CN107363950A - A kind of bamboo mat processing method - Google Patents
A kind of bamboo mat processing method Download PDFInfo
- Publication number
- CN107363950A CN107363950A CN201710411904.7A CN201710411904A CN107363950A CN 107363950 A CN107363950 A CN 107363950A CN 201710411904 A CN201710411904 A CN 201710411904A CN 107363950 A CN107363950 A CN 107363950A
- Authority
- CN
- China
- Prior art keywords
- weaving
- minutes
- fluid
- strips used
- thin bamboo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of bamboo mat processing method, following steps are specifically included:（1）Dewater treatment；（2）Immersion oil processing；（3）Bamboo mat is worked out after drying, by being surface-treated, sterilizing, bound edge obtains finished product.By experiment, a kind of bamboo mat processing method provided by the invention, the toughness of bamboo mat can be effectively improved, it is not easy to the bifurcated that ftractures by being exposed to the sun for long-time sunlight, it is more safe and reliable during use.
Description
Technical field
The invention belongs to household articles technical field, and in particular to a kind of bamboo mat processing method.
Background technology
Bamboo skin is split into thin bamboo strip silk by bamboo mat typically using bamboos such as fishscale bamboo, mao bamboon, oily bamboos as raw material, through works such as boiling, immersions
Formed after skill with craft through knitting device.Bamboo mat is different by materials, can be divided into blue or green seat, yellow seat, flower seat and dyeing thin bamboo strip flower seat again.It is blue or green
Seat is all slightd braiding by green grass or young crops and formed, and yellow seat is all woven with the yellow thin bamboo strip, and colored seat bluish yellow is alternate, bright and lustrous, and dyeing is slightd colored seat and then incited somebody to action
Bamboo, which is slightd, dyes a variety of colors, weaves floral designs, is generally used for decorating.
Bamboo mat history existing thousand in our daily lifes, it is nice and cool, comfortable and attractive in appearance and price is relatively low, people
Can receive, and sanitation performance is good.But because bamboo mat material is more crisp, bifurcated is tended to during use or even is opened
Split, cause to stab the serious consequences such as skin.
The content of the invention
In order to solve the above problems, the invention provides a kind of bamboo mat processing method, the toughness of bamboo mat is lifted.
The present invention is achieved through the following technical solutions：
A kind of bamboo mat processing method, specifically includes following steps:
（1）Dewater treatment
Choose high-quality bamboo and be processed into thin bamboo strips used for weaving, after thin bamboo strips used for weaving then is used into high-temperature steam boiling 30-45 minutes, kill thin bamboo strips used for weaving surface
With the germ of inside, drain away the water, freezing processing 90-120 minutes in -10 DEG C of freezers are placed in, then using hot-air oven in 75-
85 DEG C are uniformly toasted 15-20 minutes, and now the pico- permeability in thin bamboo strips used for weaving surface, stand-by；Thin bamboo strips used for weaving by freezing processing carries out hot blast again
Baking dehydration, effectively avoid temperature is too high from causing thin bamboo strips used for weaving sallow, while internal ice crystal receives high temperature and directly distilled, and accelerates baking
Dry efficiency, dehydration is more thorough, contributes to subsequent treatment；
（2）Immersion oil processing
After the thin bamboo strips used for weaving handled well is soaked into 30-40 minutes using normal temperature fluid A, conversion fluid B is heated to 110-130 DEG C of cooking 8-
10 minutes；It the thin bamboo strips used for weaving of dehydration is fully absorbed fluid A in cold oil, fluid A rapid osmotics is carried to inside thin bamboo strips used for weaving
The toughness of thin bamboo strips used for weaving is risen, then using the fluid B heating and cookings so that organic matter denaturation inside thin bamboo strips used for weaving, by the fluid A, oil
Active ingredient in liquid B is fixed, while fluid B can form glaze paint on thin bamboo strips used for weaving surface, lift the glossiness and aesthetics of thin bamboo strips used for weaving；
The fluid A, by palm oil, vaseline, Chinese catalpa oil, rapeseed oil 25-15 in mass ratio:8-12:3:It is made after 5 mixing；
The fluid B, is specifically made by following steps:
A according to the mass fraction, takes castor oil 15-20 parts, is heated to 180-200 DEG C, is incubated 4-5 minutes, removes surface offscum, so
After be cooled to 120-140 DEG C, add rosin 5-8 parts, after uniform stirring, in 150-160 DEG C of isothermal holding 5-8 minute, mistake while hot
80 mesh are sieved, obtain component A；
B according to the mass fraction, takes yellow wax 15-20 parts, the heating infusion mixing of beeswax 1-2 parts, obtains component B；
C is by the component A, component B in mass ratio 20:1 heating is sufficiently mixed, and produces the fluid B；
（3）Bamboo mat is worked out after drying, by being surface-treated, sterilizing, bound edge obtains finished product.
