CN107200538A - Long filament thermal non-woven fabric coating inorganic diatomite liquid wall material and its preparation, construction method - Google Patents
Long filament thermal non-woven fabric coating inorganic diatomite liquid wall material and its preparation, construction method Download PDFInfo
- Publication number
- CN107200538A CN107200538A CN201710366122.6A CN201710366122A CN107200538A CN 107200538 A CN107200538 A CN 107200538A CN 201710366122 A CN201710366122 A CN 201710366122A CN 107200538 A CN107200538 A CN 107200538A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatomite
- inorganic
- wall material
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of long filament thermal non-woven fabric coating inorganic diatomite liquid wall material and its preparation, construction method, belong to architectural decoration material field.The formula of the wall material includes inorganic adhesive and coating surface material, wherein:The inorganic cementitious material includes the component of following parts by weight:10 60 parts of sierozem power, 5 45 parts of diatomite, 1 20 parts of alumina silicate, convex 0.5 20 parts of rod soil, 0.5 20 parts of aluminium-magnesium silicate, 0.5 20 parts of kaolin etc.;The coating surface material includes the component of following parts by weight:10 60 parts of sierozem power, 5 40 parts of coarse whiting, 5 45 parts of diatomite, 1 20 parts of alumina silicate, convex 0.5 20 parts of rod soil, 0.5 20 parts of aluminium-magnesium silicate, 1 18 parts of oyster shell whiting, 0.5 20 parts of kaolin etc..The wall material that the present invention is provided possesses certain pulling force and wall cracking resistance, while having excellent sensory effects.
Description
Technical field
The present invention relates to architectural decoration material field, more particularly to a kind of long filament thermal non-woven fabric coating inorganic diatom
Native liquid wall material and its preparation, construction method.
Background technology
Non-woven cloth is fabric formed by one kind need not spin cotton and weave cloth, and simply carries out textile staple or long filament
Orientation or random support row, form fibre net structure, are then reinforced and formed using the method such as mechanical, hot sticky or chemical.Simply say just
It is:It is not by one one yarns interwoven, knit together, but fiber is directly bonded in by the method for physics
Together.Non-woven cloth breaches traditional weaving principle, and with technological process is short, speed of production is fast, yield is high, cost
The features such as low, purposes is wide, raw material sources are more.
Wherein, the products characteristics of polypropylene nonwoven:1) light weight, polypropylene proportion only 0.9, only the five of cotton/
Three, it is thin and light, with excellent bulkiness;2) it is soft, (2-3D) is constituted by fine fibre, through the shaping of point-like hot melting cohesion, finished product
Pliability is moderate, has comfort;3) pull out water breathe freely, polypropylene chip does not absorb water, moisture content zero, product pull out it is aqueous it is good, have
100% fiber is constituted, and has porous, and product gas permeability is good, easy holding cloth cover is dry and comfortable;4) nontoxic, nonirritant, product is using symbol
Close the production of FDA food grade materials, be molded in hot adhesion mode, product without other chemical compositions, stable chemical performance, it is nontoxic,
Free from extraneous odour and do not stimulate human body skin;5) anti-chemical agent, polypropylene belongs to inactivity material, and chemical resistance of concrete intensity is good, system
Product do not weather and influence intensity;6) antibiotic property, product tool pulls out aqueous, not mouldy, and can isolate and there is liquid Endophytic bacteria and worm
The erosion of class, not mould moth;7) physical property is good, and net hot adhesion is directly paved into by polypropylene spinning and is formed, the relatively general short fibre of product strength
It is better;8) two-way fastness is good, and it is a little rhombus that it, which rolls, wear-resistant, firm good hand touch.
Diatomite is a kind of biogenic siliceous sedimentary rock, and it is mainly made up of the remains of ancient times diatom, with thin
The characteristic such as greasy, loose, light weight, porous, water imbibition and permeability be strong.Requirement with people to the living environment feature of environmental protection is increasingly
Height, diatomite is increasingly becoming a kind of very popular new indoor decoration material, and with the addition of diatomaceous wall material has
The advantages of adjusting room temperature, eliminate peculiar smell, absorb harmful substance.At present, although can be on wall body surface using kieselguhr wall material
Certain texture is produced, it is ornamental to increase it, but still have improved space in this respect.
