CN107383505A - A kind of shock-absorbing type rubber - Google Patents
A kind of shock-absorbing type rubber Download PDFInfo
- Publication number
- CN107383505A CN107383505A CN201710665839.0A CN201710665839A CN107383505A CN 107383505 A CN107383505 A CN 107383505A CN 201710665839 A CN201710665839 A CN 201710665839A CN 107383505 A CN107383505 A CN 107383505A
- Authority
- CN
- China
- Prior art keywords
- parts
- shock
- absorbing type
- type rubber
- nitrosodimethylamine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of shock-absorbing type rubber, is made up of the raw material components of following number：25 36 parts of neoprene, 15 27 parts of ethylene propylene diene rubber, 58 parts of silicon powder, 6.5 8.5 parts of boron nitride, 12 15 parts of zinc Isoocatanoate, 23 parts of boric acid, 21 34 parts of carbon black, 15 18 parts of makrolon, 69 parts of toluene, 15 33 parts of di-isopropylbenzene hydroperoxide, 8.5 10.5 parts of benzoyl peroxide, 0.3 0.6 parts of urethanes, 0.8 1.2 parts of nitrosodimethylamine, 34 parts of phenylenediamine age resistor, 23 parts of paraffin, 6 15 parts of organized clay mineral, water is some, the shock-absorbing type rubber of the present invention is process using plurality of raw materials, gained rubber tube cost is cheap, damping property is good, pyroconductivity is high, endurance long lifespan.
Description
Technical field
The present invention relates to field of rubber technology, and in particular to a kind of shock-absorbing type rubber.
Background technology
In recent years, as automobile enters average family, people are while enjoying convenient and swift, to the comfortableness of vehicle
Higher requirement is proposed, therefore the effect of vibration-absorptive material is more and more important.Rubber is extensive as a kind of elastomeric material
Be used as automobile-used vibration-absorptive material, the combined shock absorption product of rubber and metal is widely used in automobile suspension system, and to ensureing
Riding comfort, stability and the tack of automobile have vital meaning.Automobile subtracts in different road conditions downward drivings
Shake element subjects different degrees of mastication forces and twisting resistance for a long time, often because the bonding failure of metal and rubber, and
Cause the damage of shock absorber part.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of shock-absorbing type rubber.
The present invention is achieved through the following technical solutions：
A kind of shock-absorbing type rubber, is made up of the raw material components of following number：Neoprene 25-36 parts, EPDM
Rubber 15-27 parts, silicon powder 5-8 parts, boron nitride 6.5-8.5 parts, zinc Isoocatanoate 12-15 parts, boric acid 2-3 parts, carbon black 21-34
Part, makrolon 15-18 parts, toluene 6-9 parts, di-isopropylbenzene hydroperoxide 15-33 parts, benzoyl peroxide 8.5-10.5 parts,
Urethanes 0.3-0.6 parts, nitrosodimethylamine 0.8-1.2 parts, phenylenediamine age resistor 3-4 parts, paraffin 2-3 parts, have
Machine clay mineral 6-15 parts, water are some.
Preferably, can be also made up of the raw material components of following number：31 parts of neoprene, 21 parts of ethylene propylene diene rubber, silicon
6.5 parts of micro mist, 7.5 parts of boron nitride, 13.5 parts of zinc Isoocatanoate, 2.5 parts of boric acid, 27 parts of carbon black, 17 parts of makrolon, 8 parts of toluene,
24 parts of di-isopropylbenzene hydroperoxide, 9.5 parts of benzoyl peroxide, 0.5 part of urethanes, 1 part of nitrosodimethylamine, benzene two
3.5 parts of amines antioxidants, 2.5 parts of paraffin, 11 parts of organized clay mineral, water are some.
A kind of shock-absorbing type rubber, preparation method are as follows：
(1) deionized water of above-mentioned mass fraction is heated to 70-85 DEG C, then by the neoprene rubber of above-mentioned mass fraction
Glue, ethylene propylene diene rubber, silicon powder, boron nitride, zinc Isoocatanoate, boric acid, carbon black, makrolon, toluene sequentially add, and mixing is equal
It is even, obtain solution A；
(2) di-isopropylbenzene hydroperoxide and benzoyl peroxide are mixed；
(3) it is the urethanes of above-mentioned solution A and above-mentioned mass fraction, nitrosodimethylamine, phenylenediamine is anti-old
After agent, paraffin, organized clay mineral are well mixed, room temperature is cooled to, that is, obtains this product.
The beneficial effects of the present invention are：The shock-absorbing type rubber of the present invention is process using plurality of raw materials, gained
Rubber tube cost is cheap, and damping property is good, pyroconductivity is high, endurance long lifespan.
