CN107473591A - Screen printing ink pottery and preparation method thereof - Google Patents
Screen printing ink pottery and preparation method thereof Download PDFInfo
- Publication number
- CN107473591A CN107473591A CN201710604811.6A CN201710604811A CN107473591A CN 107473591 A CN107473591 A CN 107473591A CN 201710604811 A CN201710604811 A CN 201710604811A CN 107473591 A CN107473591 A CN 107473591A
- Authority
- CN
- China
- Prior art keywords
- parts
- screen printing
- printing ink
- component
- frit powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of screen printing ink pottery and preparation method thereof, the component and each component mass parts that screen printing ink material that screen printing ink pottery uses includes are as follows：From burning frit powder：40 parts；Toner：10 parts；50 parts of ink；Wherein, the component and each component content included from burning frit powder is as follows：30 parts~35 parts of potassium feldspar；10 parts~15 parts of albite；4 parts~6 parts of zinc oxide；15 parts~20 parts of borax；3 parts~5 parts of Guizhou clay, 8 parts~11 parts of spodumene, 8 parts~10 parts of dolomite.The present invention, which can save, makes silk screen biscuiting process under glaze, can play the saving energy, reduce the effect of cost, while facilitate operation, yield is improved, advantage is simple to operate that speed is fast compared with traditional underglaze colour, can volume production, not only saved biscuiting cost, also reduced defect risk.
Description
Technical field
The present invention relates to a kind of screen printing ink pottery and preparation method thereof.
Background technology
At present, for domestic Shi porcelain industry all with color glaze, silk screen fills out glaze, and overglaze color is main body, it is necessary to develop a kind of screen printing
The pottery of brush, save it and make silk screen biscuiting process under glaze, the saving energy can be played, reduce the effect of cost.
The content of the invention
The technical problems to be solved by the invention are the defects of overcoming prior art, there is provided a kind of screen printing ink ceramics
Product, it, which can be saved, makes silk screen biscuiting process under glaze, can play the saving energy, reduce the effect of cost, facilitate simultaneously
Operation, improve yield, advantage is simple to operate that speed is fast with traditional underglaze colour compared with, can volume production, not only saving
Biscuiting cost, also reduce defect risk.
In order to solve the above technical problems, the technical scheme of the present invention is：A kind of screen printing ink pottery, it makes
The component and each component mass parts that screen printing ink material includes are as follows：
From burning frit powder：40 parts；Toner：10 parts；50 parts of ink；Wherein, the component and each component included from burning frit powder
Content is as follows：30 parts~35 parts of potassium feldspar；10 parts~15 parts of albite；4 parts~6 parts of zinc oxide；15 parts~20 parts of borax；Guizhou
3 parts~5 parts of soil, 8 parts~11 parts of spodumene, 8 parts~10 parts of dolomite.
Present invention also offers a kind of preparation method of screen printing ink pottery, the step of method in contain：
A) from frit powder is burnt according to its component and each component mass parts stock：
B) according to the ︰ 0.6 of mass ratio=1 ︰ 1.5 of Liao ︰ Qiu ︰ water, wet ball grinding 25~28 hours, material after ball milling 200
After mesh sieve, dry after 200 mesh sieves, obtain stand-by from frit powder is burnt；
C) will prepare from frit powder is burnt by 4：1：5 mass ratio adds toner, ink is well mixed, and obtains silk screen
Off-set oil ink is stand-by；
D) by the screen printing ink material prepared by silk-screen technology print on clean base substrate, treat silk-screen printing oil
After ink is dry, upper clear frit；
E) base substrate of first-class clear frit is put into fire in 1190 DEG C of roller kilns and formed.
After employing above-mentioned technical proposal, the present invention, which can save, makes silk screen biscuiting process under glaze, can play saving
The energy, reduces the effect of cost, while facilitates operation, improves yield, and advantage is to operate compared with traditional underglaze colour
Simply, speed is fast, can volume production, not only saved biscuiting cost, also reduced defect risk.
Embodiment
In order that present disclosure is easier to be clearly understood, below according to specific embodiment, the present invention is made into
One step is described in detail.
Embodiment one
A kind of screen printing ink pottery, the component and each component mass parts that the screen printing ink material that it is used includes
It is as follows：
From burning frit powder：40 parts；Toner：10 parts；50 parts of ink；Wherein, the component and each component included from burning frit powder
Content is as follows：30 parts of potassium feldspar；10 parts of albite；4 parts of zinc oxide；15 parts of borax；3 parts of Guizhou clay, 8 parts of spodumene, dolomite 8
Part.
