CN107304529A - A kind of high temperature resistant type automatically cleaning filter paper - Google Patents
A kind of high temperature resistant type automatically cleaning filter paper Download PDFInfo
- Publication number
- CN107304529A CN107304529A CN201610280060.2A CN201610280060A CN107304529A CN 107304529 A CN107304529 A CN 107304529A CN 201610280060 A CN201610280060 A CN 201610280060A CN 107304529 A CN107304529 A CN 107304529A
- Authority
- CN
- China
- Prior art keywords
- filter paper
- fibre
- fibres
- fibre diameter
- ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is a kind of high-temperature-resistant self-cleaning filter paper, it is that 1~2 μm of basalt fibre, fibre diameter are that 2~4 μm of ceramic fibres, fibre diameter are that 2~5 μm of Zirconium oxide fibres, fibre diameter are that 2~5 μm of alumina fibres and high-temperature Resistance Adhesives are constituted, and impregnate one layer of nano-titanium dioxide film in filter paper fiber surface by fibre diameter.Basalt fibre and ceramic fibre are as a kind of inorfil, and not only stability is good, but also with a variety of excellent properties such as electrical insulating property, anticorrosive, flame resistant, high temperature resistants, strainability is good, shear strength is high, and the multicomponent of use greatly reduces gas-flow resistance, improves filter efficiency.In addition the nano-titanium dioxide film impregnated in its surface causes filter paper to be provided with self-cleaning function, its surface is allowd to keep self-cleaning effect for a long time, titanium dioxide can also be degradable for water and titanium dioxide by harmful organic substances such as formaldehyde simultaneously, and do not cause secondary pollution, therefore service life that is not only environmentally friendly but also improving filter paper.
Description
Technical field
The present invention relates to a kind of filter paper, more particularly, to a kind of high temperature resistant type automatically cleaning filter paper, belong to filtering material field.
Background technology
With the high speed development of modernization industry, environmental pollution is seriously threaten life and the health of the mankind, and recent air is dirty
The injury contaminated to human body is particularly evident, and extensive haze weather is attacked repeatedly.Country is to the continuous of quality of air environment attention degree
Improve, PM 2.5 is included to new Air Quality Evaluation system.How pernicious gas in air is reduced using efficient filtering material
Carry out effectively filtering extremely urgent into human body or to the pernicious gas of discharge.In order to be able to realize the purpose of air cleaning, newly
The filtering material of type high-quality progressively turns into the study hotspot of researcher.Because glass fibre has dimensional stability relatively by force, no
Yielding, electrical insulating property is good, anti-medicine is good, and causes glass fibre with the good characteristic such as acid and alkali-resistance, oil resistant, corrosion-resistant
Preferred material as efficient and ultra high efficiency air cleaner, it is adaptable to the application of the air cleaning of every field.But, glass
There is also some shortcomings for fiber:Fiber Aspect Ratio is big, and surface carries electric charge, easily mutually winds and is difficult to separate;Compare on surface
It is smooth, wire-dividing broom purification can not be produced through mashing processing, physical bond is there's almost no between fiber and fiber, is not also formed
The group of hydrogen bond, page can not produce bond strength naturally;Mechanical strength is low, and non-refractory, dust containing capacity septulum are for a period of time
Need to be changed.
The A of Publication No. CN 103556544 Chinese patent provides a kind of high flame retardant glass fibre air filter paper, the height
Alkali-free glass fibre cotton of the flame-retardance fiberglass air filter paper by a diameter of 7~9 μm, a diameter of 0.3~0.4 μm of alkali-free
Glass fibre cotton and bonding sizing material are made;Described a diameter of 7~9 μm of alkali-free glass fibre cotton and a diameter of 0.3~0.4 μm
Alkali-free glass fibre cotton mass ratio is 1: 3.8~4.2;The cohesive sizing material is that acrylic emulsion and halogen-free organophosphorous hydrochlorate fire retardant are mixed
Compound.The surfacing of glass fibre air filter paper, uniform, fire resistance is good.The filter paper that the patent is provided is effectively increased
High-temperature stability, but the filter paper of patent offer can only carry out air filtration and go out, and other industry is not considered specifically, and
Its resistance to elevated temperatures is also caused to have a greatly reduced quality using glass fibre as raw material, its intensity is not high in addition, and dust containing capacity is limited,
Often replacing is needed during use.
