CN107163714A - A kind of water-soluble Camouflage painting and preparation method thereof - Google Patents
A kind of water-soluble Camouflage painting and preparation method thereof Download PDFInfo
- Publication number
- CN107163714A CN107163714A CN201710296223.0A CN201710296223A CN107163714A CN 107163714 A CN107163714 A CN 107163714A CN 201710296223 A CN201710296223 A CN 201710296223A CN 107163714 A CN107163714 A CN 107163714A
- Authority
- CN
- China
- Prior art keywords
- water
- parts
- soluble
- painting
- camouflage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to paint field, especially a kind of water-soluble Camouflage painting and preparation method thereof.A kind of water-soluble Camouflage painting, includes the raw material of following mass parts：Water-soluble resin 30.00~35.00, polyvinyl alcohol 39.00~42.00, defoamer 0.10~0.40, lauryl alcohol ester 2.00~3.00, butyl glycol ether 4.00~4.60, aqueous color paste 13.00~17.00, wetting agent 0.20~0.40, thixotropic agent 1.00~1.20 and deionized water 1.00~2.00.The present invention uses water-soluble resin for the main film forming matter of coating, and preferred pigments, blending and modifying, selected auxiliary agent, reasonable combination meet the physicochemical property and spectrum property of coating, and can be water-soluble, there is certain water resistance again, common hydraulic pressure can be resisted, drenched with rain.
Description
Technical field
The present invention relates to paint field, especially a kind of water-soluble Camouflage painting and preparation method thereof.
Background technology
There is Camouflage painting certain particularity, i.e. coating to be coated in body surface, it is desirable in visible-range
Meet colourmetric data, i.e. aberration≤3；The distinctive camouflage effectiveness of camouflage paint is met again, that is, meets each color paint film near
The requirement of reflection infrared spectrum rate β value.It can not be reached due to the film color only color effects that traditional color stuffing is made
The camouflage effectiveness of near-infrared, each color stuffing has itself specific spectral reflectance curve, therefore selects the face for having camouflage effectiveness to fill out
Collocation is the key for preparing camouflage paint to material mutually.
Due to the reflection characteristic difference of pigment, its tone absorption value is not near identical, thus after color matching coating face
Color, gloss are also discrepant.During color matching from pigment in addition to factors above to be considered, it is also contemplated that to coating environmental performance
It is required that.Near-infrared camouflage coating requires itself there is extremely low infrared absorption rate, and kept under higher temperature conditions
Performance is stable.It will not only simulate the reflectivity curve of natural chlorophyll, but also have high reflection near infrared region, so that
No matter making target be difficult in near-infrared or full color photographs being coated with after this coating, it is pigment that it, which develops key,
Selection and cooperation.Suitable pigment should be selected according to requirements.
The camouflage paint of training, it is considered to the requirement temporarily coated when training, so needing have certain water-fast after drying
Effect, be able to will also be rinsed out after having trained with water.
Traditional camouflage paint is used to apply in material, equipment and facility overlying, can reach certain puppet in training
Effect is filled, is difficult to rinse out after the completion of training, the application of serious its original equipment, and odorous, volatilizable thing is extremely more, flammable
Explosive dangerous high the shortcomings of, with the enhancing of people's environmental consciousness, it is fewer and fewer that conventional camouflage coating is used.
The content of the invention
The technical problem to be solved in the present invention is：There is provided a kind of water-soluble camouflage painting for the deficiency for overcoming in the prior art
Coating and preparation method thereof.
The technical solution adopted for the present invention to solve the technical problems is：A kind of water-soluble Camouflage painting, including such as
The raw material of lower mass parts：
The weight fraction of the polyvinyl alcohol is 10%.
The pigment that aqueous color paste is used all is to be adapted to aqueous use and the pigment without toxic heavy metal.Titanium dioxide, general choosing
Use rutile titanium dioxide；Coloring pigment, general Ceramics inorganic pigment and metal composite oxide, metal composite oxide is
One kind has excellent weather resistance, heat resistance, fast light and chemical resistance, and safety non-toxic, and they are usually rutile-type and point
Spar type metal ion substitution oxide, the titanium yellow of such as rutile-type, titanium chrome yellow, cobalt green, cobalt titanate green etc., water is then made
Property mill base is standby.
