CN107338576A - One kind melt-blown composite alloy plant fiber non-woven fabric fabric and preparation method thereof - Google Patents
One kind melt-blown composite alloy plant fiber non-woven fabric fabric and preparation method thereof Download PDFInfo
- Publication number
- CN107338576A CN107338576A CN201710735904.2A CN201710735904A CN107338576A CN 107338576 A CN107338576 A CN 107338576A CN 201710735904 A CN201710735904 A CN 201710735904A CN 107338576 A CN107338576 A CN 107338576A
- Authority
- CN
- China
- Prior art keywords
- fiber
- alloy
- woven fabric
- fabric
- string
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind melt-blown composite alloy plant fiber non-woven fabric fabric and preparation method thereof, according to mass percent, it is prepared from the following components:String 30% 50%, alloy fiber 50% 70%, the invention also discloses a kind of above-mentioned preparation method for being meltblown composite alloy plant fiber non-woven fabric fabric, step are as follows:According to above-mentioned mass percent, string and alloy fiber shredding are mixed, then combed, then hot blast adhesion is carried out, the fiber after bonding is sprayed to again and laterally and in the reception device of low speed lengthwise movement through air is cooled into non-woven fabrics at a high speed, non-woven fabrics is delivered on drum receiver again and wound, that is, product is prepared.The product that the present invention is prepared have the advantages that good toughness, be hardly damaged, service life it is long.
Description
Technical field
It is specifically a kind of to be meltblown composite alloy plant fiber non-woven fabric the present invention relates to non-woven fabric preparation field
Fabric and preparation method thereof.
Background technology
Non-woven fabrics is also known as adhesive-bonded fabric, is to be made up of fiber orient or random, is environment-friendly materials of new generation, has anti-
It is damp, ventilative, flexible, light, not combustion-supporting, easy to decompose, be nontoxic nonirritant, rich in color, cheap, recyclable etc.
Feature, such as more use polypropylene granules as raw material, through high-temperature fusion, spinneret, spread guiding principle, hot pressing batch continuous one-step produce and
Into being called cloth because of the outward appearance with cloth and some performances.
Bonded fabric product is rich in color, bright-coloured lucid and lively, Eco-Fashion, widely used, elegant in appearance, and pattern and style are all more
Sample, and light, environmentally friendly, recyclable, by the internationally recognized environment-friendly products for ecology of preserving our planet, suitable for agricultural film,
The industries such as shoemaking, process hides, mattress, child-mother-covering, decoration, chemical industry, printing, automobile, building materials, furniture, and dress lining cloth, health care
The gift bag of disposable surgical clothing, mouth mask, cap, sheet, the disposable tablecloth in hotel, beauty, Saunas or even current fashion, fine work
Bag, advertising bag etc., environment-friendly products are widely used, economical and practical.Because its outward appearance is similar to pearl, also known as pearl painting canvas.
But existing non-woven fabrics still have poor toughness, be easily torn, the defects of service life is short is, it is necessary to enter to advance
The improvement of one step, therefore a non-woven fabrics grown using birthday noodle is developed as one of current important problem.
The content of the invention
The defects of the invention aims to solve poor toughness of the prior art, be easily damaged, there is provided one kind melt-blown
Composite alloy plant fiber non-woven fabric fabric and preparation method thereof solves the above problems.
To achieve these goals, technical scheme is as follows:The invention discloses one kind melt-blown composite alloy to plant
Fibres non-woven fabric, according to mass percent, it is prepared from the following components:String 30%-50%, alloy fiber
50%-70%.
Preferably, the invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to quality percentage
Than being prepared from the following components:String 35%-45%, alloy fiber 55%-65%.
Preferably, the invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to quality percentage
Than being prepared from the following components:String 40%, alloy fiber 60%.
Preferably, the invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to quality percentage
Than being prepared from the following components:String 30%, alloy fiber 70%.
Preferably, the invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to quality percentage
Than being prepared from the following components:String 50%, alloy fiber 50%.
Nitinol fiber or Aludirome fiber are used as preferred, described alloy fiber.
Preferably, described string uses bamboo fibre or flax fiber.