The A of Publication No. CN 103721477 Chinese patent provides a kind of high-strength glass fiber air filter paper and its preparation
Method, the air filter paper is made up of glass fibre with adhesive, and described glass fibre is uniform random point in a plane
Micron-sized hole is formed between cloth, multiple glass fibres, adhesive is wrapped on the intertwined point between glass fibre, form netted company
Junction.Glass fibre is by diameter in the glass of glass chopped silk and diameter between 1 μm~10 μm between 6 μm~20 μm
Glass cotton fiber is constituted.Adhesive is formed by inorganic silica gel or colloidal alumina or combinations thereof.The air filter paper is in normal temperature and height
Enough intensity is provided with temperature and excellent gas-liquid separation, liquid-liquid separation ability, can resist wind speed, flow it is multiple
Invasion and attack.Inorganic silicon or colloidal alumina adhesive used in the filter paper that the patent is provided, intensity is not high, cohesive force is not strong, because
This reduces the intensity of integral filter paper, and also causes that its intensity is restricted using glass fibre as raw material, and dust containing capacity is low,
Need frequently to change filter paper during use.
But just, due to the limitation of glass fibre in itself, cause the resistance to elevated temperatures of glass fiber filter paper from the point of view of current research
Not strong, current means can only be improved on the original basis, and not having to filter paper significantly improves, in addition by glass
The cleaning of filter paper is also inconvenient made from glass fiber, so the filter paper of research high temperature resistant and easy cleaning will turn near
The emphasis of year development.
The content of the invention
It it is 1~2 μm by fibre diameter the invention provides a kind of high temperature resistance and high strength automatically cleaning filter paper to overcome above mentioned problem
Basalt fibre, fibre diameter are that 2~4 μm of ceramic fibres, fibre diameter are that 2~5 μm of Zirconium oxide fibres, fibre diameter are 2~5 μm
Alumina fibre and high-temperature Resistance Adhesives composition, and impregnate one layer of nano-titanium dioxide film in filter paper fiber surface.The Black Warrior
Rock fiber and ceramic fibre are as a kind of inorfil, and not only stability is good, but also with electrical insulating property, anticorrosive, fire-resistant
A variety of excellent properties such as burning, high temperature resistant, strainability is good, and shear strength is high, uses it as filter paper raw material and is greatly lifted
The intensity and high-temperature stability of filter paper, and the different Zirconium oxide fibre of the length added and alumina fibre equally have height
Intensity, resistant to elevated temperatures characteristic, and the fiber of different length can mutually tangle mutual filling so that filter paper adhesion is improved, and is adopted
Multicomponent greatly reduces gas-flow resistance, improves filter efficiency.In addition it is thin in the nano titanium oxide of its surface dipping
Film causes filter paper to be provided with self-cleaning function so that its surface can keep self-cleaning effect for a long time, while titanium dioxide is also
Can by the harmful organic substances such as formaldehyde it is degradable be water and titanium dioxide, and do not cause secondary pollution, therefore not only environmental protection raising again
The service life of filter paper.
For realize the purpose of the present invention use technical scheme be:A kind of high temperature resistant type automatically cleaning filter paper, by fibrous material and fibre
Tie up the nano coating composition of material surface, it is characterised in that described fibrous material is 1~2 μm by 50~70%wt, fibre diameter
Basalt fibre, 20~30%wt, fibre diameter are 2~4 μm of ceramic fibres, and 5~10%wt, fibre diameter are 2~5 μm of oxidations
Zirconium fiber, 5~10%wt, fibre diameter are 2~5 μm of alumina fibre compositions, and the nano coating is that thickness is 0.05~0.10nm
Titanium deoxid film.
