CN107266647A - Hard-foam polyurethane expanded material for motor-car sealing strip and preparation method thereof - Google Patents
Hard-foam polyurethane expanded material for motor-car sealing strip and preparation method thereof Download PDFInfo
- Publication number
- CN107266647A CN107266647A CN201710520050.6A CN201710520050A CN107266647A CN 107266647 A CN107266647 A CN 107266647A CN 201710520050 A CN201710520050 A CN 201710520050A CN 107266647 A CN107266647 A CN 107266647A
- Authority
- CN
- China
- Prior art keywords
- sealing strip
- motor
- hard
- parts
- expanded material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of hard-foam polyurethane expanded material for motor-car sealing strip, it is made up of following quality proportioning component, isocyanates:Combination material=1:1.2, the composition of the combination material is based on following mass fraction, and specific mass fraction is as follows:35 45 parts of polyethers HT 4110K positions;Polyethers HS 3700 is 25 32 parts;Polyethers 3320 is 30 35 parts;Silicone oil is 3.5 3.8 parts;AFM180 is 1.5 2.5 parts;Water is 3.2 4.2 parts;Fire retardant is 35 45 parts.The present invention is because recipe ingredient collocation is reasonable and preparation method is proper so that the expanded material fire resistance of preparation is high, and chance fire is nonflammable, improves anti-flammability, and can reduce the discharge of pernicious gas, so as to ensure the security of vehicle.
Description
Technical field
The present invention relates to a kind of composite and preparation method thereof, specifically a kind of hard bubbling for motor-car sealing strip
Polyurethane foam material and preparation method thereof.
Background technology
Motor-car sealing strip is mainly used in motor-car vehicle window, it may ensure that close between glass pane and the structural member of vehicle
Envelope so that can prevent the ambient influnence such as rainwater, dust and/or wind from entering vehicle interior.
Sealing strip material in the market is generally the materials such as polyvinyl chloride (PVC), vulcanization rubber, TPV:However, polychlorostyrene
Ethene (PVC) manufacturing procedure is complicated, and lower temperature resistance and resistance to ag(e)ing are poor, and feel is stiff under low temperature, influence sealing strip sealing effect
Really, PVC density is generally 1.15-1.20g/cm3, density is higher, in-convenience in use, especially in terms of smell and environmental protection by compared with
Big limitation, at relatively high temperatures, such as 50 DEG C or so will decomposite hydrogen chloride gas at leisure to polyvinyl chloride (PVC), processed
Foul smelling in journey, this gas is harmful, easily pollutes environment.Traditional vulcanization rubber processing complex procedures, basic working procedure
Including plasticating, kneading, roll or extrude, be molded and vulcanize, labor intensity is big, and plant equipment is numerous and diverse, due to addition carbon black,
The material such as the compounding ingredients such as accelerator, antiaging agent and framework material, vulcanization rubber belongs to the industry of heavy contamination, and smell is heavier,
Including the gas of the generations such as the not altogether clear refining glue of toxicity, vulcanization, plasticizing, there is different degrees of wound to human body
Evil.TPV thermoplastic dynamic perdurens, because TPV passes through sulfidation, so TPV has certain smell, it is impossible to meet current
The requirement of low smell.Except the requirement of environmental-protecting performance, special sealing strip fireproof security is also vital, is usually occurred
The situation of fire is easily triggered to occur when meeting with an accidet, it is therefore desirable to develop a kind of composite, the row of pernicious gas can be reduced
Put, can also improve fire resistance.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of high, environmentally friendly the hard bubbling for motor-car sealing strip of fire resistance
Polyurethane foam material and preparation method thereof.
In order to solve the above-mentioned technical problem, the technical scheme that the present invention is provided is as follows:It is a kind of to be used for the hard of motor-car sealing strip
Polyurethane foam material and preparation method thereof is steeped, is made up of following quality proportioning component, isocyanates:Combination material=1:1.2, institute
The composition of combination material is stated based on following mass fraction, specific mass fraction is as follows:
Further, the silicone oil is silicone oil AK8802.
Further, the fire retardant is fire retardant TCPP.
Further, the isocyanates is TDI Tao Shi.
Present invention also offers a kind of preparation method of the hard-foam polyurethane expanded material for motor-car sealing strip, including with
Lower step:
A) combination material is prepared first:By polyethers HT-4110K, polyethers HS-3700, polyethers 3320, silicone oil, AFM180, water and
Fire retardant adds in reactor and carries out hybrid reaction, and mixing speed 100-120r/min, mixing time 8-9h can must combine material;
B) and then again by isocyanates with combining material by 1:1.2 mass ratio is well mixed, you can the foaming material is made
Material.
