CN107144704A - A kind of self-driven ultraviolet light senses integrated system with wind speed - Google Patents
A kind of self-driven ultraviolet light senses integrated system with wind speed Download PDFInfo
- Publication number
- CN107144704A CN107144704A CN201710272624.2A CN201710272624A CN107144704A CN 107144704 A CN107144704 A CN 107144704A CN 201710272624 A CN201710272624 A CN 201710272624A CN 107144704 A CN107144704 A CN 107144704A
- Authority
- CN
- China
- Prior art keywords
- self
- driven
- detector
- ultraviolet light
- current value
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a kind of self-driven ultraviolet light and senses integrated system with wind speed, the system self-driven can detect ultraviolet light and air flow in environment, and the visualization of ultraviolet light and wind number can be realized, self-driven ultraviolet detector funtion part is the hetero-junctions based on zinc-oxide film and nickel oxide film formation, the built in field of heterojunction regions drives photo-generated carrier hole to separation, so as to realize self-driven ultraviolet detector, self-driven wind speed detecting function is based partially on a kind of friction nanometer power generator of contact separation formula, polytetrafluoroethylene (PTFE) and aluminium foil are respectively at the two ends of frictional series, it is separate both when there is air flow and produces electric current, and when speed air flow is different, the current value of generation is different, current acquisition and analysis by Labview softwares, size contrast is carried out to the current value and default current threshold collected, light the bulb of the different colours on different software interface, the ultraviolet light and wind in detection environment are visualized with this.
Description
Technical field
The invention belongs to nano functional device preparation field, and in particular to a kind of self-driven ultraviolet light senses integrated with wind speed
System.
Background technology
Self-driven nano-device has small volume, and performance is stable, and the low advantage of energy consumption is widely used in environment measuring,
The fields such as health monitoring, such as ultraviolet detection, wind detection, internal enzyme concentration detection, human body temperature detection etc..But simple function
Device can only detect a type of signal, increasingly complicated detection environment is not suitable for, so Multifunctional detector part becomes
It is highly desirable.
Ultraviolet detector has very important effect in fields such as military and civilians, on civilian, and it can be used to monitor
Petroleum pollution in ocean, flame detecting etc.;Militarily, available for ultraviolet guidance, optical communication etc..Over entering year, due to energy crisis,
People increasingly pay close attention to self-driven nano-device.Self-driven ultraviolet light detector is mainly divided to the major class of position two:One class is to be based on
Hetero-junctions a, class is to construct a kind of self-driven nanosystems.Zinc oxide is as a kind of direct band gap wide bandgap semiconductor, and forbidden band is wide
Degree reaches 3.37eV, and its exciton bind energy reaches 60meV, is a kind of good material for ultraviolet detection.Based on ZnO heterojunction from
Driving ultraviolet light detector can be divided into Schottky type, pn types etc..
Following mechanism can be based on by constructing the sensor of power or motion:Piezo-electric effect, piezoresistive effect and triboelectrification effect.Its
In the motion sensor based on triboelectrification effect there is low manufacture cost, service life is long, the advantage such as power density height.It is based on
Humidity in the wind that the motion sensor that triboelectrification effect is constructed can be used in the pulse of detection human body, nature, environment, weight
Ion etc..
The visualization of signal plays an important role in the application field of sensor.Signal progress visualization can be improved into people
To the monitoring efficiency of signal in environment, signal visualization is applied to robotics by people, and man-machine interface, the simulation of tactile shows
Show.
Based on above research background, a kind of detection system of self-driven visualization ultraviolet light and wind of our design constructions,
The self-driven detection system can realize self-driven ultraviolet detector, wind speed detection, and can visualize both signals.