Beneficial effects of the present invention：Thin bamboo strips used for weaving by freezing processing carries out air cooking dehydration again, effectively avoids temperature mistake
Height causes thin bamboo strips used for weaving sallow, while internal ice crystal receives high temperature and directly distilled, and accelerates the efficiency of drying, dehydration is more thorough, has
Help subsequent treatment；After the thin bamboo strips used for weaving handled well is soaked using normal temperature fluid A, fluid B heating and cookings of converting, it can so make to take off
The thin bamboo strips used for weaving of water fully absorbs fluid A in cold oil, fluid A rapid osmotics is lifted the toughness of thin bamboo strips used for weaving to inside thin bamboo strips used for weaving, is then made
With the fluid B heating and cookings so that organic matter denaturation inside thin bamboo strips used for weaving, the active ingredient in the fluid A, fluid B is fixed,
Fluid B can form glaze paint on thin bamboo strips used for weaving surface simultaneously, lift the glossiness and aesthetics of thin bamboo strips used for weaving；By experiment, the present invention provides
A kind of bamboo mat processing method, the toughness of bamboo mat can be effectively improved, make it be not easy to ftracture by being exposed to the sun for long-time sunlight
Bifurcated, it is more safe and reliable during use.
Embodiment
Embodiment 1
A kind of bamboo mat processing method, specifically includes following steps:
（1）Dewater treatment
Choose high-quality bamboo and be processed into thin bamboo strips used for weaving, then by thin bamboo strips used for weaving using after high-temperature steam boiling 30 minutes, kill thin bamboo strips used for weaving surface and
Internal germ, drains away the water, is placed in freezing processing 90 minutes in -10 DEG C of freezers, then uniform in 75 DEG C using hot-air oven
Baking 15 minutes, now the pico- permeability in thin bamboo strips used for weaving surface, stand-by；Thin bamboo strips used for weaving by freezing processing carries out air cooking dehydration again, has
Effect avoids temperature is too high from causing thin bamboo strips used for weaving sallow, while internal ice crystal receives high temperature and directly distilled, and accelerates the efficiency of drying, takes off
Water is more thorough, contributes to subsequent treatment；
（2）Immersion oil processing
After the thin bamboo strips used for weaving handled well is soaked 30 minutes using normal temperature fluid A, conversion fluid B is heated to 110 DEG C and cooked 8 minutes；This
Sample can make the thin bamboo strips used for weaving of dehydration fully absorb fluid A in cold oil, fluid A rapid osmotics is lifted thin bamboo strips used for weaving to inside thin bamboo strips used for weaving
Toughness, then using the fluid B heating and cookings so that organic matter denaturation inside thin bamboo strips used for weaving, by having in the fluid A, fluid B
Effect composition is fixed, while fluid B can form glaze paint on thin bamboo strips used for weaving surface, lift the glossiness and aesthetics of thin bamboo strips used for weaving；
The fluid A, by palm oil, vaseline, Chinese catalpa oil, rapeseed oil in mass ratio 25:8:3:It is made after 5 mixing；
The fluid B, is specifically made by following steps:
A according to the mass fraction, takes 15 parts of castor oil, is heated to 180 DEG C, is incubated 4 minutes, removes surface offscum and then is cooled to
120 DEG C, 5 parts of rosin is added, after uniform stirring, in 150 DEG C of isothermal holdings 5 minutes, sieved 80 mesh while hot, obtains component A；
B according to the mass fraction, takes 1 part of 15 parts of yellow wax, beeswax heating infusion mixing, obtains component B；
C is by the component A, component B in mass ratio 20:1 heating is sufficiently mixed, and produces the fluid B；
（3）Bamboo mat is worked out after drying, by being surface-treated, sterilizing, bound edge obtains finished product.
