CN107383970A - 一种高光泽高耐候外墙乳胶漆及其制备方法 - Google Patents
一种高光泽高耐候外墙乳胶漆及其制备方法 Download PDFInfo
- Publication number
- CN107383970A CN107383970A CN201710868066.6A CN201710868066A CN107383970A CN 107383970 A CN107383970 A CN 107383970A CN 201710868066 A CN201710868066 A CN 201710868066A CN 107383970 A CN107383970 A CN 107383970A
- Authority
- CN
- China
- Prior art keywords
- parts
- exterior wall
- latex paint
- emulsion
- wall latex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种高光泽高耐候外墙乳胶漆及其制备方法，所述乳胶漆包括如下重量份的成分：核壳型有机硅丙烯酸酯共聚乳液：30~40份，苯丙乳液：15~25份，羟乙基纤维素：10~15份，纳米二氧化硅：10~15份，醋酸乙烯：5~10份，二甲基硅油：1~5份，高岭土：5~10份，丙二醇：1~5份，聚乙烯醇：10~15份，防霉剂：1~5份，成膜助剂：1~5份，消泡剂：1~5份，流平剂：1~5份，分散剂：1~5份，去离子水：40~50份。所述外墙乳胶漆具有优异的耐候性、附着力、遮盖力、耐水性、耐洗刷性，耐久性可达5年以上，广泛适用于宾馆、住宅楼、学校、办公楼宇等。
Description
技术领域
本发明属于涂料技术领域，具体涉及一种高光泽高耐候外墙乳胶漆及其制备方法。
背景技术
乳胶漆是乳胶涂料的俗称，诞生于二十世纪七十年代中下期，是以丙烯酸酯共聚乳液为代表的一大类合成树脂乳液涂料。乳胶漆是水分散性涂料，它 是以合成树脂乳液为基料，填料经过研磨分散后加入各种助剂精制而成的涂料。乳胶漆具备了与传统墙面涂料不同的众多优点，如易于涂刷、干燥迅速、漆膜耐水、耐擦洗性好等。在我国，人们习惯上把合成树脂乳液为基料，以水为分散介质，加入颜料、填料（亦称体质颜料）和助剂，经一定工艺过程制成的涂料，叫做乳胶漆，也叫乳胶涂料。
乳胶漆是水性涂料，它们的漆膜性能比溶剂型涂料要好得多，占溶剂型涂料一半的有机溶剂在这里被水代替了，因此有机溶剂的毒性问题，基本上被乳胶漆彻底的解决了。乳胶漆是以一些聚合物水溶液做成膜物质的，除水和安全无害的不同类型聚合物或聚合物之外，还含有小量乳化剂和微量未聚合的游离单体，游离单体是一些能挥发的小分子物质，存在不同程度的毒性问题，环保漆游离单体的浓度控制在0.1%以下，助剂的用量多的有2~3%；少的只占0.05%至0.1%之间。
对于乳胶漆，目前国内主要存在如下专利文献：
公开号为107057488A的中国专利公开了一种乳胶漆及其制备方法，属于乳胶漆技术领域。本发明的聚醋酸乙烯乳胶漆包括以下按照重量份数计的原料：聚醋酸乙烯乳液40-50份、聚甲基丙烯酸钠0.05-0.1份、分散剂0.3-0.5份、五氯酚钠0.2-0.4份、羧甲基纤维素增稠剂5-7份、甲基戊醇2-4份、丙二醇2-3份、消泡剂0.05-0.20份、去离子水15-20份、钛白粉15-25份、锌钡白5-10份、轻质碳酸钙10-15份、滑石粉5-10份。本发明与现有聚醋酸乙烯乳胶漆相比，具有生产成本低，涂料与涂装表面粘结性能好，涂层经久耐用的优点。
发明内容
为解决上述存在的问题，本发明的目的在于提供一种高光泽高耐候外墙乳胶漆及其制备方法，所述外墙乳胶漆具有优异的耐候性、附着力、遮盖力、耐水性、耐洗刷性，耐久性可达5年以上，广泛适用于宾馆、住宅楼、学校、办公楼宇等。
