CN107377906B - A kind of closed amorphous band topping mechanism convenient for coutroi velocity - Google Patents
A kind of closed amorphous band topping mechanism convenient for coutroi velocity Download PDFInfo
- Publication number
- CN107377906B CN107377906B CN201710661223.6A CN201710661223A CN107377906B CN 107377906 B CN107377906 B CN 107377906B CN 201710661223 A CN201710661223 A CN 201710661223A CN 107377906 B CN107377906 B CN 107377906B
- Authority
- CN
- China
- Prior art keywords
- amorphous alloy
- amorphous
- melting furnace
- pouring ladle
- alloy melt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of closed amorphous band topping mechanisms convenient for coutroi velocity, runner is poured including the airtight melting furnace of alloy material, amorphous alloy solution pouring ladle and amorphous alloy solution, the amorphous alloy solution pours runner one end and connects the airtight melting furnace of alloy material, and the other end that the amorphous alloy solution pours runner connects the amorphous alloy solution pouring ladle；Horizontal protrusion sampling monitoring pipe is provided on the side wall of the amorphous alloy solution pouring ladle, the horizontal protrusion sampling monitoring pipe is connected to the amorphous alloy solution pouring ladle, and heated at constant temperature resistance wire is provided on the outside of the amorphous alloy solution pouring ladle, the heated at constant temperature resistance wire connects input power adjuster.The present invention can accurately control the flow velocity of alloy molten liquid, avoid flow velocity too fast or the unstable thickness for leading to amorphous alloy magnetism band is excessive, and cooling influences the performance of amorphous alloy magnetism band not in time.
Description
Technical field
The present invention relates to a kind of amorphous alloy material technical field of processing equipment, especially a kind of envelope convenient for coutroi velocity
Enclosed amorphous band topping mechanism.
Background technique
Amorphous alloy magnetism band is the alloy material being made of elements such as iron, silicon, boron, and high-saturation magnetic induction is strong
The various aspects of performance such as degree, magnetic conductivity, excitation current and iron loss are better than silicon steel sheet.Amorphous alloy magnetism band generallys use single roller
Prepared by quick quenching technique: carrying out melting firstly the need of the raw material for containing each component of amorphous alloy is put into smelting furnace and forge
It burns, then pours the amorphous alloy molten liquid sufficiently merged in quick rotation and the lower chill roll of surface temperature, melting
Fe-based amorphous alloy magnetism band is quickly cooled to after amorphous alloy material contact chill roll.Amorphous alloy magnetism band is to system
The requirement of standby condition is more harsh, and cooling velocity need to reach 100,000 degrees Celsius per second or more, usual amorphous alloy magnetism band
Thickness is lower than 0.1 millimeter, this just needs to control the flow velocity of alloy molten liquid, avoids flow velocity too fast or unstable leads to amorphous alloy
The thickness of magnetic band is excessive, and cooling influences the performance of amorphous alloy magnetism band not in time.
Summary of the invention
For overcome the deficiencies in the prior art, it is poured the present invention provides a kind of convenient for the closed amorphous band of coutroi velocity
Expect mechanism, can accurately control the flow velocity of alloy molten liquid, avoid flow velocity too fast or unstable leads to amorphous alloy magnetic recording tape
The thickness of material is excessive, and cooling influences the performance of amorphous alloy magnetism band not in time.
The technical solution adopted by the present invention to solve the technical problems is:
A kind of closed amorphous band topping mechanism convenient for coutroi velocity, including the airtight melting furnace of alloy material, amorphous
Alloy solution pouring ladle and amorphous alloy solution pour runner, and the amorphous alloy solution pours runner one end and connects the alloy material
Airtight melting furnace, the other end that the amorphous alloy solution pours runner connect the amorphous alloy solution pouring ladle；The amorphous
Horizontal protrusion sampling monitoring pipe is provided on the side wall of alloy solution pouring ladle, the level is protruded described in the connection of sampling monitoring pipe
Amorphous alloy solution pouring ladle, and heated at constant temperature resistance wire, the perseverance are provided on the outside of the amorphous alloy solution pouring ladle
Warm resistive heater connects input power adjuster.