The content of the invention
In order to solve the above problems, the present invention provides a kind of self-driven ultraviolet light and senses integrated system, the system with wind speed
System prepares two self-driven devices simultaneously in same substrate, is that self-driven ultraviolet light detector is detected with wind speed respectively
Device, and the two self-driven devices are integrated into one, a self-driven Multifunctional detector part is constructed out, is passed through
The current value that Labview software interfaces are produced to device is analyzed, so as to complete ultraviolet detector and wind speed detection;
Further, the system includes self-driven detection ultraviolet light detector, self-driven anemometer detector and integrated analysis list
Member, the self-driven detection ultraviolet light detector and self-driven anemometer detector are all connected with integrated analysis unit;
Self-driven detection ultraviolet light detector, the self-driven detection ultraviolet light detector can self-driven detection ultraviolet signal;
Self-driven anemometer detector, the self-driven anemometer detector can self-driven probe wind signal;
Integrated analysis unit, the integrated analysis unit is adopted to self-driven detection ultraviolet light detector and self-driven anemometer detector
The signal collected carries out integrated and analysis, and carries out the differentiation visualization of signal;
Further, self-driven ultraviolet detector funtion part is to be based on zinc oxide in the self-driven detection ultraviolet light detector
Film and the hetero-junctions of nickel oxide film formation, the built in field of heterojunction regions drive photo-generated carrier hole to separation, so that
Realize self-driven ultraviolet detector;
Further, self-driven probe wind semiotic function is based on a kind of contact separation formula in the self-driven anemometer detector
Friction nanometer power generator, by the way that polytetrafluoroethylene (PTFE) and aluminium foil to be separately positioned on to the two ends of frictional series, when there is air flow
The two, which separate, produces electric current, when speed air flow is different, and the current value of generation is different, so as to determine wind speed;
Further, the current value that the integrated analysis unit is produced by Labview software interfaces to device is analyzed, right
The size of the current value collected carries out size with the current threshold set and compared, when current value is in different current thresholds
During scope, the bulb of software interface different colours is triggered and lighted;
Further, the self-driven detection ultraviolet light detector construction method is as follows:
S11:By electro-conductive glass FTO substrates in acetone, ethanol is cleaned by ultrasonic 10 minutes in deionized water, dried up with nitrogen successively
It is standby;
S12:A part of base conductive face is blocked, sputtering zinc oxide, nickel oxide, ITO sputtering work(are set in magnetron sputtering apparatus
Rate is respectively 80W, and 150W, 75W, operating pressure are set to 1Pa, are sputtered;
S13:The insulating tape pasted in substrate is torn, the silver paste in the region point that FTO exposes, extraction wire;
S14:The silver paste on point on the ITO conductive electrodes of sputtering, extraction wire obtains self-driven ultraviolet detector;
Further, the construction method of the self-driven anemometer detector is as follows:
S21:One layer of aluminium foil is pasted in the non-conductive face of same substrate used in step s 12, is used as one of anemometer detector
Electrode;
S22:The glass plate of identical size is separately taken, and in pasting one layer of aluminium foil on glass plate, is used as another of anemometer detector
Electrode;
S23:The acrylic board of 0.5cm × 0.5cm × 8cm sizes is cut out, 4 altogether, as the supporter of device, and institute is used
State 4 acrylic bars and support two pieces of glass plates;
S24:The middle section between the two pieces of glass plates supported, one end of fixed teflon plate, and from two aluminium flakes
Upper extraction wire respectively, is connected on rectifier bridge, that is, obtains self-driven anemometer detector;
Further, the differentiation method for visualizing of the integrated of the integrated analysis unit, analysis and signal is as follows:
S31:The current value tested first under current value of the device in certain ultraviolet light intensity, certain wind speed, and ultraviolet light and wind
Current value in the presence of speed is equal;
S32:3 current thresholds are set in LabView softwares, I1, I2, I3 are designated as respectively;When wherein I1 is only ultraviolet light
Current value, I2 acts on the current value of device for only wind, and I2 is when simultaneously certain wind speed and the ultraviolet light of certain light intensity are made
When using on device, the current value that device is produced;
S33:Edit routine makes to reach claimed below, and electric current is in when being less than I1, and red bulb is lighted, and current value is in I1 and I2
Between when starboard sidelight: green bulb light, current value when being more than I3 blue bulb light;
Beneficial effects of the present invention are as follows:
1)The built in field of heterojunction regions can drive photo-generated carrier hole to separation, so as to realize that self-driven ultraviolet light is visited
Survey;
2)Self-driven wind speed detecting function part is based on a kind of friction nanometer power generator of contact separation formula, based on polytetrafluoroethyl-ne
Alkene and aluminium foil are respectively at the two ends of frictional series, are separate both when there is air flow and produce electric current, and work as air stream
When dynamic speed is different, the current value of generation is different;
3)Size contrast is carried out with default current threshold according to the current value collected, the difference on different software interface is lighted
The bulb of color, the ultraviolet light and wind in detection environment are visualized with this;
4)It self-driven can detect the ultraviolet light and air flow in environment;
5)The visualization of both ultraviolet light and wind signal can be realized.
