CN107459925A - A kind of coating on draw-bar box pull bar handle and preparation method thereof - Google Patents
A kind of coating on draw-bar box pull bar handle and preparation method thereof Download PDFInfo
- Publication number
- CN107459925A CN107459925A CN201710742644.1A CN201710742644A CN107459925A CN 107459925 A CN107459925 A CN 107459925A CN 201710742644 A CN201710742644 A CN 201710742644A CN 107459925 A CN107459925 A CN 107459925A
- Authority
- CN
- China
- Prior art keywords
- parts
- draw
- coating
- pull bar
- bar box
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of coating on draw-bar box pull bar handle, it is related to draw-bar box processing technical field, it is characterised in that：It is made up of the material of following parts by weight, 22 27 parts of resin, 9 15 parts of age resistor, 13 18 parts of improved silica, 49 parts of coupling agent, 7 13 parts of montmorillonite powder, 26 parts of γ (2,3 glycidoxy) propyl trimethoxy silicane, 48 parts of benzyl trimethyl tribromide ammonium, 15 parts of fatty diglycollic amide, 37 parts of DAA, 27 parts of ammonium tungstate, 27 33 parts of clear water.The inventive method is reasonable, easy to operate, wear-resisting, resistance to compression.
Description
Technical field：
The present invention relates to draw-bar box to process technical field, and in particular to a kind of coating on draw-bar box pull bar handle and
Its preparation method.
Background technology：
Draw-bar box refers to the luggage case with pull bar and roller.Because its is easy to use, carrying clothing etc. turns into travelling, go out and
Widely used.Meanwhile draw-bar box has point of single tube pull bar and two-tube pulling rod, the pipe of pull bar is also also because chest puts a pull bar
There is point of square tube and pipe, during facilitating walking in tow, reduce the heavy burdens significantly.Draw-bar box be able to can also be dragged with portable, we
The wheel of draw-bar box usually used is all located at chest bottom substantially, and modern have devised the pull bar of a neomorph
Case, chest is designed to the moulding of cylinder, then on the outside of chest, such roller designs causes this drawing to wheel for whole outsourcing
Bar case can preferably adapt to different landform, such as directly haul the light stair activity of chest can.2012 mainly with cloth
The hard case of case, ABS, leather trunk, PC etc. are main material, and usability is divided into directional wheel, universal wheel and newest detachable ten thousand
To wheel draw-bar box three major types.
In general suitcase, divide by material, it is (hard and can be divided into ABS's that two kinds of soft cloth case and hard case can be divided into
With PC etc., popular material also has pure PC for ABS or ABS+PC on the market)；Divide by construction, vertical pull bar and horizontal stroke can be divided into
Two kinds of the suitcase of formula；Divide by size, can be divided into (from small size to big size)：16 cun ', 18 cun ', 20 cun ', 22 cun ',
24 cun ', 26 cun ', 28 cun ', 30 cun ', 32 cun ' this is several！Typically conventional be 20 cun of three sides and add up 115CM and (remove
Britain Virgin Atlantic regulation is 105CM) can with the size boarded a plane and 28 cun of three sides and add up 158CM and fly
The international standard size that machine can be consigned freely.Domestic air mail can consign full-size as 32 cun.
And the pull bar of draw-bar box is a very important part, the pulling of draw-bar box, which is located against the flexible of pull bar, to be made one
Comfortably haul, and the handle on pull bar is one of part being in the most contact with people, and table often occurs in this part
The problems such as skin comes off, ftractureed, dry linting, cause to have hurt hand when in use, bring the trouble and deleterious effect of many.
The content of the invention：
The technical problems to be solved by the invention be to overcome existing technological deficiency provide a kind of method rationally, operation side
Just coating on a kind of, wear-resisting, measuring body draw-bar box pull bar handle and preparation method thereof.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of coating on draw-bar box pull bar handle, it is characterised in that：It is made up of the material of following parts by weight,
Resin 22-27 parts, age resistor 9-15 parts, improved silica 13-18 parts, coupling agent 4-9 parts, montmorillonite powder 7-13
Part, γ-(2,3- glycidoxy) propyl trimethoxy silicane 2-6 parts, benzyl trimethyl tribromide ammonium 4-8 parts, aliphatic acid two
Glycollic amide 1-5 parts, DAA 3-7 parts, ammonium tungstate 2-7 parts, clear water 27-33 parts；
The resin is one kind in organic siliconresin, fluorocarbon resin, phenolic resin, polyamide, furane resins；
The coupling agent is Silane coupling agent KH550；
The age resistor is one kind in antioxidant A W, anti-aging agent RD, antioxidant A, age resistor CPPD；
The preparation method of the improved silica is, by Silica abrasive and crosses 300-400 mesh sieves, then add with
Its weight identical pure water, 2 hours of mixing are stirred at room temperature, then adds lauric acid amide of ethanol, continues to stir
3 hours of mixing are mixed, then dries, re-grinds, produce improved silica；
The mass ratio of the lauric acid amide of ethanol and silica is 1：4.5；
The preparation method of coating on a kind of draw-bar box pull bar handle is,
I by resin, age resistor, improved silica, coupling agent, montmorillonite powder ,-(2,3- glycidoxy) propyl group front three
TMOS and clear water are stirred 15 minutes, are then placed in reactor and are stirred 20 minutes at a temperature of 40-60 DEG C；
II by the material left 10 minutes after stirring, then proceedes to add benzyl trimethyl tribromide ammonium, aliphatic acid diethyl
Alkylolamides, continue stirring 40 minutes；
After III stands 5 minutes, DAA, ammonium tungstate are added, and is warming up to 55-75 DEG C, continues to be stirred 2 hours
；
The speed of the stirring is 1500-2000r/min.
