CN107263893A - One kind embossing silica gel cloth forming method - Google Patents
One kind embossing silica gel cloth forming method Download PDFInfo
- Publication number
- CN107263893A CN107263893A CN201710647774.7A CN201710647774A CN107263893A CN 107263893 A CN107263893 A CN 107263893A CN 201710647774 A CN201710647774 A CN 201710647774A CN 107263893 A CN107263893 A CN 107263893A
- Authority
- CN
- China
- Prior art keywords
- silica gel
- embossing
- cloth
- material strip
- forming method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Silica gel cloth forming method is embossed the invention discloses one kind, is comprised the following steps：S1, using embossed paper or with textured composite be used as embossing material strip；S2, by silicone rolling it is described embossing material strip on, while by cloth pasting on silica gel face；S3, by made from step S2 product feeding drying tunnel toast at 100~160 DEG C vulcanize 4~20 minutes, make silica gel curing molding；S4, will in step S3 baking vulcanization after product take out, peel off embossing material strip, obtain textured embossing silica gel cloth.The textured composite of band is included with textured synthetic paper, with the coiled strip of textured high-temperature resistant membrane material or surface with embossing.The step S2 also includes adding 2~30% silica gel foaming agent into the silica gel before calendering operation, is prepared into foamed silica gel cloth.Compared with prior art, the inventive method has the advantages that reduction production cost, easy to operate, embossing effects are good.
Description
Technical field
The present invention relates to silica gel cloth processing technique field, and in particular to one kind embossing silica gel cloth forming method.
Background technology
As people are to beautiful pursuit more and more higher, offset printing, watermark, ink printing etc. planographic art is all on cloth
It has been difficult to the requirement for meeting modern people.Embossing silica gel cloth because have stronger third dimension be becoming increasingly popular, especially by
The welcome of young man.
The existing preparation method with the silica gel cloth being embossed typically is molded embossing, this pressure with knurling rolls on silica gel
The forming method of flower silica gel cloth has the disadvantage that：If the 1, embossed channels are tiny, knurling rolls silica gel in embossing can be sticked in embossing
On roller, embossing effects difference and fraction defective height；2nd, the surface after hot briquetting of the silica gel material after embossing is shinny, it is impossible to realize surface
Atomized surface effect.
The content of the invention
The technical problems to be solved by the invention are：There is provided a kind of embossing effects good embossing silica gel cloth forming method.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention is：One kind embossing silica gel cloth forming method, bag
Include following steps：
S1, using embossed paper or with textured composite be used as embossing material strip；
S2, by silicone rolling it is described embossing material strip on, while by cloth pasting on silica gel face；
S3, by made from step S2 product feeding drying tunnel toast at 100~160 DEG C vulcanize 4~20 minutes, make silica gel solid
Chemical conversion type；
S4, will in step S3 baking vulcanization after product take out, peel off embossing material strip, obtain textured embossing silica gel
Cloth.
The beneficial effects of the present invention are：1st, using the ready-made pattern of commercially available embossed paper, there is which type of embossed paper just
The silica gel cloth of what lines can be made, can only be realized compared with the prior art by making the knurling rolls with different lines
For different lines, cost is substantially reduced, and embossing material strip may be reused as knurling rolls；2nd, the lines of silica gel cloth
Demand can be met by customizing different embossing paper patterns, easy to make, be embossed attractive in appearance, stably；3rd, silica gel cloth uses scope
Extensively, the further processing for cutting sewing, alternative part dermatine can be carried out as handbag cladding, sofa cladding etc.；
4th, using silica gel high-low temperature resistant and the characteristic of waterproof, the product being made using silica gel cloth also has corresponding characteristic；5th, silica gel cloth
In silica gel can whole recyclings, therefore the product being made of silica gel cloth is also more environmentally-friendly；6th, turned by embossing band
Print, it is to avoid using being difficult to transfer tiny decorative pattern with textured knurling rolls, embossing effects are good and reduce embossing fraction defective；
7th, vulcanization effect is good, it is to avoid shinny phenomenon, the obtained embossing silica gel of the present invention program occurs in the embossing silica gel cloth after shaping
Cloth can have good atomized surface effect.
Embodiment
To describe technology contents, the objects and the effects of the present invention in detail, it is explained below in conjunction with embodiment.
The design of most critical of the present invention is：It is embossed with embossing material strip instead of knurling rolls, reduces production cost, is carried
The production yield of high embossing silica gel cloth improves embossing quality simultaneously；Vulcanization effect is good, it is ensured that embossing silica gel cloth has mist
Face effect.