Described basalt fibre draw ratio is 25~50, and unit weight is 110~130kg/m3, the coefficient of heat conduction is 0.03~0.04W/m
K, tensile strength is 3500~4000MPa, and modulus of elasticity is 90~110GPa.
The ceramic fibre draw ratio is 20~35, and unit weight is 90~120kg/m3, the coefficient of heat conduction is 0.05~0.10W/mK.
The invention also discloses the preparation method of high-temperature-resistant self-cleaning filter paper, it is characterised in that comprises the following steps:
(1) raw material prepares:Take 50~70 parts of basalt fibres respectively, 20~30 parts of ceramic fibres, 5~10 parts of Zirconium oxide fibres,
5~10 parts of alumina fibres;
(2) slurrying is disperseed:Raw material selected by step (1) are added in disperser to be beaten and disperse to obtain slurry, slurry is adjusted
PH value be 2.4~3.0, and adjust stock quality concentration for 1.0%~1.8%;
(3) wet moulding:Slurry obtained by step (2) is transferred to storage pool, and it is 0.1%~0.15% to be diluted to mass concentration
And PH to 2.6~2.9 is adjusted, the slurry of storage pool then is delivered into shaping on former obtains l Water Paper;
(4) suction dehydration:Three stage dewater treatments are carried out to l Water Paper obtained by step (3), the vacuum of wherein first stage is
0.01~0.02MPa, the vacuum of second stage is 0.02~0.04MPa, and the vacuum of phase III is 0.06~0.09Mpa, is made
Moisture percentage is less than 25%;
(5) drying process:10~20min, Ran Hou are handled under the conditions of 200~250 DEG C to l Water Paper prepared by step (4)
10~30min is handled under the conditions of 250~300 DEG C, 5~10min is finally handled under the conditions of 230~280 DEG C, is final aqueous of product
Rate is less than 0.05%.
(6) TiO is coated2:The titanium for being 20~25% as 4~7m, mass concentration by length using 0.1~4cm/s speed by filter paper
Acid butyl ester alcoholic solution, it is ultraviolet 3~5min of oven drying that 250nm temperature is 300 DEG C to enter back into wavelength;
(7) glue spraying is handled:Adhesive is diluted to 5~10 times, equably sprinkling or overflow is put on fiber ground paper, unnecessary
Adhesive aspirated by suction box, come back to after being separated through knockout drum circulation glue tank in.
Usefulness of the present invention is:1st, resistance to elevated temperatures 2, intensity it is high by 3, with self-cleaning function.
Embodiment
With reference to specific embodiment, the present invention is furture elucidated, it should be understood that these embodiments be merely to illustrate the present invention and without
In limitation the scope of the present invention, after the present invention has been read, those skilled in the art repair to the various equivalent form of values of the invention
Change and fall within the application appended claims and limited.
Embodiment 1
A kind of high temperature resistant type automatically cleaning filter paper, is made up of the nano coating of fibrous material and fibrous material surface, it is characterised in that
Described fibrous material is 2 μm of basalt fibres by 50%wt, fibre diameter, and 30%wt, fibre diameter are that 2 μm of ceramics are fine
Dimension, 10%wt, fibre diameter are that 2 μm of Zirconium oxide fibres, 10%wt, fibre diameter are 2 μm of alumina fibres compositions, institute
It is that thickness is 0.05nm titanium deoxid films to state nano coating.
Described basalt fibre draw ratio is 25, and unit weight is 110kg/m3, the coefficient of heat conduction is 0.03W/mK, and tension is strong
Spend for 3500MPa, modulus of elasticity is 90GPa.
The ceramic fibre draw ratio is 20, and unit weight is 90kg/m3, the coefficient of heat conduction is 0.05W/mK.
