CN107459794A - A kind of degradation plastic particle - Google Patents
A kind of degradation plastic particle Download PDFInfo
- Publication number
- CN107459794A CN107459794A CN201710830172.5A CN201710830172A CN107459794A CN 107459794 A CN107459794 A CN 107459794A CN 201710830172 A CN201710830172 A CN 201710830172A CN 107459794 A CN107459794 A CN 107459794A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic particle
- degradation plastic
- curing agent
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of degradation plastic particle, it is made up of the raw material of following parts by weight:Glass fibre:30 ~ 40 parts, PLA:30 ~ 50 parts, poly butyric:10 ~ 20 parts, polyethylene terephthalate:10 ~ 20 parts, graphene:5 ~ 8 parts, curing agent:3 ~ 5 parts, adhesive:5 ~ 10 parts.Stability of the present invention is good, safe, and can complete to degrade in a short time, avoids damaging environment.
Description
Technical field
The present invention relates to chemical technology field, more particularly to a kind of degradation plastic particle.
Background technology
It is well known that plastics(That is PP/PE plastics)It is widely used in daily life, building field, agriculture field, but it is existing
Modern plastic grain is all chemical products, is difficult to decompose under natural environment;It can just be degraded after being needed for a long time behind embedment underground,
Environment can be produced compared with havoc;So plastic garbage has turned into the thing of the generally acknowledged highly polluting environment artificially produced
Matter.
The content of the invention
For deficiencies of the prior art, it is an object of the invention to provide a kind of degradation plastic particle, surely
It is qualitative good, it is safe, and can complete to degrade in a short time, avoid damaging environment.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention is such:A kind of degradation plastic particle,
Characterized in that, it is made up of the raw material of following parts by weight:Glass fibre:30 ~ 40 parts, PLA:30 ~ 50 parts, poly butyric:
10 ~ 20 parts, polyethylene terephthalate:10 ~ 20 parts, graphene:5 ~ 8 parts, curing agent:3 ~ 5 parts, adhesive:5 ~ 10 parts.
Further, the curing agent is p-hydroxybenzenyl sulfonate.
Further, described adhesive is epoxies or polyesters.
Preferably, it is made up of the raw material of following parts by weight:Glass fibre:30 parts, PLA:40 parts, poly butyric:
10 parts, polyethylene terephthalate:20 parts, graphene:5 parts, curing agent:3 parts, adhesive:8 parts.
Preferably, it is made up of the raw material of following parts by weight:Glass fibre:40 parts, PLA:30 parts, poly- hydroxyl fourth
Acid:120 parts, polyethylene terephthalate:10 parts, graphene:8 parts, curing agent:5 parts, adhesive:5 parts.
Compared with prior art, the invention has the advantages that:The present invention is made up of a variety of environmentally friendly Raw material processings, its safety
Property it is high, stability is good, while degradation time itself is short, self degradation can be completed in the short time under field conditions (factors), will not be right
Environment causes big destruction, and the plastics entirety environmental protection index of formation is higher.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1:A kind of degradation plastic particle, is made up of the raw material of following parts by weight:Glass fibre:30 ~ 40 parts, gather
Lactic acid:30 ~ 50 parts, poly butyric:10 ~ 20 parts, polyethylene terephthalate:10 ~ 20 parts, graphene:5 ~ 8 parts, curing agent:3~
5 parts, adhesive:5 ~ 10 parts.Wherein, the curing agent is p-hydroxybenzenyl sulfonate;Described adhesive is epoxies or polyesters.
Embodiment 2, it is made up of the raw material of following parts by weight:Glass fibre:30 parts, PLA:40 parts, poly butyric:
10 parts, polyethylene terephthalate:20 parts, graphene:5 parts, curing agent:3 parts, adhesive:8 parts.
Embodiment 3, it is made up of the raw material of following parts by weight:Glass fibre:40 parts, PLA:30 parts, poly butyric:
120 parts, polyethylene terephthalate:10 parts, graphene:8 parts, curing agent:5 parts, adhesive:5 parts.
Finally it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention rather than restriction technologies side
Case, it will be understood by those within the art that, technical scheme is modified for those or equivalent substitution, and
The objective and scope of the technical program are not departed from, all should be covered among scope of the presently claimed invention.
Claims (5)
1. a kind of degradation plastic particle, it is characterised in that be made up of the raw material of following parts by weight:Glass fibre:30 ~ 40 parts,
PLA:30 ~ 50 parts, poly butyric:10 ~ 20 parts, polyethylene terephthalate:10 ~ 20 parts, graphene:5 ~ 8 parts, curing agent:
3 ~ 5 parts, adhesive:5 ~ 10 parts.
2. a kind of degradation plastic particle according to claim 1, it is characterised in that the curing agent is para hydroxybenzene sulphur
Acid.
3. a kind of degradation plastic particle according to claim 1, it is characterised in that described adhesive is epoxies or gathered
Esters.
4. a kind of degradation plastic particle according to claim 1, it is characterised in that by the raw material system of following parts by weight
Into:Glass fibre:30 parts, PLA:40 parts, poly butyric:10 parts, polyethylene terephthalate:20 parts, graphene:5 parts,
Curing agent:3 parts, adhesive:8 parts.
5. a kind of degradation plastic particle according to claim 1, it is characterised in that by the raw material system of following parts by weight
Into:Glass fibre:40 parts, PLA:30 parts, poly butyric:20 parts, polyethylene terephthalate:10 parts, graphene:8 parts,
Curing agent:5 parts, adhesive:5 parts.