CN107189791A - 一种正负混合液晶组合物及其应用 - Google Patents
一种正负混合液晶组合物及其应用 Download PDFInfo
- Publication number
- CN107189791A CN107189791A CN201610146600.8A CN201610146600A CN107189791A CN 107189791 A CN107189791 A CN 107189791A CN 201610146600 A CN201610146600 A CN 201610146600A CN 107189791 A CN107189791 A CN 107189791A
- Authority
- CN
- China
- Prior art keywords
- formula
- lead
- compound representated
- liquid
- iii
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及液晶材料领域,具体涉及一种正负混合液晶组合物及其应用,所述组合物至少包含一种通式I所代表的化合物以及至少包含一种通式II的化合物。本发明所述液晶组合物具有低粘度、高电阻率、良好的低温互溶性、快的响应速度以及优异的透过率特性,可用于多种显示模式的快响应液晶显示。目前FFS和IPS已经成为最主流的显示模式,但FFS和IPS所存在的透过率低下的问题成为待解决的关键问题;通过实验发现,具有大的垂直介电的液晶组合物具有高的透过率,因此可以达到提升亮度且不增加电能消耗的问题。本发明所提供的液晶组合物具有大的垂直介电,可有效地提升液晶显示器的透过率特性,特别是在FFS和IPS显示模式的显示器中。
Description
技术领域
本发明属于液晶材料技术领域,具体涉及一种正负混合液晶组合物,以及其在液晶显示器中的应用。
背景技术
显示是把电信号(数据信息)转变为可视光(视觉信息)的过程,完成显示的设备即人机界面(Man-Machine Interface,MMI)。平板显示器(Flat panel Display,FPD)是目前最为流行的一类显示设备。液晶显示器(Liquid Crystal Display,LCD)是FPD中最早被开发出来,并被商品化的产品。目前,薄膜晶体管液晶显示器(Thin Film Transistor LiquidCrystal Display,TFT-LCD)已经成为LCD应用中的主流产品。
从工作原理讲,LCD这种显示器件是将背光源发出的光,藉由偏光片及液晶盒(液晶分子)等,产生相应于要显示图像的光的明暗(从而使颜色变化),由此实现人们可辨识的图像显示。也就是说,LCD的亮度决定于透过液晶盒的光的相对量(称其为液晶盒的透射率)、透过彩色滤光片的光的相对量(CF的透射率)以及背光源的亮度等诸多因素。
不同显示模式的引入使得液晶显示器(LCDs)的性能有了明显的提高,并且被更加广泛地应用于智能手机,显示器,便携平板电脑,电视等不同方面。这些应用对液晶显示器提出了更高的显示要求,比如高对比度,宽视角,快速响应和高穿透率。其中,在超高分辨率下由于像素尺寸的缩小导致开口率降低,所以高穿透率的显示显得尤为重要。
液晶的介电性质用介电常数ε来表示。与液晶指向矢平行的电场介电常数用ε//表示,与液晶指向矢垂直的电场介电常数用ε⊥表示,介电各向异性常数为Δε=ε//-ε⊥。若液晶分子极性基团永久偶极距的方向与分子长轴方向一致,液晶分子长轴方向的电子偏移度最大,这样,与分子长轴平行的方向上具有大的偶极距,介电各向异性为正,Δε>0,这样的液晶叫做正性液晶。若液晶分子极性基团永久偶极距的方向与分子长轴方向垂直,液晶分子短轴方向的电子偏移度最大,这样,与分子长轴垂直的方向上具有小的偶极距,介电各向异性为负,Δε<0这样的液晶叫做负性液晶。
目前在液晶显示市场,具有竞争力的显示模式主要有,面内切换(in-planeswitching,IPS),边缘场切换(fringe-field switching,FFS),和垂直排列(verticalalignment,VA)等显示模式。在这些显示模式中,垂直排列(VA)、面内切换(IPS)和边缘场切换(FFS)都具有宽视角的特点,但是VA显示器是典型的软屏显示器,不适用于触摸设备上,而IPS和FFS显示器具有非常好的硬屏特点,是用于触摸屏设备的最佳选择。
当正性液晶用于IPS/FFS显示模式时可以获得快速响应,并且有良好的可靠性;而负性液晶用于IPS/FFS显示模式时可以获得更高的透过率,但是由于负性液晶粘度较大,所以响应时间较慢。因此在传统正性液晶混合物中添加负性组分的Hybrid液晶应运而生,使其既具有正性液晶的快速响应优点,同时又可以获得穿透率的有效提升,进而可以大幅度降低液晶显示器件的整体功耗。
发明内容
本发明所要解决的技术问题在于提供一种正负混合的液晶组合物,该组合物用于IPS和FFS模式液晶显示器,将正性液晶化合物与负性液晶化合物组合成性能优异的液晶组合物,以提高显示器的透过率特性,降低液晶显示器的整体功耗。
为了解决以上问题,本发明所提出的液晶组合物包含至少一种通式I的化合物:
以及至少一种通式II的化合物:
其中,R1、R2、R3各自独立地代表C1~C12的直链烷基、烷氧基或C2~C12的直链烯基;n1、n2、n3各自独立地代表0或1;L1、L2各自独立地代表H或F;L3、L4各自独立地代表H或CH3,其中至少一个代表CH3;X代表F、CF3或OCF3;A1、A2、A3各自独立地代表:
其中A1、A2、A3中至少一个代表
A4、A5、A6各自独立地代表:
本发明所提供的通式I所代表的化合物为含有环己烯结构的2,3-二氟类化合物,该类化合物具有负的介电各向异性和低的旋转粘度性能。
具体地说,本发明所提供的通式I的化合物选自式I-A~式I-M中的一种或多种:
其中R1代表C1~C8的直链烷基或C2~C8的直链烯基,R2代表C1~C8的直链烷基或烷氧基。
优选地,本发明所提供的液晶化合物选自式I-A-1~式I-M-15中的一种或多种:
更优选地,本发明所提供的通式I的化合物选自式I-A-10、I-A-12、I-A-14、I-A-16、I-A-22、I-B-10、I-B-12、I-B-14、I-B-16、I-B-22、I-C-1、I-C-2、I-C-9~I-C-18、I-C-27、I-C-28、I-C-29、I-C-33、I-C-34、I-C-35、I-D-1、I-D-2、I-D-9~I-D-18、I-D-27、I-D-28、I-D-29、I-D-33、I-D-34、I-D-35、I-E-1、I-E-2、I-E-9~I-E-18、I-E-27、I-E-28、I-E-29、I-E-33、I-E-34、I-E-35、I-F-1、I-F-2、I-F-9~I-F-18、I-F-27、I-F-28、I-F-29、I-F-33、I-F-34、I-F-35、I-G-9~I-G-18、I-H-9~I-H-18、I-I-9~I-I-18、I-J-9~I-J-18、I-K-6、I-K-7、I-L-6、I-L-7、I-M-6、I-M-7中的一种或多种。
在本发明所涉及的各技术方案中,以任一液晶组合物为例(总质量均为100%),通式I所代表的化合物的含量范围以1%~60%为宜,优选3.5%~40%,合适的优选范围还进一步包括如3.5%~35%、3.5%~12%、5%~12%、4%~24%、4%~30%等。
本发明所提供的通式II的化合物为含有二氟甲氧基桥键的液晶化合物,该类化合物具有极大的正介电各向异性。
具体地说,本发明所提供的通式II的化合物选自式II-A~式II-Z所代表的一种或多种:
其中R3代表C2~C8的直链烷基。
优选地,本发明所提供的通式II的化合物选自式II-A-1~式II-Z-4中的一种或多种:
更优选地,本发明所提供的通式II的化合物选自式II-E-2、II-E-3、II-F-1、II-F-2、II-F-3、II-F-4、II-J-2、II-K-1、II-K-2、II-M-2、II-M-3、II-P-1、II-P-2中的一种或多种。
在本发明所涉及的各技术方案中,以任一液晶组合物为例(总质量均为100%),通式II所代表的化合物的含量范围以1%~60%为宜,优选5%~40%,合适的优选范围还进一步包括如10%~30%、20%~39%、5%~19.5%、5%~38%、8.5%~30%等。
本发明所提供的液晶组合物还包含一种或多种通式III所代表的化合物:
其中R4、R5各自独立地代表C1~C12的直链烷基、直链烷氧基或C2~C12的直链烯基,A7、A8各自独立地代表1,4-环己基或1,4-亚苯基。
具体地,本发明所提供的通式III的液晶化合物选自式III-A~式III-C中的一种或多种:
其中,R4代表C1~C8的直链烷基,R5代表C1~C8的直链烷基、直链烷氧基或C2~C8的直链烯基。
优选地,通式III所代表的化合物选自式III-A-1~式III-C-24中的一种或多种:
更优选地,通式III所代表的化合物选自式III-A-1~III-A-5、III-A-14、III-A-19、III-A-24、III-A-25、III-B-2、III-B-4、III-B-18、III-B-22、III-C-2、III-C-4、III-C-15、III-C-20中的一种或多种。
在本发明所涉及的各技术方案中,以任一液晶组合物为例(总质量均为100%),通式III所代表的化合物的含量范围以0%~80%为宜,优选其为必选组分,当其为必选组分时,合适的添加量为13%~60.5%,合适的优选范围还进一步包括如13%~41%、19%~48%、41%~60.5%、17%~60%、55%~60.5%、13%~48%等。
本发明所提供的液晶组合物还包含一种或多种通式IV所代表的化合物:
其中R6、R7各自独立地代表C1~C12的直链烷基、直链烷氧基或C2~C12的直链烯基,A9、代表1,4-环己基或1,4-亚苯基。
具体地,本发明所提供的通式IV的液晶化合物选自式IV-A或式IV-B中的一种或多种:
其中,R6代表C1~C8的直链烷基或C2~C8的直链烯基,R7代表C1~C8的直链烷基。
优选地,通式IV所代表的化合物选自式IV-A-1~式IV-B-28中的一种或多种:
更优选地,通式IV所代表的化合物选自式IV-A-1、IV-A-2、IV-A-6、IV-A-10、IV-A-17、IV-A-25、IV-B-1、IV-B-2、IV-B-6、IV-B-8、IV-B-17、IV-B-19中的一种或多种。
在本发明所涉及的各技术方案中,以任一液晶组合物为例(总质量均为100%),通式IV所代表的化合物的含量范围以0%~40%为宜,优选0%~30%(更优选0%~25.5%),当其添加量不为0时,合适的添加范围包括如12%~24%、2%~25.5%、13%~25.5%、4%~25.5%等。
本发明所提供的液晶组合物还包含一种或多种通式V所代表的化合物:
其中,R8代表C1~C12的直链烷基或C2~C12的直链烯基,L5、L6各自独立地代表H或F,Y代表F或OCF3,A11代表:
A10代表:
具体地,本发明所提供的通式V所代表的化合物选自式V-A~式V-Q中的一种或多种:
其中,R8代表C1~C8的直链烷基或C2~C8的直链烯基;优选C2~C5的直链烷基或直链烯基。
在本发明所涉及的各技术方案中,以任一液晶组合物为例(总质量均为100%),通式V所代表的化合物的含量范围以0%~42%为宜,优选0%~39%(更优选0%~22%或0~17%),当其添加量不为0时,合适的添加范围包括如2%~42%、4%~22%、8%~39%、5%~17%、5%~42%等。
本发明所提供地液晶组合物还包含一种或多种通式VI的化合物:
其中,R9代表C1~C12的直链烷基或C2~C12的直链烯基,R10代表F、C1~C12的直链烷基或C2~C12的直链烯基。
具体地,本发明所提供的通式VI的化合物选自式VI-A或式VI-B中的一种或多种:
其中,R9、R10各自独立地代表C1~C8的直链烷基或C2~C8的直链烯基;优选C1~C5的直链烷基或C2~C5的直链烯基。
在本发明所涉及的各技术方案中,以任一液晶组合物为例(总质量均为100%),通式VI所代表的化合物的含量范围以0%~13%为宜,优选0%~11%(更优选0%~25.5%),当其添加量不为0时,合适的添加范围包括如3%~13%、5%~11%、7%~13%等。
