CN107214795A - Mould the processing method that Yunlong mulberry branch in rattan article improves low temperature cold resistance - Google Patents
Mould the processing method that Yunlong mulberry branch in rattan article improves low temperature cold resistance Download PDFInfo
- Publication number
- CN107214795A CN107214795A CN201710281991.9A CN201710281991A CN107214795A CN 107214795 A CN107214795 A CN 107214795A CN 201710281991 A CN201710281991 A CN 201710281991A CN 107214795 A CN107214795 A CN 107214795A
- Authority
- CN
- China
- Prior art keywords
- yunlong
- mulberry branch
- branch
- mulberry
- processing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of processing method for moulding Yunlong mulberry branch raising low temperature cold resistance in rattan article, comprises the following steps：Yunlong mulberry branch in 4 Mays is felled, then mulberry branch alkaline yellow soil in Yunlong is coated at once and underground is embedded to；Take out Yunlong mulberry branch and insert in the vessel for filling nutrient solution, then vessel are put into greenhouse；Cultivate the feeding freezer freezing of Yunlong mulberry branch after one week；Yunlong mulberry branch is pulled out and carries out immersion 1 hour with methane liquid again by immersion after 1 hour；Pull Yunlong mulberry branch out to be placed in hyperbaric chamber again, apply 0.4 0.8MPa pulling force to Yunlong mulberry branch in hyperbaric chamber, stop pressure after applying ten minutes, then apply 1.2 1.8MPa pulling force to Yunlong mulberry branch again.Embedment subsurface processes are carried out after Yunlong mulberry branch is felled in processing method of the present invention, then branch are activated again, so that the weatherability of branch is greatly improved, Yunlong mulberry branch after processing adapts to use under 60 DEG C of weather of extremely trembling with fear.
Description
Technical field
The present invention relates to Yunlong mulberry branch processing technology field, and in particular to Yunlong mulberry branch is improved in one kind modeling rattan article
The processing method of low temperature cold resistance.
Background technology
Wicker plaiting article is one of folks of china traditional handicraft product.People are intended only as common daily utility in ancient times, directly
Decades just gradually rise after to 20th century, also the project exported goods and earned foreign currency as selected areas of China gradually.Wicker is soft easily
Curved, thickness is well-balanced, color and luster is graceful, by novel design, can be woven into that various honesties are natural, handsome in appearance, Portable durable
Practical art product.Its product includes：Crate (bag), meal basket, food basket (circle, ellipse), bamboo strainer, needlework shallow basket made of wicker or thin bamboo strips, kang mat, reed matting
Deng.As industry is continued to develop, product is constantly brought forth new ideas, and has the face that more Nover practicals willow attractive in appearance is presented in client
Before.
Wicker products is the artifacts of China's widespread among the people, " compile basket, compile basket, every household has ".Because this
The raw material sources for planting technique are quite varied.The primary raw material that the north is used to compile basket volume basket has withy, Chinese tamarisk branch, mulberry shoot, the twigs of the chaste tree, purple
Fringe Chinese scholartree bar etc. is a variety of, is produced in salt-soda soil and marshland.
The species of wicker products is various, has seat, basket, basket, dustpan, round-bottomed basket, crate, shallow basket made of wicker or thin bamboo strips, the gaily decorated basket, Zhao at domestic aspect
The polytypes such as hedge, food dish.In terms of export trade, by developing and design formed buck basket, flower pot coat, picnic tableware basket, hanging basket,
Lampshade, kennel, cat litter, Bird's Nest etc. are a variety of, the appreciation effect that low-grade goods become high-grade are formed in foreign trade, very by foreign trade department
Attention.
Yunlong mulberry, also known as imperial mulberry, turns mulberry, dragon and turns mulberry etc., Moraceae.Perennial woody plant, is a change for common mulberry tree
Different kind.Branch natural torsion, shape such as serpentine bend shape and gain the name.Yunlong mulberry is especially fitted because of its unique natural torsion shape
Compile in collaboration with knit some have it is irregular sense, the wicker products of sense straggly.At present commonly using modeling rattan and Yunlong mulberry branch shuffling product, system
Product are due to being used for a long time, particularly in winter, especially in the cold north, and Yunlong mulberry branch easily ftractures, or even fracture.
The content of the invention
The technical problems to be solved by the invention are to provide Yunlong mulberry branch raising low temperature in a kind of modeling rattan article and resisted cold
The processing method of property.
