CN107149917A - 一种铝溶胶及其制备方法和应用以及催化裂化催化剂及其制备方法 - Google Patents
一种铝溶胶及其制备方法和应用以及催化裂化催化剂及其制备方法 Download PDFInfo
- Publication number
- CN107149917A CN107149917A CN201610124722.7A CN201610124722A CN107149917A CN 107149917 A CN107149917 A CN 107149917A CN 201610124722 A CN201610124722 A CN 201610124722A CN 107149917 A CN107149917 A CN 107149917A
- Authority
- CN
- China
- Prior art keywords
- alumina gel
- catalyst
- preparation
- contact
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及铝溶胶领域,提供了一种铝溶胶及其制备方法和应用以及催化裂化催化剂及其制备方法。该铝溶胶中铝氯摩尔比为(1~1.5):1;该铝溶胶的腐蚀率不大于1.5g/m2·h,pH值为2.8以上,粘度为500mPa·s以上。本发明提供的铝溶胶具有游离氯离子少、结构优化、粘度大、腐蚀率小、pH值高等优点,作为粘结剂用于催化裂化催化剂制备中,能够提高制备催化剂的催化剂浆液固含量达到40重量%以上,制得的催化剂中分子筛含量降低到30重量%以下,同时得到的催化剂强度及活性满足工业使用要求,且催化剂的磨损指数明显降低。
Description
技术领域
本发明涉及铝溶胶领域,具体地,涉及一种铝溶胶,以及一种铝溶胶的制备方法,以及本发明的铝溶胶作为粘结剂在催化裂化催化剂制备中的应用,以及一种催化裂化催化剂及其制备方法。
背景技术
流化催化裂化工艺是原油二次加工的最重要的手段,随着FCC进料的重质化、劣质化的加深,催化剂中活性组分分子筛的含量已由早期的15-20%增加到目前的35%甚至40%以上。而随着分子筛含量的增加,催化剂的磨损指数及球形度已成为催化剂制备工艺中一项十分重要的问题。催化剂必须满足一定强度要求同时催化剂形成粒径在20-150微米,催化剂平均粒径在60-80微米左右的微球颗粒,才能满足催化裂化催化剂在反应装置中的正常流动运转。
目前我国FCC催化剂产品主要分为全合成分子筛催化剂、半合成分子筛催化剂及原位晶化法催化剂。全合成分子筛催化剂的制备流程采用的分子筛(X型或Y型)可以是Na型的,也可以将Na型分子筛预先用稀土离子或铵离子进行交换,再经干燥和焙烧,得到RE型或REH型分子筛,加入到全合成胶体中,经喷雾干燥制成球形催化剂;而加入Na型沸石,喷雾干燥后,经再交换和二次干燥亦可制成球形催化剂。半合成分子筛催化剂制备方法较多,主要的方法是将高岭土先与胶体混合,混有高岭土的胶体浆液与超稳Y型分子筛混合而得的浆液经喷雾干燥制成微球催化剂;将喷雾干燥后的催化剂再次浆化,然后用水洗涤除去反应时形成的Na+,再用可溶性稀土离子进行交换,交换后的催化剂再经洗涤除去未反应的稀土交换剂及可溶性盐 类,二次干燥后即制成半合成分子筛催化剂。而原位晶化法则是使用天然高岭土作为初始原料,先采用一步法同时制备出活性组分和基质材料,再通过改性处理制备出高岭土型FCC催化剂。
随着催化剂活性组分分子筛含量的增加,全合成催化剂的制备方法已经不能满足催化剂对强度的要求,而采用高岭土为基质、分子筛为活性组分,各种硅/铝胶为粘结剂的半合成工艺,其制备工艺简单,制备成本低,在高分子筛含量时具有很好的强度。半合成催化剂工艺是将粘结剂、基质、活性基质制备成混合均匀的浆液再进行喷雾干燥而成,如何继续改进催化剂成胶过程已经成为制备工艺中非常重要的问题:1)提高生产率,降低能耗,降低分子筛使用量,降低成本。2)形成很好的球形度。喷雾干燥的目的是在一定的温度下蒸发掉浆液中多余的水分,固含量低时需要蒸发的水分多,而物料在干燥塔的停留时间相同,因而需要的蒸发热量多或干燥温度高,这样水分在高温下急速型颗粒内表面逸出,形成空心球或者带苹果蒂形状的微球,一方面使催化剂强度变差,另一方面在FCC反-再***中流化容易破碎。3)改进粘结剂的制备方法,提高粘结剂的粘结性能,通过对粘结剂的改进使粘结剂的粒子更加均匀,在催化剂成胶过程起到更好串联粘结作用,同时减少分子筛孔道的堵塞,提高催化剂的活性。4)开发更加合适的基质,基质作为催化裂化过程中大分子的裂化媒介,基质的孔道结构需要足够大能够满足现阶段重质油中大分子的裂化过程,增加催化剂对重油裂化能力及催化剂活性中的热稳定性。5)降低催化剂粘度,降低催化剂胶体输送阻力,提高催化剂喷雾质量,同时减少催化剂喷雾塔堵塞情况。
CN1445167A公开了一种制备铝溶胶的新工艺,制备方法包括:全部以氯化铝和氧化铝或/和氢氧化铝或/和软水铝为铝源和盐酸按照摩尔比为Al2O3:HCl=1.0-1.4:1的比例混合,在80-130℃下反应3-40个小时。