If it is possible to provide a kind of long filament thermal non-woven fabric coating inorganic diatomite liquid wall material, possessing
Wider skin texture and artistic effect are made on certain pulling force and distinctive texture, then can necessarily meet people to a certain extent
To kieselguhr wall material it is functional under the premise of possess it is fine it is ornamental require.
The content of the invention
Harmful substance can be removed the technical problem to be solved in the present invention is to provide one kind and with certain pulling force and texture
Long filament thermal non-woven fabric coating inorganic diatomite liquid wall material and its preparation, construction method.
In order to solve the above technical problems, the technical scheme that the present invention is provided is as follows:
A kind of long filament thermal non-woven fabric coating inorganic diatomite liquid wall material, the formula of the wall material includes inorganic glue
Material and coating surface material are connect, wherein:
The inorganic cementitious material includes the component of following parts by weight:10-60 parts of sierozem power, 5-45 parts of diatomite, silicic acid
1-20 parts of aluminium, convex 0.5-20 parts of rod soil, 0.5-20 parts of aluminium-magnesium silicate, 0.5-20 parts of kaolin, 0.5-16 parts of bentonite, cluster bean
0.1-1.9 parts of glue, 0.1-8 parts of natural plant gum, 0.1-15 parts of etherification starch, 0.1-2.2 parts of defoamer, 0.1-6 parts of dispersant, go from
Sub- 70 parts of water;
The coating surface material includes the component of following parts by weight:10-60 parts of sierozem power, 5-40 parts of coarse whiting, diatomite
5-45 parts, 1-20 parts of alumina silicate, convex 0.5-20 parts of rod soil, 0.5-20 parts of aluminium-magnesium silicate, 1-18 parts of oyster shell whiting, kaolin 0.5-20
Part, 0.5-16 parts of bentonite, 1-19 parts of lithopone, 1-20 parts of anatase thpe white powder, 0.1-1.9 parts of guar gum, natural plant gum
0.1-8 parts, 0.1-15 parts of etherification starch, 0.01-2.2 parts of defoamer, 0.01-6 parts of dispersant, 60 parts of deionized water.
The wall material of the present invention be by inorganic cementitious material and coating surface material transform non-woven cloth one kind is made can be with
Formaldehyde in air of going out simultaneously has certain pulling force, wall material not easy to crack, bulge.The inorganic cementitious material of the present invention is with sierozem power
It is primary raw material with diatomite, is aided with alumina silicate, aluminium-magnesium silicate, the material such as convex rod soil makes the inorganic cementitious material of the present invention not
Only there is good cohesive force, and with the effect of removal formaldehyde, while the ductility of non-woven cloth is not influenceed, and coated side
Layer material not only needs preferably caking property, and also has extraordinary effect on formaldehyde and decorative effect is removed.This
Inventing the wall material prepared not only has good pulling force and decorative effect, and can effectively remove formaldehyde, and in antibiotic property, resistance to
It is more excellent compared with traditional wall material in mill property.
Further, the inorganic adhesive includes the component of following parts by weight:10-20 parts of sierozem power, diatomite 5-
15 parts, 1-5 parts of alumina silicate, convex 0.5-2 parts of rod soil, 0.5-2 parts of aluminium-magnesium silicate, 0.5-2 parts of kaolin, 0.5-2 parts of bentonite, melon
0.1-0.5 parts of bean gum of that, 0.1-1 parts of natural plant gum, 0.1-1 parts of etherification starch, 0.1-0.5 parts of defoamer, 0.1-1 parts of dispersant,
70 parts of deionized water;
The coating surface material includes the component of following parts by weight:10-20 parts of sierozem power, 5-10 parts of coarse whiting, diatomite
5-10 parts, 1-2 parts of alumina silicate, convex 0.5-2 parts of rod soil, 0.5-2 parts of aluminium-magnesium silicate, 1-5 parts of oyster shell whiting, 0.5-2 parts of kaolin is splashed
Moisten 0.5-1.6 parts of soil, 1-9 parts of lithopone, 1-10 parts of anatase thpe white powder, 0.1-0.5 parts of guar gum, natural plant gum 0.1-0.5
Part, 0.1-1 parts of etherification starch, 0.01-0.2 parts of defoamer, 0.01-0.5 parts of dispersant, 60 parts of deionized water.
