CN107474664A - A kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel - Google Patents
A kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel Download PDFInfo
- Publication number
- CN107474664A CN107474664A CN201710785924.0A CN201710785924A CN107474664A CN 107474664 A CN107474664 A CN 107474664A CN 201710785924 A CN201710785924 A CN 201710785924A CN 107474664 A CN107474664 A CN 107474664A
- Authority
- CN
- China
- Prior art keywords
- detection device
- vehicle
- parts
- stirring wheel
- antirusting paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel, by following material composition:Organic fluorinated silicone modified acrylic acid ester emulsion, zinc oxide, defoamer, thickener, coalescents, filler, modified phosphate calcium, water.Addition of the invention rational has been arranged in pairs or groups each material composition, and mutual amalgamation is high, and final obtained coating has that water-fast, anti-corrosion, rust-preventing characteristic are good, processing using technique it is simple the characteristics of, there is good promotional value.
Description
Technical field
The present invention relates to a kind of coating, and in particular to a kind of antiseptic and rustproof painting for vehicle-carrying foodstuff detection device stirring wheel
Material.
Background technology
Food security is related to the vital interests of broad masses of the people, always is the weight of country's regulator agencies at different levels
One of work, soybean, corn equigranular agricultural product are diet essential on people's dining table, it is therefore desirable to which its quality is entered
Row control.With the improvement of people's living standards, requirement to quality of life is also increasingly specific, the especially food of safety non-pollution
Product, and the rapidly and efficiently detection of residues of pesticides occupies main status in food security.In general food inspection is using special
Instrument for detecting pesticide residue through is detected, and instrument for detecting pesticide residue through is detected primarily directed to liquid, to granular agricultural product
, it is necessary to which granular agricultural product are carried out to squeeze liquid before detection, then could complete to detect work.Stirring wheel is in detection device
One of essential part, it is mainly stirred crushing to food, is easy to squeeze liquid for detecting, and long-term powder
It is broken to be contacted with food juice, it is desirable to which that it has good antiseptic and rustproof characteristic.In existing equipment stirring wheel usually because it is long when make
With there is phenomena such as corrosion, this problem, which is needed badly, to be improved.
The content of the invention
The purpose of the present invention is to be directed to the problem of existing, there is provided a kind of for the anti-of vehicle-carrying foodstuff detection device stirring wheel
Rotten antirusting paint.
The present invention is achieved by the following technical solutions:
A kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel, by the material composition of following parts by weight:
85 ~ 90 parts of organic fluorinated silicone modified acrylic acid ester emulsions, 5 ~ 9 parts of zinc oxide, 0.3 ~ 0.8 part of defoamer, 3 ~ 5 parts of thickeners,
11 ~ 16 parts of coalescents, 15 ~ 20 parts of fillers, 22 ~ 28 parts of modified phosphate calcium, 130 ~ 150 parts of water;Described modified phosphate calcium
Preparation method is:By calcium oxide and water according to mass ratio 1:5 ~ 7 are mixed, and are then slow added into phosphoric acid solution, at stirring
Mixed liquor is obtained after managing 25 ~ 30min, then the modified nano-titanium dioxide of its gross mass 6 ~ 10%, heat temperature raising are added into mixed liquor
To 90 ~ 95 DEG C, after being stirred continuously 10 ~ 15min of processing, then it is filtered under diminished pressure, finally the material of filtering gained is dried
Handle and produce modified phosphate calcium.
Further, described defoamer is any one in mineral oil defoaming agent, organic silicon defoamer.
Further, described thickener is any in hydroxymethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose
It is a kind of.
Further, described coalescents are any one in ethylene glycol, propane diols phenylate, alcohol ester 12.
Further, described filler is any one in kaolin, attapulgite, diatomite.
Further, in the preparation process of described modified phosphate calcium, the mass fraction of phosphoric acid in phosphoric acid solution used
For 75%, its amount used is the 85 ~ 90% of calcium oxide quality.