The technical problems to be solved by the invention are realized using following technical scheme：
Yunlong mulberry branch improves the processing method of low temperature cold resistance in a kind of modeling rattan article, comprises the following steps：
(1) Yunlong mulberry branch in 4-5 months is felled, then mulberry branch alkaline yellow soil in Yunlong is coated at once and makes Huang
Soil coating thickness is not less than 3-5cm, then is embedded to underground after Yunlong mulberry branch is covered with plant ash；
(2) treat that Yunlong mulberry branch is taken out and cleaned up by the middle ten days in November then, by Yunlong mulberry branch bottom shear into
Inclined plane shape, Yunlong mulberry branch bottom is inserted in the vessel for filling nutrient solution, then vessel is put into greenhouse, and monitor greenhouse
The content of interior oxygen and carbon dioxide, makes in greenhouse carbon dioxide content maintain carbon dioxide accounting in every cubic meter of gas to be
2%-4% benchmark, oxygen content maintains the benchmark that oxygen accounting in every cubic meter of gas is 22%-23%；
(3) freezer that Yunlong mulberry branch is sent into -50 DEG C after cultivating one week is freezed 24-48 hours, then takes out Yunlong mulberry
Branch is simultaneously soaked with 70-80 DEG C of glacial acetic acid of 8.9% concentration；
(4) Yunlong mulberry branch is pulled out after soaking 1 hour and immersion 1 hour is carried out with methane liquid again；
(5) it is that 1MPa, relative humidity are the 16%, volume of hydrogen sulfide accounting gas to pull Yunlong mulberry branch out and be placed in pressure again
Percentage applies in 0.3%-0.6% hyperbaric chamber, to apply 0.4-0.8MPa pulling force to Yunlong mulberry branch in hyperbaric chamber
Stop pressure after ten minutes, then apply 1.2-1.8MPa pulling force to Yunlong mulberry branch again, then take out Yunlong mulberry branch again
It is placed under the sun and dries.
Step (1) neutral and alkali yellow soil pH value is 7.2, is lived in every 1kg yellow soils doped with 0.03kg astragalus membranaceus powders, 0.03kg
Change yeast, 0.01kg pig bloods, 0.01kg triclosans.
Carbon dioxide content maintains the benchmark that carbon dioxide accounting in every cubic meter of gas is 3%, oxygen in step (1)
Content maintains the benchmark that oxygen accounting in every cubic meter of gas is 22.5%.
In methane liquid in step (4) according further to every 1kg methane liquids add 0.01-0.03kg sorbitan carboxylic esterses,
0.02-0.04kg polyglucoses.
The percent by volume of hydrogen sulfide accounting gas is 0.5% in hyperbaric chamber in step (5).
The beneficial effects of the invention are as follows：Embedment subsurface processes are carried out after Yunlong mulberry branch is felled in treatment method, so
Branch is activated again afterwards, so that the weatherability of branch is greatly improved, Yunlong mulberry branch after processing adapts to -60 DEG C
Extremely tremble with fear weather under use, extremely tremble with fear temperature under using 5 years all without produce slight crack.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
Yunlong mulberry branch improves the processing method of low temperature cold resistance in a kind of modeling rattan article, comprises the following steps：
(1) Yunlong mulberry branch in 4-5 months is felled, then mulberry branch alkaline yellow soil in Yunlong is coated at once and makes Huang
Soil coating thickness is not less than 3-5cm, then is embedded to underground after Yunlong mulberry branch is covered with plant ash；
(2) treat that Yunlong mulberry branch is taken out and cleaned up by the middle ten days in November then, by Yunlong mulberry branch bottom shear into
Inclined plane shape, Yunlong mulberry branch bottom is inserted in the vessel for filling nutrient solution, then vessel is put into greenhouse, and monitor greenhouse
The content of interior oxygen and carbon dioxide, makes in greenhouse carbon dioxide content maintain carbon dioxide accounting in every cubic meter of gas to be
3% benchmark, oxygen content maintains the benchmark that oxygen accounting in every cubic meter of gas is 22.5%；
(3) freezer that Yunlong mulberry branch is sent into -50 DEG C after cultivating one week is freezed 24-48 hours, then takes out Yunlong mulberry
Branch is simultaneously soaked with 70-80 DEG C of glacial acetic acid of 8.9% concentration；
(4) Yunlong mulberry branch is pulled out after soaking 1 hour and immersion 1 hour is carried out with methane liquid again；
(5) it is that 1MPa, relative humidity are the 16%, volume of hydrogen sulfide accounting gas to pull Yunlong mulberry branch out and be placed in pressure again
Percentage applies ten minutes in 0.5% hyperbaric chamber, to apply 0.4-0.8MPa pulling force to Yunlong mulberry branch in hyperbaric chamber
Stop pressure afterwards, then apply 1.2-1.8MPa pulling force to Yunlong mulberry branch again, then take out Yunlong mulberry branch and be placed in again too
Dried under sun.
