CN107235702A - 一种新型建筑节能保温材料的制备方法 - Google Patents
一种新型建筑节能保温材料的制备方法 Download PDFInfo
- Publication number
- CN107235702A CN107235702A CN201710544174.8A CN201710544174A CN107235702A CN 107235702 A CN107235702 A CN 107235702A CN 201710544174 A CN201710544174 A CN 201710544174A CN 107235702 A CN107235702 A CN 107235702A
- Authority
- CN
- China
- Prior art keywords
- heat
- insulating material
- preparation
- saving
- building energy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种新型建筑节能保温材料的制备方法，包括以下制备步骤：a、将氯化镁、秸秆、粉煤灰和改性添加剂置于球磨机中进行球磨，混合均匀后制得混合料；b、将混合料兑水制成混合浆料，向混合浆料中加入聚苯乙烯树脂、玻璃棉、聚三氟氯乙烯树脂和硅藻泥高速搅拌，搅拌均匀后导入到模具中进行高温烧制，得到保温基材；c、将保温基材进行高温加压成型，得到保温材料粗品；d、将保温材料粗品自然冷却至常温后，进行打磨、修边，即可得到成品。本发明制备得到的建筑节能保温材料具有扛着强度高、导热系数低、氧指数高的特点。
Description
技术领域
本发明属于建筑材料的制备技术领域，具体涉及一种新型建筑节能保温材料的制备方法。
背景技术
随着全球性能源、资源短缺和环境污染等问题日趋深刻化，省能省资源已经成为全球经济发展的必由之路。我国政府也在各种官方场合公开多次表示，要把节能减排，可持续发展作为中国经济发展的基本国策。据报道，房屋建筑工程能源消耗约占我国能源消耗总量的25～40%。因此，做好房屋建筑的节能减排对于贯彻落实中央提出的节能减排、可持续发展的经济发展基本国策有着举足轻重的意义。
建筑节能材料就是指维持建筑物日常使用过程中能耗低的建材，通过改变材料自身的特性来达到建筑节能的目的。节能材料属于保温绝热材料；绝热材料是指用于建筑围护或者热工设备、阻抗热流传递的材料或者材料复合体，既包括保温材料，也包括保冷材料。
有机节能保温材包括稻草、稻壳、甘蔗纤维、软木木棉、木屑、刨花、木纤维及其制品。此类材料容重小，来源广，多数价格低廉，但吸湿性大，受潮后易腐烂，高温下易分解或燃烧。
用于建筑墙体的节能保温材料不仅需要具有符合要求的机械强度，同时还需要具备较高的保温性能和较好的阻燃性能。只有在具备了上述的条件下，才能保证建筑墙体用节能保温材料的长期使用。
发明内容
本发明的目的是提供一种新型建筑节能保温材料的制备方法，本发明制备得到的建筑节能保温材料具有扛着强度高、导热系数低、氧指数高的特点。
本发明提供了如下的技术方案：
一种新型建筑节能保温材料的制备方法，包括以下制备步骤：
a、将氯化镁、秸秆、粉煤灰和改性添加剂置于球磨机中进行球磨，球磨1-2h，混合均匀后制得混合料；
b、将混合料兑水制成混合浆料，向混合浆料中加入聚苯乙烯树脂、发泡剂、聚三氟氯乙烯树脂和硅藻泥高速搅拌，搅拌速度为1000-1500r/min，搅拌20-30min，搅拌均匀后导入到模具中进行高温烧制，温度为600-800℃，烧制50-60min，得到保温基材；
c、将保温基材进行高温加压成型，温度为80-100℃，加压压力为40-50MPa，加压10-15min后即可得到保温材料粗品；
d、将保温材料粗品自然冷却至常温后，进行打磨、修边，即可得到成品。