Further, in the preparation process of described modified phosphate calcium, the preparation side of modified nano-titanium dioxide used
Method is:First nano titanium oxide is put into the silane coupler of 8 ~ 10 times of its gross mass, after being stirred continuously 30 ~ 40min of processing
Filtering, the nano titanium oxide after filtering is then put into 5 ~ 8min of drying process under conditions of temperature is 85 ~ 90 DEG C, finally will
Dried nano titanium oxide is put into modification liquid and taken out after 1 ~ 1.5h of immersion treatment, and holding granular size is after drying and crushing
40 ~ 120nm;Described modification liquid is the metering system aqueous acid that mass fraction is 4 ~ 7%.
Further, in the preparation process of described modified phosphate calcium, to the temperature that is dried of material of filtering gained
For 75 ~ 80 DEG C.
For the present invention using organic fluorinated silicone modified acrylic acid ester emulsion as film forming matter, it has the excellent transparency, film forming, good
Oil resistivity and weatherability well, mechanical stability and good adhesiveness, simultaneously as organic fluorine monomer has higher heat steady
Qualitative, chemical inertness, corrosion resistance and anti-ultraviolet ageing performance, it is modified acrylic emulsion water resistance, oil resistivity, weather-proof
Property, the performance such as chemical resistance is obtained for very big raising, and because the introducing of organic silicon monomer, makes modified propylene yogurt
Stain resistance, resistant of high or low temperature and the water resistance of liquid are improved;In order to further lift the performance of coating, add again
Modified phosphate calcium component, in the preparation process of modified phosphate calcium, first synthesizes to obtain calcium hydroxy phosphate with phosphoric acid and calcium oxide,
It has good surface characteristic, then carries out cladding processing, wherein nanometer titanium dioxide to it with modified nano-titanium dioxide again
Titanium first carries out coupling modifier with silane coupler, improves its scattered, chelating ability, and has carried out modification with modification liquid,
The compatibilities such as nano titanium oxide and organic fluorinated silicone modified acrylic acid ester emulsion after being grafted by methacrylic acid are high, final modified
Nano titanium oxide afterwards wraps that performance is good to the bonding of calcium hydroxy phosphate, improves dispersiveness, the corrosion resistant of modified phosphate calcium again
Property, intensity etc., improve its performance.
The present invention has advantages below compared with prior art:
Addition of the invention rational has been arranged in pairs or groups each material composition, and mutual amalgamation is high, final obtained coating have it is water-fast,
The characteristics of anti-corrosion, rust-preventing characteristic are good, and processing uses technique simple, has good promotional value.
Embodiment
Embodiment 1
A kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel, by the material composition of following parts by weight:
85 parts of organic fluorinated silicone modified acrylic acid ester emulsions, 5 parts of zinc oxide, 0.3 part of defoamer, 3 parts of thickeners, 11 parts of film forming help
Agent, 15 parts of fillers, 22 parts of modified phosphate calcium, 130 parts of water;The preparation method of described modified phosphate calcium is:By calcium oxide and water
According to mass ratio 1:5 are mixed, and are then slow added into phosphoric acid solution, after stir process 25min mixed liquor, then to mixing
The modified nano-titanium dioxide of its gross mass 6% is added in liquid, is heated to 90 DEG C, after being stirred continuously processing 10min, then is entered
Row is filtered under diminished pressure, and finally the material of filtering gained is dried to handle and produces modified phosphate calcium.
Further, described defoamer is mineral oil defoaming agent.
Further, described thickener is hydroxymethyl cellulose.
Further, described coalescents are ethylene glycol.
Further, described filler is kaolin.
Further, in the preparation process of described modified phosphate calcium, the mass fraction of phosphoric acid in phosphoric acid solution used
For 75%, its amount used is the 85% of calcium oxide quality.
Further, in the preparation process of described modified phosphate calcium, the preparation side of modified nano-titanium dioxide used
Method is:First nano titanium oxide is put into the silane coupler of 8 times of its gross mass, filtered after being stirred continuously processing 30min, so
The nano titanium oxide after filtering is put into drying process 5min under conditions of temperature is 85 DEG C afterwards, finally by dried nanometer
Titanium dioxide is put into modification liquid and taken out after immersion treatment 1h, and it is 40 ~ 120nm that granular size is kept after drying and crushing;Institute
The modification liquid stated is the metering system aqueous acid that mass fraction is 4%.