Step (1) neutral and alkali yellow soil pH value is 7.2, is lived in every 1kg yellow soils doped with 0.03kg astragalus membranaceus powders, 0.03kg
Change yeast, 0.01kg pig bloods, 0.01kg triclosans.
In methane liquid in step (4) 0.02kg sorbitan carboxylic esterses, 0.03kg are added according further to every 1kg methane liquids
Polyglucose.
Embodiment 2
Yunlong mulberry branch improves the processing method of low temperature cold resistance in a kind of modeling rattan article, comprises the following steps：
(1) Yunlong mulberry branch in 4-5 months is felled, then mulberry branch alkaline yellow soil in Yunlong is coated at once and makes Huang
Soil coating thickness is not less than 3-5cm, then is embedded to underground after Yunlong mulberry branch is covered with plant ash；
(2) treat that Yunlong mulberry branch is taken out and cleaned up by the middle ten days in November then, by Yunlong mulberry branch bottom shear into
Inclined plane shape, Yunlong mulberry branch bottom is inserted in the vessel for filling nutrient solution, then vessel is put into greenhouse, and monitor greenhouse
The content of interior oxygen and carbon dioxide, makes in greenhouse carbon dioxide content maintain carbon dioxide accounting in every cubic meter of gas to be
2% benchmark, oxygen content maintains the benchmark that oxygen accounting in every cubic meter of gas is 22%；
(3) freezer that Yunlong mulberry branch is sent into -50 DEG C after cultivating one week is freezed 24-48 hours, then takes out Yunlong mulberry
Branch is simultaneously soaked with 70-80 DEG C of glacial acetic acid of 8.9% concentration；
(4) Yunlong mulberry branch is pulled out after soaking 1 hour and immersion 1 hour is carried out with methane liquid again；
(5) it is that 1MPa, relative humidity are the 16%, volume of hydrogen sulfide accounting gas to pull Yunlong mulberry branch out and be placed in pressure again
Percentage applies ten minutes in 0.3% hyperbaric chamber, to apply 0.4-0.8MPa pulling force to Yunlong mulberry branch in hyperbaric chamber
Stop pressure afterwards, then apply 1.2-1.8MPa pulling force to Yunlong mulberry branch again, then take out Yunlong mulberry branch and be placed in again too
Dried under sun.
Step (1) neutral and alkali yellow soil pH value is 7.2, is lived in every 1kg yellow soils doped with 0.03kg astragalus membranaceus powders, 0.03kg
Change yeast, 0.01kg pig bloods, 0.01kg triclosans.
In methane liquid in step (4) 0.01kg sorbitan carboxylic esterses, 0.02kg are added according further to every 1kg methane liquids
Polyglucose.
Embodiment 3
Yunlong mulberry branch improves the processing method of low temperature cold resistance in a kind of modeling rattan article, comprises the following steps：
(1) Yunlong mulberry branch in 4-5 months is felled, then mulberry branch alkaline yellow soil in Yunlong is coated at once and makes Huang
Soil coating thickness is not less than 3-5cm, then is embedded to underground after Yunlong mulberry branch is covered with plant ash；
(2) treat that Yunlong mulberry branch is taken out and cleaned up by the middle ten days in November then, by Yunlong mulberry branch bottom shear into
Inclined plane shape, Yunlong mulberry branch bottom is inserted in the vessel for filling nutrient solution, then vessel is put into greenhouse, and monitor greenhouse
The content of interior oxygen and carbon dioxide, makes in greenhouse carbon dioxide content maintain carbon dioxide accounting in every cubic meter of gas to be
4% benchmark, oxygen content maintains the benchmark that oxygen accounting in every cubic meter of gas is 23%；
(3) freezer that Yunlong mulberry branch is sent into -50 DEG C after cultivating one week is freezed 24-48 hours, then takes out Yunlong mulberry
Branch is simultaneously soaked with 70-80 DEG C of glacial acetic acid of 8.9% concentration；
(4) Yunlong mulberry branch is pulled out after soaking 1 hour and immersion 1 hour is carried out with methane liquid again；
(5) it is that 1MPa, relative humidity are the 16%, volume of hydrogen sulfide accounting gas to pull Yunlong mulberry branch out and be placed in pressure again
Percentage applies ten minutes in 0.6% hyperbaric chamber, to apply 0.4-0.8MPa pulling force to Yunlong mulberry branch in hyperbaric chamber
Stop pressure afterwards, then apply 1.2-1.8MPa pulling force to Yunlong mulberry branch again, then take out Yunlong mulberry branch and be placed in again too
Dried under sun.