It as a further improvement of the above technical scheme, further include alloy strip steel rolled stock fast quenching chill roll, the amorphous alloy is molten
Liquid pouring ladle is located at the surface of the alloy strip steel rolled stock fast quenching chill roll, and the bottom setting of the amorphous alloy solution pouring ladle
There is amorphous alloy solution to pour head piece, the amorphous alloy solution pours the tip-cambered that head piece is located at the alloy strip steel rolled stock fast quenching chill roll
Right above point；It is strip that the amorphous alloy solution, which pours head piece, and the amorphous alloy solution pour head piece length direction it is flat
Row is in the axis of the alloy strip steel rolled stock fast quenching chill roll.
As a further improvement of the above technical scheme, amorphous is arranged in the side wall upper part of the airtight melting furnace of the alloy material
Alloy solution outflux is provided with amorphous alloy solution inflow entrance, the amorphous at the top of the amorphous alloy solution pouring ladle
One end that alloy solution pours runner is connected to the amorphous alloy solution outflux, and the amorphous alloy solution pours the other end of runner
Bottom is connected to the amorphous alloy solution inflow entrance.
It as a further improvement of the above technical scheme, further include high-pressure refractory aspiration pump, the alloy material is airtight to be melted
The vent line that feeds intake is provided at the top of smelting furnace, the vent line that feeds intake is vertically arranged, and the vent line that feeds intake is upper
End connects the high-pressure refractory aspiration pump, and the lower end of the vent line that feeds intake is connected to the airtight melting furnace of alloy material, institute
It states to be provided on the vent line that feeds intake and vacuumizes airtight valve.
As a further improvement of the above technical scheme, closed dump bottom is provided in the airtight melting furnace of the alloy material
Supporting plate, the closed dump bottom pallets level setting, and the alloy material gas is close at the edge of the closed movable backing board
The inner sidewall of close melting furnace；The bottom of the closed movable backing board is provided with backing board drive link, the backing board driving
Connecting rod is vertically arranged.
As a further improvement of the above technical scheme, it is provided on the bottom wall of the airtight melting furnace of the alloy material for institute
The air-tightness connecting rod guide sleeve that backing board drive link passes through is stated, if being additionally provided on the bottom wall of the airtight melting furnace of the alloy material
Parch vent hole.
Compared with prior art, the beneficial effects of the present invention are:
A kind of closed amorphous band topping mechanism convenient for coutroi velocity provided by the present invention can by control
The flow velocity for accurately controlling alloy molten liquid, avoids flow velocity too fast or the unstable thickness mistake for leading to amorphous alloy magnetism band
Greatly, cooling to influence the performance of amorphous alloy magnetism band not in time.
Detailed description of the invention
Present invention will be further explained below with reference to the attached drawings and examples.
Fig. 1 is a kind of structural representation of closed amorphous band topping mechanism convenient for coutroi velocity of the present invention
Figure.
Specific embodiment
Referring to Fig.1, Fig. 1 is the structural schematic diagram of a specific embodiment of the invention.
As shown in Figure 1, a kind of closed amorphous band topping mechanism convenient for coutroi velocity, including alloy material is airtight melts
Smelting furnace 1, amorphous alloy solution pouring ladle 2 and amorphous alloy solution pour runner 3, and the amorphous alloy solution pours 3 one end of runner company
The airtight melting furnace 1 of the alloy material is connect, the other end that the amorphous alloy solution pours runner 3 connects the amorphous alloy solution
Pouring ladle 2；Horizontal protrusion sampling monitoring pipe 4, the horizontal protrusion are provided on the side wall of the amorphous alloy solution pouring ladle 2
Sampling monitoring pipe 4 is connected to the amorphous alloy solution pouring ladle 2, and the outside of the amorphous alloy solution pouring ladle 2 is provided with
Heated at constant temperature resistance wire 5, the heated at constant temperature resistance wire 5 connect input power adjuster 6.