A kind of water-soluble Camouflage painting and preparation method thereof, comprises the following steps：
(1), dispensing, adds 30.00~35.00 parts of water-soluble resin, polyvinyl alcohol 39.00~42.00 in material-compound tank
4.00~4.60 parts of part, 2.00~3.00 parts of lauryl alcohol ester and butyl glycol ether, it is stirring while adding in adding procedure, will be upper
State material to stir, set mixing speed as 400~600 turns/min, 10~15min of mixing time；
(2), doping, the mixed material that step (1) is made adds 0.20~0.40 part of wetting agent and defoamer
0.10~0.40 part, stirring while adding in adding procedure, above-mentioned material is stirred, set mixing speed as 400~
600 turns/min, 10~15min of mixing time；
(3), mix colours, 13.00~17.00 parts of aqueous color paste is added in the mixture that step (2) is made, by above-mentioned material
Stir；
(4) viscosity, is adjusted, 1.00~1.20 parts of thixotropic agent and deionized water are added in the coating that step (3) is made
1.00~2.00 parts, regulation viscosity to -4 glasss of 100-150S of painting；
(5), pack, packed after the camouflage painting for regulating viscosity is filtered with 200 mesh nets.
The beneficial effects of the invention are as follows：The present invention use water-soluble resin for the main film forming matter of coating, preferred pigments, be total to
Mixed modification, selected auxiliary agent, reasonable combination, meet the physicochemical property and spectrum property of coating, and can be water-soluble, have again certain
Water resistance, can resist common hydraulic pressure, drench with rain；For that can be reached after the painting of material, equipment and facility overlying in training
To certain camouflage effectiveness, it can be rinsed out after the completion of training, the application for not influenceing its original to equip, and asepsis environment-protecting, nothing
Smell, volatilizable thing are few, have the advantages that non-ignitable not quick-fried high security, brushing surface are big, with people's environmental consciousness
Enhancing, increasingly receives an acclaim.
Embodiment
The present invention is further illustrated for presently preferred embodiment.
Water-soluble resin AC-80 (Tao Shi chemical industry).
Defoamer is 681F defoamers.
Wetting agent HX5810 (China).
Thixotropic agent 0620 (loose tail trade).
Dispersant 270 (day and international trade)
Embodiment 1
A kind of water-soluble sandy soil color Camouflage painting, includes the raw material of following mass parts：
The weight fraction of polyvinyl alcohol is 10%.
Wherein, aqueous white slurry includes the raw material of following mass parts：
Aqueous black wash includes the raw material of following mass parts：
Aqueous iron oxide yellow slurry includes the raw material of following mass parts：
Aqueous iron oxide red slurry includes the raw material of following mass parts：
A kind of water-soluble sandy soil color Camouflage painting and preparation method thereof, comprises the following steps：
(1), dispensing, adds 32.80 parts of water-soluble resin, 41.20 parts of polyvinyl alcohol, lauryl alcohol ester 2.40 in material-compound tank
4.30 parts of part and butyl glycol ether, it is stirring while adding in adding procedure, above-mentioned material is stirred, setting stirring
Speed is 500 turns/min, mixing time 10min；
(2), doping, the mixed material that step (1) is made adds 0.3 part of 0.30 part of wetting agent and defoamer,
Stirring while adding in adding procedure, above-mentioned material is stirred, and sets mixing speed as 400 turns/min, mixing time
10min；
(3), mix colours, aqueous 15.00 parts of white slurry is added in the mixture that step (2) is made and starches 0.80 with aqueous iron oxide yellow
Part, above-mentioned material stirring is uniform, mixing speed is set as 400 turns/min, mixing time 10min；
(4) color, is finely tuned, aqueous 0.10 part of black wash is added in the mixture that step (3) is made and starches 0.20 with aqueous iron oxide red
Part, above-mentioned material stirring is uniform, mixing speed is set as 400 turns/min, mixing time 10min；
(5) viscosity, is adjusted, 1.50 parts of 1.10 parts of thixotropic agent and deionized water are added in the coating that step (4) is made, is adjusted
Viscosity is saved to -4 glasss of 100-150S of painting；
(6), pack, packed after the camouflage painting for regulating viscosity is filtered with 200 mesh nets.
