CN107418496A - High viscosity polyurethane fluid sealant - Google Patents
High viscosity polyurethane fluid sealant Download PDFInfo
- Publication number
- CN107418496A CN107418496A CN201710657269.0A CN201710657269A CN107418496A CN 107418496 A CN107418496 A CN 107418496A CN 201710657269 A CN201710657269 A CN 201710657269A CN 107418496 A CN107418496 A CN 107418496A
- Authority
- CN
- China
- Prior art keywords
- parts
- high viscosity
- fluid sealant
- tackifier
- viscosity polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of high viscosity polyurethane fluid sealant, according to the number of parts by weight, including following raw material:10~20 parts of 70~90 parts of polyurethane resin, 10~20 parts of styrene butadiene styrene block copolymer, 0.5~1 part of silane coupler, 3~6 parts of tackifier, 2~4 parts of crosslinking agent, 2~4 parts of propylene carbonate acid esters, 1~2 part of thixotropic agent, 1~3 part of ultra-violet absorber and diatomite, the tackifier are the mixture of liquid-state epoxy resin, polyvinyl acetate and flyash.The sealing adhesivity is strong, quality is good, easy to process, mar-resistance is good, ageing-resistant.
Description
Technical field
The invention belongs to encapsulant technical field, and in particular to a kind of high viscosity polyurethane fluid sealant.
Background technology
Encapsulant just refers to that can bear seam displacement is embedded in the material in building joint to reach airtight, watertight purpose
Referred to as encapsulant.Sealing member material has metal material (aluminium, lead, indium, stainless steel etc.), also there is nonmetallic materials (rubber, modeling
Material, ceramics, graphite etc.), composite (such as rubber-asbestos board, aerogel blanket-polyurethane), but most commonly used is rubber-like
Elastomeric material.Polyurethane resin is widely used as a kind of main encapsulant raw material, but due to poly- ammonia
Ester is processed more difficult in itself so that product quality is relatively general, and adhesive strength can not meet use demand instantly so that
Adhesive effect when in use is poor.And polyurethane inoxidizability itself is general, easy aging after long-time use, color occurs
Become so that using effect is deteriorated.
The content of the invention
The present invention proposes a kind of high viscosity polyurethane fluid sealant, and the sealing adhesivity is strong, quality is good, easy to process, anti-zoned
Trace is good, ageing-resistant.
The technical proposal of the invention is realized in this way:
A kind of high viscosity polyurethane fluid sealant, according to the number of parts by weight, including following raw material:
70~90 parts of polyurethane resin, 10~20 parts of SBS, silane coupler
0.5~1 part, 3~6 parts of tackifier, 2~4 parts of crosslinking agent, 2~4 parts of propylene carbonate acid esters, 1~2 part of thixotropic agent, ultraviolet radiation absorption
10~20 parts of 1~3 part of agent and diatomite, the tackifier are the mixing of liquid-state epoxy resin, polyvinyl acetate and flyash
Thing.
Preferably, the silane coupler is selected from γ-(2,3- the third oxygen of epoxy) propyl trimethoxy silicane, γ-aminopropyl
Triethoxysilane, γ-aminopropyltrimethoxysilane, N- β (aminoethyl)-gamma-aminopropyl-triethoxy-silane, N- β (ammonia second
Base)-γ-aminopropyltrimethoxysilane, N- β (aminoethyl)-γ-aminopropyltriethoxy dimethoxysilane, N- β (aminoethyl)-
γ-aminopropyltriethoxy diethoxy silane or phenylaminomethyl triethoxysilane.
Preferably, the crosslinking agent is hydroxypropyl acrylate.
Preferably, the thixotropic agent is aerosil.
Preferably, the ultraviolet absorber is single benzoic acid resorcinol.
The preparation method of high viscosity polyurethane fluid sealant of the present invention:
By polyurethane resin, SBS, crosslinking agent, silane coupler and diatom
Soil stirring heating, temperature control open vacuum pumping negative pressure, Stress control is below -0.08MPa at 100 DEG C~120 DEG C;So
After cool to less than 70 DEG C, be passed through drying nitrogen and release vacuum, temperature control adds the propylene carbonate of formula ratio at 60~70 DEG C
Acid esters and tackifier stirring reaction, reaction adds thixotropic agent after terminating and ultra-violet absorber is well mixed, you can.
Beneficial effects of the present invention:
The present invention is using polyurethane as primary raw material, using SBS, silane coupled
Agent and diatomite coordinate the viscosity for enhancing fluid sealant, and final obtained product viscosity is strong, quality is good, easy to process, anti-scratch
Good, the ageing-resistant, Anti- tarnishing of property, using effect are good.Tensile strength has reached more than 5.2MPa, shear strength reached 4.5MPa with
On.According to GB/T13477《Test method for building sealants》, fluid sealant of the invention stretches caking property 900,000 times without destruction surely.