本发明所提供的液晶组合物还包含一种或多种通式VII所代表的化合物:
其中,R11、R12各自独立地代表C1~C12的直链烷基,L7、L8各自独立地代表H或F,A12代表反式1,4-环己基或1,4-亚苯基。
具体地,本发明所提供的通式VII的化合物选自式VII-A~式VII-C中的一种或多种:
其中,R11、R12各自独立地代表C1~C8的直链烷基;优选C2~C5的直链烷基。
在本发明所涉及的各技术方案中,以任一液晶组合物为例(总质量均为100%),通式VII所代表的化合物的含量范围以0%~15%为宜,优选0%~8%(更优选0%~7%),当其添加量不为0时,合适的添加范围包括如2%~15%、3%~8%、2%~7%、7%~15%等。
本发明所提供的液晶组合物还包含一种或多种通式VIII所代表的化合物:
其中,R13代表C1~C12的直链烷基,L9、L10各自独立地代表H或F,Z代表F或OCF3,A13、A14各自独立地代表:
具体地,本发明所提供的通式VIII所代表的化合物选自式VIII-A~式VIII-L中的一种或多种:
其中,R13代表C1~C8的直链烷基;优选C2~C5的直链烷基。
在本发明所涉及的各技术方案中,以任一液晶组合物为例(总质量均为100%),通式VIII所代表的化合物的含量范围以0%~19%为宜,优选0%~14%(更优选0%~13%),当其添加量不为0时,合适的添加范围包括如1%~19%、3%~13%、5%~18%、1%~14%等。
此外,在本发明所涉及的各技术方案中,以任一液晶组合物为例(总质量均为100%),通式V~VIII所代表的化合物的总含量范围以0%~80%为宜,当其添加量不为0时,合适的添加范围包括如1%~60%、3%~55%、3%~37%、3%~47%、3%~55%、4%~35%、14%~55%、3%~41%、3%~14%、3%~25%等。
就整体配方而言,本发明所提供的液晶组合物,包含以下重量百分比的组分:
1)、1%~60%的一种或多种通式(I)所代表的化合物;
2)、1%~60%的一种或多种通式(II)所代表的化合物;
3)、0%~80%的一种或多种通式(III)所代表的化合物;
4)、0%~40%的一种或多种通式(IV)所代表的化合物;
5)、0%~80%的一种或多种通式(V)~通式(VIII)所代表的化合物。
或本发明所提供的液晶组合物,包含以下重量百分比的组分:
1)、3.5%~35%的一种或多种通式(I)所代表的化合物;
2)、5%~39%的一种或多种通式(II)所代表的化合物;
3)、13%~60.5%的一种或多种通式(III)所代表的化合物;
4)、0%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、0%~42%的一种或多种通式(V)所代表的化合物;
6)、0%~13%的一种或多种通式(VI)所代表的化合物;
7)、0%~15%的一种或多种通式(VII)所代表的化合物
8)、0%~19%的一种或多种通式(VIII)所代表的化合物。
优选地,本发明所提供的液晶组合物,包含以下重量百分比的组分:
1)、1%~12%的一种或多种通式(I)所代表的化合物;
2)、2%~50%的一种或多种通式(II)所代表的化合物;
3)、10%~70%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~60%的一种或多种通式(V)~通式(VIII)所代表的化合物。
或:
1)、13%~40%的一种或多种通式(I)所代表的化合物;
2)、5%~40%的一种或多种通式(II)所代表的化合物;
3)、10%~50%的一种或多种通式(III)所代表的化合物;
4)、10%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~40%的一种或多种通式(V)~通式(VIII)所代表的化合物。
更优选地,本发明所提供的液晶组合物,包含以下重量百分比的组分:
1)、3.5%~12%的一种或多种通式(I)所代表的化合物;
2)、5%~39%的一种或多种通式(II)所代表的化合物;
3)、17%~60.5%的一种或多种通式(III)所代表的化合物;
4)、0%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、4%~55%的一种或多种通式(V)~通式(VIII)所代表的化合物。
或:
1)、13%~35%的一种或多种通式(I)所代表的化合物;
2)、10%~30%的一种或多种通式(II)所代表的化合物;
3)、13%~41%的一种或多种通式(III)所代表的化合物;
4)、12%~24%的一种或多种通式(IV)所代表的化合物;
5)、0%~22%的一种或多种通式(V)所代表的化合物;
5)、3%~15%的一种或多种通式(VII)和/或通式(VIII)所代表的化合物。
优选地,本发明所提供的液晶组合物,包含以下重量百分比的组分:
1)、2%~40%的一种或多种通式(I)所代表的化合物;
2)、3%~19.5%的一种或多种通式(II)所代表的化合物;
3)、10%~65%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~60%的一种或多种通式(V)~通式(VIII)所代表的化合物。
或:
1)、2%~30%的一种或多种通式(I)所代表的化合物;
2)、20%~45%的一种或多种通式(II)所代表的化合物;
3)、15%~55%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~55%的一种或多种通式(V)~通式(VIII)所代表的化合物。
更优选地,本发明所提供的液晶组合物,包含以下重量百分比的组分:
1)、3.5%~35%的一种或多种通式(I)所代表的化合物;
2)、5%~19.5%的一种或多种通式(II)所代表的化合物;
3)、13%~60.5%的一种或多种通式(III)所代表的化合物;
4)、0%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、3%~55%的一种或多种通式(V)~通式(VIII)所代表的化合物。
或:
1)、4%~24%的一种或多种通式(I)所代表的化合物;
2)、20%~39%的一种或多种通式(II)所代表的化合物;
3)、19%~48%的一种或多种通式(III)所代表的化合物;
4)、0%~25%的一种或多种通式(IV)所代表的化合物;
5)、3%~47%的一种或多种通式(V)~通式(VIII)所代表的化合物。
优选地,本发明所提供的液晶组合物,包含以下重量百分比的组分:
1)、2%~40%的一种或多种通式(I)所代表的化合物;
2)、3%~45%的一种或多种通式(II)所代表的化合物;
3)、10%~40%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~60%的一种或多种通式(V)~通式(VIII)所代表的化合物。
或:
1)、3%~35%的一种或多种通式(I)所代表的化合物;
2)、3%~45%的一种或多种通式(II)所代表的化合物;
3)、41%~70%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、3%~40%的一种或多种通式(V)~通式(VIII)所代表的化合物。
更优选地,本发明所提供的液晶组合物,包含以下重量百分比的组分:
1)、3.5%~35%的一种或多种通式(I)所代表的化合物;
2)、5%~39%的一种或多种通式(II)所代表的化合物;
3)、13%~40%的一种或多种通式(III)所代表的化合物;
4)、0%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、3%~55%的一种或多种通式(V)~通式(VIII)所代表的化合物。
或:
1)、4%~30%的一种或多种通式(I)所代表的化合物;
2)、5%~38%的一种或多种通式(II)所代表的化合物;
3)、41%~60.5%的一种或多种通式(III)所代表的化合物;
4)、0%~24%的一种或多种通式(IV)所代表的化合物;
5)、4%~35%的一种或多种通式(V)~通式(VIII)所代表的化合物。
优选地,本发明所提供的液晶组合物,包含以下重量百分比的组分:
1)、2%~40%的一种或多种通式(I)所代表的化合物;
2)、3%~45%的一种或多种通式(II)所代表的化合物;
3)、10%~70%的一种或多种通式(III)所代表的化合物;
4)、1%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~45%的一种或多种通式(V)~通式(VIII)所代表的化合物。
或:
1)、3%~15%的一种或多种通式(I)所代表的化合物;
2)、2%~45%的一种或多种通式(II)所代表的化合物;
3)、10%~70%的一种或多种通式(III)所代表的化合物;
4)、10%~60%的一种或多种通式(V)~通式(VIII)所代表的化合物。
更优选地,本发明所提供的液晶组合物,包含以下重量百分比的组分:
1)、3.5%~35%的一种或多种通式(I)所代表的化合物;
2)、5%~39%的一种或多种通式(II)所代表的化合物;
3)、13%~60.5%的一种或多种通式(III)所代表的化合物;
4)、2%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、3%~41%的一种或多种通式(V)~通式(VIII)所代表的化合物。
或:
1)、5%~12%的一种或多种通式(I)所代表的化合物;
2)、5%~38%的一种或多种通式(II)所代表的化合物;
3)、17%~60%的一种或多种通式(III)所代表的化合物;
4)、14%~55%的一种或多种通式(V)~通式(VIII)所代表的化合物。
最优选,本发明所提供的液晶组合物,由以下重量百分比的组分组成:
1)、4%~24%的一种或多种通式(I)所代表的化合物;
2)、8.5%~30%的一种或多种通式(II)所代表的化合物;
3)、35%~60.5%的一种或多种通式(III)所代表的化合物;
4)、13%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、3%~14%的一种或多种通式(VI)和/或通式(VII)所代表的化合物。
优选地,本发明所提供的液晶组合物,包含以下重量百分比的组分:
1)、2%~40%的一种或多种通式(I)所代表的化合物;
2)、3%~45%的一种或多种通式(II)所代表的化合物;
3)、10%~50%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~45%的一种或多种通式(V)所代表的化合物;
5)、0%~25%的一种或多种通式(VI)~通式(VIII)所代表的化合物。
或:
1)、3%~30%的一种或多种通式(I)所代表的化合物;
2)、3%~45%的一种或多种通式(II)所代表的化合物;
3)、30%~70%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、2%~30%的一种或多种通式(VI)~通式(VIII)所代表的化合物。
更优选地,本发明所提供的液晶组合物,包含以下重量百分比的组分:
1)、3.5%~35%的一种或多种通式(I)所代表的化合物;
2)、5%~39%的一种或多种通式(II)所代表的化合物;
3)、13%~48%的一种或多种通式(III)所代表的化合物;
4)、0%~24%的一种或多种通式(IV)所代表的化合物;
5)、2%~42%的一种或多种通式(V)所代表的化合物;
5)、0%~21%的一种或多种通式(VI)~通式(VIII)所代表的化合物。
或:
1)、4%~24%的一种或多种通式(I)所代表的化合物;
2)、5%~38%的一种或多种通式(II)所代表的化合物;
3)、35%~60.5%的一种或多种通式(III)所代表的化合物;
4)、0%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、3%~25%的一种或多种通式(VI)~通式(VIII)所代表的化合物。
此外,上述液晶组合物中(每一配方),各组分的质量百分比总和均为100%。