Embodiment
Embodiment:A kind of shock-absorbing type rubber, is made up of the raw material components of following number：Neoprene 25-36 parts, three
First EP rubbers 15-27 parts, silicon powder 5-8 parts, boron nitride 6.5-8.5 parts, zinc Isoocatanoate 12-15 parts, boric acid 2-3 parts, carbon black
21-34 parts, makrolon 15-18 parts, toluene 6-9 parts, di-isopropylbenzene hydroperoxide 15-33 parts, benzoyl peroxide 8.5-
10.5 parts, urethanes 0.3-0.6 parts, nitrosodimethylamine 0.8-1.2 parts, phenylenediamine age resistor 3-4 parts, paraffin 2-
3 parts, organized clay mineral 6-15 parts, water it is some.
Further, can be also made up of the raw material components of following number：31 parts of neoprene, 21 parts of ethylene propylene diene rubber,
6.5 parts of silicon powder, 7.5 parts of boron nitride, 13.5 parts of zinc Isoocatanoate, 2.5 parts of boric acid, 27 parts of carbon black, 17 parts of makrolon, toluene 8
Part, 24 parts of di-isopropylbenzene hydroperoxide, 9.5 parts of benzoyl peroxide, 0.5 part of urethanes, 1 part of nitrosodimethylamine,
3.5 parts of phenylenediamine age resistor, 2.5 parts of paraffin, 11 parts of organized clay mineral, water are some.
A kind of shock-absorbing type rubber, preparation method are as follows：
(1) deionized water of above-mentioned mass fraction is heated to 70-85 DEG C, then by the neoprene rubber of above-mentioned mass fraction
Glue, ethylene propylene diene rubber, silicon powder, boron nitride, zinc Isoocatanoate, boric acid, carbon black, makrolon, toluene sequentially add, and mixing is equal
It is even, obtain solution A；
(2) di-isopropylbenzene hydroperoxide and benzoyl peroxide are mixed；
(3) it is the urethanes of above-mentioned solution A and above-mentioned mass fraction, nitrosodimethylamine, phenylenediamine is anti-old
After agent, paraffin, organized clay mineral are well mixed, room temperature is cooled to, that is, obtains this product.
Described above is only the preferred application implementation mode of the present invention, it is noted that for the common skill of the art
For art personnel, without departing from the technical principles of the invention, some improvement can also be made.
Claims (3)
- A kind of 1. shock-absorbing type rubber, it is characterised in that：It is made up of the raw material components of following number：Neoprene 25-36 parts, Ethylene propylene diene rubber 15-27 parts, silicon powder 5-8 parts, boron nitride 6.5-8.5 parts, zinc Isoocatanoate 12-15 parts, boric acid 2-3 parts, charcoal Black 21-34 parts, makrolon 15-18 parts, toluene 6-9 parts, di-isopropylbenzene hydroperoxide 15-33 parts, benzoyl peroxide 8.5- 10.5 parts, urethanes 0.3-0.6 parts, nitrosodimethylamine 0.8-1.2 parts, phenylenediamine age resistor 3-4 parts, paraffin 2- 3 parts, organized clay mineral 6-15 parts, water it is some.
- 2. shock-absorbing type rubber according to claim 1, it is characterised in that：It is made up of the raw material components of following number： 31 parts of neoprene, 21 parts of ethylene propylene diene rubber, 6.5 parts of silicon powder, 7.5 parts of boron nitride, 13.5 parts of zinc Isoocatanoate, boric acid 2.5 Part, 27 parts of carbon black, 17 parts of makrolon, 8 parts of toluene, 24 parts of di-isopropylbenzene hydroperoxide, 9.5 parts of benzoyl peroxide, amino 0.5 part of Ethyl formate, 1 part of nitrosodimethylamine, 3.5 parts of phenylenediamine age resistor, 2.5 parts of paraffin, organized clay mineral 11 Part, water are some.
- 3. shock-absorbing type rubber according to claim 1, it is characterised in that：Preparation method is as follows：(1) deionized water of above-mentioned mass fraction is heated to 70-85 DEG C, then by the neoprene of above-mentioned mass fraction, three First EP rubbers, silicon powder, boron nitride, zinc Isoocatanoate, boric acid, carbon black, makrolon, toluene sequentially add, and are well mixed, obtain Obtain solution A；(2) di-isopropylbenzene hydroperoxide and benzoyl peroxide are mixed；(3) by above-mentioned solution A and urethanes, nitrosodimethylamine, phenylenediamine age resistor, the stone of above-mentioned mass fraction After wax, organized clay mineral are well mixed, room temperature is cooled to, that is, obtains this product.