Embodiment 2
A kind of bamboo mat processing method, specifically includes following steps:
（1）Dewater treatment
Choose high-quality bamboo and be processed into thin bamboo strips used for weaving, then by thin bamboo strips used for weaving using after high-temperature steam boiling 45 minutes, kill thin bamboo strips used for weaving surface and
Internal germ, drains away the water, is placed in freezing processing 120 minutes in -10 DEG C of freezers, then uniform in 85 DEG C using hot-air oven
Baking 20 minutes, now the pico- permeability in thin bamboo strips used for weaving surface, stand-by；Thin bamboo strips used for weaving by freezing processing carries out air cooking dehydration again, has
Effect avoids temperature is too high from causing thin bamboo strips used for weaving sallow, while internal ice crystal receives high temperature and directly distilled, and accelerates the efficiency of drying, takes off
Water is more thorough, contributes to subsequent treatment；
（2）Immersion oil processing
After the thin bamboo strips used for weaving handled well is soaked 40 minutes using normal temperature fluid A, conversion fluid B is heated to 130 DEG C and cooked 10 minutes；This
Sample can make the thin bamboo strips used for weaving of dehydration fully absorb fluid A in cold oil, fluid A rapid osmotics is lifted thin bamboo strips used for weaving to inside thin bamboo strips used for weaving
Toughness, then using the fluid B heating and cookings so that organic matter denaturation inside thin bamboo strips used for weaving, by having in the fluid A, fluid B
Effect composition is fixed, while fluid B can form glaze paint on thin bamboo strips used for weaving surface, lift the glossiness and aesthetics of thin bamboo strips used for weaving；
The fluid A, by palm oil, vaseline, Chinese catalpa oil, rapeseed oil in mass ratio 15:12:3:It is made after 5 mixing；
The fluid B, is specifically made by following steps:
A according to the mass fraction, takes 20 parts of castor oil, is heated to 200 DEG C, is incubated 5 minutes, removes surface offscum and then is cooled to
140 DEG C, 8 parts of rosin is added, after uniform stirring, in 160 DEG C of isothermal holdings 8 minutes, sieved 80 mesh while hot, obtains component A；
B according to the mass fraction, takes 2 parts of 20 parts of yellow wax, beeswax heating infusion mixing, obtains component B；
C is by the component A, component B in mass ratio 20:1 heating is sufficiently mixed, and produces the fluid B；
（3）Bamboo mat is worked out after drying, by being surface-treated, sterilizing, bound edge obtains finished product.
Embodiment 3
A kind of bamboo mat processing method, specifically includes following steps:
（1）Dewater treatment
Choose high-quality bamboo and be processed into thin bamboo strips used for weaving, then by thin bamboo strips used for weaving using after high-temperature steam boiling 38 minutes, kill thin bamboo strips used for weaving surface and
Internal germ, drains away the water, is placed in freezing processing 100 minutes in -10 DEG C of freezers, then uniform in 80 DEG C using hot-air oven
Baking 16 minutes, now the pico- permeability in thin bamboo strips used for weaving surface, stand-by；Thin bamboo strips used for weaving by freezing processing carries out air cooking dehydration again, has
Effect avoids temperature is too high from causing thin bamboo strips used for weaving sallow, while internal ice crystal receives high temperature and directly distilled, and accelerates the efficiency of drying, takes off
Water is more thorough, contributes to subsequent treatment；
（2）Immersion oil processing
After the thin bamboo strips used for weaving handled well is soaked 35 minutes using normal temperature fluid A, conversion fluid B is heated to 120 DEG C and cooked 9 minutes；This
Sample can make the thin bamboo strips used for weaving of dehydration fully absorb fluid A in cold oil, fluid A rapid osmotics is lifted thin bamboo strips used for weaving to inside thin bamboo strips used for weaving
Toughness, then using the fluid B heating and cookings so that organic matter denaturation inside thin bamboo strips used for weaving, by having in the fluid A, fluid B
Effect composition is fixed, while fluid B can form glaze paint on thin bamboo strips used for weaving surface, lift the glossiness and aesthetics of thin bamboo strips used for weaving；
The fluid A, by palm oil, vaseline, Chinese catalpa oil, rapeseed oil in mass ratio 20:10:3:It is made after 5 mixing；
The fluid B, is specifically made by following steps:
A according to the mass fraction, takes 18 parts of castor oil, is heated to 190 DEG C, is incubated 4 minutes, removes surface offscum and then is cooled to
130 DEG C, 6 parts of rosin is added, after uniform stirring, in 155 DEG C of isothermal holdings 6 minutes, sieved 80 mesh while hot, obtains component A；
B according to the mass fraction, takes 1.5 parts of 18 parts of yellow wax, beeswax heating infusion mixing, obtains component B；
C is by the component A, component B in mass ratio 20:1 heating is sufficiently mixed, and produces the fluid B；
（3）Bamboo mat is worked out after drying, by being surface-treated, sterilizing, bound edge obtains finished product.