It specifically, further include alloy strip steel rolled stock fast quenching chill roll 7, the amorphous alloy solution pouring ladle 2 is located at the alloy
The surface of band fast quenching chill roll 7, and the bottom of the amorphous alloy solution pouring ladle 2 is provided with amorphous alloy solution and pours stream
Mouth 8, the amorphous alloy solution pour head piece 8 and are located at right above the cambered surface vertex of the alloy strip steel rolled stock fast quenching chill roll 7；It is described non-
It is strip that peritectic alloy solution, which pours head piece 8, and the length direction that the amorphous alloy solution pours head piece 8 is parallel to the alloy strip
The axis of material fast quenching chill roll 7.Amorphous alloy solution outflux 9 is arranged in the side wall upper part of the airtight melting furnace 1 of alloy material,
The top of the amorphous alloy solution pouring ladle 2 is provided with amorphous alloy solution inflow entrance 10, and the amorphous alloy solution pours stream
The one end in road 3 is connected to the amorphous alloy solution outflux 9, and the amorphous alloy solution pours the other end bottom connection of runner 3
The amorphous alloy solution inflow entrance 10.
It further, further include high-pressure refractory aspiration pump 11, the top of the airtight melting furnace 1 of alloy material is provided with throwing
Expect that vent line 12, the vent line 12 that feeds intake are vertically arranged, and the upper end of the vent line 12 that feeds intake connects the height
Press heatproof aspiration pump 11, the lower end of the vent line 12 that feeds intake is connected to the airtight melting furnace 1 of alloy material, it is described feed intake it is logical
It is provided on air pipe 12 and vacuumizes airtight valve 13.Closed movable collet is provided in the airtight melting furnace 1 of alloy material
Plate 14, the closed movable backing board 14 is horizontally disposed, and the alloy material is close at the edge of the closed movable backing board 14
Expect the inner sidewall of airtight melting furnace 1；The bottom of the closed movable backing board 14 is provided with backing board drive link 15, the bottom
Supporting plate drive link 15 is vertically arranged.It is provided on the bottom wall of the airtight melting furnace 1 of alloy material and is driven for the backing board
The air-tightness connecting rod guide sleeve 16 that connecting rod 15 passes through is additionally provided on the bottom wall of the airtight melting furnace 1 of alloy material several ventilative
Through-hole 17.
When work, amorphous alloy raw material is put into the airtight melting furnace 1 of the alloy material first, passes through the high pressure
Heatproof aspiration pump 11 vacuumizes the airtight melting furnace 1 of the alloy material, and airtight valve 13 is vacuumized described in closing, is then heated
The airtight melting furnace 1 of alloy material melts amorphous alloy raw material.Material in the airtight melting furnace 1 of alloy material is complete
After melting, it is lifted the closed movable backing board 14, passes through the aluminium alloy in the airtight melting furnace 1 of the alloy material described non-
Peritectic alloy solution pours runner 3 and enters the amorphous alloy solution pouring ladle 2, pours head piece 2 finally by the amorphous alloy solution
It falls on the high-speed rotating alloy strip steel rolled stock fast quenching chill roll 7, so that magnetism amorphous alloy strips be made.
When aluminium alloy is in the amorphous alloy solution pouring ladle 2, liquid level is located at the horizontal protrusion sampling
Between the inner sidewall bottom and top for monitoring pipe 4, the heated at constant temperature resistance wire 5 is for heating the horizontal protrusion sampling monitoring
Pipe 4 is allowed to keep constant temperature, when the liquid level in the horizontal protrusion sampling monitoring pipe 4 changes, the horizontal protrusion sampling
The integral heat sink amount and heating amount balance for monitoring pipe 4 are broken, therefore the input power adjuster 6 is caused to need described in adjusting
The input power of heated at constant temperature resistance wire 5, to keep horizontal protrusion 4 temperature of sampling monitoring pipe constant, according to the input
The input power that power governor 6 is adjusted may know that the flow velocity of aluminium alloy has been too fast or excessively slow, described close by adjusting
Close the flow velocity of the i.e. adjustable aluminium alloy of uplift rate of movable backing board 14.
