CN107189312A - Bloom exempts from spraying alloy engineering plastics and preparation method thereof - Google Patents
Bloom exempts from spraying alloy engineering plastics and preparation method thereof Download PDFInfo
- Publication number
- CN107189312A CN107189312A CN201710509180.XA CN201710509180A CN107189312A CN 107189312 A CN107189312 A CN 107189312A CN 201710509180 A CN201710509180 A CN 201710509180A CN 107189312 A CN107189312 A CN 107189312A
- Authority
- CN
- China
- Prior art keywords
- parts
- blue
- zinc
- iron
- engineering plastics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of bloom and exempts from spraying alloy engineering plastics and preparation method thereof.It is using the raw material by following parts by weight:300 parts ~ 500 parts of polymethyl methacrylate, 500 parts~600 parts of styrene-acrylonitrile acryl rubbery copolymer, 100 parts~200 parts of makrolon, 5 parts ~ 10 parts of zinc stearate, 2 parts~10 parts of antioxidant, 2 parts ~ 10 parts of UV resistant agent, 5 parts ~ 10 parts of iron oxide red, zinc-iron are yellow 5 parts ~ 10 parts, titanium blue or green blue 5 parts ~ 10 parts, 10 parts ~ 20 parts of carbon black;Above-mentioned raw materials are blended, by blend temperature be 200 DEG C~260 DEG C, screw speed be 280rpm~600rpm under conditions of extruded, extrudate is granulated.The present invention is defined respectively by adding yellow bright iron oxide red, zinc-iron, the blue or green orchid of titanium, carbon black to its particle diameter, product is showed excellent black luminance in itself, without extra to its external appearance spray finishing pigment again.
Description
Technical field
The present invention relates to technical field of polymer materials, especially a kind of engineering plastics.
Background technology
Engineering plastics can be as surface structure material, and what is used in more harsh Chemical Physics environment is high performance
High polymer material, it is widely used in the industries such as electric, automobile, building, office equipment, machinery, Aero-Space, to mould
Dai Gang, to mould Dai Muyi as international popular trend.
As industrial manufacturing level is continued to develop with social, in the environmental protection of engineering plastics, cost, complex process degree
Propose higher requirement.However, conventional engineering plastics are typically required what is sprayed at present, this not only needs consumption to apply
Material, artificial, time, increase production cost, but also due to the use of coating, cause certain pollution.
The content of the invention
The present invention provides a kind of bloom and exempts from spraying alloy engineering plastics and preparation method thereof, and it can solve existing engineering plastic
The problem of material needs to be sprayed.
In order to solve the above problems, the technical solution adopted by the present invention is:
It is using the raw material by following parts by weight:
It is 300 parts ~ 500 parts of polymethyl methacrylate, styrene-acrylonitrile -500 parts of acryl rubbery copolymer~600 parts, poly-
100 parts~200 parts of carbonic ester, 5 parts ~ 10 parts of zinc stearate, 2 parts~10 parts of antioxidant, 2 parts ~ 10 parts of UV resistant agent, iron oxide red 5
Part ~ 10 parts, 5 parts ~ 10 parts of zinc-iron Huang, titanium blue or green blue 5 parts ~ 10 parts, 10 parts ~ 20 parts of carbon black;
Its preparation method comprises the following steps:
A. above-mentioned raw materials are put into and blending working process is carried out in high mixer, obtain blend;
B. the blend obtained by step A is added in double screw extruder, is 200 DEG C~260 DEG C in temperature, screw speed is
Extrusion working process is carried out under conditions of 280rpm~600rpm, extrudate is obtained;
C. comminutor will be delivered to after the extrudate cooling obtained by step B and carries out granulation working process.
In above-mentioned technical proposal, more specifically technical scheme can also be:The styrene-acrylonitrile-acryl rubber
The molecular weight of copolymer is 20000~40000;
The molecular weight of the makrolon is 25000~35000;
The particle diameter of the carbon black is less than 50 microns;
The iron oxide red, zinc-iron are yellow, the blue or green blue particle diameter of titanium is respectively less than 1.5 microns.
By adopting the above-described technical solution, the present invention has the advantages that compared with prior art:
1. the present invention is defined respectively by adding yellow bright iron oxide red, zinc-iron, the blue or green orchid of titanium, carbon black to its particle diameter, make production
Product show excellent black luminance in itself, without again additionally to its external appearance spray finishing pigment, and then save the use of coating, saving
About the artificial and time, reduce production cost.
2. the present invention is by by polymethyl methacrylate, styrene-acrylonitrile-acryl rubbery copolymer and poly- carbonic acid
Ester is applied in combination, and its performance is occurred complementation, so that the present invention has the machines such as excellent scraping and wiping resistance performance, weather resistance
Tool performance.
Embodiment
With reference to embodiment, the invention will be further described:
Embodiment 1 --- bloom is exempted to spray the preparation method of alloy engineering plastics
It is using by following raw material:
Polymethyl methacrylate 40kg, molecular weight for 20000 styrene-acrylonitrile-acryl rubbery copolymer 55kg, point
Son amount is 25000 makrolon 15kg, zinc stearate 0.kg, antioxidant 0.5kg, UV resistant agent 0.5kg, particle diameter are less than
1.5 microns of the titanium green grass or young crops of the zinc-iron Huang 0.8kg of iron oxide red 0.6kg, particle diameter less than 1.5 microns, particle diameter less than 1.5 microns
Blue 0.7kg, particle diameter are less than 50 microns of carbon black 1.5kg;
Its preparation method comprises the following steps:
A. above-mentioned raw materials are put into and blending working process is carried out in high mixer, obtain blend;
B. the blend obtained by step A is added in double screw extruder, is 200 DEG C in temperature, screw speed is 280rpm's
Under the conditions of carry out extrusion working process, obtain extrudate;
C. comminutor will be delivered to after the extrudate cooling obtained by step B and carries out granulation working process.