Embodiment 2
A kind of water-soluble green Camouflage painting, includes the raw material of following mass parts：
The weight fraction of polyvinyl alcohol is 10%.
Wherein, aqueous chrome oxide green slurry includes the raw material of following mass parts：
Aqueous middle yellow slurry includes the raw material of following mass parts：
Aqueous iron oxide red slurry includes the raw material of following mass parts：
A kind of water-soluble green Camouflage painting and preparation method thereof, comprises the following steps：
(1), dispensing, adds 32.80 parts of water-soluble resin, 41.20 parts of polyvinyl alcohol, lauryl alcohol ester 2.40 in material-compound tank
4.30 parts of part and butyl glycol ether, it is stirring while adding in adding procedure, above-mentioned material is stirred, setting stirring
Speed is 500 turns/min, mixing time 10min；
(2), doping, the mixed material that step (1) is made adds 0.3 part of 0.30 part of wetting agent and defoamer,
Stirring while adding in adding procedure, above-mentioned material is stirred, and sets mixing speed as 400 turns/min, mixing time
10min；
(3), mix colours, aqueous chrome oxide green is added in the mixture that step (2) is made and starches 12.00 parts and aqueous middle yellow slurry
It is 3.30 parts, above-mentioned material stirring is uniform, mixing speed is set as 400 turns/min, mixing time 10min；
(4) color, is finely tuned, aqueous iron oxide red is added in the mixture that step (3) is made and starches 0.80 part, by above-mentioned material stirring
Uniformly, mixing speed is set as 400 turns/min, mixing time 10min；
(5) viscosity, is adjusted, 1.50 parts of 1.10 parts of thixotropic agent and deionized water are added in the coating that step (4) is made, is adjusted
Viscosity is saved to -4 glasss of 100-150S of painting；
(6), pack, packed after the camouflage painting for regulating viscosity is filtered with 200 mesh nets.
The water-soluble Camouflage painting being made according to embodiment 1 and embodiment 2, its examination criteria can refer to GJB/
The aqueous camouflage paint specification of the anti-visible ray near-infrareds of T1888-94 and GJB798-90 camouflage paint paint film colors, following table is water-soluble
Some main performances of property camouflage paint.
The above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow person skilled in the art
Scholar can understand present disclosure and be carried out, and it is not intended to limit the scope of the present invention, all according to the present invention
The equivalent change or modification that Spirit Essence is made, should all cover within the scope of the present invention.
Claims (2)
1. a kind of water-soluble Camouflage painting, it is characterised in that：Include the raw material of following mass parts：
The weight fraction of the polyvinyl alcohol is 10%.
2. a kind of water-soluble Camouflage painting and preparation method thereof, it is characterised in that：Comprise the following steps：
(1), dispensing, adds 30.00~35.00 parts of water-soluble resin, 39.00~42.00 parts of polyvinyl alcohol, ten in material-compound tank
4.00~4.60 parts of 2.00~3.00 parts of diol ester and butyl glycol ether, it is stirring while adding in adding procedure, by above-mentioned thing
Material is stirred, and sets mixing speed as 400~600 turns/min, 10~15min of mixing time；
(2), doping, 0.20~0.40 part of the mixed material addition wetting agent and defoamer 0.10 that step (1) is made~
0.40 part, stirring while adding in adding procedure, above-mentioned material is stirred, set mixing speed as 400~600 turns/
Min, 10~15min of mixing time；
(3), mix colours, 13.00~17.00 parts of aqueous color paste is added in the mixture that step (2) is made, by above-mentioned material stirring
Uniformly；
(4), adjust viscosity, added in the coating that step (3) is made 1.00~1.20 parts of thixotropic agent and deionized water 1.00~
2.00 parts, regulation viscosity to -4 glasss of 100-150S of painting；
(5), pack, packed after the camouflage painting for regulating viscosity is filtered with 200 mesh nets.