本发明所提供的液晶组合物中,通式I所代表的化合物具有介电各向异性为负(‐Δε),因此具有大的垂直介电常数(ε⊥),可有下提升液晶组合物的垂直介电常数。
本发明所提供的II类结构化合物具有大的正介电各向异性(+Δε),并且具有优异的互溶性优点,对于提升液晶组合物的介电各向异性非常有效。
本发明所提供的III类通式所代表的两环结构化合物为非极性组分。此类化合物对于降低体系的粘度、提高响应速度作用显著,是调配快速响应的液晶混合物必不可少的一类化合物。
本发明所提供的IV类通式所代表的化合物为三环非极性结构,其具有大的弹性常数(K11、K22、K33)和低的旋转粘度,对于提升液晶组合物的弹性常数有明显效果。
本发明所提供的V类通式所代表的化合物为三环极性结构,具有较大的极性,其互溶性良好,有利于改善强极性的I类和非极性单体的相溶性问题。
本发明所提供的VI类通式所代表的化合物为三联苯结构,具有大的光学各向异性,可有效提升液晶组合物的光学各向异性。
本发明所提供的VII类通式所代表的化合物为四环结构,具有大的光学各向异性和高的清亮点性能,对于提升组合物的清亮点和光学各向异性有显著效果。
本发明所提供的VIII类通式所代表的化合物为四环极性,具有较大的极性和高的清亮点,对于提升液晶组合物的清亮点具有显著效果。
正介电各向异性液晶组合物添加负介电各向异性成分增加显示效果最早见于中国专利CN103320142中,本发明所提供的第I类化合物为含有2-甲基-3,4,5-三氟苯基和二氟甲氧基(-CF2O-)的化合物,该结构的化合物具有大的介电各向异性,其二位的甲基为斥电子基团,可有效地增加该化合物的介电各向异性,其中I-C类单晶为含有双氧杂环的液晶化合物,该结构具有大的垂直介电,也是提升液晶组合物垂直介电的方法之一。
本发明所述液晶组合物的制备方法无特殊限制,可采用常规方法将两种或多种化合物混合进行生产,如通过在高温下混合不同组分并彼此溶解的方法制备,其中,将液晶组合物溶解在用于该化合物的溶剂中并混合,然后在减压下蒸馏出该溶剂;或者本发明所述液晶组合物可按照常规的方法制备,如将其中含量较小的组分在较高的温度下溶解在含量较大的主要组分中,或将各所属组分在有机溶剂中溶解,如丙酮、氯仿或甲醇等,然后将溶液混合去除溶剂后得到。
本发明同时提供了上述液晶组合物在液晶显示装置中的应用,本发明所述液晶组合物具有低粘度、高电阻率、良好的低温互溶性、快的响应速度以及优异的透过率特性,可用于多种显示模式的快响应液晶显示。目前FFS和IPS已经成为最主流的显示模式,但FFS和IPS所存在的透过率低下的问题成为待解决的关键问题;器件厂家一般靠提升背光亮度来达到提升亮度的方法,但由此造成的电能消耗明显增加;通过实验发现,具有大的垂直介电的液晶组合物具有高的透过率,因此可以达到提升亮度且不增加电能消耗的问题。本发明所提供的液晶组合物具有大的垂直介电,可有效地提升液晶显示器的透过率特性,特别是在FFS和IPS显示模式的显示器中。
附图说明
图1为实施例7与对比例1的透过率特性对比图;
图2为实施例62与对比例2的透过率特性对比图。
具体实施方式
以下实施例用于说明本发明,但不用来限制本发明的范围。
本发明所用的所有液晶化合物都为已知化合物,均由八亿时空提供,也可以从其他来源市购购得。
本发明实施例中液晶组合物的制备均采用如下方法:
均匀液晶的制备采用业内普遍使用的热溶解方法,首先用天平按重量百分比称量液晶化合物,其中称量加入顺序无特定要求,通常以液晶化合物熔点由高到低的顺序依次称量混合,在60-100℃下加热搅拌使得各组分熔解均匀,再经过滤、旋蒸,最后封装即得目标样品。
除非另有说明,上下文中百分比为重量百分比,所有的温度以摄氏度给出。使用下述缩写:
Δn为光学各向异性(25℃),Δε为介电各向异性(25℃,1000Hz),ε⊥为垂直介电(25℃,1000Hz),Cp为液晶组合物的清亮点(℃),γ1为旋转粘度(25℃,mpa.s),K11、K22、K33分别为展曲、扭曲、弯曲弹性常数(25℃,pN)。
为了便于表示,以下实施例中,液晶化合物中基团结构用下表所示代码表示:
以如下结构为例:
该结构用上表所列代码表示,则表示为3APUQKF。
再如以下结构:
该结构用上表所列代码表示,则表示为4SGIWO1。
再如以下结构:
该结构用上表所列代码表示,则表示为VYPWO1。
实施例1:
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表1:
表1实施例1的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3SCWO2 | 10 | △n | 0.104 |
II | 3DUQKF | 15 | Δε | +8.8 |
II | 2DPUQKF | 6 | ε⊥ | 5.0 |
II | 3DPUQKF | 6 | γ1 | 70 |
III | 3CCV | 42 | Cp | 80 |
IV | VCCP1 | 9 | K11 | 10.8 |
VIII | 3CPGUOCF3 | 10 | K22 | 5.4 |
VIII | 3PPGUF | 2 | K33 | 13.2 |
实施例2
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表2:
表2实施例2的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3SCWO2 | 6 | △n | 0.101 |
II | 3CDUQKF | 13 | Δε | +12.0 |
II | 3PUQKF | 10 | ε⊥ | 6.0 |
II | 2APUQKF | 10 | γ1 | 90 |
II | 3APUQKF | 5 | Cp | 89 |
III | 3CCV | 42 | K11 | 11.8 |
VIII | 2CCPUF | 5 | K22 | 5.9 |
VIII | 3CCPUF | 5 | K33 | 15.5 |
VIII | 4CCPUF | 4 |
实施例3
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表3:
表3实施例3的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3CSWO2 | 5 | △n | 0.103 |
I | 2CYW1 | 5 | Δε | +11.0 |
II | 3CCQKF | 13 | ε⊥ | 5.5 |
II | 3PUQKF | 12 | γ1 | 116 |
II | 3APUQKF | 14 | Cp | 90 |
III | 3CCV | 24 | K11 | 12.6 |
IV | VCCP1 | 9 | K22 | 6.3 |
V | 3CCUF | 10 | K33 | 15.6 |
VIII | 2CCPUF | 4 | ||
VIII | 3CCPUF | 4 |
实施例4
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表4:
表4实施例4的液晶组合物中各组分的重量百分比及性能参数
实施例5
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表5:
表5实施例5的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2CYW1 | 9 | △n | 0.102 |
II | 3CCQKF | 19 | Δε | +9.0 |
III | 5CCV | 13 | ε⊥ | 5.1 |
III | 3CCV1 | 4 | Cp | 101 |
V | 2CCUF | 8 | γ1 | 112 |
V | 3CCUF | 8 | K11 | 13.6 |
V | 3CPUF | 23 | K22 | 6.8 |
VIII | 2CCPUF | 4 | K33 | 17.5 |
VIII | 3CCPUF | 4 | ||
VIII | 4CCPUF | 4 | ||
VIII | 5CCPUF | 4 |
实施例6
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表6:
表6实施例6的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3SCW1 | 10 | △n | 0.093 |
II | 3PUQKF | 5 | Δε | +3.0 |
III | 3CCV | 40 | ε⊥ | 3.8 |
III | 5CCV | 10 | Cp | 85 |
III | 2CC3 | 10 | γ1 | 55 |
VII | 4CPGP3 | 5 | K11 | 14.4 |
VII | 5CPGP2 | 5 | K22 | 7.2 |
VII | 5CPGP3 | 5 | K33 | 16.4 |
VIII | 3DPGUF | 10 |
实施例7
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表7:
表7实施例7的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3SCWO2 | 4 | △n | 0.099 |
II | 3PGUQKF | 8.5 | Δε | +2.6 |
III | 3CCV | 40 | ε⊥ | 2.8 |
III | 3CCV1 | 10 | Cp | 83 |
III | 5CCV1 | 5.5 | γ1 | 54 |
III | 5PP1 | 5 | K11 | 13.8 |
IV | VCCP1 | 12.5 | K22 | 6.9 |
IV | V2CCP1 | 5 | K33 | 16.4 |
VI | 2PGPF | 6.5 | ||
VI | 3PGPF | 3 |
实施例8
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所
得的液晶组合物的性能参数见表8:
表8实施例8的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2SWY3 | 10 | △n | 0.100 |
II | 3APUQKF | 10 | Δε | +7.5 |
II | 3PUQKF | 12 | ε⊥ | 4.4 |
III | 3CCV | 45 | Cp | 75 |
V | 3CCUF | 10 | γ1 | 60 |
VI | 2PGP5 | 4 | K11 | 10.8 |
VIII | 2CCPUF | 3 | K22 | 5.4 |
VIII | 3CCPUF | 3 | K33 | 12.4 |
VIII | 4CCPUF | 3 |
实施例9
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表9:
表9实施例9的液晶组合物中各组分的重量百分比及性能参数
实施例10
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表10:
表10实施例10的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2SCWO2 | 6 | △n | 0.102 |
II | 3PUQKF | 5 | Δε | +8.5 |
II | 3CCQKF | 15 | ε⊥ | 5.1 |
II | 2APUQKF | 5 | Cp | 101 |
II | 3DPUQKF | 9 | γ1 | 100 |
III | 3CCV | 34 | K11 | 13.6 |
III | 3CCV1 | 2 | K22 | 6.8 |
IV | VCCP1 | 2 | K33 | 18.5 |
V | 3CCUF | 10 | ||
VII | 3CPPC3 | 4 | ||
VIII | 3CCPUF | 4 | ||
VIII | 3CPGUOCF3 | 4 |
实施例11
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表11:
