CN107281000A - A kind of application method of bacterial cellulose facial mask - Google Patents
A kind of application method of bacterial cellulose facial mask Download PDFInfo
- Publication number
- CN107281000A CN107281000A CN201710484211.0A CN201710484211A CN107281000A CN 107281000 A CN107281000 A CN 107281000A CN 201710484211 A CN201710484211 A CN 201710484211A CN 107281000 A CN107281000 A CN 107281000A
- Authority
- CN
- China
- Prior art keywords
- facial mask
- bacterial cellulose
- thickness
- cellulose facial
- essence
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of application method of bacterial cellulose facial mask.The present invention carries out overall merit by the thickness to bacterial cellulose facial mask and tensile capacity, the adsorption capacity to Essence and releasability, it is determined that the thickness range of the bacterial cellulose facial mask with preferable tensile capacity, the adsorption capacity to Essence and releasability, i.e. 1.25 1.50mm.The present invention can provide reliable foundation for bacterial cellulose facial mask on the market on production thickness, and in 1.25 1.50mm thickness ranges, bacterial cellulose facial mask has preferable tensile strength, adsorption capacity and releasability to Essence.
Description
Technical field
This method is related to a kind of application method of bacterial cellulose facial mask, belongs to cosmetic products technical field.
Background technology
Bacteria cellulose is a kind of a kind of polysaccharide synthesized by some bacteriums, with good biocompatibility, can be dropped
The special performance such as solution property and water-retaining property, is widely used in the numerous areas such as biomedical, organizational project and food.
Because everyone facial contours are different, shaping class facial mask is as the certain facial mask of size, shape, for difference
User, the orientation of application is slightly different.Therefore in use, in order to preferably experience the skin sense of touch that facial mask is brought
Nutriment is absorbed with more preferable, the position that each user can apply according to the hobby and shape of face of oneself to facial mask is carried out slightly
Adjustment slightly, therefore, the facial mask of good shaping class, it should with certain tensile capacity.And tensile strength it is too low if meeting
Cause facial mask once drawing brokenly, cause bad Consumer's Experience.
Adsorption capacity and releasability to Essence are the vital performances of facial mask.Comprehensive production cost is with using body
Test, it is desirable to which facial mask can have larger adsorbance and burst size in a short time, and facial mask thickness is then determining for both performances
Qualitative factor.
Due to the weight of tensile capacity of the thickness for bacterial cellulose facial mask, the adsorption capacity to Essence and releasability
Influence, applicant has investigated the thickness of the famous bacterial cellulose facial mask of commercially available comparison.The wherein tender flesh skin-active elite face of Lancome
Film thickness is 0.55mm, and the name Biofibre facial mask thickness of favour is 1.23mm, and Da Er skin moisturizing brilliant whites Biofibre facial mask is thick
Spend for 0.83mm, it is 1.68mm that cool poem, which more attains the also young Biofibre facial mask thickness of face,.
In recent years, the various improvement trials for being related to bacterial cellulose facial mask emerge in an endless stream, but because each side use it is thin
Fungin facial mask thickness is different, and the adsorption capacity and releasability to Essence are different, cause various method of modifying it
Between can not preferably be contrasted.And the thickness of the bacterial cellulose facial mask in commercially available and laboratory is also very chaotic, mixed and disorderly distribution
In 0.5-2.5mm.For these reasons, it is necessary to which providing one on production thickness for bacterial cellulose facial mask on the market can
The foundation leaned on.
The content of the invention
It is an object of the invention to provide a kind of application method of the bacterial cellulose facial mask of chain of command film thickness.
Realize that the technical scheme of the object of the invention is as follows:
A kind of application method of bacterial cellulose facial mask, the thickness of bacterial cellulose facial mask is 1.25-1.50mm.
The present invention passes through the thickness to bacterial cellulose facial mask and tensile capacity, the adsorption capacity to Essence and release energy
Power carries out overall merit, it is determined that a bacterium with preferable tensile capacity, the adsorption capacity to Essence and releasability
The thickness range of cellulose facial mask, i.e. 1.25-1.50mm.The present invention can be thick in production for bacterial cellulose facial mask on the market
Reliable foundation is provided on degree, in 1.25-1.50mm thickness ranges, bacterial cellulose facial mask have preferable tensile strength,
To the adsorption capacity and releasability of Essence.