Beneficial effects of the present invention are：By a series of product that has been mixed to prepare of materials, can ensure after usage
Performance with good resistance to compression, cracking resistance, and can be moistureproof, and there is certain decay resistance, it ensure that draw-bar box
The service life of handle.The inventive method is reasonable, easy to operate, wear-resisting, resistance to compression.
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, enter below
One step illustrates the present invention.
Embodiment 1
A kind of coating on draw-bar box pull bar handle, it is characterised in that：It is made up of the material of following parts by weight,
22 parts of resin, 9 parts of age resistor, 13 parts of improved silica, 4 parts of coupling agent, 7 parts of montmorillonite powder, γ-(2,3- rings
Oxygen propoxyl group) 2 parts of propyl trimethoxy silicane, 4 parts of benzyl trimethyl tribromide ammonium, 1 part of fatty diglycollic amide, two acetone
3 parts of alcohol, 2 parts of ammonium tungstate, 27 parts of clear water；
The resin is one kind in organic siliconresin, fluorocarbon resin, phenolic resin, polyamide, furane resins；
The coupling agent is Silane coupling agent KH550；
The age resistor is one kind in antioxidant A W, anti-aging agent RD, antioxidant A, age resistor CPPD；
The preparation method of the improved silica is, by Silica abrasive and crosses 300-400 mesh sieves, then add with
Its weight identical pure water, 2 hours of mixing are stirred at room temperature, then adds lauric acid amide of ethanol, continues to stir
3 hours of mixing are mixed, then dries, re-grinds, produce improved silica；
The mass ratio of the lauric acid amide of ethanol and silica is 1：4.5；
The preparation method of coating on a kind of draw-bar box pull bar handle is,
I by resin, age resistor, improved silica, coupling agent, montmorillonite powder ,-(2,3- glycidoxy) propyl group front three
TMOS and clear water are stirred 15 minutes, are then placed in reactor and are stirred 20 minutes at a temperature of 40-60 DEG C；
II by the material left 10 minutes after stirring, then proceedes to add benzyl trimethyl tribromide ammonium, aliphatic acid diethyl
Alkylolamides, continue stirring 40 minutes；
After III stands 5 minutes, DAA, ammonium tungstate are added, and is warming up to 55-75 DEG C, continues to be stirred 2 hours
；
The speed of the stirring is 1500-2000r/min.
Embodiment 2
A kind of coating on draw-bar box pull bar handle, it is characterised in that：It is made up of the material of following parts by weight,
27 parts of resin, 15 parts of age resistor, 18 parts of improved silica, 9 parts of coupling agent, 13 parts of montmorillonite powder, γ-(2,3-
Glycidoxy) 6 parts of propyl trimethoxy silicane, 8 parts of benzyl trimethyl tribromide ammonium, 5 parts of fatty diglycollic amide, dipropyl
7 parts of keto-alcohol, 7 parts of ammonium tungstate, 33 parts of clear water；
The resin is one kind in organic siliconresin, fluorocarbon resin, phenolic resin, polyamide, furane resins；
The coupling agent is Silane coupling agent KH550；
The age resistor is one kind in antioxidant A W, anti-aging agent RD, antioxidant A, age resistor CPPD；
The preparation method of the improved silica is, by Silica abrasive and crosses 300-400 mesh sieves, then add with
Its weight identical pure water, 2 hours of mixing are stirred at room temperature, then adds lauric acid amide of ethanol, continues to stir
3 hours of mixing are mixed, then dries, re-grinds, produce improved silica；
The mass ratio of the lauric acid amide of ethanol and silica is 1：4.5；
The preparation method of coating on a kind of draw-bar box pull bar handle is,
I by resin, age resistor, improved silica, coupling agent, montmorillonite powder ,-(2,3- glycidoxy) propyl group front three
TMOS and clear water are stirred 15 minutes, are then placed in reactor and are stirred 20 minutes at a temperature of 40-60 DEG C；
II by the material left 10 minutes after stirring, then proceedes to add benzyl trimethyl tribromide ammonium, aliphatic acid diethyl
Alkylolamides, continue stirring 40 minutes；
After III stands 5 minutes, DAA, ammonium tungstate are added, and is warming up to 55-75 DEG C, continues to be stirred 2 hours
；
The speed of the stirring is 1500-2000r/min.