为达到上述目的，本发明的技术方案是：
一种高光泽高耐候外墙乳胶漆，所述乳胶漆包括如下重量份的成分：核壳型有机硅丙烯酸酯共聚乳液：30~40份，苯丙乳液：15~25份，羟乙基纤维素：10~15份，纳米二氧化硅：10~15份，醋酸乙烯：5~10份，二甲基硅油：1~5份，高岭土：5~10份，丙二醇：1~5份，聚乙烯醇：10~15份，防霉剂：1~5份，成膜助剂：1~5份，消泡剂：1~5份，流平剂：1~5份，分散剂：1~5份，去离子水：40~50份。
进一步，所述乳胶漆包括如下重量份的成分：核壳型有机硅丙烯酸酯共聚乳液：35~40份，苯丙乳液：15~20份，羟乙基纤维素：13~15份，纳米二氧化硅：10~12份，醋酸乙烯：5~8份，二甲基硅油：1~3份，高岭土：6~10份，丙二醇：1~3份，聚乙烯醇：12~15份，防霉剂：1~3份，成膜助剂：3~5份，消泡剂：2~5份，流平剂：1~4份，分散剂：3~5份，去离子水：40~50份。
优选地，所述乳胶漆包括如下重量份的成分：核壳型有机硅丙烯酸酯共聚乳液：35份，苯丙乳液：20份，羟乙基纤维素：13份，纳米二氧化硅：12份，醋酸乙烯：7份，二甲基硅油：2份，高岭土：7份，丙二醇：2份，聚乙烯醇：13份，防霉剂：2份，成膜助剂：4份，消泡剂：3份，流平剂：2份，分散剂：4份，去离子水：45份。
优选地，所述消泡剂为酰胺类消泡剂、有机硅类消泡剂或矿物油类消泡剂。
优选地，所述成膜助剂为丙二醇丁醚、醇酯十二或丙二醇苯醚。
优选地，所述防霉剂为苯并咪唑氨基甲酸甲酯。
优选地，所述分散剂为六偏磷酸钠。
优选地，所述流平剂为聚氨酯类流平剂。
同时，本发明还提供一种高光泽高耐候外墙乳胶漆的制备方法，其特征在于，所述制备方法包括如下步骤：1)取搅拌机，按重量份将核壳型有机硅丙烯酸酯共聚乳液、苯丙乳液、羟乙基纤维素、纳米二氧化硅、醋酸乙烯、二甲基硅油、高岭土及50wt%的去离子水加入搅拌机内，在常温、500~600转/分的转速下搅拌20~30分钟；2)加入丙二醇、聚乙烯醇、防霉剂、成膜助剂、消泡剂、流平剂、分散剂及剩余去离子水，升温至30~40℃，在700~800转/分的转速下搅拌10~20分钟，冷却至室温，过滤，静置，即得所述高光泽高耐候外墙乳胶漆。
本发明具有如下优点：
所述外墙乳胶漆具有优异的耐候性、附着力、遮盖力、耐水性、耐洗刷性，耐久性可达5年以上，广泛适用于宾馆、住宅楼、学校、办公楼宇等。
具体实施方式
下面通过具体实施例对本发明做进一步的说明，但实施例并不限制本发明的保护范围。
本发明所提供的一种高光泽高耐候外墙乳胶漆，所述乳胶漆包括如下重量份的成分：核壳型有机硅丙烯酸酯共聚乳液：30~40份，苯丙乳液：15~25份，羟乙基纤维素：10~15份，纳米二氧化硅：10~15份，醋酸乙烯：5~10份，二甲基硅油：1~5份，高岭土：5~10份，丙二醇：1~5份，聚乙烯醇：10~15份，防霉剂：1~5份，成膜助剂：1~5份，消泡剂：1~5份，流平剂：1~5份，分散剂：1~5份，去离子水：40~50份。
进一步，所述乳胶漆包括如下重量份的成分：核壳型有机硅丙烯酸酯共聚乳液：35~40份，苯丙乳液：15~20份，羟乙基纤维素：13~15份，纳米二氧化硅：10~12份，醋酸乙烯：5~8份，二甲基硅油：1~3份，高岭土：6~10份，丙二醇：1~3份，聚乙烯醇：12~15份，防霉剂：1~3份，成膜助剂：3~5份，消泡剂：2~5份，流平剂：1~4份，分散剂：3~5份，去离子水：40~50份。
优选地，所述乳胶漆包括如下重量份的成分：核壳型有机硅丙烯酸酯共聚乳液：35份，苯丙乳液：20份，羟乙基纤维素：13份，纳米二氧化硅：12份，醋酸乙烯：7份，二甲基硅油：2份，高岭土：7份，丙二醇：2份，聚乙烯醇：13份，防霉剂：2份，成膜助剂：4份，消泡剂：3份，流平剂：2份，分散剂：4份，去离子水：45份。
优选地，所述消泡剂为酰胺类消泡剂、有机硅类消泡剂或矿物油类消泡剂。