表11实施例11的液晶组合物中各组分的重量百分比及性能参数
该实施例所提供的组合物拥有快的响应时间,尤其表现在低温状态下,适合于快响应液晶显示装置。
实施例12
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表12:
表12实施例12的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3CYWO2 | 8 | △n | 0.097 |
II | 2APUQKF | 5 | Δε | +11.5 |
II | 3APUQKF | 8 | ε⊥ | 6.2 |
II | 3DCQKF | 13 | Cp | 91 |
III | 3CCV | 19 | γ1 | 129 |
V | VCCGF | 10 | K11 | 12.6 |
V | 2CCUF | 5 | K22 | 6.3 |
V | 3CCUF | 10 | K33 | 16.3 |
V | 5CCUF | 5 | ||
V | 3CPGF | 5 | ||
V | 5CPUF | 2 | ||
V | 3CGUF | 5 | ||
VIII | 3CCPUF | 5 |
实施例13
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表13:
表13实施例13的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2SCWO2 | 13 | △n | 0.105 |
II | 3CCQKF | 15 | Δε | +8.6 |
II | 3PUQKF | 15 | ε⊥ | 5.2 |
III | 3CCV | 24 | Cp | 100 |
IV | V2CCP1 | 10 | γ1 | 114 |
V | 3CPUF | 10 | K11 | 12.6 |
VIII | 2CCPUF | 4 | K22 | 6.3 |
VIII | 3CCPUF | 5 | K33 | 16.3 |
VIII | 4CCPUF | 4 |
实施例14
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表14:
表14实施例14的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2CYW1 | 6 | △n | 0.103 |
II | 3PUQKF | 8 | Δε | +6.5 |
III | 3CCV | 27 | ε⊥ | 4.6 |
III | 3CCV1 | 5 | Cp | 90 |
IV | VCCP1 | 13 | γ1 | 66 |
IV | V2CCP1 | 11 | K11 | 12.2 |
V | 3CCUF | 4 | K22 | 6.1 |
V | 3CPUF | 9 | K33 | 16.6 |
V | 3CGUF | 7 | ||
V | 2PGUF | 3 | ||
VIII | 3CCPUF | 7 |
实施例15
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表15:
表15实施例15的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2CCWO2 | 5 | △n | 0.101 |
II | 3PUQKF | 15 | Δε | +6.5 |
III | 3CCV | 36 | ε⊥ | 4.3 |
IV | VCCP1 | 10 | Cp | 90 |
IV | V2CCP1 | 10 | γ1 | 64 |
V | 3CPUF | 10 | K11 | 12.2 |
VIII | 2CCPUF | 4 | K22 | 6.1 |
VIII | 3CCPUF | 4 | K33 | 16.6 |
VIII | 4CCPUF | 4 | ||
VIII | 5CCPUF | 2 |
实施例16
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表16:
表16实施例16的液晶组合物中各组分的重量百分比及性能参数
实施例17
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表17:
表17实施例17的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3SPWO2 | 4.5 | △n | 0.100 |
II | 3PUQKF | 12 | Δε | +6.0 |
II | 2APUQKF | 5.5 | ε⊥ | 3.5 |
III | 3CCV | 42 | Cp | 93 |
III | 1PP2V | 3 | γ1 | 72 |
IV | 3CPP2 | 4 | K11 | 12.5 |
V | 2CCGF | 10 | K22 | 6.3 |
VIII | 2CCPGF | 5 | K33 | 16.4 |
VIII | 3CCPGF | 5 | ||
VIII | 4CCPGF | 5 | ||
VIII | 5CCPGF | 4 |
实施例18
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表18:
表18实施例18的液晶组合物中各组分的重量百分比及性能参数
实施例19
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表19:
表19实施例19的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3SCWO1 | 6 | △n | 0.104 |
II | 3DUQKF | 7 | Δε | 6.2 |
II | 4DUQKF | 7.5 | ε⊥ | 3.9 |
II | 4DPUQKF | 2 | Cp | 95 |
III | 3CCV | 38.5 | γ1 | 72 |
III | 1PP2V | 7 | K11 | 13.2 |
IV | VCCP3 | 9 | K22 | 6.6 |
V | 3CCGF | 4 | K33 | 16.7 |
VIII | 2CCPGF | 5 | ||
VIII | 3CCPGF | 5 | ||
VIII | 4CCPGF | 5 | ||
VIII | 5CCPGF | 4 |
实施例20
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表20:
表20实施例20的液晶组合物中各组分的重量百分比及性能参数
实施例21
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表21:
表21实施例21的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3CYWO2 | 6 | △n | 0.107 |
II | 3PUQKF | 12 | Δε | 6.5 |
II | 2APUQKF | 4 | ε⊥ | 3.6 |
II | 3APUQKF | 4 | Cp | 85 |
III | 3CCV | 33 | γ1 | 67 |
III | 3CCV1 | 8 | K11 | 12.7 |
III | 1PP2V1 | 5 | K22 | 6.4 |
IV | VCCP1 | 17 | K33 | 16.4 |
IV | V2CCP1 | 7 | ||
VI | 3PGP2V | 3 | ||
VIII | 3PPGUF | 1 |
实施例22
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表22:
表22实施例22的液晶组合物中各组分的重量百分比及性能参数
实施例23
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表23:
表23实施例23的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2YPWO1 | 5 | △n | 0.101 |
II | 3PGUQKF | 6 | Δε | +5.3 |
II | 3PUQKF | 10 | ε⊥ | 3.7 |
II | 4DPUQKF | 3 | Cp | 92 |
III | 3CCV | 40 | γ1 | 65 |
III | 3CCV1 | 5 | K11 | 13.6 |
IV | VCCP1 | 6 | K22 | 6.8 |
IV | 3CPP2 | 4 | K33 | 17.5 |
IV | 3CCP1 | 6 | ||
V | 3CCPOCF3 | 6 | ||
V | 5CCPOCF3 | 4 | ||
VI | 2PGPF | 5 |
实施例24
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表24:
表24实施例24的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2CSWO1 | 4.5 | △n | 0.103 |
II | 3PUQKF | 10.5 | Δε | +6.3 |
II | 2APUQKF | 8 | ε⊥ | 3.6 |
II | 3APUQKF | 7 | Cp | 93 |
III | 3CCV | 45 | γ1 | 68 |
IV | 3CCP1 | 5 | K11 | 13.4 |
IV | 3CPP2 | 5 | K22 | 6.7 |
IV | VCCP1 | 10 | K33 | 16.3 |
VII | 3CPPC3 | 5 |
实施例25
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表25:
表25实施例25的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2SCWO1 | 5 | △n | 0.103 |
II | 3PUQKF | 10 | Δε | +6.4 |
II | 2APUQKF | 6 | ε⊥ | 3.5 |
II | 3APUQKF | 6 | Cp | 93 |
II | 4DPUQKF | 3 | γ1 | 68 |
III | 3CCV | 45 | K11 | 13.8 |
IV | 3CCP1 | 5 | K22 | 6.9 |
IV | 3CPP2 | 5 | K33 | 16.6 |
IV | VCCP1 | 10 | ||
VII | 3CPPC3 | 5 |
实施例26
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表26:
表26实施例26的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2SCW1 | 8 | △n | 0.102 |
II | 3PUQKF | 12 | Δε | +7.0 |
II | 2APUQKF | 5 | ε⊥ | 4.2 |
III | 5PP1 | 3 | Cp | 93 |
III | 3CCV | 34 | γ1 | 90 |
V | 3CPGF | 10 | K11 | 12.0 |
V | 3CCGF | 10 | K22 | 6.0 |
VIII | 2CCPGF | 5 | K33 | 15.5 |
VIII | 3CCPGF | 4 | ||
VIII | 4CCPGF | 5 | ||
VIII | 5CCPGF | 4 |
实施例27
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表27:
表27实施例27的液晶组合物中各组分的重量百分比及性能参数
实施例28
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表28:
表28实施例28的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3YCW1 | 8 | △n | 0.102 |