Preferable implementation of the invention is illustrated above, certainly, the present invention can also use and above-mentioned implementation
The different form of mode, those skilled in the art's made equivalent transformation on the premise of without prejudice to spirit of the invention
Or corresponding change, all it should belong in protection scope of the present invention.
Claims (4)
1. a kind of closed amorphous band topping mechanism convenient for coutroi velocity, including the airtight melting furnace (1) of alloy material, amorphous
Alloy molten solution pouring ladle (2) and amorphous alloy melt pour runner (3), and the amorphous alloy melt pours the connection of runner (3) one end
The airtight melting furnace (1) of alloy material, it is molten that the other end that the amorphous alloy melt pours runner (3) connects the amorphous alloy
Liquid pouring ladle (2)；
It is characterized by: horizontal protrusion sampling monitoring pipe (4) is provided on the side wall of the amorphous alloy melt pouring ladle (2),
Horizontal protrusion sampling monitoring pipe (4) is connected to the amorphous alloy melt pouring ladle (2), and the horizontal protrusion sampling monitoring
It is provided with heated at constant temperature resistance wire (5) on the outside of pipe (4), amorphous alloy melt liquid level is located at the horizontal protrusion sampling prison
Between the inner sidewall bottom and top of test tube (4), the heated at constant temperature resistance wire (5) is for heating the horizontal protrusion sampling prison
Test tube (4) is allowed to keep constant temperature, and the heated at constant temperature resistance wire (5) connects input power adjuster (6)；
Closed movable backing board (14), the closed movable backing board are provided in the airtight melting furnace (1) of alloy material
(14) it is horizontally disposed with, and the interior of the airtight melting furnace (1) of alloy material is close at the edge of the closed movable backing board (14)
Side wall；The bottom of the closed movable backing board (14) is provided with backing board drive link (15), the backing board drive link
(15) it is vertically arranged；It is provided on the bottom wall of the airtight melting furnace (1) of alloy material for the backing board drive link (15)
The air-tightness connecting rod guide sleeve (16) passed through is additionally provided on the bottom wall of the airtight melting furnace (1) of alloy material several ventilative logical
Hole (17).
2. a kind of closed amorphous band topping mechanism convenient for coutroi velocity according to claim 1, it is characterised in that:
It further include alloy strip steel rolled stock fast quenching chill roll (7), it is cooling that the amorphous alloy melt pouring ladle (2) is located at the alloy strip steel rolled stock fast quenching
The surface of roller (7), and the bottom of the amorphous alloy melt pouring ladle (2) is provided with amorphous alloy melt and pours head piece (8), institute
It states amorphous alloy melt and pours the cambered surface vertex surface that head piece (8) are located at the alloy strip steel rolled stock fast quenching chill roll (7)；The amorphous
It is strip that alloy molten solution, which pours head piece (8), and the amorphous alloy melt pours the length direction of head piece (8) and is parallel to the alloy
The axis of band fast quenching chill roll (7).
3. a kind of closed amorphous band topping mechanism convenient for coutroi velocity according to claim 2, it is characterised in that:
Amorphous alloy melt outflux (9) are arranged in the side wall upper part of the airtight melting furnace (1) of alloy material, the amorphous alloy melt
Amorphous alloy melt inflow entrance (10) is provided at the top of pouring ladle (2), one end that the amorphous alloy melt pours runner (3) connects
Lead to the amorphous alloy melt outflux (9), the other end bottom that the amorphous alloy melt pours runner (3) is connected to the amorphous
Alloy molten solution inflow entrance (10).
4. a kind of closed amorphous band topping mechanism convenient for coutroi velocity according to claim 3, it is characterised in that:
Further include high-pressure refractory aspiration pump (11), is provided with the vent line that feeds intake at the top of the airtight melting furnace (1) of alloy material
(12), the vent line that feeds intake (12) is vertically arranged, and the upper end connection high pressure of the vent line that feeds intake (12) is resistance to
Warm aspiration pump (11), the lower end of the vent line that feeds intake (12) is connected to the airtight melting furnace (1) of alloy material, described to feed intake
It is provided on vent line (12) and vacuumizes airtight valve (13).