The invention also discloses the preparation method of high-temperature-resistant self-cleaning filter paper, it is characterised in that comprises the following steps:
(1) raw material prepares:50 parts of basalt fibres, 30 parts of ceramic fibres, 10 parts of Zirconium oxide fibres, 10 parts are taken respectively
Alumina fibre;
(2) slurrying is disperseed:Raw material selected by step (1) are added in disperser to be beaten and disperse to obtain slurry, slurry is adjusted
PH value be 3.0, and adjust stock quality concentration for 1.8%;
(3) wet moulding:Slurry obtained by step (2) is transferred to storage pool, is diluted to mass concentration and is 0.15% and adjusts
PH to 2.9, is then delivered to shaping on former by the slurry of storage pool and obtains l Water Paper;
(4) suction dehydration:Three stage dewater treatments are carried out to l Water Paper obtained by step (3), the vacuum of wherein first stage is
0.01MPa, the vacuum of second stage is 0.02MPa, and the vacuum of phase III is 0.06Mpa, moisture percentage is less than 25%;
(5) drying process:20min is handled under the conditions of 200 DEG C to l Water Paper prepared by step (4), then in 250 DEG C of bars
30min is handled under part, 5~10min is finally handled under the conditions of 230~280 DEG C, is that the final moisture content of product is less than 0.05%.
(6) TiO is coated2:The butyl titanate for being 20% as 4m, mass concentration by length using 0.1cm/s speed by filter paper
Alcoholic solution, it is the ultraviolet oven drying 5min that 250nm temperature is 300 DEG C to enter back into wavelength;
(7) glue spraying is handled:Adhesive is diluted to 5 times, equably sprinkling or overflow is put on fiber ground paper, unnecessary glue
Glutinous agent is aspirated by suction box, is come back to after being separated through knockout drum in circulation glue tank.
Embodiment 2
A kind of high temperature resistant type automatically cleaning filter paper, is made up of the nano coating of fibrous material and fibrous material surface, it is characterised in that
Described fibrous material is 2 μm of basalt fibres by 70%wt, fibre diameter, and 20%wt, fibre diameter are 4 μm of ceramic fibres,
5%wt, fibre diameter are that 5 μm of Zirconium oxide fibres, 5%wt, fibre diameter are 5 μm of alumina fibres compositions, and the nanometer is applied
Layer is that thickness is 0.10nm titanium deoxid films.
Described basalt fibre draw ratio is 50, and unit weight is 130kg/m3, the coefficient of heat conduction is 0.04W/mK, and tension is strong
Spend for 4000MPa, modulus of elasticity is 110GPa.
The ceramic fibre draw ratio is 35, and unit weight is 120kg/m3, the coefficient of heat conduction is 0.10W/mK.
The invention also discloses the preparation method of high-temperature-resistant self-cleaning filter paper, it is characterised in that comprises the following steps:
(1) raw material prepares:70 parts of basalt fibres, 20 parts of ceramic fibres, 5 parts of Zirconium oxide fibres, 5 parts of oxidations are taken respectively
Aluminum fiber;
(2) slurrying is disperseed:Raw material selected by step (1) are added in disperser to be beaten and disperse to obtain slurry, slurry is adjusted
PH value be 3.0, and adjust stock quality concentration for 1.8%;
(3) wet moulding:Slurry obtained by step (2) is transferred to storage pool, is diluted to mass concentration and is 0.15% and adjusts
PH to 2.9, is then delivered to shaping on former by the slurry of storage pool and obtains l Water Paper;
(4) suction dehydration:Three stage dewater treatments are carried out to l Water Paper obtained by step (3), the vacuum of wherein first stage is
0.02MPa, the vacuum of second stage is 0.04MPa, and the vacuum of phase III is 0.09Mpa, moisture percentage is less than 25%;
(5) drying process:10min is handled under the conditions of 250 DEG C to l Water Paper prepared by step (4), then in 300 DEG C of bars
10min is handled under part, finally 5min is handled under the conditions of 280 DEG C, is that the final moisture content of product is less than 0.05%.