II | 3PUQKF | 11 | Δε | +6.3 |
II | 2APUQKF | 5 | ε⊥ | 3.8 |
III | 3CCV | 34 | Cp | 98 |
IV | 3CPP2 | 5 | γ1 | 84 |
IV | 3CCP1 | 4 | K11 | 13.5 |
V | 3CPGF | 9 | K22 | 6.8 |
V | 3CCGF | 12 | K33 | 16.4 |
VII | 3CPPC3 | 5 | ||
VIII | 3CCPGF | 3 | ||
VIII | 4CCPGF | 4 |
实施例29
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表29:
表29实施例29的液晶组合物中各组分的重量百分比及性能参数
实施例30
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表30:
表30实施例30的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3CYWO3 | 5 | △n | 0.099 |
II | 3PUQKF | 12 | Δε | +7.5 |
II | 2APUQKF | 8 | ε⊥ | 3.8 |
II | 3PGUQKF | 3 | Cp | 95 |
III | 3CCV | 36 | γ1 | 78 |
III | 3CCV1 | 5 | K11 | 13.0 |
IV | 3CPP2 | 4 | K22 | 6.5 |
V | 3CCGF | 7 | K33 | 16.4 |
V | 3CCPOCF3 | 6 | ||
VIII | 2CCPGF | 4 | ||
VIII | 3CCPGF | 5 | ||
VIII | 4CCPGF | 5 |
实施例31
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表31:
表31实施例31的液晶组合物中各组分的重量百分比及性能参数
实施例32
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表32:
表32实施例32的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3SPWO2 | 2 | △n | 0.100 |
I | 3SWO2 | 2 | Δε | 7.7 |
II | 3PUQKF | 10 | ε⊥ | 3.7 |
II | 2APUQKF | 8 | Cp | 92 |
II | 3APUQKF | 7 | γ1 | 79 |
II | 4DUQKF | 2 | K11 | 13.4 |
II | 4DPUQKF | 3 | K22 | 6.7 |
III | 3CCV | 41 | K33 | 15.8 |
IV | 3CCP1 | 6 | ||
IV | VCCP1 | 11 | ||
VII | 3CPPC3 | 5 | ||
VII | 3CGPC3 | 3 |
实施例33
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表33:
表33实施例33的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3SCWO1 | 6 | △n | 0.103 |
II | 2APUQKF | 8 | Δε | 7.7 |
II | 3APUQKF | 7 | ε⊥ | 3.7 |
II | 4DUQKF | 2 | Cp | 93 |
II | 4DPUQKF | 3 | γ1 | 75 |
II | 3PUQKF | 10 | K11 | 13.6 |
III | 3CCV | 41 | K22 | 6.8 |
IV | VCCP1 | 10 | K33 | 15.9 |
IV | 3CPP2 | 8 | ||
VII | 3CPPC3 | 5 |
实施例34
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表34:
表34实施例34的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3YPW1 | 5 | △n | 0.111 |
II | 3PUQKF | 12 | Δε | 7.5 |
II | 2PGUQKF | 2.5 | ε⊥ | 4.0 |
II | 3PGUQKF | 8 | Cp | 75 |
III | 3CCV | 42 | γ1 | 62 |
III | 5PP1 | 6 | K11 | 11.0 |
V | 3CCGF | 5.5 | K22 | 5.5 |
VI | 2PGPF | 4 | K33 | 12.4 |
VI | 3PGPF | 4 | ||
VIII | 2CCPGF | 3 | ||
VIII | 3CCPGF | 4 | ||
VIII | 4CCPGF | 4 |
实施例35
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表35:
表35实施例35的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2YGIWO1 | 6 | △n | 0.110 |
II | 3PUQKF | 12 | Δε | 5.0 |
III | 3CCV | 41 | ε⊥ | 3.8 |
III | 5PP1 | 7 | Cp | 78 |
IV | 3CPP2 | 6 | γ1 | 55 |
V | 3CPGF | 7 | K11 | 12.2 |
V | 3CCGF | 4 | K22 | 6.1 |
VI | 2PGPF | 7 | K33 | 12.7 |
VIII | 2CCPGF | 3 | ||
VIII | 3CCPGF | 3 | ||
VIII | 4CCPGF | 4 |
实施例36
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表36:
表36实施例36的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2YCW1 | 6 | △n | 0.109 |
II | 3PUQKF | 10 | Δε | 6.4 |
II | 3DUQKF | 5 | ε⊥ | 3.6 |
III | 3CCV | 36 | Cp | 92 |
IV | VCCP1 | 13 | γ1 | 77 |
IV | V2CCP1 | 6 | K11 | 13.4 |
V | 3DPUF | 10 | K22 | 6.7 |
VIII | 2CCPUF | 4 | K33 | 17.1 |
VIII | 3CCPUF | 4 | ||
VIII | 5CPGP3 | 6 |
实施例37
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表37:
表37实施例37的液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3SCWO2 | 5 | △n | 0.103 |
I | 2SCW1 | 5 | Δε | +11.0 |
II | 3APUQKF | 14 | ε⊥ | 5.9 |
II | 3CCQKF | 13 | γ1 | 120 |
II | 3PUQKF | 12 | Cp | 83 |
III | 3CCV | 24 | K11 | 12.6 |
IV | VCCP1 | 9 | K22 | 6.3 |
V | 3DGUF | 10 | K33 | 15.6 |
VIII | 2CCPUF | 4 | ||
VIII | 3CCPUF | 4 |
实施例38
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表38:
表38实施例38的液晶组合物中各组分的重量百分比及性能参数
实施例39
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表39:
表39实施例39液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2SCWO2 | 7 | △n | 0.103 |
II | 2APUQKF | 6 | Δε | +5.6 |
II | 4DPUQKF | 3 | ε⊥ | 3.6 |
II | 4DUQKF | 2 | γ1 | 70 |
II | 3PUQKF | 11.5 | Cp | 92 |
III | 3CCV | 41.5 | K11 | 13.8 |
IV | 3CPP1 | 5 | K22 | 6.9 |
IV | 3CPP2 | 7 | K33 | 17.5 |
IV | VCCP1 | 12 | ||
VII | 3CPPC3 | 5 |
实施例40
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表40:
表40实施例40液晶组合物中各组分的重量百分比及性能参数
实施例41
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表41:
表41实施例41液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3SCWO2 | 5 | △n | 0.111 |
II | 2APUQKF | 6 | Δε | +6.0 |
II | 4DPUQKF | 3 | ε⊥ | 3.8 |
II | 3PUQKF | 12.5 | γ1 | 58 |
III | 3CCV | 42 | Cp | 80 |
III | 5PP1 | 5 | K11 | 12.4 |
IV | 3CPP2 | 5 | K22 | 6.2 |
IV | 3CCP1 | 3.5 | K33 | 13.5 |
VI | 2PGPF | 6 | ||
VI | 3PGPF | 6 | ||
VII | 3CPPC3 | 4 | ||
VIII | 3CCPGF | 2 |
实施例42
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表42:
表42实施例42液晶组合物中各组分的重量百分比及性能参数
实施例43
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表43:
表43实施例43液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3SPWO2 | 8 | △n | 0.115 |
II | 3PUQKF | 12 | Δε | +6.4 |
II | 4DPUQKF | 3 | ε⊥ | 4.4 |
II | 3PGUQKF | 4.5 | γ1 | 65 |
III | 3CCV | 39 | Cp | 89 |
III | 5PP1 | 5 | K11 | 12.8 |
IV | 3CPP1 | 5 | K22 | 6.4 |
IV | 3CCP2 | 6.5 | K33 | 13.8 |
V | 3CPGF | 10 | ||
VIII | 2CCPGF | 3 | ||
VIII | 3CCPGF | 4 |
实施例44
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表44:
表44实施例44液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3CSWO3 | 4.5 | △n | 0.119 |
II | 2APUQKF | 7 | Δε | +6.3 |
II | 4DPUQKF | 3 | ε⊥ | 4.1 |
II | 3PUQKF | 12.5 | γ1 | 64 |
III | 3CCV | 39 | Cp | 85 |
III | 5PP1 | 6 | K11 | 12.5 |