优选的，所述新型建筑节能保温材料包括以下重量份的原料：氯化镁22-25份、秸秆30-45份、粉煤灰23-26份、改性添加剂11-13份、聚苯乙烯树脂12-15份、发泡剂13-17份、聚三氟氯乙烯树脂14-18份、硅藻泥20-24份和水20-22份。
优选的，所述步骤a的改性添加剂的成分包括甲基纤维素醚、无机盐类化合物、硬脂酸钙和乳胶粉。
优选的，所述改性添加剂的制备方法为：将甲基纤维素醚加入到硬脂酸钙和无机盐类化合物的混合物中，球磨50-70min，再加入乳胶粉，球磨1-2h得到。
优选的，所述无机盐类化合物为硫酸镁、硫酸钠和碳酸铵中的任一种或多种的组合。
优选的，所述步骤b的发泡剂成分包括：双氧水、氯化钙和液体石蜡。
优选的，所述发泡剂的制备方法为：将液体石蜡加入硅和氯化钙混合，球磨2-3h，制得混合物料，将混合物料加入到双氧水中，快速搅拌均匀后得到。
优选的，所述硅占发泡剂的2-4%。
本发明的有益效果是：
本发明制备得到的建筑节能保温材料具有扛着强度高、导热系数低、氧指数高的特点。
本发明的配方中选用了秸秆、粉煤灰等废料，既降低了生产成本，同时又缓解了秸秆、粉煤灰堆存处理带来的环境污染问题，秸秆、粉煤灰等废料还可改善保温材料的保温性能，具有抗风化，耐腐蚀，抗冻融等特点。
本发明选用的改性添加剂不仅具有稳泡的作用，还具有促进制备效率的功效。
本发明选用的发泡剂双氧水，发泡过程中产生水和氧气，不污染空气和环境，加入的氯化钙，液体石蜡具有稳泡的作用，添加不同量的硅粉可以调节保温材料的孔径分布，从而有利于提高保温材料的产品质量。
具体实施方式
实施例1
一种新型建筑节能保温材料的制备方法，包括以下制备步骤：
a、将氯化镁、秸秆、粉煤灰和改性添加剂置于球磨机中进行球磨，球磨2h，混合均匀后制得混合料；
b、将混合料兑水制成混合浆料，向混合浆料中加入聚苯乙烯树脂、发泡剂、聚三氟氯乙烯树脂和硅藻泥高速搅拌，搅拌速度为1500r/min，搅拌30min，搅拌均匀后导入到模具中进行高温烧制，温度为600℃，烧制60min，得到保温基材；
c、将保温基材进行高温加压成型，温度为100℃，加压压力为40MPa，加压15min后即可得到保温材料粗品；
d、将保温材料粗品自然冷却至常温后，进行打磨、修边，即可得到成品。
新型建筑节能保温材料包括以下重量份的原料：氯化镁22份、秸秆45份、粉煤灰23份、改性添加剂13份、聚苯乙烯树脂12份、发泡剂17份、聚三氟氯乙烯树脂14份、硅藻泥24份和水22份。
步骤a的改性添加剂的成分包括甲基纤维素醚、无机盐类化合物、硬脂酸钙和乳胶粉。
改性添加剂的制备方法为：将甲基纤维素醚加入到硬脂酸钙和无机盐类化合物的混合物中，球磨70min，再加入乳胶粉，球磨1h得到。
无机盐类化合物为硫酸镁、硫酸钠和碳酸铵的组合。
步骤b的发泡剂成分包括：双氧水、氯化钙和液体石蜡。
发泡剂的制备方法为：将液体石蜡加入硅和氯化钙混合，球磨2h，制得混合物料，将混合物料加入到双氧水中，快速搅拌均匀后得到。
硅占发泡剂的4%。
实施例2
一种新型建筑节能保温材料的制备方法，包括以下制备步骤：
a、将氯化镁、秸秆、粉煤灰和改性添加剂置于球磨机中进行球磨，球磨1h，混合均匀后制得混合料；
b、将混合料兑水制成混合浆料，向混合浆料中加入聚苯乙烯树脂、发泡剂、聚三氟氯乙烯树脂和硅藻泥高速搅拌，搅拌速度为1000r/min，搅拌20min，搅拌均匀后导入到模具中进行高温烧制，温度为600℃，烧制50min，得到保温基材；
c、将保温基材进行高温加压成型，温度为80℃，加压压力为40MPa，加压15min后即可得到保温材料粗品；
d、将保温材料粗品自然冷却至常温后，进行打磨、修边，即可得到成品。
新型建筑节能保温材料包括以下重量份的原料：氯化镁22份、秸秆30份、粉煤灰23份、改性添加剂11份、聚苯乙烯树脂12份、发泡剂13份、聚三氟氯乙烯树脂14份、硅藻泥20份和水20份。
步骤a的改性添加剂的成分包括甲基纤维素醚、无机盐类化合物、硬脂酸钙和乳胶粉。
改性添加剂的制备方法为：将甲基纤维素醚加入到硬脂酸钙和无机盐类化合物的混合物中，球磨50min，再加入乳胶粉，球磨1h得到。
