CN107141710A - A kind of production technology of antibiosis anti-cracking plastic tub - Google Patents
A kind of production technology of antibiosis anti-cracking plastic tub Download PDFInfo
- Publication number
- CN107141710A CN107141710A CN201710497544.7A CN201710497544A CN107141710A CN 107141710 A CN107141710 A CN 107141710A CN 201710497544 A CN201710497544 A CN 201710497544A CN 107141710 A CN107141710 A CN 107141710A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic tub
- production technology
- antibiosis anti
- cracking plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of production technology of antibiosis anti-cracking plastic tub.The raw material of the antibiosis anti-cracking plastic tub is according to weight ratio：40 50 parts of phenolic resin, 22 28 parts of polyethylene, 15 25 parts of ethylene-propylene-diene monomer rubber powder, 10 12 parts of polyolefin elastomer, 46 parts of antibacterial powder, 10 12 parts of alum.Production technology is as follows：Step one：Weigh 45 parts of phenolic resin, 25 parts of polyethylene, 20 parts of ethylene-propylene-diene monomer rubber powder, 11 parts of polyolefin elastomer, 5 parts of antibacterial powder, 11 parts of alum；Step 2：Step one gained raw material is heated at high temperature to and dissolves into liquid condition, temperature is at 130 150 degrees Celsius；Step 3：By the compound of fusing by streamline automatically into injection mold, by filling, pressing mold, pressurize, cooling, warpage, take off fiery program making and be molded；Step 4：Quality inspection, qualified products packaging and storage.It is convenient that the antibiosis anti-cracking plastic tub is prepared using production mould, and cheap, the effect with antibacterial dedusting is solid firm, is hardly damaged, can use for a long time, wide market.
Description
Technical field
The present invention relates to a kind of production technology of antibiosis anti-cracking plastic tub, belong to plastic tub production field.
Background technology
Plastics almost spread over the big and small aspect of family life, provided for the life of people as a kind of new material
It is convenient, and plastic tub is even more indispensable in people's daily life with its light, waterproof, durable.But daily finding plastics
Basin, also usually can breed bacteria, women can be made by bacterium infection, facial long whelk etc..So antibiosis anti-cracking plastic tub
Produced to solve these problems.
The content of the invention
Present invention seek to address that there is provided a kind of production technology of antibiosis anti-cracking plastic tub, the antibiosis anti-cracking for above mentioned problem
The raw material of plastic tub is according to weight ratio：40-50 parts of phenolic resin, 22-28 parts of polyethylene, 15-25 parts of ethylene-propylene-diene monomer rubber powder,
10-12 parts of polyolefin elastomer, 4-6 parts of antibacterial powder, 10-12 parts of alum.
The present invention is reaches that the technical scheme that above-mentioned technical purpose is used is：Production technology is as follows：
Step one：Weigh 45 parts of phenolic resin, 25 parts of polyethylene, 20 parts of ethylene-propylene-diene monomer rubber powder, polyolefin elastomer
POE11 parts, 5 parts of antibacterial powder, 11 parts of alum；
Step 2：Step one gained raw material is heated at high temperature to and dissolves into liquid condition, temperature is at 130-150 degrees Celsius；
Step 3：Compound obtained by step 2 is passed through into filling, pressing mold, guarantor by streamline automatically into injection mold
Pressure, cooling, warpage, take off the shaping of fiery program making；
Step 4：Quality inspection, qualified products packaging and storage.
It is convenient that antibiosis anti-cracking plastic tub of the present invention is prepared using production mould, cheap, the effect with antibacterial dedusting,
It is solid firm, it is hardly damaged, can uses for a long time, wide market.
Embodiment
Embodiment 1：
A kind of production technology of antibiosis anti-cracking plastic tub, the raw material of the antibiosis anti-cracking plastic tub is according to weight ratio：Phenolic aldehyde
40-50 parts of resin, 22-28 parts of polyethylene, 15-25 parts of ethylene-propylene-diene monomer rubber powder, 10-12 parts of polyolefin elastomer, antibacterial powder
4-6 parts, 10-12 parts of alum.
Production technology is as follows：
Step one：Weigh 40 parts of phenolic resin, 22 parts of polyethylene, 15 parts of ethylene-propylene-diene monomer rubber powder, polyolefin elastomer
POE10 parts, 4 parts of antibacterial powder, 10 parts of alum；
Step 2：Step one gained raw material is heated at high temperature to and dissolves into liquid condition, temperature is at 130-150 degrees Celsius；
Step 3：Compound obtained by step 2 is passed through into filling, pressing mold, guarantor by streamline automatically into injection mold
Pressure, cooling, warpage, take off the shaping of fiery program making；
Step 4：Quality inspection, qualified products packaging and storage.
It is preferred that, the temperature in step 2 is 130 degrees Celsius.
Embodiment 2：
A kind of production technology of antibiosis anti-cracking plastic tub, the raw material of the antibiosis anti-cracking plastic tub is according to weight ratio：Phenolic aldehyde
40-50 parts of resin, 22-28 parts of polyethylene, 15-25 parts of ethylene-propylene-diene monomer rubber powder, 10-12 parts of polyolefin elastomer, antibacterial powder
4-6 parts, 10-12 parts of alum.
Production technology is as follows：
Step one：Weigh 50 parts of phenolic resin, 28 parts of polyethylene, 25 parts of ethylene-propylene-diene monomer rubber powder, polyolefin elastomer
POE12 parts, 6 parts of antibacterial powder, 12 parts of alum；
Step 2：Step one gained raw material is heated at high temperature to and dissolves into liquid condition, temperature is at 130-150 degrees Celsius；
Step 3：Compound obtained by step 2 is passed through into filling, pressing mold, guarantor by streamline automatically into injection mold
Pressure, cooling, warpage, take off the shaping of fiery program making；
Step 4：Quality inspection, qualified products packaging and storage.
It is preferred that, the temperature in step 2 is 150 degrees Celsius.
Claims (3)
1. a kind of production technology of antibiosis anti-cracking plastic tub, it is characterised in that the raw material of the antibiosis anti-cracking plastic tub is according to weight
Than for：40-50 parts of phenolic resin, 22-28 parts of polyethylene, 15-25 parts of ethylene-propylene-diene monomer rubber powder, polyolefin elastomer 10-12
Part, 4-6 parts of antibacterial powder, 10-12 parts of alum.
2. a kind of production technology of antibiosis anti-cracking plastic tub, it is characterised in that production technology is as follows：Step one：Weigh phenolic aldehyde tree
45 parts of fat, 25 parts of polyethylene, 20 parts of ethylene-propylene-diene monomer rubber powder, 11 parts of polyolefin elastomer, 5 parts of antibacterial powder, 11 parts of alum；
Step 2：Step one gained raw material is heated at high temperature to and dissolves into liquid condition, temperature is at 130-150 degrees Celsius；Step 3：Will
Compound obtained by step 2 automatically into injection mold, by filling, pressing mold, pressurize, cooling, warpage, takes off fire by streamline
Program making is molded；Step 4：Quality inspection, qualified products packaging and storage.
3. a kind of production technology of antibiosis anti-cracking plastic tub according to claim 2, it is characterised in that the temperature in step 2
Spend for 140 degrees Celsius.