Embodiment
With reference to specific embodiment, the invention will be further described.
Because bacteria cellulose film is hydrophilic film, therefore test selects hydrophilic small molecules allantoin with nutriment.Base
The custom time of facial mask is used in people, 30min is set as the transdermal release time.Consider time cost and the absorption of production
Efficiency, sets 24h as nutriment adsorption time.
1. the tensile property test of bacterial cellulose facial mask
Universal electrical sample machine is controlled to carry out extension test to the wet film of test sample respectively using microcomputer.Will be homemade thin
Fungin film is cut into 20mm*70mm test bars, rate of extension 5mm/min.Every kind of sample test 3 times, takes its average value.
2. the transdermal release experiment of bacteria cellulose film
Pigskin is taken to be placed in the middle of reception tank and supply pool (effective transdermal area S=2.49cm2), epidermis is towards supply chamber side
To after being fixed with tweezers, the bacteria cellulose film for being adsorbed with allantoin of different-thickness is close into skin epidermis respectively.Thoroughly
Leather strap part:37 DEG C of bath temperature, reception tank rotating speed 250r/min, supply chamber is in open state.The setting of every film it is transdermal when
Between be 30min, it is transdermal finish after remove, every kind of thickness is tested 5 times and averaged respectively.It is as follows to skin treatment:Using go from
Sub- water removes the allantoin of skin surface, and skin is shredded and is dipped in deionized water, the allantoin of ultrasonic extraction corium and epidermis,
Determine the Content of Allantoin for being transported to skin.
3. the nutriment adsorption test of bacteria cellulose film
Different-thickness (0.5~2.5mm, using 0.25mm as gradient) 2 × 2cm is taken respectively2If diaphragm dry plate to be measured, fill
Sub-dip enters in allantoin after 24h, takes out, and shreds the concentration of ultrasonic extraction wherein active principle, determines the effective of membrane material absorption
The amount of material.Every kind of thickness replication 5 times, records average value.
Tensile strength, transdermal release rate and the absorption property result of the bacteria cellulose film of the different-thickness of table 1
Tensile strength is general in more than 1.0MPa, and facial mask will not cause facial mask when applying and tearing because of somewhat exerting oneself
Rupture is deformed.Meanwhile, transmission efficiency and the film thickness of the nutriment being carried on bacteria cellulose film have substantial connection,
I.e. film is thicker, and transfer rate is slower, and this is relevant with the tridimensional network of film, i.e., membrane structure causes material bang path to extend,
So transfer rate is slower.Moreover, for the transfer rate within the short time (30min), film thickness is less than 1.5mm bacterium
Cellulose membrane is preferable to the conveying effect of material, and transporting velocity is fast, and the conveying to nutriment reaches balance in a short time,
And conveying cumulative amount is larger;And the transporting velocity that thickness is more than 1.5mm bacteria cellulose film is slow, convey in a short time accumulative
Amount is small.The data result of 24h adsorbances shows that 24h adsorbances are relevant with the structure of bacteria cellulose and emulsion in table 1, in emulsion
In, allantoin is dissolved in water for continuous phase, and bacteria cellulose is the hydrophilic macromolecule for the network structure for having densification, to continuous phase
With affinity interaction, make it possible to diffuse into membrane material constantly, therefore film thickness is bigger, uptake is also greatly increased.And
Facial mask needs absorption nutriment as much as possible in 24h while with certain tensile strength, so that in 30min
The nutriment as much as possible for discharging absorption.As can be seen from Table 1, when thickness is 1.25-1.50mm, bacteria cellulose
The tensile strength of film, to the adsorption capacity and releasability of Essence all in preferable scope, meet the requirements.
Claims (1)
1. a kind of application method of bacterial cellulose facial mask, it is characterised in that the thickness of bacterial cellulose facial mask is 1.25-
1.50mm。