Preferably, the invention also discloses a kind of above-mentioned preparation side for being meltblown composite alloy plant fiber non-woven fabric fabric
Method, step are as follows:
According to above-mentioned mass percent, string and alloy fiber shredding are mixed, is then combed, then carried out
Hot blast adhesion, then the fiber after bonding is sprayed to and laterally and in the reception device of low speed lengthwise movement cools down shape through air at a high speed
Into non-woven fabrics, then non-woven fabrics is delivered on drum receiver and wound, that is, product is prepared.
Preferably, in hot blast adhesion, the fusing degree of described alloy fiber is 30%-70%.
The present invention has advantages below compared with prior art:
Melt-blown composite alloy plant fiber non-woven fabric fabric of the present invention is made by using string, alloy fiber
For raw material, string is a kind of sclerenchyma being widely distributed in seed plant, and its cell is elongated, and both ends are sharp, tool
There is thicker secondary wall, often there is simple pit on wall, the protoplast of typically no work when ripe, like that alloy is fine additionally by celestial pole
Dimension, has excellent mechanical performance, therefore the product being prepared by using alloy fiber and string has toughness increasing
Add, the advantages of non-woven fabrics is hardly damaged and service life is long.
Embodiment
The invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to mass percent, by following
Component is prepared:String 30%-50%, alloy fiber 50%-70%.
Preferably, the invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to quality percentage
Than being prepared from the following components:String 35%-45%, alloy fiber 55%-65%.
Preferably, the invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to quality percentage
Than being prepared from the following components:String 40%, alloy fiber 60%.
Preferably, the invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to quality percentage
Than being prepared from the following components:String 30%, alloy fiber 70%.
Preferably, the invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to quality percentage
Than being prepared from the following components:String 50%, alloy fiber 50%.
Nitinol fiber or Aludirome fiber are used as preferred, described alloy fiber.
Preferably, described string uses bamboo fibre or flax fiber.
Preferably, the invention also discloses a kind of above-mentioned preparation side for being meltblown composite alloy plant fiber non-woven fabric fabric
Method, step are as follows:
According to above-mentioned mass percent, string and alloy fiber shredding are mixed, is then combed, then carried out
Hot blast adhesion, then the fiber after bonding is sprayed to and laterally and in the reception device of low speed lengthwise movement cools down shape through air at a high speed
Into non-woven fabrics, then non-woven fabrics is delivered on drum receiver and wound, that is, product is prepared.
Preferably, in hot blast adhesion, the fusing degree of described alloy fiber is 30%-70%.
Embodiment 1
The invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to mass percent, by following
Component is prepared:String 40%, alloy fiber 60%.
Preferably, the invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to quality percentage
Than being prepared from the following components:String 30%, alloy fiber 70%.
Described alloy fiber uses Nitinol fiber.
Preferably, described string uses bamboo fibre.
Preferably, the invention also discloses a kind of above-mentioned preparation side for being meltblown composite alloy plant fiber non-woven fabric fabric
Method, step are as follows:
According to above-mentioned mass percent, string and alloy fiber shredding are mixed, is then combed, then carried out
Hot blast adhesion, then the fiber after bonding is sprayed to and laterally and in the reception device of low speed lengthwise movement cools down shape through air at a high speed
Into non-woven fabrics, then non-woven fabrics is delivered on drum receiver and wound, that is, product is prepared.
In hot blast adhesion, the fusing degree of described alloy fiber is 60%.
Use the synthesis pliability of the melt-blown composite alloy plant fiber non-woven fabric fabric that the above method is prepared for
50nN, water imbibition 710%, liquid penetration 3s.
Embodiment 2
The invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to mass percent, by following
Component is prepared:String 30%, alloy fiber 70%.
The invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to mass percent, by following
Component is prepared:String 50%, alloy fiber 50%.
Described alloy fiber uses Aludirome fiber.
Described string uses flax fiber.
The invention also discloses a kind of above-mentioned preparation method for being meltblown composite alloy plant fiber non-woven fabric fabric, step is such as
Under:
According to above-mentioned mass percent, string and alloy fiber shredding are mixed, is then combed, then carried out
Hot blast adhesion, then the fiber after bonding is sprayed to and laterally and in the reception device of low speed lengthwise movement cools down shape through air at a high speed
Into non-woven fabrics, then non-woven fabrics is delivered on drum receiver and wound, that is, product is prepared.
