CN107268932A - The preparation method of abrasion-resistant ground between a kind of prefabricated bathroom - Google Patents
The preparation method of abrasion-resistant ground between a kind of prefabricated bathroom Download PDFInfo
- Publication number
- CN107268932A CN107268932A CN201710560637.XA CN201710560637A CN107268932A CN 107268932 A CN107268932 A CN 107268932A CN 201710560637 A CN201710560637 A CN 201710560637A CN 107268932 A CN107268932 A CN 107268932A
- Authority
- CN
- China
- Prior art keywords
- ground
- abrasion
- curing
- ultraviolet photo
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of abrasion-resistant ground between prefabricated bathroom, by integral vacuum toilet land clearing it is clean, dry, have wax wants paraffin removal;One layer of UV ultraviolet photo-curing shadowless glue is uniformly applied on the ground, and thickness is 0.03 0.07mm;PVC abrasion-proof gauge facial masks are covered in UV ultraviolet photo-curing shadowless glues, extruded untill middle bubble-free, are allowed to fit smooth;With the 15s of ultraviolet photo-curing light irradiation ground 10, make UV ultraviolet photo-curing shadowless glue photocurings, obtain finished product.Color definition has no decline in the whole water white transparencies of material used in the present invention, contrast original surface perception.The abrasion resistance test method on floor is tested according to GB/T18102 2007, the requirement of commercial level wearability is fully meet;With 84 medicining liquid dipping that sodium hypochlorite content is 620mg/L concentration 24 hours, surface was without any colour fading and albinism;PVC wearing layers can be made to be useful in a variety of ground, be adapted to industrialized mass production, it is easy to promoted in market.
Description
Technical field
The present invention relates to a kind of preparation method of abrasion-resistant ground between prefabricated bathroom, belong to bathroom facility.
Background technology
Mainly there are three kinds of modes on the ground used between current prefabricated bathroom:SMC moldings ground, acrylic ground and resin
Gel coat ground, is primarily present following defect:1st, skidproof effect is poor, in order to increase anti-skidding, it is necessary to make many slot sticks on surface
Line, mechanically increases skid resistance, and this can cause the rubbish in surface groove striped to be not easily cleaned;2nd, wear no resistance, according to
GB/T18102-2007 is to the abrasion resistance test method on floor, and the ground of market does not reach 1000 turns generally, not as good as especially reinforcing
The 20% of floor wearability;3rd, corrosion-resistant, because surface does not have protective layer, the leaching for the cleaning agent that is corrosive in 84 thimerosals etc.
Easily turn white under bubble colour fading.The problem of in order to improve such, many producers consider that covering integrally formed PVC stones using high warm moulds
Floor, directly forms protective layer on PVC stone-plastic plates surface, but the such stone plastic floor technological requirement of production is high, need specialty
Equipment, directly enhance the difficulty of production cost and popularization and application.
The content of the invention
In view of the above-mentioned problems of the prior art, ensureing the original texture in ground it is an object of the invention to provide a kind of
Meanwhile, it is capable to be lifted, ground is anti-skidding, wear resistant corrosion resistant effect, and prefabricated that is easy to spread, being applied to multiple types of floors
The preparation method of abrasion-resistant ground between bathroom.
To achieve the above object, the technical solution adopted by the present invention is:The making of abrasion-resistant ground between a kind of prefabricated bathroom
Method, comprises the following steps:
Step one:By integral vacuum toilet land clearing it is clean, dry, have wax wants paraffin removal;
Step 2:One layer of UV ultraviolet photo-curing shadowless glue is uniformly applied on the ground, and thickness is 0.03-0.07mm;
Step 3:PVC abrasion-proof gauge facial masks are covered in UV ultraviolet photo-curing shadowless glues, extruding to middle bubble-free is
Only, it is allowed to fit smooth;
Step 4:With ultraviolet photo-curing light irradiation ground 10-15s, make UV ultraviolet photo-curing shadowless glue photocurings, obtain
To finished product.
As the preferred technical scheme of the present invention, the UV ultraviolet photo-curings shadowless glue of the step 2 coating is thick
Spend for 0.05mm.Through actual use test, can both ensure that final laminating was firm using such thickness, can save again material,
Reduce overall weight.
It is preferred that, the ultraviolet photo-curing lamp power is 2KW.Such power is used to make UV with most fast speed
Ultraviolet photo-curing shadowless glue solidifies, and PVC abrasion-proof gauges facial mask will not be made to occur aging phenomenon because of irradiation.
It is preferred that, in order to reach best protecting effect, the PVC wearing faces film thickness is 0.2-0.3mm.
