CN107200472A - H ZF62 optical glass and preparation method thereof - Google Patents
H ZF62 optical glass and preparation method thereof Download PDFInfo
- Publication number
- CN107200472A CN107200472A CN201710339673.3A CN201710339673A CN107200472A CN 107200472 A CN107200472 A CN 107200472A CN 201710339673 A CN201710339673 A CN 201710339673A CN 107200472 A CN107200472 A CN 107200472A
- Authority
- CN
- China
- Prior art keywords
- parts
- optical glass
- glass
- zno
- tio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of H ZF62 optical glass and preparation method thereof, the parts by weight of its chemical composition are:NaPO3:2.20~2.58 parts, Ba (PO3)2:18.28~18.65 parts, BaCO3:0.75~1.25 part, TiO2:4.95~5.35 parts, Nb2O5:43.80~45.35 parts, ZnO:0~1.00 part, Zn (NO3)2:0~3.00 part.Be free of in the H ZF62 optical glass of the present invention to environmental hazard very big PbO, As2O3, CdO, refractive index (nd) is 1.92279~1.92319, and Abbe number (Vd) is between 20.00~21.00, and its refractive index is high, meltdown property is good, it is easy to be molded, and optical constant is stable, uniformity is good, and cost is relatively low, can preferably meet the optical glass market demand.
Description
Technical field
The invention belongs to glass preparation field, and in particular to a kind of H-ZF62 optical glass and preparation method thereof.
Background technology
As environmental protection is increasingly subject to pay attention to, the production of glass, processing and using the influence to environment also increasingly by
To concern, the country such as China also puts into effect corresponding policy, calls Devoting Major Efforts To Developing without PbO, As2O3, CdO green and environment-friendlyglass glass.
Optical glass needs to have high index of refraction, low Abbe number, so as in special optical system design is carried out, can be achieved
Make up the purpose with correcting chromatic aberration;In addition, in addition it is also necessary to higher intensity and anti-wear performance, its service life could be extended,
Ensure product quality.And most of product of the prior art is often only focused on pursuing high index of refraction and ignoring optical glass need
Other to be possessed attribute.
At present, it is the H-ZF62 optical glass that 1.92286, Abbe number is 20.88 with refractive index (nd), contains Nb2O5、
Ta2O5、Bi2O3、GeO2Deng expensive composition, cause glass price higher, or contain PbO, As2O3, the environmental pollutants such as CdO,
Also part contains Li2The O and higher ZrO of price2Composition, this can not only make the easy crystallization of glass, and can increase glass into
This.
The content of the invention
In view of this, it is necessary to provide a kind of refractive index (nd) in 1.92279~1.92319, Abbe number (Vd) 20.00
Between~21.00, meltdown property is good, and refractive index is high, it is easy to the H-ZF62 optical glass of shaping.
A kind of H-ZF62 optical glass that the present invention is provided, the parts by weight of its chemical composition are:NaPO3:2.20~
2.58 parts, Ba (PO3)2:18.28~18.65 parts, BaCO3:0.75~1.25 part, TiO2:4.95~5.35 parts, Nb2O5:43.80
~45.35 parts, ZnO:0~1.00 part, Zn (NO3)2:0~3.00 part.
A kind of preparation method of H-ZF62 optical glass, it comprises the following steps:Each raw material is weighed by said ratio, fully
Added after well mixed in optical glass smelting furnace, the glass of this melting is poured into advance by fusing, clarification, stirring homogenizing, cooling
It is molded and anneals in preheated metal die, that is, obtains the optical glass.
The present invention has advantages below:
First, be free of in H-ZF62 optical glass of the invention to environmental hazard very big PbO, As2O3, CdO, and this production
The refractive index (nd) of product is that 1.92279~1.92319, Abbe number (Vd) is 20.00~21.00, possesses high index of refraction, low Abbe
Number, in special optical system design is carried out, can realize the purpose made up with correcting chromatic aberration;
Second, H-ZF62 optical glass meltdown properties of the invention are good, it is easy to be molded, and optical constant is stable, uniformity
Good, bubble, striped grade are excellent, simple production process, and yields is high;
3rd, expensive Ta is not contained in H-ZF62 optical glass of the invention2O5、Bi2O3、GeO2Composition, cost
It is relatively low, it can preferably meet the optical glass market demand.
Embodiment
With reference to specific embodiment, the present invention will be described in detail, and the description of this part is only exemplary and explained
Property, there should not be any restriction effect to protection scope of the present invention.
A kind of H-ZF62 optical glass that present embodiment is provided, the parts by weight of its chemical composition are:NaPO3:2.20
~2.58 parts, Ba (PO3)2:18.28~18.65 parts, BaCO3:0.75~1.25 part, TiO2:4.95~5.35 parts, Nb2O5:
43.80~45.35 parts, ZnO:0~1.00 part, Zn (NO3)2:0~3.00 part.
Preferably, the parts by weight of the H-ZF62 optical glass chemical composition are:NaPO3:2.29~2.31
Part, Ba (PO3)2:18.40~18.50 parts, BaCO3:0.85~1.03 part, TiO2:5.00~5.20 parts, Nb2O5:44.00~
44.50 part, ZnO:0~1.00 part, Zn (NO3)2:0~1.00 part.