Preferably, the inorganic adhesive includes the component of following parts by weight:15 parts of sierozem power, 5 parts of diatomite, silicic acid
2 parts of aluminium, convex 1 part of rod soil, 1 part of aluminium-magnesium silicate, 1 part of kaolin, 1 part of bentonite, 0.2 part of guar gum, 0.1 part of natural plant gum, ether
Change 0.5 part of starch, 0.1 part of defoamer, 0.2 part of dispersant, 70 parts of deionized water;
The coating surface material includes the component of following parts by weight:15 parts of sierozem power, 5 parts of coarse whiting, 5 parts of diatomite, silicon
Sour 1 part of aluminium, convex 0.5 part of rod soil, 0.5 part of aluminium-magnesium silicate, 2 parts of oyster shell whiting, 1 part of kaolin, 0.5 part of bentonite, 5 parts of lithopone,
5 parts of anatase thpe white powder, 0.1 part of guar gum, 0.15 part of natural plant gum, 0.1 part of etherification starch, 0.01 part of defoamer, dispersant
0.02 part, deionized water 60.
Further, the wall material also includes non-woven cloth, and the wall material includes base prepared by the inorganic cementitious material
Coat prepared by bottom and the coating surface material, the non-woven cloth is clipped in the basalis and coating as intermediate layer
Between layer.
Preferably, the non-woven cloth is polypropylene nonwoven.Wall material prepared by polypropylene nonwoven is keeping good
On the basis of good pulling force and decoration, compared with other non-woven cloths, with it is more wear-resisting, to be difficult bulge, anti-microbial property excellent
Resultant effect.
On the other hand there is provided a kind of preparation method of long filament thermal non-woven fabric coating inorganic diatomite liquid wall material,
Comprise the following steps:
Step 1:The inorganic adhesive is formulated as follows:
1) it is the guar gum, natural plant gum, etherification starch, defoamer and dispersant is equal successively in order according to the above ratio
It is even to be added in 50 parts of deionized waters and the obtained solution A that stirs is standby;
2) again by 1 part of the sierozem power, diatomite, alumina silicate, convex rod soil, aluminium-magnesium silicate, kaolin and bentonite by upper
State ratio and be added to 20 parts of ionized water high speeds successively in order and be uniformly dispersed, be then transferred to sand mill fineness of grind and reach 60-
80 microns of obtained B solutions are standby;
3) component A is added the B component filtrating test that stirs and obtains the finished product of inorganic adhesive;
Step 2:It is described to coat being formulated as follows for surface material;
1) by the guar gum, natural plant gum, etherification starch, defoamer and dispersant 0.01 according to the above ratio in order according to
It is secondary that uniform to be added in 30 parts of deionized waters the obtained C solution that stirs standby;
2) by the sierozem power, coarse whiting, diatomite, alumina silicate, convex rod soil, aluminium-magnesium silicate, oyster shell whiting, kaolin, Peng Run
Soil, lithopone and anatase thpe white powder are added to 30 parts of deionized water high speeds and are uniformly dispersed successively in order according to the above ratio,
Then it is transferred to and reaches that 60-80 microns of obtained solution Ds are standby into sand mill eye fineness of grind;
3) component C is added the D components filtrating test that stirs and obtains coating the finished product of surface material.
The preparation technology of the present invention is simple, and the present invention has carried out exploration discovery by the order of addition to material, wants to obtain
Wall material of the invention is obtained, not only composition of raw materials is required, and its preparation technology can also influence the workability of wall material, remove
Resultant effect in terms of effect of formaldehyde and antibacterial.
There is provided a kind of construction party of the long filament thermal non-woven fabric coating inorganic diatomite liquid wall material for another further aspect
Method, it is characterised in that comprise the following steps:
1) metope substrate is handled:Metope wall body has integrally been scraped into water-proof putty and brushing basement membrane, has made wall after being disposed
Body humidity is less than 10%, pH and is less than 10, wall body overall leveling, closely knit, clean without floating dust, without cracking hollowing;
2) the finished product twice of the inorganic adhesive are brushed in the metope substrate handled well, and by the non-woven cloth
Pasted by order from left to right or from right to left, after stickup is smooth, treat that non-woven cloth is fixed, it is described before not being completely dried to apply
The finished product of clad can layer material, brushing twice are to obtain the long filament thermal non-woven fabric coating inorganic diatomite liquid wall material.