Beneficial effects of the present invention are as follows:
After above-mentioned material and method, because recipe ingredient collocation is reasonable and preparation method is proper so that preparation
Expanded material fire resistance is high, and chance fire is nonflammable, improves anti-flammability, and can reduce the discharge of pernicious gas, so as to protect
The security of vehicle is hindered.
Embodiment
With reference to embodiment, to the present invention for the hard-foam polyurethane expanded material of motor-car sealing strip and its
Preparation method is described in further detail.
Embodiment one:
The hard-foam polyurethane expanded material of motor-car sealing strip, including following preparation process:
Combination material is prepared first:By polyethers HT-4110K, polyethers HS-3700, polyethers 3320, silicone oil, AFM180, water and resistance
Combustion agent, which is added in reactor, carries out hybrid reaction, and mixing speed 100r/min, mixing time 9h can must combine material, then again will
Isocyanates is with combining material by 1:1.2 mass ratio is well mixed, you can the expanded material is made.
Embodiment two:
The hard-foam polyurethane expanded material of motor-car sealing strip, including following preparation process:
Combination material is prepared first:By 40 parts of polyethers 4450,55 parts of polyester 1180,3 parts of plasticizer JKP508,3 parts
Silicone oil 8803 and 3.3 parts water add reactor in carry out hybrid reaction, mixing speed 100,0r/min, mixing time 9h is
Material can must be combined, then again by isocyanates with combining material by 1:1.5 mass ratio is well mixed, you can the foaming material is made
Material.
Embodiment three:
The hard-foam polyurethane expanded material of motor-car sealing strip, including following preparation process:
Combination material is prepared first:By 45 parts of polyethers 4450,62 parts of polyester 1180,3.2 parts of plasticizer JKP508,
3.2 parts of silicone oil 8803 and 3.5 parts of water, which are added in reactor, carries out hybrid reaction, mixing speed 100r/min, mixing time
9h can must combine material, then again by isocyanates with combining material by 1:1.5 mass ratio is well mixed, you can the hair is made
Foam material.
It is used for the fire resistance test result of the hard-foam polyurethane expanded material of motor-car sealing strip for the present invention below:
Test stone requirement:The burning velocity of fire proofing should be not more than 100mm/min, distinguish if there are following situations
Result of the test is identified on request, and assay is divided into A, B, C, D, E5 grades:
A:(0mm/min):Sample is exposed to 15S in flame, and extinguishing burning things which may cause a fire disaster sample is still unburned, or sample can burn, but
Flame reaches extinguishing before the first measurement graticule, and no burning extent can be counted.
B:When tester, flame self-extinguish in 60s, and burning extent is not more than 50mm, then it is assumed that meet
Standard requirement.
C:Burning velocity measured value (mm/min)
When tester, flame extinguishes between two measurement graticules, and when being unsatisfactory for the 2nd article of situation, then by mark
Standard calculates burning velocity.
D:Burning velocity measured value (mm/min)
When tester, flame combustion reaches the second graticule, or since timing, sample long-time smoulder,
Then can in tester termination test during 20min, and record burning time and burning extent and by criterion calculation burning velocity.
E:Sample has burnt in flame ignition 15s and has reached the first graticule, then it is assumed that sample can not meet burning speed
The requirement of degree.
Assay:A-B (0mm/min), is sent out using the hard-foam polyurethane manufactured in the present embodiment for motor-car sealing strip
Foam material meets fire resistance requirement.
Claims (5)
1. a kind of hard-foam polyurethane expanded material for motor-car sealing strip, it is characterised in that:By following quality proportioning component structure
Into isocyanates:Combination material=1:1.2, the composition of the combination material is based on following mass fraction, and specific mass fraction is as follows:
2. according to the hard-foam polyurethane expanded material for motor-car sealing strip described in claim 1, it is characterised in that:The silicon
Oil is silicone oil AK8802.
3. according to the hard-foam polyurethane expanded material for motor-car sealing strip described in claim 1, it is characterised in that:The resistance
Combustion agent is fire retardant TCPP.
4. according to the hard-foam polyurethane expanded material for motor-car sealing strip described in claim 1, it is characterised in that:It is described different
Cyanate is TDI Tao Shi.
5. a kind of hard-foam polyurethane expanded material as claimed in claim 1 for motor-car sealing strip, it is characterised in that including
Following preparation process:
A) combination material is prepared first:By polyethers HT-4110K, polyethers HS-3700, polyethers 3320, silicone oil, AFM180, water and fire-retardant
Agent adds in reactor and carries out hybrid reaction, and mixing speed 100-120r/min, mixing time 8-9h can must combine material;
B) and then again by isocyanates with combining material by 1:1.2 mass ratio is well mixed, you can the expanded material is made.