The present invention provides a kind of embossing silica gel cloth forming method, comprises the following steps：
S1, using embossed paper or with textured composite be used as embossing material strip；
S2, by silicone rolling it is described embossing material strip on, while by cloth pasting on silica gel face；
S3, by made from step S2 product feeding drying tunnel toast at 100~160 DEG C vulcanize 4~20 minutes, make silica gel solid
Chemical conversion type；
S4, will in step S3 baking vulcanization after product take out, peel off embossing material strip, obtain textured embossing silica gel
Cloth.
It was found from foregoing description, the beneficial effects of the present invention are：1st, using the ready-made pattern of commercially available embossed paper, there is assorted
The embossed paper of sample can just make the silica gel cloth of what lines, compared with the prior art can only be by making with different lines
Knurling rolls are come for the different lines realized, cost is substantially reduced, and embossing material strip may be reused as knurling rolls；
2nd, the lines demand of silica gel cloth can be met by customizing different embossing paper patterns, easy to make, be embossed attractive in appearance, stably；3、
Silica gel cloth is wide using scope, and the further processing for cutting sewing can be carried out as handbag cladding, sofa cladding etc., alternative
Part dermatine；4th, using silica gel high-low temperature resistant and the characteristic of waterproof, the product being made using silica gel cloth also has corresponding
Characteristic；5th, the silica gel in silica gel cloth can whole recyclings, therefore the product being made of silica gel cloth is also more environmentally-friendly；6th, lead to
Cross the transfer of embossing band, it is to avoid using being difficult to transfer tiny decorative pattern with textured knurling rolls, embossing effects are good and reduce
Embossing fraction defective；7th, vulcanization effect is good, it is to avoid shinny phenomenon, the present invention program system occurs in the embossing silica gel cloth after shaping
The embossing silica gel cloth obtained can have good atomized surface effect.
Further, the textured composite of the band is included with textured synthetic paper, with textured high temperature resistant
The coiled strip of thin-film material or surface with embossing.
Further, the cloth is cotton, adhesive-bonded fabric or staple fibre cloth.
Further, the step S2 also includes adding 2~30% silica gel foaming agent into the silica gel before calendering operation.
It was found from foregoing description, the beneficial effects of the present invention are：Silica gel foaming agent is added in silica gel, foaming is prepared into
Silica gel cloth, lifts the thickness of silica gel cloth, while reducing the weight of silica gel cloth.
Further, the step of step S2 also includes being pre-processed for different types of cloth, the pre- place
Reason step is included in design on fabric surface spraying or is coated with targetedly surface conditioning agent, and the surface conditioning agent includes adhesive.
Preferably, coupling agent is added with described adhesive.
It was found from foregoing description, the beneficial effects of the present invention are：Targetedly surface is sprayed or is coated with design on fabric surface
Inorganic agent, improves and strengthens the Bonding strength between silica gel and cloth.
Further, the step S4 also include peel off embossing material after again to embossing silica gel cloth silica gel face on spray feel
Drying forms the embossing silica gel cloth of matcoveredn after oil or protection oil.
It was found from foregoing description, the beneficial effects of the present invention are：The spraying feel oil on the silica gel face of embossing silica gel cloth
Or protection oil, improve surface slip sense and the rub proofness of embossing silica gel cloth.
Further, the preparation method of the embossing material strip in the step S1 is as follows：Printed on plane material strip for turning
The pattern of print, then embossing material strip, the plane material strip is made in extrusion lines on the plane material strip of printing good pattern with embossing machine
The coiled strip that can be embossed for paper, synthetic paper, high-temperature resistant membrane material or surface.
Further, the preparation method of the embossing material strip in the step S1 is as follows：Printed on plane material strip for turning
The multicolour pattern of print, then extrude lines on the plane material strip of the pattern printed with embossing machine embossing material strip is made, and in step
After rapid S3 operations are completed, oil is protected in layer of silica gel surface spraying transparent silica gel, after drying, the silica gel with multicolour pattern is made
Cloth.
It was found from foregoing description, the beneficial effects of the present invention are：Extruded by embossing machine on plane material strip to be transferred
Pattern lines, the silica gel cloth being made silica gel layer surface simultaneous with multicolour pattern and solid grain, then spray transparent silicon
Glue protection oil, may also be fabricated which the silica gel cloth of colour after drying.
Further, the silica gel in the step S2, adds functional material, the feature material in preparation process
Material includes the one or more in Heat Conduction Material, far infrared nano material and nano-silver powder.