Further, in the preparation process of described modified phosphate calcium, to the temperature that is dried of material of filtering gained
For 75 DEG C.
Embodiment 2
A kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel, by the material composition of following parts by weight:
88 parts of organic fluorinated silicone modified acrylic acid ester emulsions, 8 parts of zinc oxide, 0.5 part of defoamer, 4 parts of thickeners, 14 parts of film forming help
Agent, 18 parts of fillers, 25 parts of modified phosphate calcium, 140 parts of water;The preparation method of described modified phosphate calcium is:By calcium oxide and water
According to mass ratio 1:6 are mixed, and are then slow added into phosphoric acid solution, after stir process 28min mixed liquor, then to mixing
The modified nano-titanium dioxide of its gross mass 8% is added in liquid, is heated to 93 DEG C, after being stirred continuously processing 12min, then is entered
Row is filtered under diminished pressure, and finally the material of filtering gained is dried to handle and produces modified phosphate calcium.
Further, described defoamer is organic silicon defoamer.
Further, described thickener is hydroxyethyl cellulose.
Further, described coalescents are propane diols phenylate.
Further, described filler is attapulgite.
Further, in the preparation process of described modified phosphate calcium, the mass fraction of phosphoric acid in phosphoric acid solution used
For 75%, its amount used is the 87% of calcium oxide quality.
Further, in the preparation process of described modified phosphate calcium, the preparation side of modified nano-titanium dioxide used
Method is:First nano titanium oxide is put into the silane coupler of 9 times of its gross mass, filtered after being stirred continuously processing 35min, so
The nano titanium oxide after filtering is put into drying process 7min under conditions of temperature is 89 DEG C afterwards, finally by dried nanometer
Titanium dioxide is put into modification liquid and taken out after immersion treatment 1.2h, and it is 40 ~ 120nm that granular size is kept after drying and crushing;
Described modification liquid is the metering system aqueous acid that mass fraction is 6%.
Further, in the preparation process of described modified phosphate calcium, to the temperature that is dried of material of filtering gained
For 77 DEG C.
Embodiment 3
A kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel, by the material composition of following parts by weight:
90 parts of organic fluorinated silicone modified acrylic acid ester emulsions, 9 parts of zinc oxide, 0.8 part of defoamer, 5 parts of thickeners, 16 parts of film forming help
Agent, 20 parts of fillers, 28 parts of modified phosphate calcium, 150 parts of water;The preparation method of described modified phosphate calcium is:By calcium oxide and water
According to mass ratio 1:7 are mixed, and are then slow added into phosphoric acid solution, after stir process 30min mixed liquor, then to mixing
The modified nano-titanium dioxide of its gross mass 10% is added in liquid, is heated to 95 DEG C, after being stirred continuously processing 15min, then is entered
Row is filtered under diminished pressure, and finally the material of filtering gained is dried to handle and produces modified phosphate calcium.
Further, described defoamer is organic silicon defoamer.
Further, described thickener is hydroxypropyl cellulose.
Further, described coalescents are alcohol ester 12.
Further, described filler is diatomite.
Further, in the preparation process of described modified phosphate calcium, the mass fraction of phosphoric acid in phosphoric acid solution used
For 75%, its amount used is the 90% of calcium oxide quality.
Further, in the preparation process of described modified phosphate calcium, the preparation side of modified nano-titanium dioxide used
Method is:First nano titanium oxide is put into the silane coupler of 10 times of its gross mass, filtered after being stirred continuously processing 40min,
Then the nano titanium oxide after filtering is put into drying process 8min under conditions of temperature is 90 DEG C, finally received dried
Rice titanium dioxide is put into modification liquid to be taken out after immersion treatment 1.5h, and it is that 40 ~ 120nm is that granular size is kept after drying and crushing
Can;Described modification liquid is the metering system aqueous acid that mass fraction is 7%.
Further, in the preparation process of described modified phosphate calcium, to the temperature that is dried of material of filtering gained
For 80 DEG C.
Comparative example 1
This comparative example 1 compared with Example 2, in modified phosphate calcium preparation process, with etc. mass parts common nanometer two
Titanium oxide substituting modification nano titanium oxide, method and step all same in addition.