Brief description of the drawings
Fig. 1 is the structural representation of the self-driven multi-functional detection system constructed by the present invention;
Fig. 2 is the present invention to ultraviolet light(365nm)Periodic response figure;
Response currents of the Fig. 3 for the present invention under different wind speed;
Fig. 4 is the corresponding external condition diagram of visual signals lamp of the present invention.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, it is right below in conjunction with drawings and Examples
The present invention is explained in further detail.It should be appreciated that specific embodiment described herein is used only for explaining the present invention, and
It is not used in the restriction present invention.On the contrary, the present invention cover it is any be defined by the claims the present invention spirit and scope on do
Replacement, modification, equivalent method and scheme.Further, in order that the public has a better understanding to the present invention, below to this
It is detailed to describe some specific detail sections in the detailed description of invention.It is thin without these for a person skilled in the art
The description of section part can also understand the present invention completely.
The invention will be further described with specific embodiment below in conjunction with the accompanying drawings, but not as a limitation of the invention.
Below most preferred embodiment is enumerated for the present invention:
As Figure 1-Figure 4, the present invention provides a kind of self-driven ultraviolet light and senses integrated system with wind speed, and the system is same
Two self-driven devices are prepared simultaneously in individual substrate, are self-driven ultraviolet light detector and anemometer detector respectively, and incite somebody to action
The two self-driven devices are integrated into one, construct out a self-driven Multifunctional detector part, pass through Labview softwares circle
The current value produced in face of device is analyzed, so as to complete ultraviolet detector and wind speed detection, the system includes self-driven
Detect ultraviolet light detector, self-driven anemometer detector and integrated analysis unit, the self-driven detection ultraviolet light detector and
Self-driven anemometer detector is all connected with integrated analysis unit;
Self-driven detection ultraviolet light detector, the self-driven detection ultraviolet light detector can self-driven detection ultraviolet signal;
Self-driven anemometer detector, the self-driven anemometer detector can self-driven probe wind signal;
Integrated analysis unit, the integrated analysis unit is adopted to self-driven detection ultraviolet light detector and self-driven anemometer detector
The signal collected carries out integrated and analysis, and carries out the differentiation visualization of signal.
Self-driven ultraviolet detector funtion part is to be based on zinc-oxide film in the self-driven detection ultraviolet light detector
With the hetero-junctions of nickel oxide film formation, the built in field of heterojunction regions drives photo-generated carrier hole to separation, so as to realize
Self-driven ultraviolet detector.
Self-driven probe wind semiotic function is based on a kind of friction of contact separation formula in the self-driven anemometer detector
Nano generator, by the way that polytetrafluoroethylene (PTFE) and aluminium foil to be separately positioned on to the two ends of frictional series, both when there is air flow
It separate and produces electric current, when speed air flow is different, the current value of generation is different, so as to determine wind speed.
The current value that the integrated analysis unit is produced by Labview software interfaces to device is analyzed, to collection
The size of the current value arrived carries out size with the current threshold set and compared, when current value is in the scope of different current thresholds
When, trigger and light the bulb of software interface different colours.
The self-driven detection ultraviolet light detector construction method is as follows:
S11:By electro-conductive glass FTO substrates in acetone, ethanol is cleaned by ultrasonic 10 minutes in deionized water, dried up with nitrogen successively
It is standby;
S12:A part of base conductive face is blocked, sputtering zinc oxide, nickel oxide, ITO sputtering work(are set in magnetron sputtering apparatus
Rate is respectively 80W, and 150W, 75W, operating pressure are set to 1Pa, are sputtered;
S13:The insulating tape pasted in substrate is torn, the silver paste in the region point that FTO exposes, extraction wire;
S14:The silver paste on point on the ITO conductive electrodes of sputtering, extraction wire obtains self-driven ultraviolet detector.