It was found from foregoing description, the beneficial effects of the present invention are：Received by adding Heat Conduction Material, far infrared in silica gel
The functional materials such as rice material, nano-silver powder so that obtained silica gel cloth has the effects such as heat conduction, far infrared, sterilization.
Further, drying tunnel includes three regions successively in the step S3, and the baking curing temperature of first area is 100
~120 DEG C, the baking curing temperature of second area is 125~135 DEG C, and the baking curing temperature in the 3rd region is 140~160
DEG C, the baking cure time of first area is 1~5min, and the baking cure time of second area is 1~10min, the 3rd region
Baking cure time be 1~15min.
It was found from foregoing description, the beneficial effects of the present invention are：Using staged heating baking vulcanization, lifting vulcanization effect
Really, it is to avoid embossing silica gel cloth surface after hot briquetting is shinny.
Further, the thickness of the cloth can not limited according to customer requirement.
Preferably, the thickness of the cloth is 0.02mm-5mm.
It was found from foregoing description, the beneficial effects of the present invention are：The silica gel thickness of rational design calendering, it is ensured that silica gel
The thickness of layer, also ensures that the stereoeffect of embossing.
Embodiments of the invention one are：One kind embossing silica gel cloth forming method, comprises the following steps：
S1, print on plane material strip pattern for transfer, then by the pattern printed lines system is extruded with embossing machine
Into embossing material strip, the plane material strip is the coiled strip that paper, synthetic paper, high-temperature resistant membrane material or surface can be embossed, and will be pressed
Line paper is used as embossing material strip with textured composite；
S2, by the silicone rolling added with 15% silica gel foaming agent on the embossing material strip, while by cloth pasting
On silica gel face, wherein, roll embossing material strip on silica gel thickness be 0.2mm, wherein the cloth for 3mm adhesive-bonded fabric and
Before laminating G-988A adhesives are coated to design on fabric surface；
S3, product feeding drying tunnel baking made from step S2 vulcanized, make silica gel curing molding, the drying tunnel includes first
Region, second area and the 3rd region, the baking curing temperature of the first area is 120 DEG C, and the time is 1min；Second area
Baking curing temperature be 135 DEG C, the time is 1min；The baking curing temperature in the 3rd region is 160 DEG C, and the time is 2min；
S4, will in step S3 baking vulcanization after product take out, peel off embossing material strip, to embossing silica gel cloth lines silica gel
Dried after feel oil or protection oil are sprayed on face, obtain the embossing silica gel cloth of matcoveredn.
Embodiments of the invention two are：One kind embossing silica gel cloth forming method, comprises the following steps：
S1, print on plane material strip multicolour pattern for transfer, then in the pattern printed line is extruded with embossing machine
Embossing material strip is made in road, and the plane material strip is the coiled strip that paper, synthetic paper, high-temperature resistant membrane material or surface can be embossed,
Embossing material strip is used as using embossed paper or with textured composite；
S2, by the silicone rolling added with Heat Conduction Material and 30% silica gel foaming agent it is described embossing material strip on, simultaneously
By cloth pasting on silica gel face, wherein, the silica gel thickness rolled on embossing material strip is 0.5mm, wherein the cloth is
0.5mm woven dacron；
S3, product feeding drying tunnel baking made from step S2 vulcanized, make silica gel curing molding, the drying tunnel includes first
Region, second area and the 3rd region, the baking curing temperature of the first area is 100 DEG C, and the time is 2min；Second area
Baking curing temperature be 130 DEG C, the time is 3min；The baking curing temperature in the 3rd region is 140 DEG C, and the time is 15min；
S4, will in step S3 baking vulcanization after product take out, peel off embossing material strip, in layer of silica gel surface spraying transparent silicon
Glue protection oil, after drying again, sprays drying after feel oil or protection oil to being embossed on the silica gel face of silica gel cloth, has obtained protection
The colored embossing silica gel cloth of layer.
In summary, the present invention provides a kind of embossing silica gel cloth forming method, and this method has 1, utilizes commercially available embossed paper
Ready-made pattern, there is which type of embossed paper just to make the silica gel cloth of what lines, can only pass through compared with the prior art
For the different lines for making the knurling rolls with different lines to realize, cost is substantially reduced, and embossing material strip and embossing
Roller equally may be reused；2nd, the lines demand of silica gel cloth can be met by customizing different embossing paper patterns, making side
Just, emboss attractive in appearance, stably；3rd, silica gel cloth is wide using scope, can further be cut out as handbag cladding, sofa cladding etc.
