CN107501867A - Solid granulates reinforced epoxy and preparation method thereof - Google Patents
Solid granulates reinforced epoxy and preparation method thereof Download PDFInfo
- Publication number
- CN107501867A CN107501867A CN201710859755.0A CN201710859755A CN107501867A CN 107501867 A CN107501867 A CN 107501867A CN 201710859755 A CN201710859755 A CN 201710859755A CN 107501867 A CN107501867 A CN 107501867A
- Authority
- CN
- China
- Prior art keywords
- solid granulates
- epoxy resin
- preparation
- reinforced epoxy
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of solid granulates reinforced epoxy, described epoxy resin includes the component of following parts by weight：80~95 parts of bisphenol A type epoxy resin, 3~15 parts of curing agent, 2~5 parts of elastic nano solid granulates.Present invention also offers a kind of preparation method of solid granulates reinforced epoxy.Solid granulates reinforced epoxy of the present invention and preparation method thereof is employed, stirs raw material and mixed liquor under vacuum, reduces the influences of the gas to mixed process such as oxygen, hydrogen；Controlled on temperature and time strict, when temperature after epoxy resin and curing agent are sufficiently mixed is 60 70 DEG C, add elastic nano solid granulates, elastic nano solid granulates are made preferably to be mixed with mixed liquor, and the present invention is using addition elastic nano solid granulates by different level, it is preferably contacted and is acted on mixed liquor, neither reduce the Tg of epoxy resin solid, and can ensures the use technique of epoxy resin.
Description
Technical field
The present invention relates to the technical field in Epoxy Resin Technology field, more particularly to reinforced epoxy, is specifically one kind
Solid granulates reinforced epoxy and preparation method thereof.
Background technology
At present, epoxy resin enhancing is mainly two schemes：One kind is to add liquid toughener, but can reduce solidfied material
Tg；One kind is to add fiberfill, does not drop solidfied material Tg, but manufacturability is bad, and cost is also higher.
Therefore, it is necessary to a kind of technique is simple, cost is cheap, improve epoxy resin cured product performance reinforced epoxy and
Its preparation method.
The content of the invention
The purpose of the present invention is the shortcomings that overcoming above-mentioned prior art, there is provided a kind of skill is simple, cost is cheap, improves ring
Reinforced epoxy of oxygen tree fat condensate performance and preparation method thereof.
To achieve these goals, first aspect present invention provides a kind of solid granulates reinforced epoxy, and its is main
Feature is：
Described epoxy resin includes the component of following parts by weight：80~95 parts of bisphenol A type epoxy resin, curing agent 3~
15 parts, 2~5 parts of elastic nano solid granulates.
It is preferred that described elastic nano solid granulates are one or more in carbon black, silica or alundum (Al2O3)
The composite nanometer particle of individual modified rubber.
Present invention also offers a kind of preparation method of solid granulates reinforced epoxy, it is mainly characterized by, described
Preparation method comprises the following steps：
Step (1)：Raw materials bisphenol A types epoxy resin, curing agent are stirred under vacuum；
Step (2)：Bisphenol A type epoxy resin after vacuum stirring, curing agent are delivered in mixing kettle, by described bullet
Property the described mixing kettle of nano solid particle input in auxiliary material storage at, then described mixing kettle is vacuumized；
Step (3)：Make mixing kettle heating stirring, mix 0.5~1h；
Step (4) adds described elastic nano solid granulates mixing at auxiliary material storage, and holding mixing kettle temperature is
60 DEG C~70 DEG C, keep 0.5~1h；
Mixed liquor is placed in 80 DEG C~100 DEG C of mould by step (5), solidification, cooling and demolding, solidify afterwards, you can obtain
Described solid granulates reinforced epoxy.
It is preferred that described raw materials bisphenol A types epoxy resin, curing agent are liquid.
It is preferred that institute's elastic nano solid granulates are put into described mixing kettle by described step (2) after fully drying
In auxiliary material storage at.
The beneficial effect of the solid granulates reinforced epoxy of the present invention and preparation method thereof is：With traditional enhancing ring
Oxygen tree fat and preparation method are compared, and preparation method provided by the invention stirs raw material and mixed liquor under vacuum, reduce oxygen
Influence of the gases such as gas, hydrogen to mixed process；Controlled on temperature and time strictly, it is fully mixed in epoxy resin and curing agent
When temperature is 60-70 DEG C after conjunction, elastic nano solid granulates are added, elastic nano solid granulates is preferably mixed with mixed liquor
Close, and the present invention makes it preferably contact and act on mixed liquor using elastic nano solid granulates are added by different level, and it is similar
Compare, elongation at break substantially increases, and its toughness and splitting resistance are remarkably reinforced, and neither reduces epoxy resin solid
Tg, and can ensure the use technique of epoxy resin, ensure the toughness and splitting resistance of solidfied material.