Comparative example 2
This comparative example 2 compared with Example 2, in modified phosphate calcium preparation process, does not add modified nano-titanium dioxide
Modification, method and step all same in addition.
Comparative example 3
This comparative example 3 compared with Example 2, with etc. mass parts common calcium phosphate substituting modification calcium phosphate, in addition
Method and step all same.
In order to contrast effect of the present invention, to above-described embodiment 2, comparative example 1, comparative example 2, comparative example 3
Described coating carries out attribute test, and specific correction data is as shown in table 1 below:
Table 1
Water resistance(h) | Acid resistance(h) | Salt fog resistance(h) | |
Embodiment 2 | 1520 | 330 | 1100 |
Comparative example 1 | 1430 | 303 | 970 |
Comparative example 2 | 1280 | 275 | 920 |
Comparative example 3 | 1200h | 240h | 860h |
Note:Water resistance described in upper table 1 is tested with reference to GB/T1733-1993, and described acid resistance is with reference to GB/T9274-
1988 are tested, and described salt fog resistance is tested with reference to GB/T1771-1991.
Coating produced by the present invention has lifting in water-fast, acidproof, salt fog resistance etc. it can be seen from upper table 1, comprehensive
It is good to close using effect, promotional value is high.
Claims (8)
1. a kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel, it is characterised in that by following parts by weight
Material composition:
85 ~ 90 parts of organic fluorinated silicone modified acrylic acid ester emulsions, 5 ~ 9 parts of zinc oxide, 0.3 ~ 0.8 part of defoamer, 3 ~ 5 parts of thickeners,
11 ~ 16 parts of coalescents, 15 ~ 20 parts of fillers, 22 ~ 28 parts of modified phosphate calcium, 130 ~ 150 parts of water;Described modified phosphate calcium
Preparation method is:By calcium oxide and water according to mass ratio 1:5 ~ 7 are mixed, and are then slow added into phosphoric acid solution, at stirring
Mixed liquor is obtained after managing 25 ~ 30min, then the modified nano-titanium dioxide of its gross mass 6 ~ 10%, heat temperature raising are added into mixed liquor
To 90 ~ 95 DEG C, after being stirred continuously 10 ~ 15min of processing, then it is filtered under diminished pressure, finally the material of filtering gained is dried
Handle and produce modified phosphate calcium.
2. a kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel according to claim 1, its feature
It is, described defoamer is any one in mineral oil defoaming agent, organic silicon defoamer.
3. a kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel according to claim 1, its feature
It is, described thickener is any one in hydroxymethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose.
4. a kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel according to claim 1, its feature
It is, described coalescents are any one in ethylene glycol, propane diols phenylate, alcohol ester 12.
5. a kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel according to claim 1, its feature
It is, described filler is any one in kaolin, attapulgite, diatomite.
6. a kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel according to claim 1, its feature
It is, in the preparation process of described modified phosphate calcium, the mass fraction of phosphoric acid is 75% in phosphoric acid solution used, and it is used
Amount be calcium oxide quality 85 ~ 90%.
7. a kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel according to claim 1, its feature
It is, in the preparation process of described modified phosphate calcium, the preparation method of modified nano-titanium dioxide used is:First by nanometer
Titanium dioxide is put into the silane coupler of 8 ~ 10 times of its gross mass, is filtered after being stirred continuously 30 ~ 40min of processing, is then incited somebody to action
It is 5 ~ 8min of drying process under conditions of 85 ~ 90 DEG C that nano titanium oxide after filter, which is put into temperature, finally by dried nanometer
Titanium dioxide is put into modification liquid and taken out after 1 ~ 1.5h of immersion treatment, and it is that 40 ~ 120nm is that granular size is kept after drying and crushing
Can;Described modification liquid is the metering system aqueous acid that mass fraction is 4 ~ 7%.
8. a kind of anti-corrosive antirusting paint for vehicle-carrying foodstuff detection device stirring wheel according to claim 1, its feature
It is, in the preparation process of described modified phosphate calcium, the temperature that the material of filtering gained is dried is 75 ~ 80 DEG C.