CN1743267A公开了一种制备含氯铝溶胶的方法,包括将通式为 Al2(OH)1-3Cl3-5的聚合氯化铝的水溶液与金属铝充分接触反应,制成铝含量为5~13质量%、Al/Cl质量比为0.6~2.0的铝溶胶。该法用聚合氯化铝代替部分金属铝生产铝溶胶,生产过程中不使用盐酸,对设备的腐蚀小,排放的氢气量小,操作更为安全。生产的铝溶胶成本低,适用于催化剂的粘结剂。
但是,随着原油重质化(原油相对密度在0.9~1.0g/cm3(20℃))程度加强,对催化剂性质要求增高,要求制备出适应原油重质化加工要求的催化剂。
发明内容
本发明的目的在于为了适应原油重质化加工要求,提供一种具有游离氯离子少、结构优化、粘度大、腐蚀率小、pH值高的铝溶胶及其制备方法和应用以及一种催化裂化催化剂的制备方法。
本发明的发明人研究发现,对制备催化剂的成胶步骤中所使用的粘结剂进行改进,提供具有游离氯离子少、结构优化、粘度大、腐蚀率小、pH值高的铝溶胶为粘结剂,可以强化粘结剂粒子结构,增加粘结剂粘结性能的同时,减少粘结剂对催化剂中活性组分分子筛结构的堵塞,降低粘结剂对催化剂活性的影响程度,能够减少分子筛的使用量,降低催化剂的成本。
为实现前述目的,根据本发明的第一方面,本发明提供了一种铝溶胶,该铝溶胶中铝氯摩尔比为(1~1.5):1;该铝溶胶的腐蚀率不大于1.5g/m2·h,pH值为2.8以上,粘度为500mPa·s以上。
根据本发明的第二方面,本发明提供了一种铝溶胶的制备方法,该方法包括:(1)将金属铝与盐酸进行第一接触;(2)将第一接触后的混合物与铝源进行第二接触;所述第一接触的温度高于第二接触的温度20~30℃。
根据本发明的第三方面,本发明提供了本发明的制备方法得到的铝溶胶。
根据本发明的第四方面,本发明提供了本发明的铝溶胶作为粘结剂在制备催化裂化催化剂中的应用。
根据本发明的第五方面,本发明提供了一种催化裂化催化剂的制备方法,其中,该方法包括:将粘结剂、粘土、分子筛和任选的大孔基质进行打浆得到催化剂浆液,将所述催化剂浆液进行喷雾干燥,所述粘结剂含有本发明的铝溶胶。
根据本发明的第六方面,本发明提供了本发明的制备方法得到的催化裂化催化剂。
本发明的铝溶胶具有游离氯离子少、结构优化、粘度大、腐蚀率小、pH值高等优点,在制备催化裂化催化剂时,能够提高制备的催化裂化催化剂浆液的固含量达到40重量%以上,制得的催化裂化催化剂中的分子筛含量可降低到30重量%以下,例如为5~30重量%;同时得到的催化剂强度及活性满足工业使用要求,且催化剂的磨损指数明显降低。
本发明的制备铝溶胶的方法工序简单且条件易控制,能够在较低温度下制备铝溶胶,且制备的铝溶胶具有游离氯离子少、结构优化、粘度大、腐蚀率小、pH值高等优点。
本发明的制备铝溶胶的方法,降低了盐酸的使用量,减少了氯离子的加入量,减少游离酸对铝溶胶性质的破坏,提高了铝溶胶的活性且减少避免出现盐酸过量,导致铝溶胶pH值过低,从而破坏分子筛,影响催化剂活性的缺陷。
同时本发明的制备铝溶胶的方法,能够使用无机铝化合物代替部分金属铝,明显降低了铝溶胶的生产成本。
本发明的制备铝溶胶的方法,在优选实施方式中,可以进一步加入稀土化合物,降低盐酸的使用量,获得的铝溶胶粒子更均匀适中,比表面积更大,增加铝溶胶粘结性能。相比于传统的催化剂制备过程(为了提高活性在催化 剂成型后在催化剂表面沉积一定量的稀土),加入稀土化合物而进一步得到的铝溶胶可以有以下有益效果:
(1)能够将稀土化合物更有效利用,提高稀土利用率,减少稀土在分子筛及催化剂制备过程中的加入量及流失;
(2)改善稀土在催化剂基质中的分布,使稀土在基质中分布更加均匀,提高催化剂重油裂化能力;
(3)加入稀土元素的铝溶胶,可以使铝溶胶更好地富集沉积在分子筛表面及基质表面,粘结性能更加优良,加强催化剂抗重金属的能力;
(4)铝溶胶粘结性能加强,改善相应催化剂性能。
本发明的制备催化裂化催化剂的方法,浆液粘度降低很多,降低了成胶时间及分子筛含量,简化了生产工艺,降低了生产成本。
本发明的其它特征和优点将在随后的具体实施方式部分予以详细说明。
附图说明
附图是用来提供对本发明的进一步理解,并且构成说明书的一部分,与下面的具体实施方式一起用于解释本发明,但并不构成对本发明的限制。在附图中:
图1是实施例1和对比例1分别制备的铝溶胶的27Al核磁谱图。
具体实施方式
以下对本发明的具体实施方式进行详细说明。应当理解的是,此处所描述的具体实施方式仅用于说明和解释本发明,并不用于限制本发明。
本发明提供了一种铝溶胶,该铝溶胶中铝氯摩尔比为(1~1.5):1;该铝溶胶的腐蚀率不大于1.5g/m2·h,pH值为2.8以上,粘度为500mPa·s以上。
本发明所述铝溶胶的粘度为20℃下的粘度。
根据本发明的铝溶胶,其中,优选铝溶胶的铝氯摩尔比为(1.35~1.5):1。
根据本发明的铝溶胶,其中,优选铝溶胶中铝元素的重量含量为11.5~13%。
根据本发明的铝溶胶,其中,优选所述铝溶胶的密度为1.31g/cm3~1.35g/cm3。本发明所述铝溶胶的密度为20℃下的密度。
根据本发明的铝溶胶,其中,优选所述铝溶胶的粘度为500mPa·s~10000mPa·s。优选所述铝溶胶的粘度为20℃下的粘度。
优选情况下,本发明所提供的铝溶胶在20℃下的粘度为500mPa·s以上,例如为500mPa·s~10000mPa·s且密度为1.31g/cm3~1.35g/cm3。