优选地，所述成膜助剂为丙二醇丁醚、醇酯十二或丙二醇苯醚。
优选地，所述防霉剂为苯并咪唑氨基甲酸甲酯。
优选地，所述分散剂为六偏磷酸钠。
优选地，所述流平剂为聚氨酯类流平剂。
同时，本发明还提供一种高光泽高耐候外墙乳胶漆的制备方法，其特征在于，所述制备方法包括如下步骤：1)取搅拌机，按重量份将核壳型有机硅丙烯酸酯共聚乳液、苯丙乳液、羟乙基纤维素、纳米二氧化硅、醋酸乙烯、二甲基硅油、高岭土及50wt%的去离子水加入搅拌机内，在常温、500~600转/分的转速下搅拌20~30分钟；2)加入丙二醇、聚乙烯醇、防霉剂、成膜助剂、消泡剂、流平剂、分散剂及剩余去离子水，升温至30~40℃，在700~800转/分的转速下搅拌10~20分钟，冷却至室温，过滤，静置，即得所述高光泽高耐候外墙乳胶漆。
本发明所提供的一种高光泽高耐候外墙乳胶漆，具有优异的耐候性、附着力、遮盖力、耐水性、耐洗刷性，耐久性可达5年以上，广泛适用于宾馆、住宅楼、学校、办公楼宇等。
需要说明的是，以上实施例仅用以说明本发明的技术方案而非限制。尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的范围，其均应涵盖在本发明的权利要求范围中。
Claims (9)
1.一种高光泽高耐候外墙乳胶漆，其特征在于，所述乳胶漆包括如下重量份的成分：核壳型有机硅丙烯酸酯共聚乳液：30~40份，苯丙乳液：15~25份，羟乙基纤维素：10~15份，纳米二氧化硅：10~15份，醋酸乙烯：5~10份，二甲基硅油：1~5份，高岭土：5~10份，丙二醇：1~5份，聚乙烯醇：10~15份，防霉剂：1~5份，成膜助剂：1~5份，消泡剂：1~5份，流平剂：1~5份，分散剂：1~5份，去离子水：40~50份。
2.根据权利要求1所述的高光泽高耐候外墙乳胶漆，其特征在于，所述乳胶漆包括如下重量份的成分：核壳型有机硅丙烯酸酯共聚乳液：35~40份，苯丙乳液：15~20份，羟乙基纤维素：13~15份，纳米二氧化硅：10~12份，醋酸乙烯：5~8份，二甲基硅油：1~3份，高岭土：6~10份，丙二醇：1~3份，聚乙烯醇：12~15份，防霉剂：1~3份，成膜助剂：3~5份，消泡剂：2~5份，流平剂：1~4份，分散剂：3~5份，去离子水：40~50份。
3.根据权利要求1所述的高光泽高耐候外墙乳胶漆，其特征在于，所述乳胶漆包括如下重量份的成分：核壳型有机硅丙烯酸酯共聚乳液：35份，苯丙乳液：20份，羟乙基纤维素：13份，纳米二氧化硅：12份，醋酸乙烯：7份，二甲基硅油：2份，高岭土：7份，丙二醇：2份，聚乙烯醇：13份，防霉剂：2份，成膜助剂：4份，消泡剂：3份，流平剂：2份，分散剂：4份，去离子水：45份。
4.根据权利要求1所述的高光泽高耐候外墙乳胶漆，其特征在于，所述消泡剂为酰胺类消泡剂、有机硅类消泡剂或矿物油类消泡剂。
5.根据权利要求1所述的高光泽高耐候外墙乳胶漆，其特征在于，所述成膜助剂为丙二醇丁醚、醇酯十二或丙二醇苯醚。
6.根据权利要求1所述的高光泽高耐候外墙乳胶漆，其特征在于，所述防霉剂为苯并咪唑氨基甲酸甲酯。
7.根据权利要求1所述的高光泽高耐候外墙乳胶漆，其特征在于，所述分散剂为六偏磷酸钠。
8.根据权利要求1所述的高光泽高耐候外墙乳胶漆，其特征在于，所述流平剂为聚氨酯类流平剂。
9.一种如权利要求1~8中任一项所述的高光泽高耐候外墙乳胶漆的制备方法，其特征在于，所述制备方法包括如下步骤：1)取搅拌机，按重量份将核壳型有机硅丙烯酸酯共聚乳液、苯丙乳液、羟乙基纤维素、纳米二氧化硅、醋酸乙烯、二甲基硅油、高岭土及50wt%的去离子水加入搅拌机内，在常温、500~600转/分的转速下搅拌20~30分钟；2)加入丙二醇、聚乙烯醇、防霉剂、成膜助剂、消泡剂、流平剂、分散剂及剩余去离子水，升温至30~40℃，在700~800转/分的转速下搅拌10~20分钟，冷却至室温，过滤，静置，即得所述高光泽高耐候外墙乳胶漆。