The present invention, it is necessary to metope wall body has integrally been scraped into water-proof putty and brushing basement membrane, is used in combination when handling metope substrate
U.S. line paper protects wall body corner;If wall body base material is different, bandage or grid cloth processing should be also sticked in junction;
Require that wall body humidity is less than 10%, pH and is less than 10 after being disposed, it is wall body overall leveling, closely knit, clean without floating dust, without cracking
Hollowing.The inorganic adhesive twice are brushed on metope substrate is handled well, and start to paste long filament heat seal non-woven cloth, are pressed
Order from left to right is pasted, and order that can also be from right to left is pasted, and seam is preferably selected at inner corner trim, it is ensured that its surface of wall
Not with regard to seam., just can be in the long filament thermal non-woven fabric as long as can fix without being completely dried after stickup is smooth
The upper coating coating surface material, brushing twice, if other color rags or sponge etc. can also be used by doing artistic effect
Art tool makes Protean technological effect on its surface.
The decoration wall material of the present invention has the advantages that:
The wall material of the present invention be by inorganic cementitious material and coating surface material transform non-woven cloth one kind is made can be with
Formaldehyde in air of going out simultaneously has certain pulling force, wall material not easy to crack, bulge.The inorganic cementitious material of the present invention is with sierozem power
It is primary raw material with diatomite, is aided with alumina silicate, aluminium-magnesium silicate, the material such as convex rod soil makes the inorganic cementitious material of the present invention not
Only there is good cohesive force, and with the effect of removal formaldehyde, while the ductility of non-woven cloth is not influenceed, and coated side
Layer material not only needs preferably caking property, and also has extraordinary effect on formaldehyde and decorative effect is removed.This
Inventing the wall material prepared not only has good pulling force and decorative effect, and can effectively remove formaldehyde, and in antibiotic property, resistance to
It is more excellent compared with traditional wall material in mill property.
Embodiment
To make the technical problem to be solved in the present invention, technical scheme and advantage clearer, with reference to specific embodiment
It is described in detail.
Method used in following embodiments is conventional method unless otherwise specified.
Material, reagent used etc., unless otherwise specified, are commercially obtained in following embodiments.
On the one hand, the present invention provide a kind of long filament thermal non-woven fabric coating inorganic diatomite liquid wall material and its
Construction method, it is the fluent material allocated by various ingredients, and concrete component refers to following examples.
Embodiment 1:
Long filament thermal non-woven fabric coating inorganic diatomite liquid wall material includes inorganic cementitious material and coating surface layer material
Material, inorganic cementitious material includes the component of following parts by weight:10 parts of sierozem power, 45 parts of diatomite, 1 part of alumina silicate, convex rod soil 0.5
Part, 20 parts of aluminium-magnesium silicate, 20 parts of kaolin, 0.5 part of bentonite, 0.1 part of guar gum, 8 parts of natural plant gum, 0.1 part of etherification starch,
0.1 part of defoamer, 6 parts of dispersant, 70 parts of deionized water;Coating surface material includes the component of following parts by weight:Sierozem power 60
Part, 5 parts of coarse whiting, 45 parts of diatomite, 1 part of alumina silicate, convex 0.5 part of rod soil, 20 parts of aluminium-magnesium silicate, 18 parts of oyster shell whiting, kaolin 0.5
Part, 0.5 part of bentonite, 19 parts of lithopone, 1 part of anatase thpe white powder, 0.1 part of guar gum, 8 parts of natural plant gum, etherification starch 0.1
Part, 0.01 part of defoamer, 6 parts of dispersant, 60 parts of deionized water.