根据本发明的铝溶胶,其中,优选所述铝溶胶的腐蚀率为1g/m2·h~1.5g/m2·h。
根据本发明的铝溶胶,其中,优选所述铝溶胶的pH值为2.8~3.5。
本发明中,提供的铝溶胶可以还含有任选的稀土氧化物。本发明的一种优选实施方式,铝溶胶还含有稀土氧化物,此时,铝溶胶中,稀土氧化物以RE2O3计,RE2O3与铝溶胶中的Al2O3的重量比=(0.01~1.5):1;优选RE2O3:Al2O3的重量比=(0.01~0.8):1。
本发明中,可以通过沉降的方法测定铝溶胶中游离氯离子,如,使用氨水调节铝溶胶pH值为5~6,铝溶胶出现絮状沉淀,分离出沉淀,测量上层清液的氯离子的含量,确定所述铝溶胶的游离氯离子含量。
本发明中,所述铝溶胶的密度通过玻璃密度仪测定。
本发明中,所述铝溶胶的粘度通过旋转粘度仪测定。
本发明中,所述铝溶胶的腐蚀率可以通过挂片实验的方法测定。
本发明中,所述铝溶胶中元素含量通过XRF荧光法测定。
本发明中,可以通过铝溶胶的27Al核磁谱图观察铝溶胶的结构优化。本发明的铝溶胶的27Al核磁谱图中,如图1所示(标记为实施例1),化学位移为0~3处出现的信号峰的峰高低、峰面积小,表明单聚铝的数量少;化学位移为60~63处出现的信号峰的峰高高、峰面积大,说明高聚合态的铝多。27Al核磁谱图的结果表明本发明的铝溶胶是以高聚合态铝为主的结构。同样测定的现有技术得到的铝溶胶(CN1445167A的实施例方法)(图1中标记为对比例1),却是化学位移为0~3处的信号峰的峰高高、峰面积大,化学位移为60~63处峰的信号峰的峰高低、峰面积小,表明现有技术的铝溶胶是以单聚铝为主的结构。
优选情况下,所述铝溶胶的27Al核磁谱图中,化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积比为1以上;优选,化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积的比值为1~1.6,例如此比值为1.1、1.2、1.3、1.4或1.5。由此可以间接体现本发明的铝溶胶中高聚合态铝与单聚铝在含量上的比值在1以上,优选比值为1~1.5。
本发明的铝溶胶具有游离氯离子少、结构优化、粘度大、腐蚀率小、pH值高等优点,在制备催化裂化催化剂时,能够提高制备的催化裂化催化剂浆液的固含量达到40重量%以上,制得的催化裂化催化剂中的分子筛含量可降低到30重量%以下;同时得到的催化剂强度及活性满足工业使用要求,且催化剂的磨损指数明显降低。
本发明还提供了一种铝溶胶的制备方法,该方法包括:(1)将金属铝与盐酸进行第一接触;(2)将第一接触后的混合物与铝源进行第二接触;所述第一接触的温度高于第二接触的温度20~30℃。
本发明的制备铝溶胶的方法,可以降低盐酸的使用量,减少氯离子的加入量,减少游离酸对铝溶胶性质的破坏,提高铝溶胶的活性,同时可以避免 出现盐酸过量导致铝溶胶pH值过低,破坏分子筛而影响催化剂活性的缺陷。
本发明中,进行所述第一接触和第二接触的过程中伴随搅拌,停止搅拌即所述第一接触和第二接触的过程结束。以下所述第一接触和第二接触时间为在搅拌持续进行下的时间。
根据本发明的一种优选的实施方式,第一接触的温度为50~80℃。
根据本发明的一种优选的实施方式,第二接触的温度为20~50℃。
根据本发明的一种优选的实施方式,以Al计,步骤(1)中金属铝的用量与步骤(2)中所述铝源的用量的摩尔比为(5~10):1。
根据本发明的一种优选实施方式,该方法还包括:在进行步骤(2)之前,将所述第一接触后的混合物在常温下静置1~30h,优选静置2~6h。所述静置是指在所述第一接触进行时所伴随的搅拌停止后,所述第一接触后的混合物在无搅拌状态下放置。
根据本发明的方法,常温例如一般为0~40℃。
根据本发明的一种优选的实施方式,第一接触的条件还包括:相对于1mol的盐酸,金属铝的用量为0.8mol~1.3mol。
根据本发明的一种优选的实施方式,第一接触的条件还包括:第一接触时间为2~5h。
根据本发明的一种优选的实施方式,第一接触的条件还包括:盐酸的浓度为31重量%~36重量%。
根据本发明的一种优选的实施方式,第二接触的条件还包括:第二接触时间为3~4h。
根据本发明的一种优选的实施方式,第二接触中所述铝源优选为金属铝和/或无机铝化合物。
本发明中,所述无机铝化合物的种类的可选范围较宽,针对本发明,优选所述无机铝化合物为氯化铝、氧化铝、氢氧化铝和软水铝中的一种或多种; 更优选所述无机铝化合物为Al2O3,更优选为γ-Al2O3和/或η-Al2O3。
根据本发明的一种优选实施方式,该方法还包括,将第二接触得到的混合物与稀土化合物进行第三接触。
根据本发明的方法,将第二接触得到的混合物与稀土化合物接触的条件的可选范围较宽,针对本发明,优选包括:第三接触温度为10~50℃,更优选第三接触时间大于10min;优选第三接触时间为10~60min。
根据本发明的一种优选实施方式,所述稀土化合物的种类可选范围较宽,本领域熟知的稀土化合物种类均可用于本发明,针对本发明,优选所述稀土化合物中的稀土元素包括La、Ce、Sc、Pr和Nd中的至少一种,例如含镧和Ce的混合稀土化合物。优选所述稀土化合物为氧化稀土、氢氧化稀土、硝酸稀土和草酸稀土中的至少一种。