BaO is optical glass network outer body in the present invention, and it can increase refractive index, density, glossiness and the chemistry of glass
Stability, BaO can effectively accelerate glass melting when content is relatively low, but content is too low, and the refractive index and Abbe number of glass can not
It is in required scope, and the meltdown property of glass is bad;But when content is excessive, clarification can be made secondary bubble, glass occur
The chemical stability of glass is deteriorated, and crystallization property can also be deteriorated.In the present invention, BaO is with Ba (PO3)2And BaCO3Two kinds of raw materials are introduced.
TiO in the present invention2The increase of glass network oxide content can be made, glass refraction and dispersion can be effectively improved, and
Stability, glass can be increased.But if TiO2Too high levels when, the degree of staining of glass can be poor, and crystallization property can also be deteriorated.
ZnO is with zinc oxygen octahedra [ZnO in the present invention6] as network modifying oxide, when the free oxygen in glass is enough
When, zinc oxygen tetrahedron [ZnO can be formed4] and then into the network structure of glass, glass structure is more stablized.ZnO can
Adjust the optical constant of glass, it is possible to decrease the optical glass high temperature viscosity coefficient of expansion, the chemical stability and heat for improving glass are steady
Qualitative and refractive index.If ZnO too high levels, glass has the danger of devitrification.In the present invention, ZnO is with ZnO and Zn (NO3)2For
Raw material is introduced.
Nb in the present invention2O5It is high index of refraction, the neccessary composition of high-dispersive optical glass, can effectively improves the change of glass
Learn stability and improve the devitrification resistance property of glass, improve the crystallization property of glass, when content is too low, it is to improving glass folding
Penetrate the DeGrain of rate and dispersion, and tendency towards devitrification increase, when its too high levels, the reduction of glass devitrification resistance property.
The specific raw material for 5 embodiments that 1 present invention of table is enumerated see and obtained optical glass each parameter (institute's total
According to be surveyed data after -4 DEG C/h annealing).
Table 1
Present embodiment also provides a kind of preparation method of H-ZF62 optical glass, and this method comprises the following steps:By upper
State proportioning and weigh each raw material, be sufficiently mixed in uniform rear addition optical glass smelting furnace, fusing, clarification, stirring are homogenized, cooled, will
The glass of this melting is poured into metal die preheated in advance and is molded and anneals, that is, obtains the optical glass.
The H-ZF62 optical glass environmental-protecting performances that the present invention is provided are excellent, refractive index (nd) 1.92279~1.92319,
Abbe number (Vd) is between 20.00~21.00.Optical constant is stable in actual production, and uniformity is good, bubble, striped grade
It is excellent;Simple production process, yields is high, and cost is relatively low, can preferably meet the optical glass market demand.
The embodiment of present invention described above, is not intended to limit the scope of the present invention..Any basis
Various other corresponding changes and deformation that the technical concept of the present invention is made, should be included in the guarantor of the claims in the present invention
In the range of shield.
Claims (6)
1. a kind of H-ZF62 optical glass, it is characterised in that:The parts by weight of its chemical composition are:NaPO3:2.20~2.58 parts,
Ba(PO3)2:18.28~18.65 parts, BaCO3:0.75~1.25 part, TiO2:4.95~5.35 parts, Nb2O5:43.80~45.35
Part, ZnO:0~1.00 part, Zn (NO3)2:0~3.00 part.
2. H-ZF62 optical glass according to claim 1, it is characterised in that:The parts by weight of its chemical composition are:
NaPO3:2.29~2.31 parts, Ba (PO3)2:18.40~18.50 parts, BaCO3:0.85~1.03 part, TiO2:5.00~5.20
Part, Nb2O5:44.00~44.50 parts, ZnO:0~1.00 part, Zn (NO3)2:0~1.00 part.
3. H-ZF62 optical glass according to claim 1, it is characterised in that:The parts by weight of its chemical composition are:
NaPO3:2.295 parts, Ba (PO3)2:18.46 part, BaCO3:0.9 part, TiO2:5.1 parts, Nb2O5:44.35 part, ZnO:0.5 part.
4. H-ZF62 optical glass according to claim 1, it is characterised in that:The parts by weight of its chemical composition are:
NaPO3:2.3 parts, Ba (PO3)2:18.45 part, BaCO3:0.9 part, TiO2:5.1 parts, Nb2O5:44.5 parts, Zn (NO3)2:0.5 part.
5. a kind of preparation method of H-ZF62 optical glass as claimed in claim 1, it is characterised in that:This method includes as follows
Step:Each raw material is weighed by proportioning, is sufficiently mixed in uniform rear addition optical glass smelting furnace, fusing, clarification, stirring are homogenized, dropped
Temperature, the glass of this melting is poured into metal die preheated in advance and is molded and anneals, that is, obtains required optical glass.
6. the preparation method of H-ZF62 optical glass according to claim 5, it is characterised in that:Described H-ZF62 optics
The refractive index (nd) of glass is 1.92279~1.92319, and Abbe number (Vd) is 20.00~21.00.