IV | 3CPP2 | 7 | K22 | 6.3 |
VI | 2PGPF | 7 | K33 | 13.7 |
VI | 3PGPF | 6 | ||
VII | 3CPPC3 | 5 | ||
VIII | 3CCPGF | 3 |
实施例45
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表45:
表45实施例45液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2SCWO1 | 6 | △n | 0.1110 |
II | 3PUQKF | 10 | Δε | +7.5 |
II | 2APUQKF | 6 | ε⊥ | 3.7 |
II | 2PGUQKF | 4 | γ1 | 84 |
II | 4DPUQKF | 2 | Cp | 105 |
II | 3PGUQKF | 4 | K11 | 14.4 |
III | 3CCV | 40 | K22 | 7.2 |
III | 3CCV1 | 5 | K33 | 16.8 |
IV | 3CPP2 | 5 | ||
VII | 3CPPC3 | 5 | ||
VIII | 3CCPGF | 4 | ||
VIII | 4CCPGF | 5 | ||
VIII | 2CCPGF | 4 |
实施例46
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表46:
表46实施例46液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | V2YWO2 | 5 | △n | 0.106 |
II | 3PUQKF | 3 | Δε | +5.7 |
II | 2APUQKF | 6 | ε⊥ | 3.4 |
II | 2PGUQKF | 4 | γ1 | 75 |
II | 4DPUQKF | 2 | Cp | 102 |
II | 3PGUQKF | 5 | K11 | 14.6 |
III | 3CCV | 40 | K22 | 7.3 |
III | 3CCV1 | 6 | K33 | 17.1 |
IV | VCCP1 | 9 | ||
IV | 3CPP2 | 5 | ||
VII | 3CPPC3 | 5 | ||
VIII | 2CCPGF | 3 | ||
VIII | 3CCPGF | 3 | ||
VIII | 4CCPGF | 4 |
实施例47
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表47:
表47实施例47液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3CYW1 | 6 | △n | 0.086 |
II | 4DUQKF | 5 | Δε | +5.3 |
II | 2APUQKF | 4 | ε⊥ | 3.5 |
II | 4DPUQKF | 3 | γ1 | 67 |
II | 3PUQKF | 8 | Cp | 90 |
III | 3CCV | 38 | K11 | 13.4 |
III | 3CC2 | 4 | K22 | 6.7 |
IV | VCCP1 | 11 | K33 | 16.7 |
IV | V2CCP1 | 6 | ||
IV | 3CCP1 | 7 | ||
V | 3CCGF | 4 | ||
VII | 3CPPC3 | 4 |
实施例48
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表48:
表48实施例48液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3SWO2 | 3.5 | △n | 0.091 |
II | 2APUQKF | 4 | Δε | +5.3 |
II | 4DPUQKF | 3 | ε⊥ | 3.4 |
II | 4DUQKF | 3.5 | γ1 | 71 |
II | 3PUQKF | 9 | Cp | 90 |
III | 3CCV | 38 | K11 | 13.2 |
IV | VCCP1 | 10 | K22 | 6.6 |
IV | V2CCP1 | 7 | K33 | 17.2 |
IV | 3CCP1 | 7 | ||
V | 3CPGF | 4 | ||
V | 3CCPOCF3 | 6 | ||
VII | 3CPPC3 | 5 |
实施例49
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表49:
表49实施例49液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3YCWO1 | 6 | △n | 0.097 |
II | 4DUQKF | 4 | Δε | +5.4 |
II | 2APUQKF | 4 | ε⊥ | 3.8 |
II | 4DPUQKF | 3 | γ1 | 74 |
II | 3PUQKF | 9 | Cp | 93 |
III | 3CCV | 30 | K11 | 13.7 |
III | 5PP1 | 5 | K22 | 6.9 |
III | 3CPO1 | 3 | K33 | 16.9 |
III | 3CC2 | 4 | ||
IV | VCCP1 | 11 | ||
IV | V2CCP1 | 6 | ||
IV | 3CCP1 | 7 | ||
VII | 3CPPC3 | 4 | ||
VIII | 3CCPGF | 4 |
实施例50
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表50:
表50实施例50液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3YWO4 | 4 | △n | 0.106 |
II | 4DUQKF | 4 | Δε | +5.8 |
II | 3PGUQKF | 4 | ε⊥ | 3.5 |
II | 4DPUQKF | 3 | γ1 | 72 |
II | 3PUQKF | 9.5 | Cp | 91 |
III | 3CCV | 26.5 | K11 | 14.2 |
III | 3CCV1 | 5 | K22 | 7.1 |
III | 5PP1 | 7 | K33 | 16.4 |
IV | VCCP1 | 10 | ||
IV | 3CCP1 | 6 | ||
IV | 3CPP2 | 7 | ||
V | 3CCPOCF3 | 6 | ||
VII | 3CPPC3 | 4 | ||
VIII | 3CCPGF | 4 |
实施例51
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表51:
表51实施例51液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2YPWO1 | 4 | △n | 0.112 |
II | 4DUQKF | 3 | Δε | +5.6 |
II | 3PGUQKF | 5 | ε⊥ | 3.4 |
II | 4DPUQKF | 3 | γ1 | 74 |
II | 3PUQKF | 9 | Cp | 92 |
III | 3CCV | 31 | K11 | 14.0 |
III | 5PP1 | 7 | K22 | 7.0 |
III | 3CPO1 | 4 | K33 | 16.1 |
IV | VCCP1 | 11 | ||
IV | 3CCP1 | 6 | ||
IV | 3CPP2 | 7 | ||
VII | 3CPPC3 | 5 | ||
VIII | 3CCPGF | 5 |
实施例52
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表52:
表52实施例52液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2SGIWO2 | 5.5 | △n | 0.113 |
II | 3PGUQKG | 4.5 | Δε | 5.7 |
II | 4DPUQKF | 3 | ε⊥ | 3.7 |
II | 3PUQKF | 12 | γ1 | 70 |
III | 3CCV | 33 | Cp | 95 |
III | 5PP1 | 7 | K11 | 14.4 |
IV | VCCP1 | 9 | K22 | 7.2 |
IV | 3CPP2 | 8 | K33 | 16.1 |
IV | 3CCP1 | 5 | ||
V | 3CCPOCF3 | 5 | ||
VII | 3CPPC3 | 4 | ||
VIII | 3CCPGF | 4 |
实施例53
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表53:
表53实施例53液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3CSW1 | 6 | △n | 0.123 |
II | 3PGUQKG | 4.5 | Δε | 5.5 |
II | 4DPUQKF | 3 | ε⊥ | 3.5 |
II | 3PUQKF | 10 | γ1 | 71 |
III | 3CCV | 30 | Cp | 91 |
III | 5PP1 | 7 | K11 | 14.2 |
IV | VCCP1 | 12 | K22 | 7.1 |
IV | V2CCP1 | 6 | K33 | 15.7 |
IV | 3CPP2 | 2.5 | ||
IV | 3CCP1 | 5 | ||
VI | 2PGPF | 5 | ||
VI | 3PGPF | 5 | ||
VII | 3CPPC3 | 4 |
实施例54
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表54:
表54实施例54液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3SCWO2 | 5 | △n | 0.127 |
II | 3PGUQKG | 5 | Δε | 5.4 |
II | 4DPUQKF | 3 | ε⊥ | 3.7 |
II | 3PUQKF | 10 | γ1 | 73 |
III | 3CCV | 30 | Cp | 95 |
III | 5PP1 | 7 | K11 | 13.8 |
IV | VCCP1 | 12 | K22 | 6.9 |
IV | 3CPP2 | 7 | K33 | 16.3 |
V | 3CPGF | 5 | ||
VI | 2PGPF | 6 | ||
VI | 3PGPF | 5 | ||
VII | 3CPPC3 | 5 |
实施例55
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表55:
表55实施例55液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2SPWO2 | 7 | △n | 0.110 |
I | 2SPW1 | 8 | Δε | +4.0 |
I | 3YWO2 | 5 | ε⊥ | 5.3 |
I | 3SWO2 | 5 | γ1 | 72 |
I | 2CYWO1 | 10 | Cp | 85 |
II | 3PUQKF | 4.5 | K11 | 12.8 |
II | 4DUQKF | 1.5 | K22 | 6.4 |
II | 3PGUQKF | 2.5 | K33 | 15.3 |
II | 4DPUQKF | 1.5 | ||
III | 3CCV | 29 | ||
III | 5PP1 | 5 | ||
III | 3CPO1 | 2 | ||
IV | VCCP1 | 5.5 | ||
IV | 3CCP1 | 3 | ||
IV | 3CPP2 | 3.5 | ||
V | 3CPGF | 2 | ||
VII | 3CPPC3 | 2 | ||
