problems, the present invention provides intelligent atomizer metal mesh sheet, using the formula of complexity, improve and use
In the life-span, reduce and change number.
To realize above-mentioned technical purpose and the technique effect, the present invention is achieved through the following technical solutions:
Intelligent atomizer metal mesh sheet, its raw material composition are:
Aluminium-manganese glass powder:3-4 parts;
Magnesium:10-16 parts;
Zirconium:1-2 parts;
Binding agent:1-1.5 part;
Nickel:4-6 parts;
Hafnium:1-1.5 part;
Titanium alloy:1.5-2.5 part;
Chromium:3-5 parts;
Cosolvent:1.5-2.5 part;
Above-mentioned number is mass fraction.
It is preferred that the aluminium-manganese glass powder is 3.5 parts, number is mass fraction.
It is preferred that the magnesium is 14 parts, number is mass fraction.
It is preferred that the titanium alloy is 2 parts, number is mass fraction.
It is preferred that the chromium is 4 parts, number is mass fraction.
It is preferred that the hafnium is 1 part, number is mass fraction.
The beneficial effects of the invention are as follows:Using the formula of complexity, service life is improved, service life surpasses 3000 hours, subtracted
Number is changed less.
Embodiment
Technical solution of the present invention is described in further detail with reference to specific embodiment, so that the skill of this area
Art personnel can be better understood from the present invention and can be practiced, but illustrated embodiment is not as a limitation of the invention.
Intelligent atomizer metal mesh sheet, its raw material composition are:
Aluminium-manganese glass powder:3-4 parts;
Magnesium:10-16 parts;
Zirconium:1-2 parts;
Binding agent:1-1.5 part;
Nickel:4-6 parts;
Hafnium:1-1.5 part;
Titanium alloy:1.5-2.5 part;
Chromium:3-5 parts;
Cosolvent:1.5-2.5 part;
Above-mentioned number is mass fraction.
It is preferred that the aluminium-manganese glass powder is 3.5 parts, number is mass fraction.
It is preferred that the magnesium is 14 parts, number is mass fraction.
It is preferred that the titanium alloy is 2 parts, number is mass fraction.
It is preferred that the chromium is 4 parts, number is mass fraction.
It is preferred that the hafnium is 1 part, number is mass fraction.
The beneficial effects of the invention are as follows:Using the formula of complexity, service life is improved, service life surpasses 3000 hours, subtracted
Number is changed less.
The preferred embodiments of the present invention are these are only, are not intended to limit the scope of the invention, it is every to utilize this hair
The equivalent structure that bright description is made either equivalent flow conversion or is directly or indirectly used in other related technologies
Field, it is included within the scope of the present invention.
Claims (6)
1. intelligent atomizer metal mesh sheet, it is characterised in that its raw material, which forms, is:
Aluminium-manganese glass powder:3-4 parts;
Magnesium:10-16 parts;
Zirconium:1-2 parts;
Binding agent:1-1.5 part;
Nickel:4-6 parts;
Hafnium:1-1.5 part;
Titanium alloy:1.5-2.5 part;
Chromium:3-5 parts;
Cosolvent:1.5-2.5 part;
Above-mentioned number is mass fraction.
2. intelligent atomizer metal mesh sheet according to claim 1, it is characterised in that the aluminium-manganese glass powder is
3.5 parts, number is mass fraction.
3. intelligent atomizer metal mesh sheet according to claim 2, it is characterised in that the magnesium is 14 parts, number
For mass fraction.
4. intelligent atomizer metal mesh sheet according to claim 3, it is characterised in that the titanium alloy is 2 parts, part
Number is mass fraction.
5. intelligent atomizer metal mesh sheet according to claim 4, it is characterised in that the chromium is 4 parts, and number is
Mass fraction.
6. intelligent atomizer metal mesh sheet according to claim 5, it is characterised in that the hafnium is 1 part, and number is
Mass fraction.