无机盐类化合物为硫酸镁、硫酸钠和碳酸铵的组合。
步骤b的发泡剂成分包括：双氧水、氯化钙和液体石蜡。
发泡剂的制备方法为：将液体石蜡加入硅和氯化钙混合，球磨2h，制得混合物料，将混合物料加入到双氧水中，快速搅拌均匀后得到。
硅占发泡剂的2%。
实施例3
一种新型建筑节能保温材料的制备方法，包括以下制备步骤：
a、将氯化镁、秸秆、粉煤灰和改性添加剂置于球磨机中进行球磨，球磨2h，混合均匀后制得混合料；
b、将混合料兑水制成混合浆料，向混合浆料中加入聚苯乙烯树脂、发泡剂、聚三氟氯乙烯树脂和硅藻泥高速搅拌，搅拌速度为1500r/min，搅拌30min，搅拌均匀后导入到模具中进行高温烧制，温度为800℃，烧制60min，得到保温基材；
c、将保温基材进行高温加压成型，温度为100℃，加压压力为50MPa，加压15min后即可得到保温材料粗品；
d、将保温材料粗品自然冷却至常温后，进行打磨、修边，即可得到成品。
新型建筑节能保温材料包括以下重量份的原料：氯化镁25份、秸秆45份、粉煤灰26份、改性添加剂13份、聚苯乙烯树脂15份、发泡剂17份、聚三氟氯乙烯树脂18份、硅藻泥24份和水22份。
步骤a的改性添加剂的成分包括甲基纤维素醚、无机盐类化合物、硬脂酸钙和乳胶粉。
改性添加剂的制备方法为：将甲基纤维素醚加入到硬脂酸钙和无机盐类化合物的混合物中，球磨70min，再加入乳胶粉，球磨2h得到。
无机盐类化合物为硫酸镁、硫酸钠和碳酸铵的组合。
步骤b的发泡剂成分包括：双氧水、氯化钙和液体石蜡。
发泡剂的制备方法为：将液体石蜡加入硅和氯化钙混合，球磨3h，制得混合物料，将混合物料加入到双氧水中，快速搅拌均匀后得到。
硅占发泡剂的4%。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种新型建筑节能保温材料的制备方法，其特征在于，包括以下制备步骤：
a、将氯化镁、秸秆、粉煤灰和改性添加剂置于球磨机中进行球磨，球磨1-2h，混合均匀后制得混合料；
b、将混合料兑水制成混合浆料，向混合浆料中加入聚苯乙烯树脂、发泡剂、聚三氟氯乙烯树脂和硅藻泥高速搅拌，搅拌速度为1000-1500r/min，搅拌20-30min，搅拌均匀后导入到模具中进行高温烧制，温度为600-800℃，烧制50-60min，得到保温基材；
c、将保温基材进行高温加压成型，温度为80-100℃，加压压力为40-50MPa，加压10-15min后即可得到保温材料粗品；
d、将保温材料粗品自然冷却至常温后，进行打磨、修边，即可得到成品。
2.根据权利要求1所述的一种新型建筑节能保温材料的制备方法，其特征在于，所述新型建筑节能保温材料包括以下重量份的原料：氯化镁22-25份、秸秆30-45份、粉煤灰23-26份、改性添加剂11-13份、聚苯乙烯树脂12-15份、发泡剂13-17份、聚三氟氯乙烯树脂14-18份、硅藻泥20-24份和水20-22份。
3.根据权利要求1所述的一种新型建筑节能保温材料的制备方法，其特征在于，所述步骤a的改性添加剂的成分包括甲基纤维素醚、无机盐类化合物、硬脂酸钙和乳胶粉。
4.根据权利要求3所述的一种新型建筑节能保温材料的制备方法，其特征在于，所述改性添加剂的制备方法为：将甲基纤维素醚加入到硬脂酸钙和无机盐类化合物的混合物中，球磨50-70min，再加入乳胶粉，球磨1-2h得到。
5.根据权利要求3或4所述的一种新型建筑节能保温材料的制备方法，其特征在于，所述无机盐类化合物为硫酸镁、硫酸钠和碳酸铵中的任一种或多种的组合。
6.根据权利要求1所述的一种新型建筑节能保温材料的制备方法，其特征在于，所述步骤b的发泡剂成分包括：双氧水、氯化钙和液体石蜡。
7.根据权利要求6所述的一种新型建筑节能保温材料的制备方法，其特征在于，所述发泡剂的制备方法为：将液体石蜡加入硅和氯化钙混合，球磨2-3h，制得混合物料，将混合物料加入到双氧水中，快速搅拌均匀后得到。
8.根据权利要求7所述的一种新型建筑节能保温材料的制备方法，其特征在于，所述硅占发泡剂的2-4%。