VIII | 3CCPGF | 3 |
实施例56
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表56:
表56实施例56液晶组合物中各组分的重量百分比及性能参数
实施例57
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表57:
表57实施例57液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2YGIWO2 | 6 | △n | 0.099 |
II | 4DUQKF | 5 | Δε | +6.5 |
III | 3CCV | 30 | ε⊥ | 4.6 |
III | 2CCV1 | 5 | γ1 | 72 |
IV | VCCP1 | 13 | Cp | 86 |
IV | V2CCP1 | 11 | K11 | 12.6 |
V | 2PGUF | 3 | K22 | 6.3 |
V | 3DCUF | 4 | K33 | 15.8 |
V | 3DPUF | 9 | ||
V | 3DGUF | 7 | ||
VIII | 3CCPUF | 7 |
实施例58
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表58:
表58实施例58液晶组合物中各组分的重量百分比及性能参数
实施例59
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表59:
表59实施例59液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 3YPWO2 | 4 | △n | 0.101 |
I | 5YWO2 | 3 | Δε | 3.8 |
I | 2CYWO2 | 4 | ε⊥ | 4.5 |
I | 3YWO2 | 4 | γ1 | 70 |
II | 3PUQKF | 9 | Cp | 90 |
II | 4DUQKF | 1.5 | K11 | 13.6 |
II | 3APUQKF | 4.5 | K22 | 6.8 |
II | 4DPUQKF | 3 | K33 | 15.6 |
III | 3CCV | 35 | ||
III | 1PP2V | 5 | ||
IV | VCCP1 | 9 | ||
IV | V2CCP1 | 4.5 | ||
IV | 3CPP2 | 6 | ||
IV | 3CCP1 | 4.5 | ||
VII | 3CPPC3 | 3 |
实施例60
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表60:
表60实施例60液晶组合物中各组分的重量百分比及性能参数
实施例61
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表61:
表61实施例61液晶组合物中各组分的重量百分比及性能参数
类别 | 组分 | 重量百分比(%) | 性能参数 | 参数值 |
I | 2SPWO2 | 6 | △n | 0.105 |
I | 3SPWO2 | 6 | Δε | 2.2 |
II | 3PGUQKF | 4.7 | ε⊥ | 3.5 |
II | 3PUQKF | 4 | γ1 | 55 |
III | 3CCV | 40 | Cp | 75 |
III | 3CCV1 | 12 | K11 | 12.5 |
III | 5PP1 | 6 | K22 | 6.3 |
IV | VCCP1 | 13 | K33 | 14.3 |
VI | 2PGPF | 6.3 | ||
VI | 3PGPF | 2 |
实施例62
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表62:
表62实施例62液晶组合物中各组分的重量百分比及性能参数
对比例1
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表63:
表63对比例1的液晶组合物中各组分的重量百分比及性能参数
组分 | 重量百分比(%) | 性能参数 | 参数值 |
3PGUQUF | 6.5 | △n | 0.098 |
3APUQUF | 5 | Δε | +2.6 |
3CCV | 40 | ε⊥ | 2.6 |
3CCV1 | 12 | γ1 | 52 |
1V2PP1 | 7 | Cp | 80 |
VCCP1 | 13 | K11 | 13.6 |
V2CCP1 | 12 | K22 | 6.8 |
2PGP3 | 4 | K33 | 16.2 |
3PPGUF | 0.5 |
对比实施例7与对比例1,其参数如表64:
表64对比例1与实施例7性能参数
项目 | 对比例1 | 实施例7 |
△n | 0.098 | 0.099 |
Δε | +2.6 | +2.6 |
ε⊥ | 2.6 | 2.8 |
Cp | 80 | 83 |
γ1 | 52 | 54 |
K11 | 13.6 | 13.8 |
K22 | 6.8 | 6.9 |
K33 | 16.2 | 16.4 |
经对比可知,实施例7的垂直介电相对于对比例1提升10%左右,可有效提升液晶显示器的透过率特性,起透过率提升3%左右,其光学数据如表65:
表65对比例1与实施例7的色坐标及透过率测试结果
项目 | 对比例1 | 实施例7 |
色温 | 7901 | 7554 |
亮度 | 24.18 | 24.99 |
x | 0.2947 | 0.2984 |
y | 0.3105 | 0.3145 |
其透过率特性对比图见图1。
对比例2
取以下重量百分比的液晶化合物并以本发明中所述方法配制液晶组合物,具体配比及所得的液晶组合物的性能参数见表66:
表66对比例2的液晶组合物中各组分的重量百分比及性能参数
组分 | 重量百分比(%) | 性能参数 | 参数值 |
3PGUQUF | 8 | △n | 0.104 |
3CCV | 40 | Δε | +2.6 |
3CCV1 | 12 | ε⊥ | 2.6 |
1PP2V1 | 7 | γ1 | 76 |
2PGPF | 6 | Cp | 51 |
3PGPF | 4 | K11 | 13.6 |
VCCP1 | 10 | K22 | 6.8 |
V2CCP1 | 10 | K33 | 16.2 |
3CPP2 | 3 |
对比实施例62与对比例2,其参数如表67:
表67对比例2与实施例62性能参数
项目 | 对比例2 | 实施例62 |
△n | 0.104 | 0.104 |
Δε | +2.6 | 2.5 |
ε⊥ | 2.6 | 3.5 |
Cp | 76 | 75 |
γ1 | 51 | 56 |
K11 | 13.6 | 12.5 |
K22 | 6.8 | 6.3 |
K33 | 16.2 | 14.4 |
经对比可知,实施例62的垂直介电相对于对比例2提升30%左右,可有效提升液晶显示器的透过率特性,起透过率提升6%左右,其光学数据如表68:
表68对比例2与实施例62的色坐标及透过率测试结果
项目 | 对比例2 | 实施例62 |
色温 | 6421.00 | 6167 |
亮度 | 27.16 | 28.67 |
x | 0.3140 | 0.3188 |
y | 0.3304 | 0.3318 |
其透过率特性对比图见图2。
发明所提出的组合物具有大的垂直介电,可有效地提升液晶显示器的透过率特性,具体实现方式为添加第II类化合物提升液晶组合物的平行介电,添加第I类具有负介电各向异性的化合物增加组合物的垂直介电,利用第III类化合物降低液晶组合物的旋转粘度,以此达到具有快相应和高透过率的液晶组合物,本发明所提供的液晶组合物使用于IPS和FFS型液晶显示器。
虽然,上文中已经用一般性说明及具体实施方案对本发明作了详尽的描述,但在本发明基础上,可以对之作一些修改或改进,这对本领域技术人员而言是显而易见的。因此,在不偏离本发明精神的基础上所做的这些修改或改进,均属于本发明要求保护的范围。
Claims (10)
1.一种正负混合液晶组合物,其特征在于:所述组合物包含至少一种通式I的化合物:
以及至少一种通式II的化合物:
其中,R1、R2、R3各自独立地代表C1~C12的直链烷基、烷氧基或C2~C12的直链烯基;n1、n2、n3各自独立地代表0或1;L1、L2各自独立地代表H或F;L3、L4各自独立地代表H或CH3,其中至少一个代表CH3;X代表F、CF3或OCF3;A1、A2、A3各自独立地代表:
其中A1、A2、A3中至少一个代表
A4、A5、A6各自独立地代表:
2.根据权利要求1所述的液晶组合物,其特征在于:通式I所代表的化合物选自下式中所代表的化合物的一种或几种:
其中R1代表C1~C8的直链烷基或C2~C8的直链烯基,R2代表C1~C8的直链烷基或烷氧基;
优选地,通式I所代表的化合物选自式I-A-1~式I-M-15中的一种或多种:
更优选地,通式I所代表的化合物选自式I-A-10、I-A-12、I-A-14、I-A-16、I-A-22、I-B-10、I-B-12、I-B-14、I-B-16、I-B-22、I-C-1、I-C-2、I-C-9~I-C-18、I-C-27、I-C-28、I-C-29、I-C-33、I-C-34、I-C-35、I-D-1、I-D-2、I-D-9~I-D-18、I-D-27、I-D-28、I-D-29、I-D-33、I-D-34、I-D-35、I-E-1、I-E-2、I-E-9~I-E-18、I-E-27、I-E-28、I-E-29、I-E-33、I-E-34、I-E-35、I-F-1、I-F-2、I-F-9~I-F-18、I-F-27、I-F-28、I-F-29、I-F-33、I-F-34、I-F-35、I-G-9~I-G-18、I-H-9~I-H-18、I-I-9~I-I-18、I-J-9~I-J-18、I-K-6、I-K-7、I-L-6、I-L-7、I-M-6、I-M-7中的一种或多种。
3.根据权利要求1所述的液晶组合物,其特征在于:所述通式II所代表的化合物选自式II-A~式II-Z所代表的一种或多种:
其中R3代表C2~C8的直链烷基;
优选地,通式II所代表的化合物选自式II-A-1~式II-Z-4中的一种或多种:
更优选地,通式II所代表的化合物选自选自式II-E-2、II-E-3、II-F-1、II-F-2、II-F-3、II-F-4、II-J-2、II-K-1、II-K-2、II-M-2、II-M-3、II-P-1、II-P-2中的一种或多种。
4.根据权利要求1-3任一项所述的液晶组合物,其特征在于:所述液晶组合物还包含一种或多种选自通式III结构的化合物:
其中R4、R5各自独立地代表C1~C12的直链烷基、直链烷氧基或C2~C12的直链烯基,A7、A8各自独立地代表1,4-环己基或1,4-亚苯基;
优选通式III所代表的化合物选自式III-A~式III-C中的一种或多种:
其中,R4代表C1~C8的直链烷基,R5代表C1~C8的直链烷基、直链烷氧基或C2~C8的直链烯基;
更优选地,通式III所代表化合物选自式III-A-1~式III-C-24中的一种或多种:
更优选地,通式III所代表的化合物选自式III-A-1~III-A-5、III-A-14、III-A-19、III-A-24、III-A-25、III-B-2、III-B-4、III-B-18、III-B-22、III-C-2、III-C-4、III-C-15、III-C-20中的一种或多种。
5.根据权利要求1-4任一项所述的液晶组合物,其特征在于:所述液晶组合物还包含一种或多种选自通式IV的化合物:
其中R6、R7各自独立地代表C1~C12的直链烷基、直链烷氧基或C2~C12的直链烯基,A9代表1,4-环己基或1,4-亚苯基;
优选通式IV所代表的化合物选自式IV-A或式IV-B中的一种或多种:
其中,R6代表C1~C8的直链烷基或C2~C8的直链烯基,R7代表C1~C8的直链烷基;
更优选通式IV的化合物选自式IV-A-1~式IV-B-28中的一种或多种:
更优选地,通式III所代表的化合物选自式IV-A-1、IV-A-2、IV-A-6、IV-A-10、IV-A-17、IV-A-25、IV-B-1、IV-B-2、IV-B-6、IV-B-8、IV-B-17、IV-B-19中的一种或多种。