本发明中,优选情况下,所述稀土化合物以RE2O3计,所述第二接触得到的混合物以Al2O3计,所述稀土化合物的用量使RE2O3:Al2O3的重量比=(0.01~1.5):1;优选RE2O3:Al2O3的重量比=(0.01~0.8):1。
本发明的制备铝溶胶的方法可以连续进行。
如前所述,本发明还提供了按照本发明的制备方法得到的铝溶胶。该铝溶胶中可以含有任选的稀土氧化物,该铝溶胶具有前述的特征,在此不再赘述。
如前所述,本发明还提供了本发明的铝溶胶作为粘结剂在制备催化裂化催化剂中的应用。
如前所述,本发明还提供了一种催化裂化催化剂的制备方法,其中,该方法包括:将粘结剂、粘土、分子筛和任选的大孔基质进行打浆得到的催化剂浆液,将所述催化剂浆液进行喷雾干燥,所述粘结剂含有本发明的铝溶胶。
根据本发明的催化裂化催化剂的制备方法,优选,喷雾干燥后进行洗涤、干燥得到催化裂化催化剂。
根据本发明的第一种优选实施方式,所述催化裂化催化剂的制备方法包括:
(1)加入含有铝溶胶的粘结剂,搅拌;
(2)加入分子筛干粉或者研磨好的分子筛浆液分散5~120分钟,优选5~40分钟;
(3)加入粘土、任选的大孔基质,搅拌30~200分钟,优选60~120分钟;
(4)喷雾干燥;
(5)洗涤,再干燥即得产品。
根据本发明的第二种优选实施方式,所述催化裂化催化剂的制备方法包括:
(1)加入铝溶胶,搅拌,加入粘土,搅拌,加入任选的大孔基质,搅拌5-200分钟,优选30~90分钟;
(2)加入分子筛干粉或者研磨好的分子筛浆液分散5~120分钟,优选5~50分钟;
(3)喷雾干燥;
(4)洗涤,再干燥即得产品。
根据本发明的催化裂化催化剂的制备方法,优选以所述催化剂浆液的干基重量计,分子筛的用量为10~50重量%,粘土的用量为10~50重量%,粘结剂以氧化物计的用量为5~35重量%,大孔基质的用量为0~25重量%。优选大孔基质的用量为2~25重量%。
根据本发明的催化裂化催化剂的制备方法,优选大孔基质的平均孔径为100~200nm。
本发明中,本领域常用的具有大孔结构的基质均可以用作本发明的所述大孔基质。优选情况下,所述大孔基质为氧化铝、二氧化硅、氧化物复合物、 镁铝尖晶石、磷铝尖晶石或改性镁铝尖晶石,其中所述氧化物复合物为金属Mg、Ca、Sr、Ba、Cu、V、Zn、Ti及非金属B、P氧化物与氧化铝、氧化硅的复合物。针对本发明,优选所述大孔基质可以是氧化铝,例如可以是具有一水铝石结构水合氧化铝、具有三水铝石结构水合氧化铝、具有拜耳石结构的水合氧化铝的一种或多种,也可以为χ-Al2O3、δ-Al2O3、η-Al2O3、κ-Al2O3、θ-Al2O3、ρ-Al2O3、α-Al2O3和γ-Al2O3,其中κ-Al2O3、δ-Al2O3、θ-Al2O3和α-Al2O3是脱水温度在900~1000℃制备的高温氧化铝,χ-Al2O3、η-Al2O3、γ-Al2O3、ρ-Al2O3是在脱水温度小于600℃制备的氧化铝,其比表面积和孔容一般都较大,称为活性氧化铝,常用的为γ-Al2O3和η-Al2O3。所述大孔基质也可以是二氧化硅,包括硅酸钠、硅酸等提供硅源的基质;也可以是金属Mg、Ca、Sr、Ba、Cu、V、Zn、Ti及非金属B、P氧化物与氧化铝、氧化硅的复合物;也可以是镁铝尖晶石,磷铝尖晶石,可以优选为镁铝尖晶石。
根据本发明的催化裂化催化剂的制备方法,优选所述催化剂浆液的固含量在40重量%以上,优选为40重量%~55重量%。
本发明所述的粘土为本领域技术人员所熟知的粘土原料,常用的粘土种类均可以用于本发明,针对本发明,优选所述粘土为高岭土、多水高岭土、蒙脱土、硅藻土、埃洛石、准埃洛石、皂石、累托土、海泡石、凹凸棒石、水滑石和膨润土中的一种或多种。其中,海泡石是一种富镁纤维状硅酸盐粘土矿物,在其结构单元中,硅氧四面体和镁氧八面体相互交替,具有层状和链状的过渡性结构特征。用酸改性海泡石作为FCC催化剂基质,可以有效提高催化剂的比表面积、孔容以及中孔孔容,能够加强催化剂的抗重金属作用。而高岭土及准埃洛石有比较接近的性质,而埃洛石则具有比表面积大、孔容大,孔径分布表现出大孔较少、中孔较多的特点,埃洛石还具有表面酸性大、微活指数高、孔结构稳定性好等特点。针对本发明,优选所述粘土为海泡石、高岭土和埃洛石中一种或者多种。
本发明中,所述的分子筛为本领域熟知的分子筛原料,本领域常用的分子筛种类均可以用于本发明,针对本发明优选所述分子筛是指REY、REHY、REUSY、USY、采用气相化学法(SiCl4脱Al补Si法)、液相化学法((NH4)2SiF6抽铝补硅法)及其它方法制备的不同硅铝比改性的Y沸石或它们的混合物,以及含其它各类高硅铝比的ZSM-5类、β类沸石或它们的混合物。
本发明所提供的制备催化裂化催化剂的方法,使用本发明的铝溶胶可以降低分子筛孔道的堵塞,同时将基质更好地用粘结剂包裹,提高催化剂的成形度和催化剂的强度。另外使用本发明的铝溶胶,制备催化裂化催化剂时,可以不用加入大量酸进行酸化,使分子筛避免当处于过低pH值的胶体中时而受到破坏,提高催化剂的活性。此外,该催化裂化催化剂的制备方法也可以降低催化剂成胶过程的时间,增大成胶浆液固含量,降低浆液粘度,缩短工艺流程且降低能耗,增大产量。