(6) TiO is coated2:The butyl titanate wine for being 25% as 7m, mass concentration by length using 4cm/s speed by filter paper
Smart solution, it is ultraviolet 3~5min of oven drying that 250nm temperature is 300 DEG C to enter back into wavelength;
(7) glue spraying is handled:Adhesive is diluted to 10 times, equably sprinkling or overflow is put on fiber ground paper, unnecessary
Adhesive is aspirated by suction box, is come back to after being separated through knockout drum in circulation glue tank.
Single embodiment of the invention is above are only, but the design concept of the present invention is not limited thereto, it is all to utilize this design
The change of unsubstantiality is carried out to the present invention, the behavior for invading the scope of protection of the invention all should be belonged to.In every case it is without departing from this hair
The content of bright technical scheme, it is any type of simple modification that the technical spirit according to the present invention is made to above example, equivalent
Change and remodeling, still fall within the protection domain of technical solution of the present invention.
Claims (4)
1. a kind of high temperature resistant type automatically cleaning filter paper, is made up of the nano coating of fibrous material and fibrous material surface, its feature exists
By 50~70%wt, fibre diameter it is 1~2 μm of basalt fibre in described fibrous material, 20~30%wt, fibre diameter are
2~4 μm of ceramic fibres, 5~10%wt, fibre diameter are that 2~5 μm of Zirconium oxide fibres, 5~10%wt, fibre diameter are 2~5 μm
Alumina fibre is constituted, and it is that thickness is 0.05~0.10nm titanium deoxid films to tell nano coating.
2. filter paper according to claim 1, it is characterised in that described basalt fibre draw ratio is 25~50, unit weight
For 110~130kg/m3, the coefficient of heat conduction is 0.03~0.04W/mK, and tensile strength is 3500~4000MPa, and modulus of elasticity is
90~110GPa.
3. filter paper according to claim 1, it is characterised in that the ceramic fibre draw ratio is 20~35, unit weight is
90~120kg/m3, the coefficient of heat conduction is 0.05~0.10W/mK.
4. the invention also discloses the preparation method of high-temperature-resistant self-cleaning filter paper, it is characterised in that comprises the following steps:
(1) raw material prepares:Take 50~70 parts of basalt fibres respectively, 20~30 parts of ceramic fibres, 5~10 parts of Zirconium oxide fibres,
5~10 parts of alumina fibres;
(2) slurrying is disperseed:Raw material selected by step (1) are added in disperser to be beaten and disperse to obtain slurry, slurry is adjusted
PH value be 2.4~3.0, and adjust stock quality concentration for 1.0%~1.8%;
(3) wet moulding:Slurry obtained by step (2) is transferred to storage pool, and it is 0.1%~0.15% to be diluted to mass concentration
And PH to 2.6~2.9 is adjusted, the slurry of storage pool then is delivered into shaping on former obtains l Water Paper;
(4) suction dehydration:Three stage dewater treatments are carried out to l Water Paper obtained by step (3), the vacuum of wherein first stage is
0.01~0.02MPa, the vacuum of second stage is 0.02~0.04MPa, and the vacuum of phase III is 0.06~0.09Mpa, is made
Moisture percentage is less than 25%;
(5) drying process:10~20min, Ran Hou are handled under the conditions of 200~250 DEG C to l Water Paper prepared by step (4)
10~30min is handled under the conditions of 250~300 DEG C, 5~10min is finally handled under the conditions of 230~280 DEG C, is final aqueous of product
Rate is less than 0.05%.
(6) TiO is coated2:The titanium for being 20~25% as 4~7m, mass concentration by length using 0.1~4cm/s speed by filter paper
Acid butyl ester alcoholic solution, it is ultraviolet 3~5min of oven drying that 250nm temperature is 300 DEG C to enter back into wavelength;
(7) glue spraying is handled:Adhesive is diluted to 5~10 times, equably sprinkling or overflow is put on fiber ground paper, unnecessary
Adhesive aspirated by suction box, come back to after being separated through knockout drum circulation glue tank in.