CN107287919A - A kind of waterproof antiwear cloth and preparation method thereof - Google Patents
A kind of waterproof antiwear cloth and preparation method thereof Download PDFInfo
- Publication number
- CN107287919A CN107287919A CN201710570711.6A CN201710570711A CN107287919A CN 107287919 A CN107287919 A CN 107287919A CN 201710570711 A CN201710570711 A CN 201710570711A CN 107287919 A CN107287919 A CN 107287919A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- antifriction layer
- burlap
- proof antifriction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of waterproof antiwear cloth and preparation method thereof, the waterproof antiwear cloth is made up of burlap and water-proof antifriction layer, and water-proof antifriction layer is coated on burlap surface, and the water-proof antifriction layer is prepared from the following raw materials in parts by weight：60-85 parts of Corvic, 3-6 parts of dibutyl phthalate, 6-15 parts of epoxy resin, 5 10 parts of stearic acid, 3-8 parts of THPC, 3-7 parts of polyvinylether, 0.8 2 parts of mould inhibitor, 0.5 1.2 parts of age resistor, 10 18 parts of modification infusorial earth, 59 parts of diisocyanate, 1-3 parts of dimethicone, 13 parts of nano titanium oxide, 2-5 parts of Cocoamidopropyl betaine, 1-5 parts of potassium hydroxide.Compared with prior art, the waterproof antiwear cloth in the present invention has good water proofing property, wearability, greatly improves its performance.
Description
Technical field
The invention belongs to textile industry technical field, more particularly to a kind of waterproof antiwear cloth and preparation method thereof.
Background technology
Cloth is widely used in the every field of industrial society, for example, cloth can be fabricated to packaging bag and for clothes
Dress, textile are packed.At present, the packaging bag wide variety in China market, the wherein packaging bag of plastic products are most, by
It is larger to environmental hazard and often disposable by people in plastic products, thus cause the waste of resource；In addition, traditional
Cloth packaging bag do not have waterproof efficacy generally, extraneous rainwater is easy to get wet the product in packaging bag.
The content of the invention
It is an object of the invention to provide a kind of waterproof antiwear cloth and preparation method thereof, it has good waterproof performance, preparation side
The advantages of method is simple.
To achieve the above object, the present invention provides following technical scheme：
A kind of waterproof antiwear cloth, the waterproof antiwear cloth is made up of burlap and water-proof antifriction layer, and water-proof antifriction layer is applied
Burlap surface is overlying on, the water-proof antifriction layer is prepared from the following raw materials in parts by weight：60-85 parts of Corvic, adjacent benzene
3-6 parts of dibutyl carboxylic acid, 6-15 parts of epoxy resin, 5-10 parts of stearic acid, 3-8 parts of THPC, polyvinylether
3-7 parts, 0.8-2 parts of mould inhibitor, 0.5-1.2 parts of age resistor, 10-18 parts of modification infusorial earth, 5-9 parts of diisocyanate, dimethyl
1-3 parts of silicone oil, 1-3 parts of nano titanium oxide, 2-5 parts of Cocoamidopropyl betaine, 1-5 parts of potassium hydroxide.
Preferably, the water-proof antifriction layer is prepared from the following raw materials in parts by weight：68 parts of Corvic, adjacent benzene two
5 parts of formic acid dibutyl ester, 12 parts of epoxy resin, 7 parts of stearic acid, 5 parts of THPC, 4.6 parts of polyvinylether, mould inhibitor
1.2 parts, 1 part of age resistor, 14 parts of modification infusorial earth, 7 parts of diisocyanate, 1.6 parts of dimethicone, nano titanium oxide 2.5
Part, 3 parts of Cocoamidopropyl betaine, 3 parts of potassium hydroxide.
Preferably, the water-proof antifriction layer is prepared from the following raw materials in parts by weight：80 parts of Corvic, adjacent benzene two
3 parts of formic acid dibutyl ester, 8 parts of epoxy resin, 8 parts of stearic acid, 6 parts of THPC, 4.8 parts of polyvinylether, mould inhibitor 1.3
Part, 0.8 part of age resistor, 14 parts of modification infusorial earth, 8 parts of diisocyanate, 1.6 parts of dimethicone, nano titanium oxide 2.2
Part, 5 parts of Cocoamidopropyl betaine, 3.5 parts of potassium hydroxide.
A kind of preparation method of waterproof antiwear cloth, comprises the following steps：
1) burlap, is prepared；
2), by Corvic, dibutyl phthalate, epoxy resin, stearic acid, THPC, poly-
Vinethene, mould inhibitor, age resistor, modification infusorial earth, diisocyanate, dimethicone, nano titanium oxide, coconut oleoyl amine third
Base glycine betaine and potassium hydroxide are uniformly mixed, and water-proof antifriction layer maceration extract is made in 28-32 degree in temperature control；
3), by step 1) in institute ready burlap be placed in step 2) in water-proof antifriction layer maceration extract in progress pad place
Reason, 0.8-1.6MPa of pressure；
4), drying and processing is carried out at 140-145 DEG C.