本发明还提供了本发明的制备方法得到的催化裂化催化剂。
根据本发明,优选所述催化裂化催化剂中分子筛的含量在30重量%以下。
按照本发明,得到的催化裂化催化剂,以干重计(800℃,1小时灼减含量),含有分子筛10~50重量%,优选25~30重量%;粘土10~50重量%,优选35~45重量%;铝溶胶(按Al2O3计)10~30重量%,优选15~25重量%;大孔基质2~25重量%,优选6~16重量%。
本发明提供的催化裂化催化剂可以降低粘结剂及分子筛的使用量。
下面的实施例对本发明的特点做进一步的说明,但本发明的内容并不受实施例的限制。
铝溶胶的游离氯离子含量,通过沉降的方法测定,使用氨水调节铝溶胶pH值为5~6,铝溶胶出现絮状沉淀,分离出沉淀,测量上层清液的氯离子 的含量。
铝溶胶的密度通过玻璃密度计(深圳市鼎鑫宜实验设备有限公司)测定。
铝溶胶的粘度通过旋转粘度仪(上海恆平科学仪器有限公司,NDJ-1型旋转式粘度计)测定。
铝溶胶中元素含量通过XRF荧光分析方法(RIPP 117-90标准方法(见《石油化工分析方法》(RIPP试验方法)杨翠定等编,科学出版社,1990年出版))测定。
铝溶胶的腐蚀率可以通过挂片实验的方法测定:
实验器材:采用20#碳钢试片(银白色)作为挂片(尺寸为50mm×25mm×2mm)、恒温水浴、磁力搅拌器、吹风机、脱脂棉;
实验药品:无水乙醇、盐酸(10重量%)、六次甲基四胺(0.5重量%)、5N的氢氧化钠;
实验步骤:首先将挂片用无水乙醇清洗样品,去除试样表面的油脂;然后在无水乙醇中浸泡5min,进一步脱脂和脱水。待上面的工作进行完毕,取出样品放置于滤纸上,冷风吹干后用滤纸包裹,放置于干燥器内保存,24h后称量,所得刮片重量,记为W1。将挂片悬挂放入盛在容器中的铝溶胶1L中于0~30℃下静置24h,然后将盛放有挂片和铝溶胶的容器置于恒温水浴中在温度80℃下反应时间6h。反应完成后先用10重量%盐酸与0.5重量%六次甲基四铵混合物(混合物制备方法:将10重量%盐酸与0.5重量%六次甲基四铵相混合,制备出pH值为5~7的溶液)清洗除去挂片上的黑色腐蚀产物,直至把黑色腐蚀产物完全清理干净,挂片呈现银白色,清洗后的挂片立即浸入5N的氢氧化钠溶液中进行钝化1min;取出后浸入清洁的无水乙醇中浸泡1min,用滤纸擦干,冷风吹干后用滤纸包裹,放置于干燥器内保存,24h后称量,所得重量记为W2;按照下面公式计算腐蚀率,腐蚀率=△W/(T×A);式中:△W=挂片挂入前称重W1-挂片取出后称重W2;T为挂片 挂入的时间(6h);A为挂片的面积(0.28dm2)。
铝溶胶27Al核磁测定:将铝溶胶加入去阳离子水稀释至1重量%(Al2O3含量)制成溶液样;通过Varian公司INOVA500型超导核磁共振仪进行测定,测试条件包括:共振频率130MHz(27Al),脉冲程序s2pul,谱宽90090Hz,累加次数800,延迟时间1.0s,采样时间0.5s,容剂D2O,外标样NaAlO2。
催化剂制备例中使用的原料规格如下:
高岭土:固含量81.2重量%,中国高岭土有限公司(苏州)生产;
REY型分子筛:中国石化催化剂有限公司齐鲁分公司生产,固含量80重量%,稀土氧化物(La或Ce)含量为17~18重量%;
镁铝尖晶石:Al2O3含量43重量%,MgO含量54重量%,河北省邢台市鼎镁科技化工有限公司生产,固含量70.8重量%,平均孔径为120~150nm;
氧化稀土溶液浓度:328.46g/L,含La、Ce(La:Ce摩尔比为1:1),中国石化催化剂有限公司齐鲁分公司生产。
催化剂制备例得到的催化剂中各组成按各原料的投料量计算确定。
实施例1
(1)将0.8mol金属铝(中国铝业公司)与1mol(HCl)盐酸进行第一接触,控制第一接触过程温度为50℃,第一接触时间为3h,所用盐酸的初始浓度为32重量%;
(2)将第一接触后的混合物在常温20℃下静置6h,然后与γ-Al2O3(山东铝厂)和η-Al2O3(山东铝厂)进行第二接触,第二接触温度为30℃,第二接触时间为4h,以铝计的γ-Al2O3、以铝计的η-Al2O3与步骤(1)的金属铝的摩尔比为0.05:0.05:1。铝溶胶的物化性质见表1。
将铝溶胶进行27Al核磁测定,谱图见图1,其中,化学位移为0~3处 的信号峰的峰高低、峰面积小,表明单聚铝的数量少;化学位移为60~63处的信号峰的峰高高、峰面积大,说明高聚合态的铝多。表明该铝溶胶是以高聚合态铝为主的结构。计算化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积的比值为1.3。
实施例2
(1)将1.3mol金属铝与1mol(HCl)盐酸进行第一接触,控制第一接触过程温度为80℃,时间为2h,盐酸的浓度为36重量%;
(2)将第一接触后的混合物在常温30℃下静置2h,然后与γ-Al2O3和η-Al2O3进行第二接触,第二接触温度为50℃,第二接触时间为3h,以铝计的γ-Al2O3、以铝计的η-Al2O3与步骤(1)的金属铝的摩尔比为0.07:0.06:1。铝溶胶的物化性质见表1。
计算化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积的比值为1.1。
实施例3
