CN107435276A - A kind of manufacture method of quick-dry type heat sublimation paper - Google Patents
A kind of manufacture method of quick-dry type heat sublimation paper Download PDFInfo
- Publication number
- CN107435276A CN107435276A CN201710770251.1A CN201710770251A CN107435276A CN 107435276 A CN107435276 A CN 107435276A CN 201710770251 A CN201710770251 A CN 201710770251A CN 107435276 A CN107435276 A CN 107435276A
- Authority
- CN
- China
- Prior art keywords
- paper
- coating
- water
- interfacial agent
- transfer printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of manufacture method of quick-dry type heat sublimation paper, is related to the manufacturing field of thermal dye sublimation transfer printing paper, can solve the problem that the rate of transform of transfer paper and the contradiction of rate of drying, accelerates rate of drying.The present invention includes following operating procedure：From the stronger body paper of water-resistance, supported ink well coating in body paper front coating thermal dye sublimation transfer printing first；Then in a kind of coating for being beneficial to lifting paper water imbibition of backsize of the body paper, the sizing material of described back coating is water+interfacial agent or water+starch+interfacial agent, wherein the mass percent of interfacial agent is 0.5% 5%, and the mass percent of starch is 0.5% 3%.
Description
Technical field
The invention belongs to the manufacturing field of thermal dye sublimation transfer printing paper, more particularly to a kind of manufacturer of quick-dry type heat sublimation paper
Method.
Background technology
Thermal dye sublimation transfer printing is that the picture and text such as portrait, landscape, word are used into the ink-jet printer equipped with thermal dye sublimation transfer printing ink
It is printed upon with mirror image posture in thermal dye sublimation transfer printing ink jet paper, then 200 DEG C or so is heated to by thermal transfer equipment, makes heat sublimation
Thermal transfer ink distillation on paper penetrates into stock, so as to which the chromatic image on paper is realistically transferred to textile, porcelain cup, porcelain
A kind of new technology in the materials such as disk, porcelain plate, metal.Thermal dye sublimation transfer printing picture and text are bright in luster, abundant, and its effect can be with printing phase
Match in excellence or beauty.
Consumptive material thermal dye sublimation transfer printing paper used in initial thermal transfer sublimating technologe can only rely on import, the technology to be obtained after passing to the country
To developing rapidly, but producer's technology of the thermal dye sublimation transfer printing paper of most domestic production at present is perfect not enough, and equipment relatively falls
Afterwards, low and middle-grade thermal dye sublimation transfer printing paper can only be produced, for the less demanding production of thermal dye sublimation transfer printing, for requiring higher
Thermal dye sublimation transfer printing is also needed using the higher foreign paper of price, and main cause is gone out in domestic thermal dye sublimation transfer printing paper production process
The existing rate of transform is low, the problem of slow drying speed.Rate of drying after thermal dye sublimation transfer printing paper marking ink directly determines heat sublimation
The efficiency of transfer, rate of drying can make it that user is easy to use soon, conveniently can continuously print, improve delivery rate.
After usual thermal dye sublimation transfer printing paper printing water-base ink, the water in ink is absorbed by coating absorbent material and body paper
Point, so as to reach dry target.The drying property of thermal dye sublimation transfer printing paper is mainly relevant with coating formula and body paper water imbibition.It is former
The water absorbing capacity of paper is relevant with applying glue intensity, if body paper applying glue is too poor（As water imbibition is too strong）, then easily made in coating
Into heat sublimation coating it is excessive toward migrating in paper, so as to reduce the ability for obstructing heat sublimation ink of coating, cause in ink
Dye molecule migrates toward original paper layer, although can supply a gap by lifting coating layer thickness, overweight coating, can cause to roll up
Qu Wenti, cause it is inconvenient for use, so as to influence the application performance of product.Speed is dried for lifting thermal dye sublimation transfer printing paper by part producer
Degree is started with from coating, is increased the ratio of water-absorbing material in coating, such as silica, aluminum oxide equal size, is applied so as to be lifted
The water imbibition ability of layer, but these materials while the heat sublimation dye molecule that can absorb water, can cause dye molecule in thermal transfer process
In be difficult to be sublimate on textile, cause the decline of the rate of transform, influence the performance of product.
The content of the invention
The invention provides a kind of manufacture method of quick-dry type heat sublimation paper, the rate of transform of thermal dye sublimation transfer printing paper can solve the problem that
Contradiction between rate of drying, improve the rate of transform and rate of drying.
To realize object above, the present invention takes following scheme：
A kind of manufacture method of quick-dry type heat sublimation paper, comprises the following steps：
（1）Supported ink well coating in body paper front coating thermal dye sublimation transfer printing, the coating of supporting ink well is cellulose substances；
（2）In a kind of coating for being beneficial to lifting paper water imbibition of the backsize of the body paper, the sizing material of described back coating
For water+interfacial agent or water+starch+interfacial agent, the mass percent of the interfacial agent is 0.5%-5%, institute
The mass percent for stating starch is 0.5%-3%.