Cut the processing of sewing, alternative part dermatine；4th, using silica gel high-low temperature resistant and the characteristic of waterproof, it is made using silica gel cloth
Product also have corresponding characteristic；5th, the silica gel in silica gel cloth can whole recyclings, therefore be made of silica gel cloth
Product is also more environmentally-friendly；6th, transferred by embossing band, it is to avoid using being difficult to transfer tiny flower with textured knurling rolls
Line, embossing effects are good and reduce embossing fraction defective；7th, vulcanization effect is good, it is to avoid the embossing silica gel cloth after shaping occurs shinny
Phenomenon, the obtained embossing silica gel cloth of the present invention program can have good atomized surface effect.8th, silica gel hair is added in silica gel
Infusion, lifts the thickness of silica gel cloth, while reducing the weight of silica gel cloth.Spray or be coated with targetedly surface in design on fabric surface
Agent is managed, improves and strengthen the Bonding strength between silica gel and cloth.9th, spraying feel oil or guarantor on the silica gel face of embossing silica gel cloth
Shield oil, improves surface slip sense and the rub proofness of embossing silica gel cloth.10th, using staged heating baking vulcanization, lifting vulcanization
Effect, it is to avoid embossing silica gel cloth surface after hot briquetting is shinny.11st, the silica gel thickness of rational design calendering, it is ensured that silica gel
The thickness of layer, also ensures that the stereoeffect of embossing.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
The equivalents that bright description is made, or the technical field of correlation is directly or indirectly used in, similarly it is included in this hair
In bright scope of patent protection.
Claims (10)
1. one kind embossing silica gel cloth forming method, it is characterised in that：Comprise the following steps：
S1, using embossed paper or with textured composite be used as embossing material strip；
S2, by silicone rolling it is described embossing material strip on, while by cloth pasting on silica gel face；
S3, by made from step S2 product feeding drying tunnel toast at 100~160 DEG C vulcanize 4~20 minutes, be solidified into silica gel
Type；
S4, will in step S3 baking vulcanization after product take out, peel off embossing material strip, obtain textured embossing silica gel cloth.
2. embossing silica gel cloth forming method according to claim 1, it is characterised in that：The textured composite of band
Including with textured synthetic paper, with the coiled strip of textured high-temperature resistant membrane material or surface with embossing.
3. embossing silica gel cloth forming method according to claim 1, it is characterised in that：The step S2 is also included to calendering
The silica gel foaming agent of addition 2~30% in preoperative silica gel.
4. embossing silica gel cloth forming method according to claim 1, it is characterised in that：The step S2 is also included for not
The step of congener cloth is pre-processed, the pre-treatment step is included in design on fabric surface spraying or is coated with targetedly table
Face inorganic agent, the surface conditioning agent includes adhesive.
5. embossing silica gel cloth forming method according to claim 1, it is characterised in that：The step S4 also includes peeling off pressure
Form the embossing silica gel of matcoveredn after line material to drying after spraying feel oil on the silica gel face of embossing silica gel cloth or protection oil again
Cloth.
6. embossing silica gel cloth forming method according to claim 1, it is characterised in that：Embossing material strip in the step S1
Preparation method it is as follows：The pattern for transfer is printed on plane material strip, then the plane material of good pattern is being printed with embossing machine
Take extrusion lines and embossing material strip is made, the plane material strip is that paper, synthetic paper, high-temperature resistant membrane material or surface can be pressed
The coiled strip of line.
7. embossing silica gel cloth forming method according to claim 6, it is characterised in that：Embossing material strip in the step S1
Preparation method it is as follows：The multicolour pattern for transfer is printed on plane material strip, then with embossing machine in the pattern printed
Lines is extruded on plane material strip embossing material strip is made, and after step S3 operations are completed, in layer of silica gel surface spraying transparent silicon
Glue protection oil, after drying, is made the silica gel cloth with multicolour pattern.
8. embossing silica gel cloth forming method according to claim 1, it is characterised in that：Silica gel in the step S2,
Functional material is added in preparation process, the functional material includes Heat Conduction Material, far infrared nano material and nanometer
One or more in silver powder.
9. embossing silica gel cloth forming method according to claim 1, it is characterised in that：Drying tunnel described in the step S3 according to
Secondary including three regions, the baking curing temperature of first area is 100~120 DEG C, and the baking curing temperature of second area is 125
~135 DEG C, the baking curing temperature in the 3rd region is 140~160 DEG C, and the baking cure time of first area is 1~5min, the
The baking cure time in two regions is 1~10min, and the baking cure time in the 3rd region is 1~15min.
10. embossing silica gel cloth forming method according to claim 1, it is characterised in that：In the step S2, the cloth
For cotton, adhesive-bonded fabric or staple fibre cloth.