Compared with prior art, the beneficial effects of the invention are as follows：
Waterproof antiwear cloth in the present invention coats water-proof antifriction layer, waterproof antiwear using burlap as base-material on its surface
Corvic, stearic acid, THPC, diisocyanate, dimethicone, cocounut oil acyl have been especially added with layer
Amine CAB, thus water-proof antifriction layer has good waterproof, abrasion resistant effect；The waterproof antiwear cloth being packed for especially is fitted
For packaging industry, and greatly improve its performance.
Embodiment
Technical scheme is described in detail with reference to embodiment, but protection domain is not limited thereto.
Embodiment one：
A kind of waterproof antiwear cloth, the waterproof antiwear cloth is made up of burlap and water-proof antifriction layer, and water-proof antifriction layer is applied
Burlap surface is overlying on, the water-proof antifriction layer is prepared from the following raw materials in parts by weight：68 parts of Corvic, O-phthalic
4.5 parts of dibutyl phthalate, 11 parts of epoxy resin, 8 parts of stearic acid, 5 parts of THPC, 4 parts of polyvinylether, mould inhibitor 1.3
Part, 1 part of age resistor, 15 parts of modification infusorial earth, 7 parts of diisocyanate, 1.3 parts of dimethicone, 1 part of nano titanium oxide, coconut palm
4 parts of oleamide CAB, 3 parts of potassium hydroxide.
The preparation method of the waterproof antiwear cloth, comprises the following steps：
1) burlap, is prepared；
2), by Corvic, dibutyl phthalate, epoxy resin, stearic acid, THPC, poly-
Vinethene, mould inhibitor, age resistor, modification infusorial earth, diisocyanate, dimethicone, nano titanium oxide, coconut oleoyl amine third
Base glycine betaine and potassium hydroxide are uniformly mixed, and water-proof antifriction layer maceration extract is made in 28-32 degree in temperature control；
3), by step 1) in institute ready burlap be placed in step 2) in water-proof antifriction layer maceration extract in progress pad place
Reason, 0.8-1.6MPa of pressure；
4), drying and processing is carried out at 140-145 DEG C.
Embodiment two：
A kind of waterproof antiwear cloth, the waterproof antiwear cloth is made up of burlap and water-proof antifriction layer, and water-proof antifriction layer is applied
Burlap surface is overlying on, the water-proof antifriction layer is prepared from the following raw materials in parts by weight：80 parts of Corvic, O-phthalic
6 parts of dibutyl phthalate, 12 parts of epoxy resin, 7 parts of stearic acid, 4.8 parts of THPC, 5 parts of polyvinylether, mould inhibitor 1.6
Part, 0.6 part of age resistor, 11 parts of modification infusorial earth, 7 parts of diisocyanate, 1.5 parts of dimethicone, 2 parts of nano titanium oxide,
2.8 parts of Cocoamidopropyl betaine, 4.5 parts of potassium hydroxide.
The preparation method of the waterproof antiwear cloth, comprises the following steps：
1) burlap, is prepared；
2), by Corvic, dibutyl phthalate, epoxy resin, stearic acid, THPC, poly-
Vinethene, mould inhibitor, age resistor, modification infusorial earth, diisocyanate, dimethicone, nano titanium oxide, coconut oleoyl amine third
Base glycine betaine and potassium hydroxide are uniformly mixed, and water-proof antifriction layer maceration extract is made in 28-32 degree in temperature control；
3), by step 1) in institute ready burlap be placed in step 2) in water-proof antifriction layer maceration extract in progress pad place
Reason, 0.8-1.6MPa of pressure；
4), drying and processing is carried out at 140-145 DEG C.
Embodiment three：
A kind of waterproof antiwear cloth, the waterproof antiwear cloth is made up of burlap and water-proof antifriction layer, and water-proof antifriction layer is applied
Burlap surface is overlying on, the water-proof antifriction layer is prepared from the following raw materials in parts by weight：68 parts of Corvic, O-phthalic
5 parts of dibutyl phthalate, 12 parts of epoxy resin, 7 parts of stearic acid, 5 parts of THPC, 4.6 parts of polyvinylether, mould inhibitor 1.2
Part, 1 part of age resistor, 14 parts of modification infusorial earth, 7 parts of diisocyanate, 1.6 parts of dimethicone, 2.5 parts of nano titanium oxide,
3 parts of Cocoamidopropyl betaine, 3 parts of potassium hydroxide.
