CN107393647A - A kind of cable low-temperature resistant fiber braiding layer - Google Patents
A kind of cable low-temperature resistant fiber braiding layer Download PDFInfo
- Publication number
- CN107393647A CN107393647A CN201710674970.3A CN201710674970A CN107393647A CN 107393647 A CN107393647 A CN 107393647A CN 201710674970 A CN201710674970 A CN 201710674970A CN 107393647 A CN107393647 A CN 107393647A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature resistant
- cable
- braiding layer
- resistant fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of cable low-temperature resistant fiber braiding layer, and it is formed according to the parts by weight of following raw material:58 parts of 50 100 parts of polypropylene fibre, 10 20 parts of acrylic fibers, 15 20 parts of polypropylene fibre, 20 30 parts of spandex, 5 10 parts of Black Warrior mineral wool and fiber surface coating.Influence of the environment to cable drops in the cable of present invention low-temperature resistant fiber braiding layer, effectively raises the resistance to low temperature of cable.
Description
Technical field
The present invention relates to a kind of fiber braiding layer, more particularly to a kind of cable low-temperature resistant fiber braiding layer.
Background technology
At present, with the development of the social economy, cable market demand is constantly expanded in China and the scientific research to cable is thrown
What is entered is deepened continuously, while the quality requirement of cable is also constantly improved, and the particularly requirement to cable cover(ing) is higher, it is desirable to
The side such as its insulating properties, high and low temperature resistance, fatigue durability, anti-broken string ability, antijamming capability, mechanical resistant damage, water proofing property
Face requires all especially high.
The content of the invention
The purpose of the present invention is that to solve the above problems and provides a kind of influence for reducing environment to cable, has
The cable low-temperature resistant fiber braiding layer of the resistance to low temperature for improving cable of effect.
To achieve these goals, the present invention is achieved by the following technical solutions, and a kind of cable is compiled with low-temperature resistant fiber
Tissue layer, it is formed according to the parts by weight of following raw material:Polypropylene fibre 50-100 parts, acrylic fibers 10-20 parts, polypropylene fibre 15-20 parts,
Spandex 20-30 parts, Black Warrior mineral wool 5-10 parts and fiber surface coating 5-8 parts.
Further, a kind of cable low-temperature resistant fiber braiding layer, it is formed according to the parts by weight of following raw material:Poly- third
Alkene fiber 60-80 parts, acrylic fibers 12-15 parts, polypropylene fibre 15-18 parts, spandex 25-27 parts, Black Warrior mineral wool 6-9 parts and fiber surface
Coating 6-8 parts.
Further, a kind of cable low-temperature resistant fiber braiding layer, it is formed according to the parts by weight of following raw material:It is poly-
7 parts of 70 parts of tacryl, 13 parts of acrylic fibers, 17 parts of polypropylene fibre, 27 parts of spandex, 7 parts of Black Warrior mineral wool and fiber surface coating.
Particularly, the fiber surface coating its according to following raw material parts by weight form:Acrylic resin 20-30
Part, biocolloid 1-5 parts, binding agent 3-10 parts, curing agent 2-5 parts, coupling agent 1-5 parts and stabilizer 2-6 parts.
The beneficial effects of the invention are as follows:Influence of the environment to cable drops in the cable of present invention low-temperature resistant fiber braiding layer,
Effectively raise the resistance to low temperature of cable.
Embodiment
Specific embodiment 1:A kind of cable low-temperature resistant fiber braiding layer, it is formed according to the parts by weight of following raw material:
5 parts of 50 parts of polypropylene fibre, 10 parts of acrylic fibers, 15 parts of polypropylene fibre, 20 parts of spandex, 5 parts of Black Warrior mineral wool and fiber surface coating.
Wherein fiber surface coating its according to following raw material parts by weight form:20 parts of acrylic resin, biocolloid 1
Part, 3 parts of binding agent, 2 parts of curing agent, 1 part of coupling agent and 2 parts of stabilizer.
Specific embodiment 2:A kind of cable low-temperature resistant fiber braiding layer, it is formed according to the parts by weight of following raw material:
7 parts of 70 parts of polypropylene fibre, 13 parts of acrylic fibers, 17 parts of polypropylene fibre, 27 parts of spandex, 7 parts of Black Warrior mineral wool and fiber surface coating.
Wherein fiber surface coating its according to following raw material parts by weight form:25 parts of acrylic resin, biocolloid 3
Part, 6 parts of binding agent, 3 parts of curing agent, 3 parts of coupling agent and 4 parts of stabilizer.
Specific embodiment 3:A kind of cable low-temperature resistant fiber braiding layer, it is formed according to the parts by weight of following raw material:
8 parts of 100 parts of polypropylene fibre, 20 parts of acrylic fibers, 20 parts of polypropylene fibre, 30 parts of spandex, 10 parts of Black Warrior mineral wool and fiber surface coating.
Wherein fiber surface coating its according to following raw material parts by weight form:30 parts of acrylic resin, biocolloid 5
Part, 10 parts of binding agent, 5 parts of curing agent, 5 parts of coupling agent and 6 parts of stabilizer.
Embodiment provided above is the better embodiment of the present invention, is only used for the convenient explanation present invention, not to this hair
It is bright to make any formal limitation, any those of ordinary skill in the art, if putting forward skill not departing from the present invention
In the range of art feature, using the equivalent embodiment for locally changing or modifying made by disclosed technology contents, and
Without departing from the technical feature content of the present invention, in the range of still falling within the technology of the present invention feature.
Claims (4)
- A kind of 1. cable low-temperature resistant fiber braiding layer, it is characterised in that:Formed according to the parts by weight of following raw material:Polypropylene Fiber 50-100 parts, acrylic fibers 10-20 parts, polypropylene fibre 15-20 parts, spandex 20-30 parts, Black Warrior mineral wool 5-10 parts and fiber surface Coating 5-8 parts.
- A kind of 2. cable low-temperature resistant fiber braiding layer according to claim 1, it is characterised in that:According to following raw material Parts by weight form:Polypropylene fibre 60-80 parts, acrylic fibers 12-15 parts, polypropylene fibre 15-18 parts, spandex 25-27 parts, Black Warrior mineral wool 6-9 parts and fiber surface coating 6-8 parts.
- A kind of 3. cable low-temperature resistant fiber braiding layer according to claim 1, it is characterised in that:According to following raw material Parts by weight form:70 parts of polypropylene fibre, 13 parts of acrylic fibers, 17 parts of polypropylene fibre, 27 parts of spandex, 7 parts of Black Warrior mineral wool and fiber 7 parts of surface coating.
- A kind of 4. cable low-temperature resistant fiber braiding layer according to claim 1 or 2 or 3, it is characterised in that:The fiber Surface coating its according to following raw material parts by weight form:Acrylic resin 20-30 parts, biocolloid 1-5 parts, binding agent 3- 10 parts, curing agent 2-5 parts, coupling agent 1-5 parts and stabilizer 2-6 parts.