Embodiment 2:
Long filament thermal non-woven fabric coating inorganic diatomite liquid wall material includes inorganic cementitious material and coating surface layer material
Material, inorganic cementitious material includes the component of following parts by weight:60 parts of sierozem power, 5 parts of diatomite, 20 parts of alumina silicate, convex rod soil 20
Part, 0.5 part of aluminium-magnesium silicate, 0.5 part of kaolin, 16 parts of bentonite, 1.9 parts of guar gum, 0.1 part of natural plant gum, etherification starch 15
Part, 2.2 parts of defoamer, 0.1 part of dispersant, 70 parts of deionized water;Coating surface material includes the component of following parts by weight:Grey calcium
10 parts of powder, 40 parts of coarse whiting, 5 parts of diatomite, 20 parts of alumina silicate, convex 20 parts of rod soil, 0.5 part of aluminium-magnesium silicate, 1 part of oyster shell whiting, kaolinite
20 parts of soil, 16 parts of bentonite, 1 part of lithopone, 20 parts of anatase thpe white powder, 19 parts of guar gum, 0.1 part of natural plant gum, etherificate is formed sediment
15 parts of powder, 2.2 parts of defoamer, 0.01 part of dispersant, 60 parts of deionized water.
Embodiment 3:
Long filament thermal non-woven fabric coating inorganic diatomite liquid wall material includes inorganic cementitious material and coating surface layer material
Material, inorganic cementitious material includes the component of following parts by weight:40 parts of sierozem power, 30 parts of diatomite, 5 parts of alumina silicate, convex rod soil 10
Part, 10 parts of aluminium-magnesium silicate, 10 parts of kaolin, 8 parts of bentonite, 1 part of guar gum, 4 parts of natural plant gum, 10 parts of etherification starch, froth breaking
1.5 parts of agent, 3 parts of dispersant, 70 parts of deionized water;Coating surface material includes the component of following parts by weight:30 parts of sierozem power, weight
20 parts of calcium, 27 parts of diatomite, 13 parts of alumina silicate, convex 10 parts of rod soil, 10 parts of aluminium-magnesium silicate, 8 parts of oyster shell whiting, 10 parts of kaolin is splashed
8 parts of profit soil, 7 parts of lithopone, 10 parts of anatase thpe white powder, 1.2 parts of guar gum, 4 parts of natural plant gum, 10 parts of etherification starch, froth breaking
1.2 parts of agent, 3 parts of dispersant, 60 parts of deionized water.
Embodiment 4:
Long filament thermal non-woven fabric coating inorganic diatomite liquid wall material includes inorganic cementitious material and coating surface layer material
Material, inorganic adhesive includes the component of following parts by weight:20 parts of sierozem power, 15 parts of diatomite, 5 parts of alumina silicate, convex rod soil 2
Part, 2 parts of aluminium-magnesium silicate, 2 parts of kaolin, 2 parts of bentonite, 0.5 part of guar gum, 1 part of natural plant gum, 1 part of etherification starch, defoamer
0.5 part, 1 part of dispersant, 70 parts of deionized water;Coating surface material includes the component of following parts by weight:20 parts of sierozem power, coarse whiting
10 parts, 10 parts of diatomite, 2 parts of alumina silicate, convex 2 parts of rod soil, 2 parts of aluminium-magnesium silicate, 5 parts of oyster shell whiting, 2 parts of kaolin, bentonite 1.6
Part, 9 parts of lithopone, 10 parts of anatase thpe white powder, 0.5 part of guar gum, 0.5 part of natural plant gum, 1 part of etherification starch, defoamer 0.2
Part, 0.5 part of dispersant, 60 parts of deionized water.
Embodiment 5:
Long filament thermal non-woven fabric coating inorganic diatomite liquid wall material includes inorganic cementitious material and coating surface layer material
Material, inorganic adhesive includes the component of following parts by weight:10 parts of sierozem power, 10 parts of diatomite, 4 parts of alumina silicate, convex rod soil 0.5
Part, 2 parts of aluminium-magnesium silicate, 1 part of kaolin, 0.5 part of bentonite, 0.5 part of guar gum, 0.1 part of natural plant gum, 1 part of etherification starch disappears
0.1 part of infusion, 1 part of dispersant, 70 parts of deionized water;Coating surface material includes the component of following parts by weight:20 parts of sierozem power,
5 parts of coarse whiting, 8 parts of diatomite, 1 part of alumina silicate, convex 2 parts of rod soil, 1 part of aluminium-magnesium silicate, 5 parts of oyster shell whiting, 1 part of kaolin, bentonite
0.6 part, 7 parts of lithopone, 10 parts of anatase thpe white powder, 0.1 part of guar gum, 0.5 part of natural plant gum, 0.5 part of etherification starch, froth breaking
0.1 part of agent, 0.1 part of dispersant, 60 parts of deionized water.