Embodiment
Embodiment 1
A kind of high viscosity polyurethane fluid sealant, according to the number of parts by weight, including following raw material:
80 parts of polyurethane resin, 14 parts of SBS, γ-(2,3- the third oxygen of epoxy) third
0.5 part of base trimethoxy silane, 3 parts of tackifier, 3 parts of hydroxypropyl acrylate, 3 parts of propylene carbonate acid esters, aerosil 1
16 parts of part, 1 part of single benzoic acid resorcinol and diatomite.Tackifier are liquid-state epoxy resin, polyvinyl acetate and fine coal
The mixture of ash.
Embodiment 2
A kind of high viscosity polyurethane fluid sealant, according to the number of parts by weight, including following raw material:
70 parts of polyurethane resin, 20 parts of SBS, N- β (aminoethyl)-γ-ammonia third
1 part of ethyl triethoxy silicane alkane, 4 parts of tackifier, 3 parts of hydroxypropyl acrylate, 3 parts of propylene carbonate acid esters, 2 parts of aerosil,
10 parts of 3 parts of single benzoic acid resorcinol and diatomite.Tackifier are liquid-state epoxy resin, polyvinyl acetate and flyash
Mixture.
Embodiment 3
A kind of high viscosity polyurethane fluid sealant, according to the number of parts by weight, including following raw material:
82 parts of polyurethane resin, 18 parts of SBS, phenylaminomethyl triethoxy
Between 1 part of silane, 6 parts of tackifier, 4 parts of hydroxypropyl acrylate, 4 parts of propylene carbonate acid esters, 2 parts of aerosil, single benzoic acid
20 parts of 3 parts of benzenediol ester and diatomite, tackifier are the mixture of liquid-state epoxy resin, polyvinyl acetate and flyash.
Embodiment 4
A kind of high viscosity polyurethane fluid sealant, according to the number of parts by weight, including following raw material:
90 parts of polyurethane resin, 10 parts of SBS, N- β (aminoethyl)-γ-ammonia third
0.5 part of ylmethyl diethoxy silane, 6 parts of tackifier, 2 parts of hydroxypropyl acrylate, 4 parts of propylene carbonate acid esters, gas phase titanium dioxide
16 parts of 1 part of silicon, 3 parts of single benzoic acid resorcinol and diatomite, the tackifier are liquid-state epoxy resin, polyvinyl acetate
With the mixture of flyash.
Embodiment 5
A kind of high viscosity polyurethane fluid sealant, according to the number of parts by weight, including following raw material:
85 parts of polyurethane resin, 12 parts of SBS, N- β (aminoethyl)-γ-ammonia third
0.5 part of ylmethyl diethoxy silane, 6 parts of tackifier, 2 parts of hydroxypropyl acrylate, 4 parts of propylene carbonate acid esters, gas phase titanium dioxide
18 parts of 1 part of silicon, 3 parts of single benzoic acid resorcinol and diatomite, the tackifier are liquid-state epoxy resin, polyvinyl acetate
With the mixture of flyash.
Embodiment 6
A kind of high viscosity polyurethane fluid sealant, according to the number of parts by weight, including following raw material:
80 parts of polyurethane resin, 14 parts of SBS, gamma-aminopropyl-triethoxy silicon
1 part of alkane, 5 parts of tackifier, 4 parts of hydroxypropyl acrylate, 2 parts of propylene carbonate acid esters, 1 part of aerosil, single benzoic acid isophthalic
10 parts of two 3 parts of phenolic esters and diatomite, the tackifier are the mixture of liquid-state epoxy resin, polyvinyl acetate and flyash.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
God any modification, equivalent substitution and improvements made etc., should be included in the scope of the protection with principle.
Claims (5)
- A kind of 1. high viscosity polyurethane fluid sealant, it is characterised in that according to the number of parts by weight, including following raw material:70~90 parts of polyurethane resin, 10~20 parts of SBS, silane coupler 0.5~ 1 part, 3~6 parts of tackifier, 2~4 parts of crosslinking agent, 2~4 parts of propylene carbonate acid esters, 1~2 part of thixotropic agent, ultra-violet absorber 1~ 3 parts and 10~20 parts of diatomite, the tackifier are the mixture of liquid-state epoxy resin, polyvinyl acetate and flyash.
- 2. high viscosity polyurethane fluid sealant according to claim 1, it is characterised in that the silane coupler be selected from γ- (2,3- the third oxygen of epoxy) propyl trimethoxy silicane, gamma-aminopropyl-triethoxy-silane, γ-aminopropyltrimethoxysilane, N- β (aminoethyl)-gamma-aminopropyl-triethoxy-silane, N- β (aminoethyl)-γ-aminopropyltrimethoxysilane, N- β (ammonia second Base)-γ-aminopropyltriethoxy dimethoxysilane, N- β (aminoethyl)-γ-aminopropyltriethoxy diethoxy silane or phenylamino MTES.
- 3. high viscosity polyurethane fluid sealant according to claim 1, it is characterised in that the crosslinking agent is acrylic acid hydroxypropyl Ester.
- 4. high viscosity polyurethane fluid sealant according to claim 1, it is characterised in that the thixotropic agent is gas phase titanium dioxide Silicon.
- 5. high viscosity polyurethane fluid sealant according to claim 1, it is characterised in that the ultraviolet absorber is single benzene first Sour resorcinol.