6.根据权利要求1-5任一项所述液晶组合物,其特征在于:所述液晶组合物还包含一种或多种通式V所代表的化合物:
其中,R8代表C1~C12的直链烷基或C2~C12的直链烯基,L5、L6各自独立地代表H或F,Y代表F或OCF3,A11代表:
A10代表:
优选通式V所代表的化合物选自式V-A~式V-Q中的一种或多种:
其中,R8代表C1~C8的直链烷基或C2~C8的直链烯基;优选C2~C5的直链烷基或直链烯基。
7.根据权利要求1-6任一项所述的液晶组合物,其特征在于:所述液晶组合物还进一步包含一种或多种通式VI所代表的化合物:
其中,R9代表C1~C12的直链烷基或C2~C12的直链烯基,R10代表F、C1~C12的直链烷基或C2~C12的直链烯基;
优选通式VI所代表的化合物选自式VI-A或式VI-B中的一种或多种:
其中,R9、R10各自独立地代表C1~C8的直链烷基或C2~C8的直链烯基;优选C1~C5的直链烷基或C2~C5的直链烯基;
和/或,所述液晶组合物还包含一种或多种通式VII所代表的化合物:
其中,R11、R12各自独立地代表C1~C12的直链烷基,L7、L8各自独立地代表H或F,A12代表反式1,4-环己基或1,4-亚苯基;
优选通式VII所代表的化合物选自式VII-A~式VII-C中的一种或多种:
其中,R11、R12各自独立地代表C1~C8的直链烷基;优选C2~C5的直链烷基;
和/或,所述液晶组合物还包含一种或多种通式VIII所代表的化合物:
其中,R13代表C1~C12的直链烷基,L9、L10各自独立地代表H或F,Z代表F或OCF3,A13、A14各自独立地代表:
优选通式VIII所代表的化合物选自式VIII-A~式VIII-L中的一种或多种:
其中,R13代表C1~C8的直链烷基;优选C2~C5的直链烷基。
8.根据权利要求7所述的液晶组合物,其特征在于:包括如下组分
1)、1%~60%的一种或多种通式(I)所代表的化合物;
2)、1%~60%的一种或多种通式(II)所代表的化合物;
3)、0%~80%的一种或多种通式(III)所代表的化合物;
4)、0%~40%的一种或多种通式(IV)所代表的化合物;
5)、0%~80%的一种或多种通式(V)~通式(VIII)所代表的化合物;
或:
1)、3.5%~35%的一种或多种通式(I)所代表的化合物;
2)、5%~39%的一种或多种通式(II)所代表的化合物;
3)、13%~60.5%的一种或多种通式(III)所代表的化合物;
4)、0%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、0%~42%的一种或多种通式(V)所代表的化合物;
6)、0%~13%的一种或多种通式(VI)所代表的化合物;
7)、0%~15%的一种或多种通式(VII)所代表的化合物
8)、0%~19%的一种或多种通式(VIII)所代表的化合物;
优选地,所述液晶组合物,包含以下重量百分比的组分:
1)、1%~12%的一种或多种通式(I)所代表的化合物;
2)、2%~50%的一种或多种通式(II)所代表的化合物;
3)、10%~70%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~60%的一种或多种通式(V)~通式(VIII)所代表的化合物;
或:
1)、13%~40%的一种或多种通式(I)所代表的化合物;
2)、5%~40%的一种或多种通式(II)所代表的化合物;
3)、10%~50%的一种或多种通式(III)所代表的化合物;
4)、10%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~40%的一种或多种通式(V)~通式(VIII)所代表的化合物;
更优选地,所述液晶组合物,包含以下重量百分比的组分:
1)、3.5%~12%的一种或多种通式(I)所代表的化合物;
2)、5%~39%的一种或多种通式(II)所代表的化合物;
3)、17%~60.5%的一种或多种通式(III)所代表的化合物;
4)、0%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、4%~55%的一种或多种通式(V)~通式(VIII)所代表的化合物;
或:
1)、13%~35%的一种或多种通式(I)所代表的化合物;
2)、10%~30%的一种或多种通式(II)所代表的化合物;
3)、13%~41%的一种或多种通式(III)所代表的化合物;
4)、12%~24%的一种或多种通式(IV)所代表的化合物;
5)、0%~22%的一种或多种通式(V)所代表的化合物;
5)、3%~15%的一种或多种通式(VII)和/或通式(VIII)所代表的化合物;
或,所述液晶组合物,包含以下重量百分比的组分:
1)、2%~40%的一种或多种通式(I)所代表的化合物;
2)、3%~19.5%的一种或多种通式(II)所代表的化合物;
3)、10%~65%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~60%的一种或多种通式(V)~通式(VIII)所代表的化合物;
或:
1)、2%~30%的一种或多种通式(I)所代表的化合物;
2)、20%~45%的一种或多种通式(II)所代表的化合物;
3)、15%~55%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~55%的一种或多种通式(V)~通式(VIII)所代表的化合物;
更优选地,所述液晶组合物,包含以下重量百分比的组分:
1)、3.5%~35%的一种或多种通式(I)所代表的化合物;
2)、5%~19.5%的一种或多种通式(II)所代表的化合物;
3)、13%~60.5%的一种或多种通式(III)所代表的化合物;
4)、0%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、3%~55%的一种或多种通式(V)~通式(VIII)所代表的化合物;
或:
1)、4%~24%的一种或多种通式(I)所代表的化合物;
2)、20%~39%的一种或多种通式(II)所代表的化合物;
3)、19%~48%的一种或多种通式(III)所代表的化合物;
4)、0%~25%的一种或多种通式(IV)所代表的化合物;
5)、3%~47%的一种或多种通式(V)~通式(VIII)所代表的化合物;
优选地,所述液晶组合物,包含以下重量百分比的组分:
1)、2%~40%的一种或多种通式(I)所代表的化合物;
2)、3%~45%的一种或多种通式(II)所代表的化合物;
3)、10%~40%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~60%的一种或多种通式(V)~通式(VIII)所代表的化合物;
或:
1)、3%~35%的一种或多种通式(I)所代表的化合物;
2)、3%~45%的一种或多种通式(II)所代表的化合物;
3)、41%~70%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、3%~40%的一种或多种通式(V)~通式(VIII)所代表的化合物;
更优选地,所述液晶组合物,包含以下重量百分比的组分:
1)、3.5%~35%的一种或多种通式(I)所代表的化合物;
2)、5%~39%的一种或多种通式(II)所代表的化合物;
3)、13%~40%的一种或多种通式(III)所代表的化合物;
4)、0%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、3%~55%的一种或多种通式(V)~通式(VIII)所代表的化合物;
或:
1)、4%~30%的一种或多种通式(I)所代表的化合物;
2)、5%~38%的一种或多种通式(II)所代表的化合物;
3)、41%~60.5%的一种或多种通式(III)所代表的化合物;
4)、0%~24%的一种或多种通式(IV)所代表的化合物;
5)、4%~35%的一种或多种通式(V)~通式(VIII)所代表的化合物;
优选地,所述液晶组合物,包含以下重量百分比的组分:
1)、2%~40%的一种或多种通式(I)所代表的化合物;
2)、3%~45%的一种或多种通式(II)所代表的化合物;
3)、10%~70%的一种或多种通式(III)所代表的化合物;
4)、1%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~45%的一种或多种通式(V)~通式(VIII)所代表的化合物;
或:
1)、3%~15%的一种或多种通式(I)所代表的化合物;
2)、2%~45%的一种或多种通式(II)所代表的化合物;
3)、10%~70%的一种或多种通式(III)所代表的化合物;
4)、10%~60%的一种或多种通式(V)~通式(VIII)所代表的化合物;
更优选地,所述液晶组合物,包含以下重量百分比的组分:
1)、3.5%~35%的一种或多种通式(I)所代表的化合物;
2)、5%~39%的一种或多种通式(II)所代表的化合物;
3)、13%~60.5%的一种或多种通式(III)所代表的化合物;
4)、2%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、3%~41%的一种或多种通式(V)~通式(VIII)所代表的化合物;
或:
1)、5%~12%的一种或多种通式(I)所代表的化合物;
2)、5%~38%的一种或多种通式(II)所代表的化合物;
3)、17%~60%的一种或多种通式(III)所代表的化合物;
4)、14%~55%的一种或多种通式(V)~通式(VIII)所代表的化合物;
最优选,所述液晶组合物,由以下重量百分比的组分组成:
1)、4%~24%的一种或多种通式(I)所代表的化合物;
2)、8.5%~30%的一种或多种通式(II)所代表的化合物;
3)、35%~60.5%的一种或多种通式(III)所代表的化合物;
4)、13%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、3%~14%的一种或多种通式(VI)和/或通式(VII)所代表的化合物;
优选地,所述液晶组合物,包含以下重量百分比的组分:
1)、2%~40%的一种或多种通式(I)所代表的化合物;
2)、3%~45%的一种或多种通式(II)所代表的化合物;
3)、10%~50%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、1%~45%的一种或多种通式(V)所代表的化合物;
5)、0%~25%的一种或多种通式(VI)~通式(VIII)所代表的化合物;
或:
1)、3%~30%的一种或多种通式(I)所代表的化合物;
2)、3%~45%的一种或多种通式(II)所代表的化合物;
3)、30%~70%的一种或多种通式(III)所代表的化合物;
4)、0%~30%的一种或多种通式(IV)所代表的化合物;
5)、2%~30%的一种或多种通式(VI)~通式(VIII)所代表的化合物;
更优选地,所述液晶组合物,包含以下重量百分比的组分:
1)、3.5%~35%的一种或多种通式(I)所代表的化合物;
2)、5%~39%的一种或多种通式(II)所代表的化合物;
3)、13%~48%的一种或多种通式(III)所代表的化合物;
4)、0%~24%的一种或多种通式(IV)所代表的化合物;
5)、2%~42%的一种或多种通式(V)所代表的化合物;
5)、0%~21%的一种或多种通式(VI)~通式(VIII)所代表的化合物;
或:
1)、4%~24%的一种或多种通式(I)所代表的化合物;
2)、5%~38%的一种或多种通式(II)所代表的化合物;
3)、35%~60.5%的一种或多种通式(III)所代表的化合物;
4)、0%~25.5%的一种或多种通式(IV)所代表的化合物;
5)、3%~25%的一种或多种通式(VI)~通式(VIII)所代表的化合物。
9.根据权利要求8所述的液晶组合物,其特征在于:所述液晶组合物中,各组分的质量百分比总和为100%。
10.权利要求1-9任一项所述化合物或权利要求9所述组合物在液晶显示装置中的应用;优选所述的液晶显示装置为FFS和IPS显示模式的液晶显示器。