In hot blast adhesion, the fusing degree of described alloy fiber is 70%.
Use the synthesis pliability of the melt-blown composite alloy plant fiber non-woven fabric fabric that the above method is prepared for
55nN, water imbibition 780%, liquid penetration 5s.
Embodiment 3
The invention discloses one kind to be meltblown composite alloy plant fiber non-woven fabric fabric, according to mass percent, by following
Component is prepared:String 50%, alloy fiber 50%.
Described alloy fiber uses Nitinol fiber.
Described string uses bamboo fibre.
The invention also discloses a kind of above-mentioned preparation method for being meltblown composite alloy plant fiber non-woven fabric fabric, step is such as
Under:
According to above-mentioned mass percent, string and alloy fiber shredding are mixed, is then combed, then carried out
Hot blast adhesion, then the fiber after bonding is sprayed to and laterally and in the reception device of low speed lengthwise movement cools down shape through air at a high speed
Into non-woven fabrics, then non-woven fabrics is delivered on drum receiver and wound, that is, product is prepared.
In hot blast adhesion, the fusing degree of described alloy fiber is 60%.
Use the synthesis pliability of the melt-blown composite alloy plant fiber non-woven fabric fabric that the above method is prepared for
54nN, water imbibition 810%, liquid penetration 5s.
In summary, present invention melt-blown composite alloy plant fiber non-woven fabric fabric and preparation method thereof, is prepared
It is meltblown composite alloy plant fiber non-woven fabric fabric, hence it is evident that the pliability, bulkiness, being unlikely to deform property of product are improved, and
Excellent feel and usage comfort, product have higher class, substantially increase added value of product, and plant by adding
Fibres, alloy fiber, good toughness, service life length, have preferable promotion prospect.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
For personnel it should be appreciated that the present invention is not limited to the above embodiments, that described in above-described embodiment and specification is the present invention
Principle, various changes and modifications of the present invention are possible without departing from the spirit and scope of the present invention, these change and
Improvement is both fallen within the range of claimed invention.The protection domain of application claims by appended claims and its
Equivalent defines.
Claims (9)
1. one kind melt-blown composite alloy plant fiber non-woven fabric fabric, it is characterised in that:According to mass percent, by following components
It is prepared:String 30%-50%, alloy fiber 50%-70%.
A kind of 2. melt-blown composite alloy plant fiber non-woven fabric fabric according to claim 1, it is characterised in that:According to matter
Percentage is measured, is prepared from the following components:String 35%-45%, alloy fiber 55%-65%.
A kind of 3. melt-blown composite alloy plant fiber non-woven fabric fabric according to claim 1, it is characterised in that:According to matter
Percentage is measured, is prepared from the following components:String 40%, alloy fiber 60%.
A kind of 4. melt-blown composite alloy plant fiber non-woven fabric fabric according to claim 1, it is characterised in that:According to matter
Percentage is measured, is prepared from the following components:String 30%, alloy fiber 70%.
A kind of 5. melt-blown composite alloy plant fiber non-woven fabric fabric according to claim 1, it is characterised in that:According to matter
Percentage is measured, is prepared from the following components:String 50%, alloy fiber 50%.
6. according to a kind of any described melt-blown composite alloy plant fiber non-woven fabric fabrics of claim 1-5, it is characterised in that:
Described alloy fiber uses Nitinol fiber or Aludirome fiber.
7. according to a kind of any described melt-blown composite alloy plant fiber non-woven fabric fabrics of claim 1-5, it is characterised in that:
Described string uses bamboo fibre or flax fiber.
8. according to a kind of preparation method of any described melt-blown composite alloy plant fiber non-woven fabric fabrics of claim 1-5,
It is characterized in that:Step is as follows:
According to above-mentioned mass percent, string and alloy fiber shredding are mixed, is then combed, then carries out hot blast
Bonding, then the fiber after bonding is sprayed to and laterally and in the reception device of low speed lengthwise movement through air is cooled into nothing at a high speed
Cloth is spun, then non-woven fabrics is delivered on drum receiver and wound, that is, product is prepared.
A kind of 9. melt-blown composite alloy plant fiber non-woven fabric fabric according to claim 8, it is characterised in that:Hot blast glues
In conjunction, the fusing degree of described alloy fiber is 30%-70%.