Embodiment 6:
Long filament thermal non-woven fabric coating inorganic diatomite liquid wall material includes inorganic cementitious material and coating surface layer material
Material, inorganic adhesive includes the component of following parts by weight:15 parts of sierozem power, 5 parts of diatomite, 2 parts of alumina silicate, convex 1 part of rod soil,
1 part of aluminium-magnesium silicate, 1 part of kaolin, 1 part of bentonite, 0.2 part of guar gum, 0.1 part of natural plant gum, 0.5 part of etherification starch, froth breaking
0.1 part of agent, 0.2 part of dispersant, 70 parts of deionized water;
The coating surface material includes the component of following parts by weight:15 parts of sierozem power, 5 parts of coarse whiting, 5 parts of diatomite, silicon
Sour 1 part of aluminium, convex 0.5 part of rod soil, 0.5 part of aluminium-magnesium silicate, 2 parts of oyster shell whiting, 1 part of kaolin, 0.5 part of bentonite, 5 parts of lithopone,
5 parts of anatase thpe white powder, 0.1 part of guar gum, 0.15 part of natural plant gum, 0.1 part of etherification starch, 0.01 part of defoamer, dispersant
0.02 part, deionized water 60..
Above-described embodiment is prepared to the finished product of inorganic cementitious material respectively by the following method and surface material is coated
Finished product:
Step 1:The inorganic adhesive is formulated as follows:
1) it is the guar gum, natural plant gum, etherification starch, defoamer and dispersant is equal successively in order according to the above ratio
It is even to be added in 50 parts of deionized waters and the obtained solution A that stirs is standby;
2) again by 1 part of the sierozem power, diatomite, alumina silicate, convex rod soil, aluminium-magnesium silicate, kaolin and bentonite by upper
State ratio and be added to 20 parts of ionized water high speeds successively in order and be uniformly dispersed, be then transferred to sand mill fineness of grind and reach 60-
80 microns of obtained B solutions are standby;
3) component A is added the B component filtrating test that stirs and obtains the finished product of inorganic adhesive;
Step 2:It is described to coat being formulated as follows for surface material;
1) by the guar gum, natural plant gum, etherification starch, defoamer and dispersant 0.01 according to the above ratio in order according to
It is secondary that uniform to be added in 30 parts of deionized waters the obtained C solution that stirs standby;
2) by the sierozem power, coarse whiting, diatomite, alumina silicate, convex rod soil, aluminium-magnesium silicate, oyster shell whiting, kaolin, Peng Run
Soil, lithopone and anatase thpe white powder are added to 30 parts of deionized water high speeds and are uniformly dispersed successively in order according to the above ratio,
Then it is transferred to and reaches that 60-80 microns of obtained solution Ds are standby into sand mill eye fineness of grind;
3) component C is added the D components filtrating test that stirs and obtains coating the finished product of surface material.
The finished product of the finished product of the inorganic cementitious material prepared and coating surface material is constructed acquisition by the following method
The long filament thermal non-woven fabric coating inorganic diatomite liquid wall material:
1) metope substrate is handled:Metope wall body has integrally been scraped into water-proof putty and brushing basement membrane, has made wall after being disposed
Body humidity is less than 10%, pH and is less than 10, wall body overall leveling, closely knit, clean without floating dust, without cracking hollowing;
2) the finished product twice of the inorganic adhesive are brushed in the metope substrate handled well, and by the non-woven cloth
Pasted by order from left to right or from right to left, after stickup is smooth, treat that non-woven cloth is fixed, it is described before not being completely dried to apply
The finished product of clad can layer material, brushing twice are to obtain the long filament thermal non-woven fabric coating inorganic diatomite liquid wall material.