Embodiment
In order to more clearly describe the technology contents of the present invention, carried out with reference to specific embodiment further
Description.
First aspect present invention provides a kind of solid granulates reinforced epoxy, and it is mainly characterized by：
Described epoxy resin includes the component of following parts by weight：80~95 parts of bisphenol A type epoxy resin, curing agent 3~
15 parts, 2~5 parts of elastic nano solid granulates.
Wherein, described elastic nano solid granulates are one or more of carbon black, silica or alundum (Al2O3)
The composite nanometer particle of modified rubber.
Present invention also offers a kind of preparation method of solid granulates reinforced epoxy, it is mainly characterized by, described
Preparation method comprises the following steps：
Step (1)：Raw materials bisphenol A types epoxy resin, curing agent are stirred under vacuum；
Step (2)：Bisphenol A type epoxy resin after vacuum stirring, curing agent are delivered in mixing kettle, by described bullet
Property the described mixing kettle of nano solid particle input in auxiliary material storage at, then described mixing kettle is vacuumized；
Step (3)：Make mixing kettle heating stirring, mix 0.5~1h；
Step (4) adds described elastic nano solid granulates mixing at auxiliary material storage, and holding mixing kettle temperature is
60 DEG C~70 DEG C, keep 0.5~1h；
Mixed liquor is placed in 80 DEG C~100 DEG C of mould by step (5), solidification, cooling and demolding, solidify afterwards, you can obtain
Described solid granulates reinforced epoxy.
Wherein, described raw materials bisphenol A types epoxy resin, curing agent are liquid；In described step (2) by bullet
Property nano solid particle put into after fully drying at the auxiliary material storage in described mixing kettle.
The beneficial effect of the solid granulates reinforced epoxy of the present invention and preparation method thereof is：With traditional enhancing ring
Oxygen tree fat and preparation method are compared, and preparation method provided by the invention stirs raw material and mixed liquor under vacuum, reduce oxygen
Influence of the gases such as gas, hydrogen to mixed process；Controlled on temperature and time strictly, it is fully mixed in epoxy resin and curing agent
When temperature is 60-70 DEG C after conjunction, elastic nano solid granulates are added, elastic nano solid granulates is preferably mixed with mixed liquor
Close, and the present invention makes it preferably contact and act on mixed liquor using elastic nano solid granulates are added by different level, and it is similar
Compare, elongation at break substantially increases, and its toughness and splitting resistance are remarkably reinforced, and neither reduces epoxy resin solid
Tg, and can ensure the use technique of epoxy resin, ensure the toughness and splitting resistance of solidfied material.
In this description, the present invention is described with reference to its specific embodiment.But it is clear that it can still make
Various modifications and alterations are without departing from the spirit and scope of the present invention.Therefore, specification is considered as illustrative rather than limit
Property processed.
Claims (5)
1. a kind of solid granulates reinforced epoxy, it is characterised in that described epoxy resin includes the component of following parts by weight：
80~95 parts of bisphenol A type epoxy resin, 3~15 parts of curing agent, 2~5 parts of elastic nano solid granulates.
2. solid granulates reinforced epoxy according to claim 1, it is characterised in that described elastic nano solid-state
Grain is the composite nanometer particle of one or more of carbon black, silica or alundum (Al2O3) modified rubber.
A kind of 3. preparation method of the solid granulates reinforced epoxy described in claim 1, it is characterised in that described system
Preparation Method comprises the following steps：
Step (1)：Raw materials bisphenol A types epoxy resin, curing agent are stirred under vacuum；
Step (2)：Bisphenol A type epoxy resin after vacuum stirring, curing agent are delivered in mixing kettle, described elasticity is received
At auxiliary material storage in the described mixing kettle of rice solid granulates input, then described mixing kettle is vacuumized；
Step (3)：Make mixing kettle heating stirring, mix 0.5~1h；
Step (4) adds described elastic nano solid granulates mixing at auxiliary material storage, and it is 60 DEG C to keep mixing kettle temperature
~70 DEG C, keep 0.5~1h；
Mixed liquor is placed in 80 DEG C~100 DEG C of mould by step (5), solidification, cooling and demolding, solidify afterwards, you can is obtained described
Solid granulates reinforced epoxy.
4. the preparation method of solid granulates reinforced epoxy according to claim 3, it is characterised in that described raw material
Bisphenol A type epoxy resin, curing agent are liquid.
5. the preparation method of solid granulates reinforced epoxy according to claim 3, it is characterised in that described step
(2) elastic nano solid granulates are put at the auxiliary material storage in described mixing kettle after fully drying.