Embodiment 2 --- bloom is exempted to spray the preparation method of alloy engineering plastics
It is using by following raw material:
Polymethyl methacrylate 30kg, molecular weight for 40000 styrene-acrylonitrile-acryl rubbery copolymer 60kg, point
Son amount is 35000 makrolon 20kg, zinc stearate 0.5kg, antioxidant 0.8kg, UV resistant agent 0.8kg, particle diameter are small
Iron oxide red 0.8kg, particle diameter in 1.5 microns are less than the titanium that 1.5 microns of zinc-iron Huang 0.6kg, particle diameter are less than 1.5 microns
Blue or green orchid 0.7kg, particle diameter are less than 50 microns of carbon black 2kg;
Its preparation method comprises the following steps:
A. above-mentioned raw materials are put into and blending working process is carried out in high mixer, obtain blend;
B. the blend obtained by step A is added in double screw extruder, is 230 DEG C in temperature, screw speed is 500rpm's
Under the conditions of carry out extrusion working process, obtain extrudate;
C. comminutor will be delivered to after the extrudate cooling obtained by step B and carries out granulation working process.
Embodiment 3 --- bloom is exempted to spray the preparation method of alloy engineering plastics
It is using by following raw material:
Polymethyl methacrylate 500kg, molecular weight for 20000 styrene-acrylonitrile-acryl rubbery copolymer 50kg,
Molecular weight is that 35000 makrolon 13kg, zinc stearate 1kg, antioxidant 0.7kg, UV resistant agent 0.7kg, particle diameter are small
Iron oxide red 0.5kg, particle diameter in 1.5 microns are less than the titanium that 1.5 microns of zinc-iron Huang 0.7kg, particle diameter are less than 1.5 microns
Blue or green orchid 0.6kg, particle diameter are less than 50 microns of carbon black 1.7kg;
Its preparation method comprises the following steps:
A. above-mentioned raw materials are put into and blending working process is carried out in high mixer, obtain blend;
B. the blend obtained by step A is added in double screw extruder, is 260 DEG C in temperature, screw speed is 600rpm's
Under the conditions of carry out extrusion working process, obtain extrudate;
C. comminutor will be delivered to after the extrudate cooling obtained by step B and carries out granulation working process.
Performance test
Bloom obtained by 1~embodiment of above example 3 is exempted to spray alloy engineering plastics, makes a service test, adopts simultaneously
With traditional gunite work plastics as control, its result of the test is as shown in table 1.
Table 1
As can be seen from the table, the present invention has excellent mechanical property, and bending strength is up to more than 70MPa, and tensile strength can
Up to more than 52MPa, blackness can reach more than 23 degree, and glossiness can reach more than 84, and Rockwell hardness can reach
More than 50HRBA;The present invention can substitute the conventional spray paint engineering plastics of control completely.
Claims (4)
1. a kind of bloom is exempted to spray alloy engineering plastics, it is characterised in that be prepared from the following raw materials in parts by weight:
It is 300 parts ~ 500 parts of polymethyl methacrylate, styrene-acrylonitrile -500 parts of acryl rubbery copolymer~600 parts, poly-
100 parts~200 parts of carbonic ester, 5 parts ~ 10 parts of zinc stearate, 2 parts~10 parts of antioxidant, 2 parts ~ 10 parts of UV resistant agent, iron oxide red 5
Part ~ 10 parts, 5 parts ~ 10 parts of zinc-iron Huang, titanium blue or green blue 5 parts ~ 10 parts, 10 parts ~ 20 parts of carbon black.
2. a kind of bloom according to claim 1 is exempted to spray alloy engineering plastics, it is characterised in that:The styrene-the third
The molecular weight of alkene nitrile-acryl rubbery copolymer is 20000~40000;
The molecular weight of the makrolon is 25000~35000;
The particle diameter of the carbon black is less than 50 microns;
The iron oxide red, zinc-iron are yellow, the blue or green blue particle diameter of titanium is respectively less than 1.5 microns.
3. a kind of bloom is exempted to spray the preparation method of alloy engineering plastics, it is characterised in that:
Using the raw material of following parts by weight:
It is 300 parts ~ 500 parts of polymethyl methacrylate, styrene-acrylonitrile -500 parts of acryl rubbery copolymer~600 parts, poly-
100 parts~200 parts of carbonic ester, 5 parts ~ 10 parts of zinc stearate, 2 parts~10 parts of antioxidant, 2 parts ~ 10 parts of UV resistant agent, iron oxide red 5
Part ~ 10 parts, 5 parts ~ 10 parts of zinc-iron Huang, titanium blue or green blue 5 parts ~ 10 parts, 10 parts ~ 20 parts of carbon black;
Its preparation method comprises the following steps:
A. above-mentioned raw materials are put into and blending working process is carried out in high mixer, obtain blend;
B. the blend obtained by step A is added in double screw extruder, is 200 DEG C~260 DEG C in temperature, screw speed is
Extrusion working process is carried out under conditions of 280rpm~600rpm, extrudate is obtained;
C. comminutor will be delivered to after the extrudate cooling obtained by step B and carries out granulation working process.
4. a kind of bloom according to claim 3 is exempted to spray the preparation method of alloy engineering plastics, it is characterised in that:
The molecular weight of the styrene-acrylonitrile-acryl rubbery copolymer is 20000~40000;
The molecular weight of the makrolon is 25000~35000;
The particle diameter of the carbon black is less than 50 microns;
The iron oxide red, zinc-iron are yellow, the blue or green blue particle diameter of titanium is respectively less than 1.5 microns.