The construction method of the self-driven anemometer detector is as follows:
S21:One layer of aluminium foil is pasted in the non-conductive face of same substrate used in step s 12, is used as one of anemometer detector
Electrode;
S22:The glass plate of identical size is separately taken, and in pasting one layer of aluminium foil on glass plate, is used as another of anemometer detector
Electrode;
S23:The acrylic board of 0.5cm × 0.5cm × 8cm sizes is cut out, 4 altogether, as the supporter of device, and institute is used
State 4 acrylic bars and support two pieces of glass plates;
S24:The middle section between the two pieces of glass plates supported, one end of fixed teflon plate, and from two aluminium flakes
Upper extraction wire respectively, is connected on rectifier bridge, that is, obtains self-driven anemometer detector.
The differentiation method for visualizing of the integrated of the integrated analysis unit, analysis and signal is as follows:
S31:The current value tested first under current value of the device in certain ultraviolet light intensity, certain wind speed, and ultraviolet light and wind
Current value in the presence of speed is equal;
S32:3 current thresholds are set in LabView softwares, I1, I2, I3 are designated as respectively;When wherein I1 is only ultraviolet light
Current value, I2 acts on the current value of device for only wind, and I2 is when simultaneously certain wind speed and the ultraviolet light of certain light intensity are made
When using on device, the current value that device is produced;
S33:Edit routine makes to reach claimed below, and electric current is in when being less than I1, and red bulb is lighted, and current value is in I1 and I2
Between when starboard sidelight: green bulb light, current value when being more than I3 blue bulb light.
Embodiment 1
(1)The structure of self-driven ultraviolet light detector:A. by electro-conductive glass FTO substrates in acetone, ethanol, in deionized water according to
It is secondary to be cleaned by ultrasonic 10 minutes, dried up with nitrogen standby;B. a part of base conductive face is blocked, is set in magnetron sputtering apparatus
Sputtering zinc oxide, nickel oxide, ITO sputtering powers are respectively 80W, and 150W, 75W, operating pressure are set to 1Pa, are sputtered;
C. the insulating tape pasted in substrate is torn, the silver paste in the region point that FTO exposes, extraction wire;D. in the ITO of sputtering
Upper silver paste is put on conductive electrode, extraction wire obtains self-driven ultraviolet detector.
(2)The structure of self-driven anemometer detector:A. in step(1)In the non-conductive face of used same substrate paste
One layer of aluminium foil, is used as an electrode of anemometer detector;B. the glass plate of identical size is separately taken, and in pasting one on glass plate
Layer aluminium foil, is used as another electrode of anemometer detector;C. the acrylic board of 0.5cm × 0.5cm × 8cm sizes is cut out,
4 altogether, two pieces of glass plates are supported as the supporter of device, and with the acrylic bar of this 4 certain sizes;D. in branch
Middle section between the two pieces of glass plates come, one end of fixed teflon plate are propped up, and extraction is led respectively from two aluminium flakes
Line, is connected on rectifier bridge, that is, obtains self-driven anemometer detector.
(3)The design and application of visualization interface:A. current value of the device in certain ultraviolet light intensity is tested first, necessarily
Current value under wind speed, and ultraviolet light and wind speed it is equal in the presence of current value;B., 3 electric currents are set in LabView softwares
Threshold value, is designated as I1, I2, I3 respectively.Current value when wherein I1 is only ultraviolet light, I2 acts on the electricity of device for only wind
Flow valuve, I2 is the current value that device is produced when certain wind speed and the ultraviolet light of certain light intensity are applied on device simultaneously; c.
Edit routine makes to reach claimed below, and electric current is in when being less than I1, and red bulb is lighted, and current value is green when being between I1 and I2
Colored lights bubble is lighted, and blue bulb is lighted when current value is more than I3.
Embodiment 2:
(1)The structure of self-driven ultraviolet light detector:A. by electro-conductive glass ITO substrate in acetone, ethanol, in deionized water according to
It is secondary to be cleaned by ultrasonic 10 minutes, dried up with nitrogen standby;B. a part of base conductive face is blocked, is set in magnetron sputtering apparatus
Sputtering zinc oxide, nickel oxide, ITO sputtering powers are respectively 80W, and 120W, 75W, operating pressure are set to 1Pa, are sputtered;
C. the insulating tape pasted in substrate is torn, the silver paste in the region point that FTO exposes, extraction wire;D. in the ITO of sputtering
Upper silver paste is put on conductive electrode, extraction wire obtains self-driven ultraviolet detector.