(1)将1mol金属铝与1mol(HCl)盐酸进行第一接触,控制第一接触过程温度为60℃,时间为5h,盐酸的浓度为31重量%;
(2)将第一接触后的混合物在常温10℃下静置4h,然后与γ-Al2O3和η-Al2O3进行第二接触,第二接触温度为35℃,第二接触时间为3.5h,以铝计的γ-Al2O3、以铝计的η-Al2O3与步骤(1)的金属铝的摩尔比为0.12:0.08:1。铝溶胶的物化性质见表1。
计算化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积的比值为1.2。
实施例4
按照实施例3的方法制备铝溶胶,不同的是,单独使用γ-Al2O3作为步骤(2)的铝源,以铝计的γ-Al2O3与金属铝的摩尔比为0.2:1。
铝溶胶的物化性质见表1。
计算化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积的比值为1.2。
实施例5
按照实施例4的方法制备铝溶胶,不同的是,使用金属铝代替γ-Al2O3作为步骤(2)的铝源,步骤(2)中引入的Al与步骤(1)中引入的Al的摩尔比为0.2:1。
铝溶胶的物化性质见表1。
计算化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积的比值为1.2。
实施例6
按照实施例3的方法制备铝溶胶,不同的是,第一接触的温度为90℃,第二接触的温度为60℃。
铝溶胶的物化性质见表1。
计算化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积的比值为1.2。
实施例7
向实施例1制备的铝溶胶(以Al2O3计)中加入氧化稀土溶液(以RE2O3计,La和Ce的总和),RE2O3:Al2O3=0.8:1,搅拌0.5h,混合后过滤,得 到稳定的铝溶胶产品。
铝溶胶的物化性质见表1。
计算化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积的比值为1.5。
对比例1
按照CN1445167A的实施例方法制备铝溶胶。
将氧化铝和盐酸按摩尔比为Al2O3:HCl=1:3的比例投入到反应釜中,控制反应温度为140℃,保持2小时,制备氯化铝溶液,反应过程中连续加入稀硫酸溶液,然后根据所需铝溶胶中铝的含量将补充的金属铝分4次加入到反应釜中,保持1个大气压、控制温度为80℃下反应40小时,反应过程中不间断搅拌得到铝溶胶,铝溶胶的物化性质见表1。
将铝溶胶进行27Al核磁测定,谱图见图1,其中,化学位移为0~3处的信号峰的峰高高、峰面积大,表明单聚铝的数量少,化学位移为60~63处的信号峰的峰高低、峰面积小,说明单聚铝多。表明该铝溶胶是以单聚铝为主的结构。
计算化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积的比值为0.6。
对比例2
向对比例1制备的铝溶胶(以Al2O3计)中加入氧化稀土溶液(以RE2O3计,La和Ce的总和),RE2O3:Al2O3=0.8:1,搅拌0.5h,混合后过滤,得到稳定的铝溶胶产品,铝溶胶的物化性质见表1。
计算化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积的比值为0.7。
对比例3
按照CN1743267A的实施例1的方法制备铝溶胶。
取6.5g通式为Al2(OH)2.9Cl3.1的聚合氯化铝,其中含29.0重量%的Al2O3、31.8重量%的Cl,将其溶解在10mL水中,加入1.3g纯度为99.5重量%的金属铝,在50℃、0.1MPa下搅拌反应7.5小时,过滤,得到16.71g的铝溶胶。
铝溶胶的物化性质见表1。
计算化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积的比值为0.4。
对比例4
向对比例3制备的铝溶胶(以Al2O3计)中加入氧化稀土溶液(以RE2O3计,La和Ce的总和),RE2O3:Al2O3=0.8:1,搅拌0.5h,混合后过滤,得到稳定的铝溶胶产品,铝溶胶的物化性质见表1。
计算化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积的比值为0.5。
表1 铝溶胶的物化性质
将实施例1-3、对比例1和3制得的铝溶胶进行游离氯离子含量测定,发现采用实施例1所制备的铝溶胶游离氯离子较少,实验结果见表2。
表2 沉降后铝溶胶上层清液的性质
项目 | 实施例1 | 实施例2 | 实施例3 | 对比例1 | 对比例3 |
上层清液的pH | 5.5 | 5.7 | 5.8 | 4.8 | 6.0 |
Cl-,重量% | 1.23 | 1.59 | 1.78 | 5.63 | 2.63 |
催化剂制备例
(1)分别在反应釜中加入实施例1-7制备的铝溶胶69.12kg,搅拌,加入高岭土49.26kg,再加入镁铝尖晶石21.19kg,搅拌30min;加入研磨好的REY分子筛的浆液(中国石化催化剂有限公司齐鲁分公司生产,浆液固含量31.4重量%)95.54kg,搅拌30min,喷雾干燥,将所得催化剂微球在500℃焙烧1h;再按水:干基催化剂的重量比为1:8将催化剂以脱阳离子水洗涤两遍,120℃恒温干燥2小时,得到样品C1~C7,催化剂浆液和产品性能见表3。