Step (1) neutral and alkali yellow soil pH value is 7.2, is lived in every 1kg yellow soils doped with 0.03kg astragalus membranaceus powders, 0.03kg
Change yeast, 0.01kg pig bloods, 0.01kg triclosans.
In methane liquid in step (4) 0.03kg sorbitan carboxylic esterses, 0.04kg are added according further to every 1kg methane liquids
Polyglucose.
Experiment
Yunlong mulberry branch of the processing of embodiment 1,2,3 is tested, result of the test is as follows：
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (5)
1. a kind of mould the processing method that Yunlong mulberry branch in rattan article improves low temperature cold resistance, it is characterised in that including following step
Suddenly：
(1) Yunlong mulberry branch in 4-5 months is felled, then mulberry branch alkaline yellow soil in Yunlong is coated at once and makes yellow soil
Coating thickness is not less than 3-5cm, then is embedded to underground after Yunlong mulberry branch is covered with plant ash；
(2) treat that Yunlong mulberry branch is taken out and cleaned up by the middle ten days in November then, by Yunlong mulberry branch bottom shear into inclined-plane
Shape, Yunlong mulberry branch bottom is inserted in the vessel for filling nutrient solution, then vessel is put into greenhouse, and monitor warm indoor oxygen
The content of gas and carbon dioxide, it is 2%- carbon dioxide content is maintained carbon dioxide accounting in every cubic meter of gas
4% benchmark, oxygen content maintains the benchmark that oxygen accounting in every cubic meter of gas is 22%-23%；
(3) freezer that Yunlong mulberry branch is sent into -50 DEG C after cultivating one week is freezed 24-48 hours, then takes out Yunlong mulberry branch
And soaked with 70-80 DEG C of glacial acetic acid of 8.9% concentration；
(4) Yunlong mulberry branch is pulled out after soaking 1 hour and immersion 1 hour is carried out with methane liquid again；
(5) it is that 1MPa, relative humidity are the 16%, volume basis of hydrogen sulfide accounting gas to pull Yunlong mulberry branch out and be placed in pressure again
Than in the hyperbaric chamber for 0.3%-0.6%, applying 0.4-0.8MPa pulling force to Yunlong mulberry branch in hyperbaric chamber, apply very
Stop pressure after clock, then apply 1.2-1.8MPa pulling force to Yunlong mulberry branch again, then take out Yunlong mulberry branch and be placed in again
Dried under the sun.
2. Yunlong mulberry branch improves the processing method of low temperature cold resistance, its feature in modeling rattan article according to claim 1
It is, step (1) neutral and alkali yellow soil pH value is 7.2, is activated in every 1kg yellow soils doped with 0.03kg astragalus membranaceus powders, 0.03kg
Yeast, 0.01kg pig bloods, 0.01kg triclosans.
3. Yunlong mulberry branch improves the processing method of low temperature cold resistance, its feature in modeling rattan article according to claim 1
It is, carbon dioxide content maintains the benchmark that carbon dioxide accounting in every cubic meter of gas is 3% in step (2), oxygen contains
Amount maintains the benchmark that oxygen accounting in every cubic meter of gas is 22.5%.
4. Yunlong mulberry branch improves the processing method of low temperature cold resistance, its feature in modeling rattan article according to claim 1
Be, in the methane liquid in step (4) according further to every 1kg methane liquids add 0.01-0.03kg sorbitan carboxylic esterses,
0.02-0.04kg polyglucoses.
5. Yunlong mulberry branch improves the processing method of low temperature cold resistance, its feature in modeling rattan article according to claim 1
It is, the percent by volume of hydrogen sulfide accounting gas is 0.5% in the hyperbaric chamber in step (5).