The preparation method of the waterproof antiwear cloth, comprises the following steps：
1) burlap, is prepared；
2), by Corvic, dibutyl phthalate, epoxy resin, stearic acid, THPC, poly-
Vinethene, mould inhibitor, age resistor, modification infusorial earth, diisocyanate, dimethicone, nano titanium oxide, coconut oleoyl amine third
Base glycine betaine and potassium hydroxide are uniformly mixed, and water-proof antifriction layer maceration extract is made in 28-32 degree in temperature control；
3), by step 1) in institute ready burlap be placed in step 2) in water-proof antifriction layer maceration extract in progress pad place
Reason, 0.8-1.6MPa of pressure；
4), drying and processing is carried out at 140-145 DEG C.
Example IV：
A kind of waterproof antiwear cloth, the waterproof antiwear cloth is made up of burlap and water-proof antifriction layer, and water-proof antifriction layer is applied
Burlap surface is overlying on, the water-proof antifriction layer is prepared from the following raw materials in parts by weight：80 parts of Corvic, O-phthalic
3 parts of dibutyl phthalate, 8 parts of epoxy resin, 8 parts of stearic acid, 6 parts of THPC, 4.8 parts of polyvinylether, mould inhibitor 1.3
Part, 0.8 part of age resistor, 14 parts of modification infusorial earth, 8 parts of diisocyanate, 1.6 parts of dimethicone, nano titanium oxide 2.2
Part, 5 parts of Cocoamidopropyl betaine, 3.5 parts of potassium hydroxide.
The preparation method of the waterproof antiwear cloth, comprises the following steps：
1) burlap, is prepared；
2), by Corvic, dibutyl phthalate, epoxy resin, stearic acid, THPC, poly-
Vinethene, mould inhibitor, age resistor, modification infusorial earth, diisocyanate, dimethicone, nano titanium oxide, coconut oleoyl amine third
Base glycine betaine and potassium hydroxide are uniformly mixed, and water-proof antifriction layer maceration extract is made in 28-32 degree in temperature control；
3), by step 1) in institute ready burlap be placed in step 2) in water-proof antifriction layer maceration extract in progress pad place
Reason, 0.8-1.6MPa of pressure；
4), drying and processing is carried out at 140-145 DEG C.
Embodiment five：
A kind of waterproof antiwear cloth, the waterproof antiwear cloth is made up of burlap and water-proof antifriction layer, and water-proof antifriction layer is applied
Burlap surface is overlying on, the water-proof antifriction layer is prepared from the following raw materials in parts by weight：75 parts of Corvic, O-phthalic
3 parts of dibutyl phthalate, 13 parts of epoxy resin, 9 parts of stearic acid, 6 parts of THPC, 6 parts of polyvinylether, 1 part of mould inhibitor is prevented
Old 1 part of agent, 15 parts of modification infusorial earth, 6 parts of diisocyanate, 2.3 parts of dimethicone, 1.8 parts of nano titanium oxide, cocounut oil acyl
5 parts of amine CAB, 4 parts of potassium hydroxide.
The preparation method of the waterproof antiwear cloth, comprises the following steps：
1) burlap, is prepared；
2), by Corvic, dibutyl phthalate, epoxy resin, stearic acid, THPC, poly-
Vinethene, mould inhibitor, age resistor, modification infusorial earth, diisocyanate, dimethicone, nano titanium oxide, coconut oleoyl amine third
Base glycine betaine and potassium hydroxide are uniformly mixed, and water-proof antifriction layer maceration extract is made in 28-32 degree in temperature control；
3), by step 1) in institute ready burlap be placed in step 2) in water-proof antifriction layer maceration extract in progress pad place
Reason, 0.8-1.6MPa of pressure；
4), drying and processing is carried out at 140-145 DEG C.
Embodiment six：
A kind of waterproof antiwear cloth, the waterproof antiwear cloth being packed for is made up of burlap and water-proof antifriction layer, waterproof
Wearing layer is coated on burlap surface, and the water-proof antifriction layer is prepared from the following raw materials in parts by weight：60 parts of Corvic,
3 parts of dibutyl phthalate, 6 parts of epoxy resin, 5 parts of stearic acid, 3 parts of THPC, 3 parts of polyvinylether is mould proof
0.8 part of agent, 0.5 part of age resistor, 10 parts of modification infusorial earth, 5 parts of diisocyanate, 1 part of dimethicone, nano titanium oxide 1
Part, 2 parts of Cocoamidopropyl betaine, 1 part of potassium hydroxide.
The preparation method of the waterproof antiwear cloth, comprises the following steps：
1) burlap, is prepared；
2), by Corvic, dibutyl phthalate, epoxy resin, stearic acid, THPC, poly-
Vinethene, mould inhibitor, age resistor, modification infusorial earth, diisocyanate, dimethicone, nano titanium oxide, coconut oleoyl amine third
Base glycine betaine and potassium hydroxide are uniformly mixed, and water-proof antifriction layer maceration extract is made in 28-32 degree in temperature control；
3), by step 1) in institute ready burlap be placed in step 2) in water-proof antifriction layer maceration extract in progress pad place
Reason, 0.8-1.6MPa of pressure；
4), drying and processing is carried out at 140-145 DEG C.