Comparative example 1
This comparative example 1 compared with Example 1, without step（1）The operation, using only conventional dehydration methods, except this
Outer method and step all same.
Comparative example 2
This comparative example 2 compared with Example 2, without step（2）The soak at room temperature fluid A operations, side in addition
Method step all same.
Comparative example 3
This comparative example 3 compared with Example 3, without using step（2）The fluid B, using only conventional fluid, in addition
Method and step all same.
Control group
Existing bamboo mat processing method.
The bamboo mat that above-mentioned 7 kinds of methods treat is exposed to the sun 200 hours in the sun respectively, determines the hair of every kind of bamboo mat cracking
Raw rate, as a result such as table 1：
Table 1
| Ftracture incidence（%） | |
| Embodiment 1 | 5.8 |
| Embodiment 2 | 4.7 |
| Embodiment 3 | 5.5 |
| Comparative example 1 | 11.1 |
| Comparative example 2 | 8.8 |
| Comparative example 3 | 7.4 |
| Control group | 16.3 |
As shown in Table 1, a kind of bamboo mat processing method provided by the invention, can be effectively improved the toughness of bamboo mat, make it through long
Being exposed to the sun of time sunlight is not easy to the bifurcated that ftractures, more safe and reliable during use.
Claims (4)
1. a kind of bamboo mat processing method, it is characterised in that specifically include following steps:
（1）Dewater treatment
Choose high-quality bamboo and be processed into thin bamboo strips used for weaving, after thin bamboo strips used for weaving then is used into high-temperature steam boiling 30-45 minutes, drain away the water, put
The freezing processing 90-120 minutes in -10 DEG C of freezers, 15-20 minutes are uniformly then toasted in 75-85 DEG C using hot-air oven, this
When thin bamboo strips used for weaving surface pico- permeability, it is stand-by；
（2）Immersion oil processing
After the thin bamboo strips used for weaving handled well is soaked into 30-40 minutes using normal temperature fluid A, conversion fluid B is heated to 110-130 DEG C of cooking 8-
10 minutes；
The fluid A, by palm oil, vaseline, Chinese catalpa oil, rapeseed oil 25-15 in mass ratio:8-12:3:It is made after 5 mixing；
The fluid B, is specifically made by following steps:
A according to the mass fraction, takes castor oil 15-20 parts, is heated to 180-200 DEG C, is incubated 4-5 minutes, removes surface offscum, so
After be cooled to 120-140 DEG C, add rosin 5-8 parts, after uniform stirring, in 150-160 DEG C of isothermal holding 5-8 minute, mistake while hot
80 mesh are sieved, obtain component A；
B according to the mass fraction, takes yellow wax 15-20 parts, the heating infusion mixing of beeswax 1-2 parts, obtains component B；
C is by the component A, component B in mass ratio 20:1 heating is sufficiently mixed, and produces the fluid B；
（3）Bamboo mat is worked out after drying, by being surface-treated, sterilizing, bound edge obtains finished product.
A kind of 2. bamboo mat processing method according to claim 1, it is characterised in that step（1）The dewater treatment, specifically
Method is:Choose high-quality bamboo and be processed into thin bamboo strips used for weaving, after thin bamboo strips used for weaving then is used into high-temperature steam boiling 38 minutes, drain away the water, put
Freezing processing 100 minutes in -10 DEG C of freezers, then using hot-air oven in 80 DEG C of uniform baking 16 minutes, now thin bamboo strips used for weaving table
The pico- permeability in face, it is stand-by.
A kind of 3. bamboo mat processing method according to claim 1, it is characterised in that step（2）The fluid A, by
Palm oil, vaseline, Chinese catalpa oil, rapeseed oil in mass ratio 20:10:3:It is made after 5 mixing.
A kind of 4. bamboo mat processing method according to claim 1, it is characterised in that step（2）The fluid B, specifically by
Following steps are made:
A according to the mass fraction, takes 18 parts of castor oil, is heated to 190 DEG C, is incubated 4 minutes, removes surface offscum and then is cooled to
130 DEG C, 6 parts of rosin is added, after uniform stirring, in 155 DEG C of isothermal holdings 6 minutes, sieved 80 mesh while hot, obtains component A；
B according to the mass fraction, takes 1.5 parts of 18 parts of yellow wax, beeswax heating infusion mixing, obtains component B；
C is by the component A, component B in mass ratio 20:1 heating is sufficiently mixed, and produces the fluid B.