(2)在反应釜中加入实施例1制备的铝溶胶69.12kg,搅拌,加入高岭土67.73kg,搅拌30min;加入研磨好的REY分子筛的浆液(中国石化催化剂有限公司齐鲁分公司生产,浆液固含量31.4重量%)95.54kg,搅拌30min,喷雾干燥,将所得催化剂微球在500℃焙烧1h;再按水:干基催化剂的重量比为1:8将催化剂以脱阳离子水洗涤两遍,120℃恒温干燥2小时,得到样品C8,催化剂浆液和产品性能见表3。
(3)分别在反应釜中加入对比例1-4制备的铝溶胶92.17kg,搅拌,加入高岭土33.25kg,再加入镁铝尖晶石21.19kg,搅拌30min;加入研磨好的REY分子筛的浆液(中国石化催化剂有限公司齐鲁分公司生产,浆液固含量31.4重量%)121.02kg,搅拌30min,喷雾干燥,将所得催化剂微球在500℃焙烧1h,再按水:干基催化剂的重量比为1:8将催化剂以脱阳离子水洗 涤两遍,120℃恒温干燥2小时,得到样品D1~D4,催化剂浆液和产品性能见表4。
催化剂表征:
(1)根据GB/T 5816-1995方法采用美国康塔公司Autosorb-1氮气吸脱附仪检测所述裂化催化剂的比表面积,在测试前样品需要在300℃下脱气6小时,结果见表3、4。
(2)根据RIPP 151-90标准方法(见《石油化工分析方法》(RIPP试验方法),杨翠定编,科学出版社,1990年出版)检测所述裂化催化剂的总孔体积,结果见表3、4。
(3)采用德国莱驰公司的Camsizer XT干湿两用多功能粒径及形态分析仪,检测所述裂化催化剂的球形度指数SPHT,结果见表3、4。
球形度指数SPHT是指与物体相同体积的球体的表面积(4πA)和物体的表面积(P2)的比,见公式1。
表3
项目 | C1 | C2 | C3 | C4 | C5 | C6 | C7 | C8 |
高岭土,重量% | 40 | 40 | 40 | 40 | 40 | 40 | 40 | 55 |
分子筛,重量% | 30 | 30 | 30 | 30 | 30 | 30 | 30 | 30 |
铝溶胶(Al2O3计),重量% | 15 | 15 | 15 | 15 | 15 | 15 | 15 | 15 |
镁铝尖晶石,重量% | 15 | 15 | 15 | 15 | 15 | 15 | 15 | 0 |
催化剂浆液固含量,重量% | 42 | 42 | 42 | 42 | 42 | 42 | 42 | 50 |
催化剂浆液粘度,20℃,mPa·s | 500 | 300 | 800 | 5600 | 6000 | 6500 | 1600 | 600 |
催化剂比表面积,m2·g-1 | 262 | 258 | 272 | 268 | 260 | 262 | 275 | 215 |
催化剂总孔体积,mL/g | 0.375 | 0.375 | 0.368 | 0.379 | 0.368 | 0.359 | 0.376 | 0.370 |
催化剂SPHT | 0.948 | 0.949 | 0.948 | 0.938 | 0.929 | 0.935 | 0.950 | 0.935 |
催化剂磨损指数,m%/h | 1.5 | 0.9 | 0.6 | 1.7 | 1.5 | 1.4 | 0.8 | 1.6 |
催化剂微反活性(17h),% | 75 | 77 | 78 | 74 | 72 | 71 | 78 | 71 |
表4
项目 | D1 | D2 | D3 | D4 |
高岭土,重量% | 27 | 27 | 27 | 27 |
分子筛,重量% | 38 | 38 | 38 | 38 |
铝溶胶(Al2O3计),重量% | 20 | 20 | 20 | 20 |
镁铝尖晶石,重量% | 15 | 15 | 15 | 15 |
催化剂浆液固含量,重量% | 37 | 37 | 37 | 37 |
催化剂浆液粘度,20℃,mPa·s | 4500 | 12000 | 8000 | 10000 |
催化剂比表面积,m2·g-1 | 241 | 252 | 251 | 256 |
催化剂总孔体积,mL/g | 0.353 | 0.368 | 0.352 | 0.353 |
催化剂SPHT | 0.915 | 0.937 | 0.930 | 0.935 |
催化剂磨损指数,m%/h | 2.2 | 1.6 | 2.2 | 2.0 |
催化剂微反活性(17h),% | 69 | 68 | 71 | 72 |
催化剂评价
评价本发明催化剂与对比催化剂的裂解反应性能。
原料油为武混三原料油,物化性质数据见表5。
表6、7列出了固定流化床装置上的评价结果。催化剂经过800℃,17小时,100%水蒸汽老化失活处理,催化剂装量9g,剂油比为5,反应温度500℃。
其中,转化率=汽油收率+液化气收率+干气收率+焦炭收率
液体收率=液化气收率+汽油收率+柴油收率
轻质油收率=汽油收率+柴油收率
焦炭选择性=焦炭产率/转化率
表5
表6
表7