Contain in the step of preparation method of the screen printing ink pottery：
A) from frit powder is burnt according to its component and each component mass parts stock：
B) according to the ︰ 0.6 of mass ratio=1 ︰ 1.5 of Liao ︰ Qiu ︰ water, wet ball grinding 25 hours, material after ball milling 200 mesh sieves
Afterwards, dry after 200 mesh sieves, obtain stand-by from frit powder is burnt；
C) will prepare from frit powder is burnt by 4：1：5 mass ratio adds toner, ink is well mixed, and obtains silk screen
Off-set oil ink is stand-by；
D) by the screen printing ink material prepared by silk-screen technology print on clean base substrate, treat silk-screen printing oil
After ink is dry, upper clear frit；
E) base substrate of first-class clear frit is put into fire in 1190 DEG C of roller kilns and formed.
Embodiment two
A kind of screen printing ink pottery, the component and each component mass parts that the screen printing ink material that it is used includes
It is as follows：
From burning frit powder：40 parts；Toner：10 parts；50 parts of ink；Wherein, the component and each component included from burning frit powder
Content is as follows：35 parts of potassium feldspar；15 parts of albite；6 parts of zinc oxide；20 parts of borax；5 parts of Guizhou clay, 11 parts of spodumene, dolomite
10 parts.
Contain in the step of preparation method of the screen printing ink pottery：
A) from frit powder is burnt according to its component and each component mass parts stock：
B) according to the ︰ 0.6 of mass ratio=1 ︰ 1.5 of Liao ︰ Qiu ︰ water, wet ball grinding 28 hours, material after ball milling 200 mesh sieves
Afterwards, dry after 200 mesh sieves, obtain stand-by from frit powder is burnt；
C) will prepare from frit powder is burnt by 4：1：5 mass ratio adds toner, ink is well mixed, and obtains silk screen
Off-set oil ink is stand-by；
D) by the screen printing ink material prepared by silk-screen technology print on clean base substrate, treat silk-screen printing oil
After ink is dry, upper clear frit；
E) base substrate of first-class clear frit is put into fire in 1190 DEG C of roller kilns and formed.
Embodiment three
A kind of screen printing ink pottery, the component and each component mass parts that the screen printing ink material that it is used includes
It is as follows：
From burning frit powder：40 parts；Toner：10 parts；50 parts of ink；Wherein, the component and each component included from burning frit powder
Content is as follows：33 parts of potassium feldspar；13 parts of albite；5 parts of zinc oxide；18 parts of borax；4 parts of Guizhou clay, 10 parts of spodumene, dolomite
9 parts.
Contain in the step of preparation method of the screen printing ink pottery：
A) from frit powder is burnt according to its component and each component mass parts stock：
B) according to the ︰ 0.6 of mass ratio=1 ︰ 1.5 of Liao ︰ Qiu ︰ water, wet ball grinding 26 hours, material after ball milling 200 mesh sieves
Afterwards, dry after 200 mesh sieves, obtain stand-by from frit powder is burnt；
C) will prepare from frit powder is burnt by 4：1：5 mass ratio adds toner, ink is well mixed, and obtains silk screen
Off-set oil ink is stand-by；
D) by the screen printing ink material prepared by silk-screen technology print on clean base substrate, treat silk-screen printing oil
After ink is dry, upper clear frit；
E) base substrate of first-class clear frit is put into fire in 1190 DEG C of roller kilns and formed.
Screen printing ink pottery prepared by three above embodiment meets the original intention of research and development, and effect is good, clear patterns,
It is easy to operate simple.
Particular embodiments described above, the purpose of the present invention, technical scheme and beneficial effect are carried out further in detail
Describe in detail it is bright, should be understood that the foregoing is only the present invention specific embodiment, be not intended to limit the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution and improvements done etc., it should be included in the guarantor of the present invention
Within the scope of shield.
Claims (2)
- A kind of 1. screen printing ink pottery, it is characterised in that component that the screen printing ink material that it is used includes and each Constituent mass part is as follows：From burning frit powder：40 parts；Toner：10 parts；50 parts of ink；Wherein, the component and each component content included from burning frit powder It is as follows：30 parts~35 parts of potassium feldspar；10 parts~15 parts of albite；4 parts~6 parts of zinc oxide；15 parts~20 parts of borax；Guizhou clay 3 Part~5 parts, 8 parts~11 parts of spodumene, 8 parts~10 parts of dolomite.
- 2. a kind of preparation method of screen printing ink pottery as claimed in claim 1, it is characterised in that the step of method In contain：A) from frit powder is burnt according to its component and each component mass parts stock：B) according to the ︰ 0.6 of mass ratio=1 ︰ 1.5 of Liao ︰ Qiu ︰ water, wet ball grinding 25~28 hours, material after ball milling 200 mesh sieves Afterwards, dry after 200 mesh sieves, obtain stand-by from frit powder is burnt；C) will prepare from frit powder is burnt by 4：1：5 mass ratio adds toner, ink is well mixed, and obtains silk-screen printing Printing ink material is stand-by；D) by the screen printing ink material prepared by silk-screen technology print on clean base substrate, treat screen printing ink material After dry, upper clear frit；E) base substrate of first-class clear frit is put into fire in 1190 DEG C of roller kilns and formed.