Color definition has no decline in the whole water white transparencies of material used in the present invention, contrast original surface perception.Tool
There are excellent wear-resisting antiskid, corrosion resistant performance, according to abrasion resistance test methods of the GB/T18102-2007 to floor, reach 1
Thickness reduces 0.042mm at ten thousand turns, and thickness reduces 0.074mm altogether when reaching 20,000 turns, and fullying meet commercial level wearability will
Ask;With 84 medicining liquid dipping that sodium hypochlorite content is 620mg/L concentration 24 hours, surface was without any colour fading and albinism;
Because outer surface uses skidproof effect under frosted material, dampness obvious;Resistant and antibacterial is easy to clean simultaneously;
Also had no toxic side effect in the equal Environmental Safety of raw material used in the present invention, production process, do not have waste discharge, no
Can be to human body and environmental pollution;
The equipment used and technique of the present invention is simple, and PVC wearing layer convenient material drawings, glue uses UV ultraviolet photo-curings
Shadowless glue, as long as solidification minimum 10 second time, production efficiency is high, can make PVC wearing layers be useful in a variety of ground, fit
Close industrialized mass production, it is easy to promote in market.
Embodiment
The present invention is described in further detail with reference to embodiment.
Embodiment 1
In the present embodiment, PVC abrasion-proof gauges facial mask selects the PVC transparent wear-resistant membrane of LG brands, and thickness is 0.2mm, surface
Frosted;The UV ultraviolet photo-curing shadowless glues produced using Dongguan City Xuanyuan chemical materials Co., Ltd, the prefabricated that need to strengthen
The ground top layer of integral vacuum toilet is colour PVC coating layers.
By top layer for colour PVC overlay films integral vacuum toilet land clearing totally, dry, one layer of UV ultraviolet of even application
PVC transparent wear-resistant membrane is put down and overlayed in the UV ultraviolet photo-curing shadowless glues sprayed in 0.03mm by photocuring shadowless glue, thickness
Face, rolling or dense extrusion bubble-free, irradiate ground 15 seconds with the ultraviolet lamp of 2KW power, obtain finished product.
Finished product test project:
Anti-wear performance:According to abrasion resistance test methods of the GB/T18102-2007 to floor, thickness is reduced when reaching 10,000 turns
0.042mm, thickness reduces 0.074mm altogether when reaching 20,000 turns, fullys meet the requirement of commercial level wearability;
Corrosion Protection:With 84 medicining liquid dipping that sodium hypochlorite content is 620mg/L concentration 24 hours, surface was without any
Fade and albinism;
Non-skid property:Because outer surface uses skidproof effect under frosted material, dampness obvious;
Tack coat is peeled off, PVC transparent wearing layer, which is drawn, badly has no glue delamination;Contrast color in original surface, perception clear
Clear degree has no decline.
Embodiment 2
In the present embodiment, PVC abrasion-proof gauges facial mask selects the PVC transparent wear-resistant membrane of LG brands, and thickness is in 0.3mm, surface
Frosted.The universal UV ultraviolet photo-curings shadowless glue produced using Dongguan City Xuanyuan chemical materials Co., Ltd, need to strengthen
The ground top layer of prefabricated integral vacuum toilet is artificial stone resin surface layer.
By artificial stone resin facing surface paraffin removal, dry, one layer of UV ultraviolet photo-curing shadowless glue of even application, thickness exists
0.07mm, overlays on PVC transparent wear-resistant membrane is flat above glue spray, rolls or dense extrusion bubble-free, ultraviolet with 2KW power
Line light irradiation ground 10 seconds, obtains finished product.
Finished product test project:
According to abrasion resistance test methods of the GB/T18102-2007 to floor, thickness reduces 0.040mm when reaching 10,000 turns,
Thickness reduces 0.075mm altogether when reaching 20,000 turns, fullys meet the requirement of commercial level wearability;
With 84 medicining liquid dipping that sodium hypochlorite content is 620mg/L concentration 24 hours, surface was without any colour fading and albefaction
Phenomenon;
Because outer surface uses skidproof effect under frosted material, dampness obvious;
Tack coat is peeled off, PVC wearing layers, which are drawn, badly has no glue delamination;Contrast color definition in original surface, perception
Have no decline.
The application of the present invention is not limited to above-mentioned citing, for those of ordinary skills, can be according to above stating
It is bright to be improved or convert in rational scope, and should all belong to this hair with all these modifications and variations on basis of the invention
Bright scope of the claims.
Claims (4)
1. the preparation method of abrasion-resistant ground between a kind of prefabricated bathroom, it is characterised in that comprise the following steps:
Step one:By integral vacuum toilet land clearing it is clean, dry, have wax wants paraffin removal;
Step 2:One layer of UV ultraviolet photo-curing shadowless glue is uniformly applied on the ground, and thickness is 0.03-0.07mm;
Step 3:PVC abrasion-proof gauge facial masks are covered in UV ultraviolet photo-curing shadowless glues, extruded untill middle bubble-free,
It is allowed to fit smooth;
Step 4:With ultraviolet photo-curing light irradiation ground 10-15s, make UV ultraviolet photo-curing shadowless glue photocurings, obtain into
Product.
2. the preparation method of abrasion-resistant ground between prefabricated bathroom according to claim 1, it is characterised in that the step 2
The UV ultraviolet photo-curing shadowless glues thickness of coating is 0.05mm.
3. the preparation method of abrasion-resistant ground between prefabricated bathroom according to claim 1, it is characterised in that the ultraviolet
Light-solidified lamp power is 2KW.
4. the preparation method of abrasion-resistant ground between prefabricated bathroom according to claim 1, it is characterised in that the PVC is resistance to
Mill surface film thicknesses are 0.2-0.3mm.