CN107163630A - 一种环保涂料及其制备方法 - Google Patents
一种环保涂料及其制备方法 Download PDFInfo
- Publication number
- CN107163630A CN107163630A CN201710439631.7A CN201710439631A CN107163630A CN 107163630 A CN107163630 A CN 107163630A CN 201710439631 A CN201710439631 A CN 201710439631A CN 107163630 A CN107163630 A CN 107163630A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmental protection
- protection coating
- coating material
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于建筑材料技术领域,具体涉及一种环保涂料及其制备方法;包括以下重量组分原料:柠檬油3‑4份、橘子油3‑4份、滑石粉20‑25份、石膏粉35‑45份、甲基纤维素3‑5份、环烷酸2‑3份、二氧化钛3‑5份和水70‑90份;本发明采用柠檬油和橘子油两种天然的原料作为颜料的成分,使得制备的涂料安全无毒的前提下,还具有天然的颜色;无毒无害,成膜效果好,较好的涂抹附着力,加入了光触媒物质—二氧化钛,使得本发明兼具净化空气的作用;本发明制备工艺简单,工艺成本较低,能够使得制备的涂料与墙体或材料结合紧密,粘接度度较高。
Description
技术领域
本发明属于建筑材料技术领域,具体涉及一种环保涂料及其制备方法。
背景技术
由于人口增长和经济发展,对资源的过量开采和不合理开发利用而产生的影响资源质量的一系列问题,这些问题已经直接威胁到我们和子孙后代的生存。
所谓涂料是指涂布于物体表面在一定的条件下能形成薄膜而起保护、装饰或其他特殊功能(绝缘、防锈、防霉、耐热等)的一类液体或固体材料。因早期的涂料大多以植物油为主要原料,故又称作油漆。现在合成树脂已大部分或全部取代了植物油,故称为涂料。
目前市场上涂料的品种繁多,但是很多涂料使用后会散发出甲醛等对人体有害的物质,不能满足人们对环保的要求。现有的装潢涂料种类很多,随着现代人认知水平和生活水平的提高,对家装环保要求越来越高,为适应市场需求,涂料生产厂家对环保涂料的研究也在不断提高,但是现有的环保涂料会带来很多问题,比如只是对挥发物的指数降低了使其符合标准,但是化学挥发物还是有的。
发明内容
为了克服背景技术中存在的不足,本发明提出一种环保涂料及其制备方法,该涂料无毒无害,并且能够具有净化空气的作用。
为了达到上述目的,本发明通过如下技术方案实现的:
一种环保涂料,包括以下组分原料:柠檬油、橘子油、滑石粉、石膏粉、甲基纤维素、环烷酸、二氧化钛和水。
进一步,包括以下重量组分原料:柠檬油3-4份、橘子油3-4份、滑石粉20-25份、石膏粉35-45份、甲基纤维素3-5份、环烷酸2-3份、二氧化钛3-5份和水70-90份。
进一步,包括以下重量组分原料:柠檬油3份、橘子油3份、滑石粉23份、石膏粉40份、甲基纤维素4份、环烷酸2份、二氧化钛4份和水80份。
进一步,所述的环保涂料还包括阻燃剂。
进一步,所述的阻燃剂由聚磷酸铵、氢氧化镁和水滑石混合而成。
进一步,所述的柠檬油和橘子油的质量浓度均为50%。
一种环保涂料的制备方法,包括以下具体步骤:
1)按照重量份数称取滑石粉、石膏粉、甲基纤维素和二氧化钛放入搅拌机中进行搅拌,搅拌时间30-45min,得到组分A;
2)将相同重量份数比称取聚磷酸铵、氢氧化镁和水滑石,混合均匀,得到组分B;
3)将组分A和组分B混合,然后加入柠檬油、橘子油和环烷酸,在搅拌机中混合30-45min;
4)在步骤3)得到的混合物中加入重量组分的水,混合均匀即得环保涂料。
与现有技术相比,本发明的有益效果是:
1.采用柠檬油和橘子油两种天然的原料作为颜料的成分,使得制备的涂料安全无毒的前提下,还具有天然的颜色;
2.本发明制备的环保涂料无毒无害,成膜效果好,较好的涂抹附着力,加入了光触媒物质—二氧化钛,使得本发明兼具净化空气的作用。