(2)The structure of self-driven anemometer detector:A. in step(1)In the non-conductive face of used same substrate paste
One layer of copper foil, is used as an electrode of anemometer detector;B. the glass plate of identical size is separately taken, and in pasting one on glass plate
Layer copper foil, is used as another electrode of anemometer detector;C. the acrylic board of 0.5cm × 0.5cm × 8cm sizes is cut out,
4 altogether, two pieces of glass plates are supported as the supporter of device, and with the acrylic bar of this 4 certain sizes;D. in branch
Middle section between the two pieces of glass plates come, one end of fixed polyethyleneimine, and the extraction wire respectively from two aluminium flakes are propped up,
It is connected on rectifier bridge, that is, obtains self-driven anemometer detector.
(3)The design and application of visualization interface:A. ultraviolet light intensity of the device under another light intensity is tested first
Current value, the current value under another wind speed size, and ultraviolet light and wind speed it is equal in the presence of current value;B. in LabView
3 current thresholds are set in software, I1, I2, I3 are designated as respectively.Current value when wherein I1 is only ultraviolet light, I2 is only
Wind acts on the current value of device, and I2 is the device when certain wind speed and the ultraviolet light of certain light intensity are applied on device simultaneously
The current value of generation;C. edit routine makes to reach claimed below, and electric current is in when being less than I1, and red bulb is lighted, current value
Starboard sidelight: green bulb is lighted when between I1 and I2, and blue bulb is lighted when current value is more than I3.
Embodiment 3:
(1)The structure of self-driven ultraviolet light detector:A. by electro-conductive glass ITO substrate in acetone, ethanol, in deionized water according to
It is secondary to be cleaned by ultrasonic 10 minutes, dried up with nitrogen standby;B. a part of base conductive face is blocked, is set in magnetron sputtering apparatus
Sputtering zinc oxide, nickel oxide, ITO sputtering powers are respectively 80W, and 120W, 75W, operating pressure are set to 1Pa, are sputtered;
C. the insulating tape pasted in substrate is torn, the gold paste in the region point that FTO exposes, extraction wire;D. in the ITO of sputtering
Upper gold paste is put on conductive electrode, extraction wire obtains self-driven ultraviolet detector.
(2)The structure of self-driven anemometer detector:A. in step(1)In the non-conductive face of used same substrate paste
One layer of copper foil, is used as an electrode of anemometer detector;B. the glass plate of identical size is separately taken, and in pasting one on glass plate
Layer copper foil, is used as another electrode of anemometer detector;C. the acrylic board of 0.5cm × 0.5cm × 8cm sizes is cut out,
4 altogether, two pieces of glass plates are supported as the supporter of device, and with the acrylic bar of this 4 certain sizes;D. in branch
Middle section between the two pieces of glass plates come, one end of fixed polyethyleneimine, and the extraction wire respectively from two aluminium flakes are propped up,
It is connected on rectifier bridge, that is, obtains self-driven anemometer detector.
(3)The design and application of visualization interface:A. ultraviolet light intensity of the device under another light intensity is tested first
Current value, the current value under another wind speed size, and ultraviolet light and wind speed it is equal in the presence of current value;B. in LabView
3 current thresholds are set in software, I1, I2, I3 are designated as respectively.Current value when wherein I1 is only ultraviolet light, I2 is only
Wind acts on the current value of device, and I2 is the device when certain wind speed and the ultraviolet light of certain light intensity are applied on device simultaneously
The current value of generation;C. edit routine makes to reach claimed below, and electric current is in when being less than I1, and red bulb is lighted, current value
Starboard sidelight: green bulb is lighted when between I1 and I2, and blue bulb is lighted when current value is more than I3.
One kind of embodiment described above, simply more preferably embodiment of the invention, those skilled in the art
The usual variations and alternatives that member is carried out in the range of technical solution of the present invention all should be comprising within the scope of the present invention.
Claims (8)
1. a kind of self-driven ultraviolet light senses integrated system with wind speed, it is characterised in that the system is same in same substrate
When prepare two self-driven devices, be self-driven ultraviolet light detector and anemometer detector respectively, and by the two self-powereds
Dynamic device is integrated into one, constructs out a self-driven Multifunctional detector part, and device is produced by Labview software interfaces
Raw current value is analyzed, so as to complete ultraviolet detector and wind speed detection.