Embodiment 3
A kind of coating on draw-bar box pull bar handle, it is characterised in that：It is made up of the material of following parts by weight,
25 parts of resin, 12 parts of age resistor, 14 parts of improved silica, 8 parts of coupling agent, 10 parts of montmorillonite powder, γ-(2,3-
Glycidoxy) 4 parts of propyl trimethoxy silicane, 6 parts of benzyl trimethyl tribromide ammonium, 4 parts of fatty diglycollic amide, dipropyl
5 parts of keto-alcohol, 6 parts of ammonium tungstate, 30 parts of clear water；
The resin is one kind in organic siliconresin, fluorocarbon resin, phenolic resin, polyamide, furane resins；
The coupling agent is Silane coupling agent KH550；
The age resistor is one kind in antioxidant A W, anti-aging agent RD, antioxidant A, age resistor CPPD；
The preparation method of the improved silica is, by Silica abrasive and crosses 300-400 mesh sieves, then add with
Its weight identical pure water, 2 hours of mixing are stirred at room temperature, then adds lauric acid amide of ethanol, continues to stir
3 hours of mixing are mixed, then dries, re-grinds, produce improved silica；
The mass ratio of the lauric acid amide of ethanol and silica is 1：4.5；
The preparation method of coating on a kind of draw-bar box pull bar handle is,
I by resin, age resistor, improved silica, coupling agent, montmorillonite powder ,-(2,3- glycidoxy) propyl group front three
TMOS and clear water are stirred 15 minutes, are then placed in reactor and are stirred 20 minutes at a temperature of 40-60 DEG C；
II by the material left 10 minutes after stirring, then proceedes to add benzyl trimethyl tribromide ammonium, aliphatic acid diethyl
Alkylolamides, continue stirring 40 minutes；
After III stands 5 minutes, DAA, ammonium tungstate are added, and is warming up to 55-75 DEG C, continues to be stirred 2 hours
；
The speed of the stirring is 1500-2000r/min.
A kind of coating, including 10 parts of epoxy resin, 6 parts of antioxidant A, 6 parts of silica, 4 parts of silane coupler, montmorillonite
10 parts of powder, 4 parts of benzyl trimethyl tribromide ammonium, 10 parts of ammonium tungstate, 20 parts of clear water, it is made up of reactor reaction.
Determine the performance and effect of 1-3 of the embodiment of the present invention and comparative example, such as following table：
Performance is divided into high, medium and low in table, it is strong, in, it is weak.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (8)
- A kind of 1. coating on draw-bar box pull bar handle, it is characterised in that：It is made up of the material of following parts by weight,Resin 22-27 parts, age resistor 9-15 parts, improved silica 13-18 parts, coupling agent 4-9 parts, montmorillonite powder 7-13 parts, γ-(2,3- glycidoxy) propyl trimethoxy silicane 2-6 parts, benzyl trimethyl tribromide ammonium 4-8 parts, aliphatic acid diethanol Acid amides 1-5 parts, DAA 3-7 parts, ammonium tungstate 2-7 parts, clear water 27-33 parts.
- 2. the coating on a kind of draw-bar box pull bar handle according to claim 1, it is characterised in that：The resin is organic One kind in silicones, fluorocarbon resin, phenolic resin, polyamide, furane resins.
- 3. the coating on a kind of draw-bar box pull bar handle according to claim 1, it is characterised in that：The coupling agent is silicon Alkane coupling agent KH550.
- 4. the coating on a kind of draw-bar box pull bar handle according to claim 1, it is characterised in that：The age resistor is anti- One kind in old agent AW, anti-aging agent RD, antioxidant A, age resistor CPPD.
- 5. the coating on a kind of draw-bar box pull bar handle according to claim 1, it is characterised in that：The modified titanium dioxide The preparation method of silicon is by Silica abrasive and to cross 300-400 mesh sieves, then addition and its weight identical pure water, 2 hours are stirred at room temperature, then add lauric acid amide of ethanol, continue to be stirred 3 hours, Ran Hougan It is dry, re-grind, produce improved silica.
- 6. the coating on a kind of draw-bar box pull bar handle according to claim 5, it is characterised in that：The coconut oil diethyl The mass ratio of alkylolamides and silica is 1：4.5.
- 7. the coating on a kind of draw-bar box pull bar handle according to claim 1, it is characterised in that：A kind of draw-bar box The preparation method of coating on pull bar handle is,I by resin, age resistor, improved silica, coupling agent, montmorillonite powder ,-(2,3- glycidoxy) propyl trimethoxy Silane and clear water are stirred 15 minutes, are then placed in reactor and are stirred 20 minutes at a temperature of 40-60 DEG C；II by the material left 10 minutes after stirring, then proceedes to add benzyl trimethyl tribromide ammonium, aliphatic acid diethanol acyl Amine, continue stirring 40 minutes；After III stands 5 minutes, DAA, ammonium tungstate are added, and is warming up to 55-75 DEG C, continues to be stirred 2 hours i.e. Can.
- 8. the coating on a kind of draw-bar box pull bar handle according to claim 7, it is characterised in that：The speed of the stirring For 1500-2000r/min.