3.本发明制备工艺简单,工艺成本较低,能够使得制备的涂料与墙体或材料结合紧密,粘接度度较高。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白,以下结合实施例,对发明进行进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
实施例1
一种环保涂料,包括以下重量组分原料:柠檬油3份、橘子油3份、滑石粉20份、石膏粉35份、甲基纤维素3份、环烷酸2份、二氧化钛3份和水70份。
所述的柠檬油和橘子油的质量浓度均为50%。
以上所述的环保涂料的制备方法,包括以下具体步骤:
1)按照重量份数称取滑石粉、石膏粉、甲基纤维素和二氧化钛放入搅拌机中进行搅拌,搅拌时间30-45min,得到组分A;
2)将相同重量份数比称取聚磷酸铵、氢氧化镁和水滑石,混合均匀,得到组分B;
3)将组分A和组分B混合,然后加入柠檬油、橘子油和环烷酸,在搅拌机中混合30-45min;
4)在步骤3)得到的混合物中加入重量组分的水,混合均匀即得环保涂料。
实施例2
一种环保涂料,包括以下重量组分原料:柠檬油3份、橘子油3份、滑石粉23份、石膏粉40份、甲基纤维素4份、环烷酸2份、二氧化钛4份和水80份。
所述的柠檬油和橘子油的质量浓度均为50%。
以上所述的环保涂料的制备方法,包括以下具体步骤:
1)按照重量份数称取滑石粉、石膏粉、甲基纤维素和二氧化钛放入搅拌机中进行搅拌,搅拌时间30-45min,得到组分A;
2)将相同重量份数比称取聚磷酸铵、氢氧化镁和水滑石,混合均匀,得到组分B;
3)将组分A和组分B混合,然后加入柠檬油、橘子油和环烷酸,在搅拌机中混合30-45min;
4)在步骤3)得到的混合物中加入重量组分的水,混合均匀即得环保涂料。
实施例3
一种环保涂料,包括以下重量组分原料:柠檬油3份、橘子油3份、滑石粉23份、石膏粉40份、甲基纤维素4份、环烷酸2份、二氧化钛4份和水80份。
所述的环保涂料还包括阻燃剂,阻燃剂由聚磷酸铵、氢氧化镁和水滑石混合而成。
所述的柠檬油和橘子油的质量浓度均为50%。
以上所述的环保涂料的制备方法,包括以下具体步骤:
1)按照重量份数称取滑石粉、石膏粉、甲基纤维素和二氧化钛放入搅拌机中进行搅拌,搅拌时间30-45min,得到组分A;
2)将相同重量份数比称取聚磷酸铵、氢氧化镁和水滑石,混合均匀,得到组分B;
3)将组分A和组分B混合,然后加入柠檬油、橘子油和环烷酸,在搅拌机中混合30-45min;
4)在步骤3)得到的混合物中加入重量组分的水,混合均匀即得环保涂料。
本发明采用柠檬油和橘子油两种天然的原料作为颜料的成分,使得制备的涂料安全无毒的前提下,还具有天然的颜色;无毒无害,成膜效果好,较好的涂抹附着力,加入了光触媒物质—二氧化钛,使得本发明兼具净化空气的作用;本发明制备工艺简单,工艺成本较低,能够使得制备的涂料与墙体或材料结合紧密,粘接度度较高。
应当理解的是,本发明的应用不限于上述的举例,对本领域普通技术人员来说,可以根据上述说明加以改进或变换,所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (7)
1.一种环保涂料,其特征在于:包括以下组分原料:柠檬油、橘子油、滑石粉、石膏粉、甲基纤维素、环烷酸、二氧化钛和水。
2.根据权利要求1所述的一种环保涂料,其特征在于:包括以下重量组分原料:柠檬油3-4份、橘子油3-4份、滑石粉20-25份、石膏粉35-45份、甲基纤维素3-5份、环烷酸2-3份、二氧化钛3-5份和水70-90份。
3.根据权利要求1所述的一种环保涂料,其特征在于:包括以下重量组分原料:柠檬油3份、橘子油3份、滑石粉23份、石膏粉40份、甲基纤维素4份、环烷酸2份、二氧化钛4份和水80份。
4.根据权利要求1-3任意一条权利要求所述的一种环保涂料,其特征在于:所述的环保涂料还包括阻燃剂。
5.根据权利要求4所述的一种环保涂料,其特征在于:所述的阻燃剂由聚磷酸铵、氢氧化镁和水滑石混合而成。
6.根据权利要求4所述的一种环保涂料,其特征在于:所述的柠檬油和橘子油的质量浓度均为50%。
7.一种环保涂料的制备方法,其特征在于:包括以下具体步骤:
1)按照重量份数称取滑石粉、石膏粉、甲基纤维素和二氧化钛放入搅拌机中进行搅拌,搅拌时间30-45min,得到组分A;
2)将相同重量份数比称取聚磷酸铵、氢氧化镁和水滑石,混合均匀,得到组分B;
3)将组分A和组分B混合,然后加入柠檬油、橘子油和环烷酸,在搅拌机中混合30-45min;
4)在步骤3)得到的混合物中加入重量组分的水,混合均匀即得环保涂料。