2. system according to claim 1, it is characterised in that the system include self-driven detection ultraviolet light detector,
Self-driven anemometer detector and integrated analysis unit, the self-driven detection ultraviolet light detector and self-driven anemometer detector are equal
Connect integrated analysis unit;
Self-driven detection ultraviolet light detector, the self-driven detection ultraviolet light detector can self-driven detection ultraviolet signal;
Self-driven anemometer detector, the self-driven anemometer detector can self-driven probe wind signal;
Integrated analysis unit, the integrated analysis unit is adopted to self-driven detection ultraviolet light detector and self-driven anemometer detector
The signal collected carries out integrated and analysis, and carries out the differentiation visualization of signal.
3. system according to claim 2, it is characterised in that self-driven purple in the self-driven detection ultraviolet light detector
Outer optical detection funtion part is the hetero-junctions based on zinc-oxide film and nickel oxide film formation, and the built in field of heterojunction regions drives
Make photo-generated carrier hole to separation, so as to realize self-driven ultraviolet detector.
4. system according to claim 2, it is characterised in that self-driven detection wind in the self-driven anemometer detector
Number function is, based on a kind of friction nanometer power generator of contact separation formula, to be rubbed by the way that polytetrafluoroethylene (PTFE) and aluminium foil are separately positioned on
The two ends of sequence are wiped, is separate both when there is air flow and produces electric current, when speed air flow is different, generation
Current value is different, so as to determine wind speed.
5. system according to claim 2, it is characterised in that the integrated analysis unit passes through Labview software interfaces
The current value that device is produced is analyzed, size ratio is carried out to the size of current value and the current threshold of setting collected
Compared with, when current value be in different current thresholds scope when, trigger and light the bulb of software interface different colours.
6. system according to claim 3, it is characterised in that the self-driven detection ultraviolet light detector construction method is such as
Under:
S11:By electro-conductive glass FTO substrates in acetone, ethanol is cleaned by ultrasonic 10 minutes in deionized water, dried up with nitrogen successively
It is standby;
S12:A part of base conductive face is blocked, sputtering zinc oxide, nickel oxide, ITO sputtering work(are set in magnetron sputtering apparatus
Rate is respectively 80W, and 150W, 75W, operating pressure are set to 1Pa, are sputtered;
S13:The insulating tape pasted in substrate is torn, the silver paste in the region point that FTO exposes, extraction wire;
S14:The silver paste on point on the ITO conductive electrodes of sputtering, extraction wire obtains self-driven ultraviolet detector.
7. system according to claim 6, it is characterised in that the construction method of the self-driven anemometer detector is as follows:
S21:One layer of aluminium foil is pasted in the non-conductive face of same substrate used in step s 12, is used as one of anemometer detector
Electrode;
S22:The glass plate of identical size is separately taken, and in pasting one layer of aluminium foil on glass plate, is used as another of anemometer detector
Electrode;
S23:The acrylic board of 0.5cm × 0.5cm × 8cm sizes is cut out, 4 altogether, as the supporter of device, and institute is used
State 4 acrylic bars and support two pieces of glass plates;
S24:The middle section between the two pieces of glass plates supported, one end of fixed teflon plate, and from two aluminium flakes
Upper extraction wire respectively, is connected on rectifier bridge, that is, obtains self-driven anemometer detector.
8. system according to claim 7, it is characterised in that the integrated of the integrated analysis unit, analysis and signal
Distinguish method for visualizing as follows:
S31:The current value tested first under current value of the device in certain ultraviolet light intensity, certain wind speed, and ultraviolet light and wind
Current value in the presence of speed is equal;
S32:3 current thresholds are set in LabView softwares, I1, I2, I3 are designated as respectively;When wherein I1 is only ultraviolet light
Current value, I2 acts on the current value of device for only wind, and I2 is when simultaneously certain wind speed and the ultraviolet light of certain light intensity are made
When using on device, the current value that device is produced;
S33:Edit routine makes to reach claimed below, and electric current is in when being less than I1, and red bulb is lighted, and current value is in I1 and I2
Between when starboard sidelight: green bulb light, current value when being more than I3 blue bulb light.