Embodiment seven：
A kind of waterproof antiwear cloth, the waterproof antiwear cloth being packed for is made up of burlap and water-proof antifriction layer, waterproof
Wearing layer is coated on burlap surface, and the water-proof antifriction layer is prepared from the following raw materials in parts by weight：85 parts of Corvic,
6 parts of dibutyl phthalate, 15 parts of epoxy resin, 10 parts of stearic acid, 8 parts of THPC, 7 parts of polyvinylether is prevented
Mould dose 2 parts, 1.2 parts of age resistor, 18 parts of modification infusorial earth, 9 parts of diisocyanate, 3 parts of dimethicone, nano titanium oxide 3
Part, 5 parts of Cocoamidopropyl betaine, 5 parts of potassium hydroxide.
The preparation method of the waterproof antiwear cloth, comprises the following steps：
1) burlap, is prepared；
2), by Corvic, dibutyl phthalate, epoxy resin, stearic acid, THPC, poly-
Vinethene, mould inhibitor, age resistor, modification infusorial earth, diisocyanate, dimethicone, nano titanium oxide, coconut oleoyl amine third
Base glycine betaine and potassium hydroxide are uniformly mixed, and water-proof antifriction layer maceration extract is made in 28-32 degree in temperature control；
3), by step 1) in institute ready burlap be placed in step 2) in water-proof antifriction layer maceration extract in progress pad place
Reason, 0.8-1.6MPa of pressure；
4), drying and processing is carried out at 140-145 DEG C.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to skill of the invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of the technical program, it all should cover in the present invention
Right among.
Claims (4)
1. a kind of waterproof antiwear cloth, it is characterised in that：The waterproof antiwear cloth is made up of burlap and water-proof antifriction layer, waterproof
Wearing layer is coated on burlap surface, and the water-proof antifriction layer is prepared from the following raw materials in parts by weight：Corvic 60-
85 parts, 3-6 parts of dibutyl phthalate, 6-15 parts of epoxy resin, 5-10 parts of stearic acid, THPC 3-8
Part, 3-7 parts of polyvinylether, 0.8-2 parts of mould inhibitor, 0.5-1.2 parts of age resistor, 10-18 parts of modification infusorial earth, diisocyanate
5-9 parts, 1-3 parts of dimethicone, 1-3 parts of nano titanium oxide, 2-5 parts of Cocoamidopropyl betaine, potassium hydroxide 1-
5 parts.
2. a kind of waterproof antiwear cloth according to claim 1, it is characterised in that the water-proof antifriction layer is by following weight
The raw material of number is made：68 parts of Corvic, 5 parts of dibutyl phthalate, 12 parts of epoxy resin, 7 parts of stearic acid, four
5 parts of methylol phosphorus chloride, 4.6 parts of polyvinylether, 1.2 parts of mould inhibitor, 1 part of age resistor, 14 parts of modification infusorial earth, diisocyanate
7 parts, 1.6 parts of dimethicone, 2.5 parts of nano titanium oxide, 3 parts of Cocoamidopropyl betaine, 3 parts of potassium hydroxide.
3. a kind of waterproof antiwear cloth according to claim 1, it is characterised in that the water-proof antifriction layer is by following weight
The raw material of number is made：80 parts of Corvic, 3 parts of dibutyl phthalate, 8 parts of epoxy resin, 8 parts of stearic acid, four
6 parts of methylol phosphorus chloride, 4.8 parts of polyvinylether, 1.3 parts of mould inhibitor, 0.8 part of age resistor, 14 parts of modification infusorial earth, two isocyanic acids
8 parts of ester, 1.6 parts of dimethicone, 2.2 parts of nano titanium oxide, 5 parts of Cocoamidopropyl betaine, 3.5 parts of potassium hydroxide.
4. the preparation method of the waterproof antiwear cloth according to any one of claim 1-3, it is characterised in that including following
Step：
1) burlap, is prepared；
2), by Corvic, dibutyl phthalate, epoxy resin, stearic acid, THPC, polyethylene
Ether, mould inhibitor, age resistor, modification infusorial earth, diisocyanate, dimethicone, nano titanium oxide, cocamidopropyl propyl amide sweet tea
Dish alkali and potassium hydroxide are uniformly mixed, and water-proof antifriction layer maceration extract is made in 28-32 degree in temperature control；
3), by step 1) in institute ready burlap be placed in step 2) in water-proof antifriction layer maceration extract in progress pad processing,
0.8-1.6MPa of pressure；
4), drying and processing is carried out at 140-145 DEG C.