从实施例可以看出,本发明提供一种铝溶胶,该铝溶胶的27Al核磁谱图(图1)可以看出,该铝溶胶是以高聚合态铝为主的结构。而现有技术(对比例1)得到的铝溶胶(图1)是以单聚铝为主的结构。表1的数据可以显示,本发明的铝溶胶腐蚀率更低,粘度更大,pH值更高。表2的数据显示,本发明得到的铝溶胶(实施例1-3)可以比对比例1和3获得的铝溶胶具有更低的游离氯离子含量。本发明提供的铝溶胶具有游离氯离子少、结构优化、粘度大、腐蚀率小、pH值高的特点,因此用于制备催化裂化催化剂,得到的催化剂有更好的催化效果。
实施例7制备的铝溶胶加入稀土元素,以该铝溶胶进一步制备的催化剂有更好的催化活性。
从催化剂制备例得到的催化剂的结果数据可以看出,采用本发明的铝溶胶制备的催化剂更适应原油重质化加工要求。从表3、4的数据可以看出,采用本发明的铝溶胶(实施例1-7)制备的催化剂(C1~C7),组成中可以比现有技术的铝溶胶而制得的催化剂(D1~D4)降低分子筛和铝溶胶的加入量,并且催化剂浆液的固含量可以更高,制得的催化剂的物化性能:比表面积、总孔体积、SPHT、磨损指数和微反活性都明显好于现有技术制得的催化剂(D1~D4)。从表6、7的结果数据可以看出,进行重质原油加工时,采用本发明的铝溶胶制得的催化剂(C1~C7),相比于现有技术的铝溶胶而 制得的催化剂(D1~D4)可以获得更高的转化率、液体收率和轻质油收率,且焦炭量降低。
另外,催化剂C8中未加入大孔基质,相比于催化剂(C1~C7),活性、汽油产率高及焦炭选择性要差,说明本发明的催化裂化催化剂中加入大孔基质更有利于改善催化剂的活性、汽油产率高及焦炭选择性。
本发明中减低分子筛和铝溶胶的加入量,有利于降低催化剂的生产成本。
Claims (15)
1.一种铝溶胶,其特征在于,该铝溶胶中铝氯摩尔比为(1~1.5):1;该铝溶胶的腐蚀率不大于1.5g/m2·h,pH值为2.8以上,粘度为500mPa·s以上。
2.根据权利要求1所述的铝溶胶,其中,所述铝溶胶中铝元素的重量含量为11.5%~13%;所述铝溶胶的腐蚀率为1g/m2·h~1.5g/m2·h,pH值为2.8~3.5,密度为1.31g/cm3~1.35g/cm3,粘度为500mPa·s~10000mPa·s。
3.根据权利要求1或2所述的铝溶胶,其中,所述铝溶胶的27Al核磁谱图中,化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积比为1以上;优选,化学位移为60~63处出峰的峰面积与化学位移为0~3处出峰的峰面积的比值为1~1.6。
4.一种铝溶胶的制备方法,其特征在于,该方法包括:
(1)将金属铝与盐酸进行第一接触;
(2)将第一接触后的混合物与铝源进行第二接触;
所述第一接触的温度高于第二接触的温度20~30℃。
5.根据权利要求4所述的制备方法,其中,第一接触的温度为50~80℃;第二接触的温度为20~50℃。
6.根据权利要求4或5所述的制备方法,其中,以Al计,步骤(1)中金属铝的用量与步骤(2)中所述铝源的用量的摩尔比为(5~10):1。
7.根据权利要求4或5所述的制备方法,其中,该方法还包括:在进行步骤(2)之前,将所述第一接触后的混合物在常温下静置1~30h,优选静置2~6h。
8.根据权利要求4或5所述的制备方法,其中,
第一接触的条件还包括:相对于以HCl计的1mol的盐酸,金属铝的用量为0.8mol~1.3mol,第一接触时间为2~5h,盐酸的浓度为31重量%~36重量%;
第二接触的条件还包括:第二接触时间为3~4h,所述铝源为金属铝和/或无机铝化合物,所述无机铝化合物为氯化铝、氧化铝、氢氧化铝和软水铝中的一种或多种;优选所述无机铝化合物为Al2O3,更优选为γ-Al2O3和/或η-Al2O3。
9.根据权利要求4或5所述的制备方法,其中,该方法还包括,将第二接触得到的混合物与稀土化合物进行第三接触;
第三接触的条件包括:第三接触温度为10~50℃,第三接触时间为10min以上;
所述稀土化合物以RE2O3计,所述第二接触得到的混合物以Al2O3计,所述稀土化合物的用量使RE2O3:Al2O3的重量比=(0.01~1.5):1;更优选RE2O3:Al2O3的重量比=(0.01~0.8):1;所述稀土化合物中的稀土元素包括La、Ce、Sc、Pr和Nd中的至少一种;所述稀土化合物为氧化稀土、氢氧化稀土、硝酸稀土和草酸稀土中的至少一种。
10.权利要求4-9中任意一项所述的制备方法得到的铝溶胶。
11.权利要求1-3和10中任意一项所述的铝溶胶作为粘结剂在制备催化裂化催化剂中的应用。
12.一种催化裂化催化剂的制备方法,其中,该方法包括:将粘结剂、粘土、分子筛和任选的大孔基质进行打浆得到的催化剂浆液,将所述催化剂浆液进行喷雾干燥,其特征在于,所述粘结剂含有权利要求1-3和10中任意一项所述的铝溶胶。
13.根据权利要求12所述的制备方法,其中,以所述催化剂浆液的干基重量计,分子筛的用量为10~50重量%,粘土的用量为10~50重量%,粘结剂以氧化物计的用量为5~35重量%,大孔基质的用量为0~25重量%。
14.根据权利要求12或13所述的制备方法,其中,所述催化剂浆液的固含量在40重量%以上,优选为40重量%~55重量%。
15.权利要求12-14中任意一项所述的制备方法得到的催化裂化催化剂。