The wall material prepared to above-described embodiment carries out performance detection, through actual verification, long filament provided by the present invention
Thermal non-woven fabric coating inorganic diatomite liquid wall material, it possesses certain pulling force and wall cracking resistance, while also having
Excellent sensory effects are more attractive in appearance true to nature.Also, the long filament thermal non-woven fabric coating inorganic that wherein embodiment 4-6 is obtained
Diatomite liquid wall material is significantly larger than embodiment 1 to 3, and the long filament that embodiment 6 is provided in terms of cracking resistance, anti-microbial property
The wall cracking resistance of thermal non-woven fabric coating inorganic diatomite liquid wall material is optimal, and is demonstrated by excellent purifying formaldehyde
Performance, anti-microbial property.Meanwhile, researcher has found that polypropylene nonwoven is better than other non-thermoplastic in the effect of the wall material of preparation
Cloth.The polypropylene nonwoven cloth of the present invention is purchased from Taiwan Hua Rui Industry Co., Ltd.
Above-mentioned long filament thermal non-woven fabric coating inorganic diatomite liquid wall material provided by the present invention makes what is obtained
Wall body decorative pattern, it possesses certain pulling force and wall cracking resistance, while also having excellent sensory effects are more attractive in appearance to force
Very.
Described above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, on the premise of principle of the present invention is not departed from, some improvements and modifications can also be made, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (7)
1. a kind of long filament thermal non-woven fabric coating inorganic diatomite liquid wall material, it is characterised in that the formula of the wall material
Including inorganic adhesive and coating surface material, wherein:
The inorganic cementitious material includes the component of following parts by weight:10-60 parts of sierozem power, 5-45 parts of diatomite, alumina silicate 1-
20 parts, convex 0.5-20 parts of rod soil, 0.5-20 parts of aluminium-magnesium silicate, 0.5-20 parts of kaolin, 0.5-16 parts of bentonite, guar gum
0.1-1.9 parts, 0.1-8 parts of natural plant gum, 0.1-15 parts of etherification starch, 0.1-2.2 parts of defoamer, 0.1-6 parts of dispersant, deionization
70 parts of water;
The coating surface material includes the component of following parts by weight:10-60 parts of sierozem power, 5-40 parts of coarse whiting, diatomite 5-45
Part, 1-20 parts of alumina silicate, convex 0.5-20 parts of rod soil, 0.5-20 parts of aluminium-magnesium silicate, 1-18 parts of oyster shell whiting, 0.5-20 parts of kaolin,
0.5-16 parts of bentonite, 1-19 parts of lithopone, 1-20 parts of anatase thpe white powder, 0.1-1.9 parts of guar gum, natural plant gum 0.1-8
Part, 0.1-15 parts of etherification starch, 0.01-2.2 parts of defoamer, 0.01-6 parts of dispersant, 60 parts of deionized water.
2. long filament thermal non-woven fabric coating inorganic diatomite liquid wall material according to claim 1, it is characterised in that
The inorganic adhesive includes the component of following parts by weight:10-20 parts of sierozem power, 5-15 parts of diatomite, 1-5 parts of alumina silicate,
Convex 0.5-2 parts of rod soil, 0.5-2 parts of aluminium-magnesium silicate, 0.5-2 parts of kaolin, 0.5-2 parts of bentonite, 0.1-0.5 parts of guar gum,
0.1-1 parts of natural plant gum, 0.1-1 parts of etherification starch, 0.1-0.5 parts of defoamer, 0.1-1 parts of dispersant, 70 parts of deionized water;
The coating surface material includes the component of following parts by weight:10-20 parts of sierozem power, 5-10 parts of coarse whiting, diatomite 5-10
Part, 1-2 parts of alumina silicate, convex 0.5-2 parts of rod soil, 0.5-2 parts of aluminium-magnesium silicate, 1-5 parts of oyster shell whiting, 0.5-2 parts of kaolin, bentonite
0.5-1.6 parts, 1-9 parts of lithopone, 1-10 parts of anatase thpe white powder, 0.1-0.5 parts of guar gum, 0.1-0.5 parts of natural plant gum, ether
Change 0.1-1 parts of starch, 0.01-0.2 parts of defoamer, 0.01-0.5 parts of dispersant, 60 parts of deionized water.