Body paper described in above step is using the stronger body paper of water-resistance, Cobb60≤25g/ ㎡, described interfacial activity
Agent can be liquid dihydric alcohols, sodium n-alkylbenzenesulfonate, alkylsulfonate or petroleum sulfonate, and its function is to change body paper
Surface tension, destroy the water resistant ability that possesses because adding water repellent agent in body paper manufacturing process.
The beneficial effects of the invention are as follows：The invention provides a kind of manufacture method of quick-dry type heat sublimation paper, manufacturing
Cheng Zhong, using the stronger body paper of water-resistance, in favor of coating keeping in paper surface, reach the purpose of the high rate of transform；And carry on the back
Finishing coat use can lift the sizing material of paper water imbibition, destroy the water resistant ability of body paper in itself, lift the water absorbing capacity of body paper,
The ability of moisture in ink is absorbed so as to lift thermal dye sublimation transfer printing paper in printing because now front support ink well it is coating cured solidifying
Knot, positive coating performance can not influenceed again by lifting the water imbibition of body paper, so as to solve the contradiction of the rate of transform and rate of drying,
Improve rate of drying.
Specific embodiment
Embodiment 1
Body paper of the water imbibition for Cobb60=25gsm is used, thermal dye sublimation transfer printing paper and coating, coating amount 8gsm, the back of the body are applied in front
Face applies the interfacial agent aqueous solution, and interfacial agent is ethylene glycol, concentration 1%, coating weight 0.1gsm, heat sublimation is made
Transferring paper product, the rate of transform is 95% after testing, and drying time is 2 minutes, and drying time test condition is humidity RH50%, temperature
23 DEG C, printing ink amount is 240%.
Embodiment 2
Body paper of the water imbibition for Cobb60=20gsm is used, thermal dye sublimation transfer printing paper and coating, coating amount 8gsm, the back of the body are applied in front
Face applies interfacial agent and amidin, interfacial agent type sodium n-alkylbenzenesulfonate, starch concentration 2%, straight chain
Alkyl benzene sulphonate na concn is 2%, coating weight 0.5gsm, and thermal dye sublimation transfer printing paper product is made, and the rate of transform is 96% after testing, is done
The dry time is 3 minutes, and drying time test condition is humidity RH50%, and 23 DEG C of temperature, printing ink amount is 240%.
Embodiment 3
Body paper of the water imbibition for Cobb60=22gsm is used, thermal dye sublimation transfer printing paper and coating, coating amount 8gsm, the back of the body are applied in front
Face applies interfacial agent and amidin, interfacial agent type alkyl sulfonates, starch concentration 1%, straight chained alkyl
Benzene sulfonic acid sodium salt concentration is 0.5%, coating weight 0.3gsm, and thermal dye sublimation transfer printing paper product is made, and the rate of transform is 96% after testing, is dried
Time is 1 minute, and drying time test condition is humidity RH50%, and 23 DEG C of temperature, printing ink amount is 240%.
Embodiment 4
Body paper of the water imbibition for Cobb60=20gsm is used, thermal dye sublimation transfer printing paper and coating, coating amount 8gsm, the back of the body are applied in front
Surface starch aqueous solution starch concentration is 1%, and thermal dye sublimation transfer printing paper product is made, and the rate of transform is 96% after testing, and drying time is 7 points
Clock.
Embodiment 1-3 uses technical scheme in above example, and embodiment 4 is contrast experiment, backing layer sizing material
In without addition interfacial agent, from assay it can be seen that backing layer sizing material does not add heat sublimation made from interfacial agent
The drying time of transfer paper is obviously prolonged, and illustrates that the present invention efficiently solves the contradiction between the rate of transform and rate of drying, accelerates
Rate of drying.
Described above is only the preferred embodiment of the present invention, it should be pointed out that for those skilled in the art
For, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications should also regard
For protection scope of the present invention.
Claims (3)
1. a kind of manufacture method of quick-dry type heat sublimation paper, it is characterised in that comprise the following steps：
（1）Supported ink well coating in body paper front coating thermal dye sublimation transfer printing；
（2）In a kind of sizing material of the backsize of the body paper, described back coating sizing material be water+interfacial agent or water+
Starch+interfacial agent, the mass percent of the interfacial agent is 0.5%-5%, and the mass percent of the starch is
0.5%-3%。
2. the manufacture method of quick-dry type heat sublimation paper according to claim 1, it is characterised in that the body paper uses
Cobb60≤25g/ ㎡ body paper.
3. the manufacture method of quick-dry type heat sublimation paper according to claim 1, it is characterised in that described interfacial agent
For liquid dihydric alcohols, sodium n-alkylbenzenesulfonate, alkylsulfonate or petroleum sulfonate.