3. long filament thermal non-woven fabric coating inorganic diatomite liquid wall material according to claim 2, it is characterised in that
The inorganic adhesive includes the component of following parts by weight:15 parts of sierozem power, 5 parts of diatomite, 2 parts of alumina silicate, convex rod soil 1
Part, 1 part of aluminium-magnesium silicate, 1 part of kaolin, 1 part of bentonite, 0.2 part of guar gum, 0.1 part of natural plant gum, 0.5 part of etherification starch disappears
0.1 part of infusion, 0.2 part of dispersant, 70 parts of deionized water;
The coating surface material includes the component of following parts by weight:15 parts of sierozem power, 5 parts of coarse whiting, 5 parts of diatomite, alumina silicate 1
Part, convex 0.5 part of rod soil, 0.5 part of aluminium-magnesium silicate, 2 parts of oyster shell whiting, 1 part of kaolin, 0.5 part of bentonite, 5 parts of lithopone, anatase titanium dioxide
5 parts of titanium dioxide, 0.1 part of guar gum, 0.15 part of natural plant gum, 0.1 part of etherification starch, 0.01 part of defoamer, 0.02 part of dispersant,
Deionized water 60.
4. according to any described long filament thermal non-woven fabric coating inorganic diatomite liquid wall material of claims 1 to 3, it is special
Levy and be, the wall material also includes non-woven cloth, the wall material includes basalis and described prepared by the inorganic cementitious material
Coat prepared by surface material is coated, the non-woven cloth is clipped between the basalis and coat as intermediate layer.
5. long filament thermal non-woven fabric coating inorganic diatomite liquid wall material according to claim 5, it is characterised in that
The non-woven cloth is polypropylene nonwoven.
6. the preparation side of any described long filament thermal non-woven fabric coating inorganic diatomite liquid wall material of claim 1 to 5
Method, it is characterised in that comprise the following steps:
Step 1:The inorganic adhesive is formulated as follows:
1) guar gum, natural plant gum, etherification starch, defoamer and dispersant are uniformly added successively in order according to the above ratio
It is added in 50 parts of deionized waters and the obtained solution A that stirs is standby;
2) 1 part of the sierozem power, diatomite, alumina silicate, convex rod soil, aluminium-magnesium silicate, kaolin and bentonite are pressed into above-mentioned ratio again
Example is added to 20 parts of ionized water high speeds and is uniformly dispersed successively in order, is then transferred to sand mill fineness of grind and reaches that 60-80 is micro-
It is standby that the metric system obtains B solution;
3) component A is added the B component filtrating test that stirs and obtains the finished product of inorganic adhesive;
Step 2:It is described to coat being formulated as follows for surface material;
1) it is the guar gum, natural plant gum, etherification starch, defoamer and dispersant 0.01 is equal successively in order according to the above ratio
It is even that to be added in 30 parts of deionized waters the obtained C solution that stirs standby;
2) by the sierozem power, coarse whiting, diatomite, alumina silicate, convex rod soil, aluminium-magnesium silicate, oyster shell whiting, kaolin, bentonite, vertical
Moral powder and anatase thpe white powder are added to 30 parts of deionized water high speeds and are uniformly dispersed successively in order according to the above ratio, Ran Houzhuan
Reach that 60-80 microns of obtained solution Ds are standby into sand mill eye fineness of grind;
3) component C is added the D components filtrating test that stirs and obtains coating the finished product of surface material.
7. the construction of the long filament thermal non-woven fabric coating inorganic diatomite liquid wall material of the preparation described in claim 6
Method, it is characterised in that comprise the following steps:
1) metope substrate is handled:Wall body metope wall body has been scraped into water-proof putty and brushing basement membrane, has made wall body wet after being disposed
Degree is less than 10%, pH is less than 10, wall body overall leveling, closely knit, clean without floating dust, without cracking hollowing;
2) brush the finished product twice of the inorganic adhesive in the metope substrate handled well, and by the non-woven cloth press from
Order left-to-right or from right to left is pasted, and after stickup is smooth, treats that non-woven cloth is fixed, the coated side before not being completely dried
The finished product of layer material, brushing twice are to obtain the long filament thermal non-woven fabric coating inorganic diatomite liquid wall material.